Influence of the water to cement ratio W/C on the compressive strength of concrete ? An application of the cement hydration equation to concrete

1996 ◽  
Vol 3 (5) ◽  
pp. 335-343 ◽  
Author(s):  
K. K. Sideris ◽  
M. Konsta-Gdoutos
Keyword(s):  
Compressive Strength ◽  
Cement Hydration ◽  
Cement Ratio ◽  
Water To Cement Ratio ◽  
Compressive Strength Of Concrete

scholarly journals Influence of cement replacement with limestone filler on the properties of concrete

2021 ◽  
Vol 64 (3) ◽  
pp. 165-170
Author(s):  
Ksenija Tešić ◽  
Snežana Marinković ◽  
Aleksandar Savić
Keyword(s):  
Particle Size ◽  
Compressive Strength ◽  
Mineralogical Composition ◽  
Limestone Filler ◽  
Green Concrete ◽  
Cement Ratio ◽  
Cement Replacement ◽  
Concrete Mixtures ◽  
Water To Cement Ratio ◽  
Compressive Strength Of Concrete

This paper presents an experimental research of one type of green concrete in which Portland cement was replaced with two types of limestone filler of the same origin and mineralogical composition, but with a different fineness of particles. Ten concrete mixtures were designed in which 0%, 15%, 30% and 45% (by mass) of cement were replaced with filler. The water to cement ratio for each mixture was constant (w/c=0.54), and the water to powder ratio was decreasing with increasing cement replacement. Particle size distribution was selected using Funk and Dinger, as well as using Fuller's model. The results showed that it is possible to increase the compressive strength of concrete by reducing 45% of cement, but further research should be focused on improving the workability.

Experimental Study on Sand and Cement Replacement by Termite Mound Soil

2019 ◽  
pp. 279-287
Author(s):  
Harish R ◽  
Ramesh S ◽  
Tharani A ◽  
Mageshkumar P
Keyword(s):  
Experimental Study ◽  
Experimental Investigation ◽  
Compressive Strength ◽  
Natural Environment ◽  
Fine Aggregate ◽  
Test Results ◽  
Termite Mound ◽  
Cement Concrete ◽  
Cement Ratio ◽  
Compressive Strength Of Concrete

This paper presents the results of an experimental investigation of the compressive strength of concrete cubes containing termite mound soil. The specimens were cast using M20 grade of concrete. Two mix ratios for replacement of sand and cement are of 1:1.7:2.7 and 1:1.5:2.5 (cement: sand: aggregate) with water- cement ratio of 0.45 and varying combination of termite mound soil in equal amount ranging from 30% and 40% replacing fine aggregate (sand) and cement from 10%,15%,20% were used. A total of 27 cubes, 18 cylinders and 6 beams were cast by replacing fine aggregate, specimens were cured in water for 7,14 and 28 days. The test results showed that the compressive strength of the concrete cubes increases with age and decreases with increasing percentage replacement of cement and increases with increasing the replacement of sand with termite mound soil cured in water. The study concluded that termite mound cement concrete is adequate to use for construction purposes in natural environment.

scholarly journals Effect of Water Cement Ratios on Compressive Strength of Palm Kernel Shell Concrete

2019 ◽  
Vol 2 (Issue 1) ◽  
Author(s):  
A.O Adeyemi ◽  
M.A Anifowose ◽  
I.O Amototo ◽  
S.A Adebara ◽  
M.Y Olawuyi
Keyword(s):  
Compressive Strength ◽  
Coarse Aggregate ◽  
Fresh Concrete ◽  
Palm Kernel ◽  
Hardened Concrete ◽  
Cement Ratio ◽  
Water Cement Ratio ◽  
Palm Kernel Shell ◽  
Compressive Strength Of Concrete ◽  
Palm Kernel Shells

This study examined the effect of varying water cement ratio on the compressive strength of concrete produced using palm kernel shell (PKS) as coarse aggregate at different replacement levels. The replacement levels of coarse aggregate with palm kernel shells (PKS) were 0%, 25%, 50%, and 100% respectively. PKS concrete cubes (144 specimens) of sizes 150mm x 150mm x 150mm were cast and cured in water for 7, 14, 21 and 28 days respectively. A mix ratio of 1:2:4 was adopted with water-cement ratio of 0.45, 0.5, and 0.6 respectively while the batching was done by weight. Slump test was conducted on fresh concrete while compressive strength test was carried out on the hardened concrete cubes using a compression testing machine of 2000kN capacity. The result of tests on fresh concrete shows that the slump height of 0.45 water cement ratio (w/c) increases with an increase in PKS%. This trend was similar to 0.50 and 0.60 w/c. However, the compressive strength of concrete cube decreases with an increase in w/c (from 0.45 to 0.60) but increases with respect to curing age and also decreases with increase in PKS%. Concrete with 0.45 water-cement ratio possess the highest compressive strength. It was observed that PKS is not a good substitute for coarse aggregate in mix ratio 1:2:4 for concrete productions. Hence, the study suggest the use of chemical admixture such as superplasticizer or calcium chloride in order to improve the strength of palm kernel shells-concrete.

Chloride Ingress Control and Promotion of Internal Curing in Concrete Using Superabsorbent Polymer

2021 ◽  
Vol 888 ◽  
pp. 67-75
Author(s):  
Ariel Verzosa Melendres ◽  
Napoleon Solo Dela Cruz ◽  
Araceli Magsino Monsada ◽  
Rolan Pepito Vera Cruz
Keyword(s):  
Compressive Strength ◽  
Cementitious Materials ◽  
Internal Curing ◽  
Mix Design ◽  
Chloride Ingress ◽  
Superabsorbent Polymer ◽  
Cement Slurry ◽  
Chloride Permeability ◽  
Cement Ratio ◽  
Water To Cement Ratio

Chloride ingress into concrete from the surrounding environment can result in the corrosion of the embedded steel reinforcement and cause damage to the concrete. Superabsorbent polymer (SAP) with fine particle size was incorporated into the structure of concrete for controlling the chloride ingress and improving its compressive strength via promotion of internal curing. The SAP used in this study was evaluated for its absorbency property when exposed to cementitious environment such as aqueous solution of Ca (OH)2 and cement slurry. The results were compared to that in sodium chloride solution, the environment where absorbency of most of the SAP found in the market are well studied. Results showed that although SAP absorbency decreased with increasing concentration of Ca (OH)2 and cement, the results suggest that water containing cementitious materials are able to be absorbed by SAP. Chloride ingress into 28-day cured concrete specimens were determined using Rapid Chloride Penetration Test (RCPT) method employing 60V DC driving force. Concrete samples with size of 50 mm height x 100 mm diameter were prepared using a M25 mix design with 0.4 and 0.45 water to cement ratios and different percentages of SAP such as 0.05%, 0.1% and 0.15% with respect to cement mass. Results showed that concrete with 0.15% SAP gave the best result with 14% less chloride permeability than concrete with no SAP for a 0.4 water to cement ratio. Concrete samples for compressive strength tests with size of 200 mm height x 100 mm diameter were prepared using the same mix design and percentages of SAP and cured for 28 days. Results showed that the best results for compressive strength was found at 0.1% SAP at a 0.4 water to cement ratio which can be attributed to internal curing provided by SAP.

scholarly journals Use of Recycled Tyre Rubber in Non-structural Concrete

2018 ◽  
Vol 203 ◽  
pp. 06001
Author(s):  
Muhammad Bilal Waris ◽  
Hussain Najwani ◽  
Khalifa Al-Jabri ◽  
Abdullah Al-Saidy
Keyword(s):  
Compressive Strength ◽  
Water Absorption ◽  
Coarse Aggregate ◽  
Partial Replacement ◽  
Fine Aggregate ◽  
Structural Concrete ◽  
Cement Ratio ◽  
Mix Proportion ◽  
Water To Cement Ratio ◽  
Concrete Blocks

To manage tyre waste and conserve natural aggregate resource, this research investigates the use of waste tyre rubber as partial replacement of fine aggregates in non-structural concrete. The research used Taguchi method to study the influence of mix proportion, water-to-cement ratio and tyre rubber replacement percentage on concrete. Nine mixes were prepared with mix proportion of 1:2:4, 1:5:4 and 1:2.5:3; water-to-cement ratio of 0.25, 0.35 and 0.40 and rubber to fine aggregate replacement of 20%, 30% and 40%. Compressive strength and water absorption tests were carried out on 100 mm cubes. Compressive strength was directly proportional to the amount of coarse aggregate in the mix. Water-to-cement ratio increased the strength within the range used in the study. Strength was found to be more sensitive to the overall rubber content than the replacement ratio. Seven out of the nine mixes satisfied the minimum strength requirement for concrete blocks set by ASTM. Water absorption and density for all mixes satisfied the limits applicable for concrete blocks. The study indicates that mix proportions with fine to coarse aggregate ratio of less than 1.0 and w/c ratio around 0.40 can be used with tyre rubber replacements of up to 30 % to satisfy requirements for non-structural concrete.

Effects of Fly Ash Addition on Compressive Strength and Flexural Strength of Foamed Cement Composites

2013 ◽  
Vol 795 ◽  
pp. 664-668 ◽  
Author(s):  
Roshasmawi Abdul Wahab ◽  
Mohd Noor Mazlee ◽  
Shamsul Baharin Jamaludin ◽  
Khairul Nizar Ismail
Keyword(s):  
Mechanical Properties ◽  
Compressive Strength ◽  
Fly Ash ◽  
Flexural Strength ◽  
Cement Composites ◽  
Volume Percent ◽  
Foaming Agent ◽  
Cement Ratio ◽  
Water To Cement Ratio

In this study, the mixing of polystyrene (PS) beads and fly ash as a sand replacement material in foamed cement composites (FCC) has been investigated. Specifically, the mechanical properties such as compressive strength and flexural strength were measured. Different proportions of fly ash were added in cement composites to replace the sand proportion at 3 wt. %, 6 wt. %, 9 wt. % and 12 wt. % respectively. The water to cement ratio was fixed at 0.65 meanwhile ratios of PS beads used was 0.25 volume percent of samples as a foaming agent. All samples at different mixed were cured at 7 and 28 days respectively. Based on the results of compressive strength, it was found that the compressive strength was increased with the increasing addition of fly ash. Meanwhile, flexural strength was decreased with the increasing addition of fly ash up to 9 wt. %. The foamed cement composites with 12 wt. % of fly ash produced the highest strength of compressive strength meanwhile 3 wt. % of fly ash produced the highest strength of flexural strength.

Dispersion and Absorption of SBR Latex in the System of Mono-Dispersed Cement Particles in Water

2013 ◽  
Vol 687 ◽  
pp. 347-353 ◽  
Author(s):  
Xiao Xin Shi ◽  
Ru Wang ◽  
Pei Ming Wang
Keyword(s):  
Cement Hydration ◽  
Single Layer ◽  
Optical Microscope ◽  
Solution Phase ◽  
Environmental Scanning ◽  
Cement Particle ◽  
Microstructure Formation ◽  
Cement Ratio ◽  
Water To Cement Ratio ◽  
Cement Based Materials

This paper investigates the dispersion of cement particles in water at different mix proportions using optical microscope, and the dispersion and absorption of SBR latex in the system of mono-dispersed cement particles in water using environmental scanning electron microscope (ESEM). The results show that the mono-dispersed cement can be well obtained at the water to cement ratio (mw/mc) of 10:1. The ESEM images present that SBR latex is dispersed on the surface of the cement particles as well as the solution phase. SBR latex does not prefer to be absorbed on the cement particles in spite of their opposite electric charge but chooses to be dispersed in the system proportionally. In addition, SBR particles are single-layer absorbed on the surface of cement particles in all the SBR latex to cement ratios (mp/mc). Several SBR particles absorbed on the surface of cement particle get close enough to form groups at the mp/mc of 15% and 20%. The results of this paper provide some bases for analyzing the influence of polymer on cement hydration and the microstructure formation of polymer-modified cement-based materials in a new view.

scholarly journals Resistencia de concreto con agregado de alta absorción y baja relación a/c

2012 ◽  
Vol 2 (1) ◽  
pp. 21-28
Author(s):  
R. G. Solís ◽  
E. Moreno ◽  
E. Arjona
Keyword(s):  
Compressive Strength ◽  
Coarse Aggregate ◽  
Construction Site ◽  
Cement Ratio ◽  
Limestone Aggregate ◽  
Concrete Mixtures ◽  
Water To Cement Ratio ◽  
Maximum Compressive Strength ◽  
Crushed Limestone ◽  
High Absorption

RESUMENLa resistencia del concreto depende de la calidad de la pasta de cemento y de las características de los agregados pétreos. La primera es controlada por la relación agua - cemento, mientras que las propiedades de los agregados generalmente no pueden ser manipuladas ya que se suele utilizar aquellos que están disponibles cerca de la construcción. En muchas regiones rocas con propiedades no deseables son utilizadas como agregado. Por lo tanto, el objetivo de este trabajo fue responder a la pregunta sobre cuál sería la máxima resistencia de diseño que se podría utilizar para concretos fabricados con un tipo específico de agregados obtenidos a partir de la trituración de roca caliza de alta absorción. Se probaron concretos con seis relaciones agua - cemento y dos tamaños de agregado grueso. Se concluyó que con los agregados estudiados es posible fabricar concretos de hasta 500 k/cm2 de f’c.Palabras clave: Absorción; agregados calizos; concreto; relación agua/cemento; resistencia.ABSTRACTConcrete strength depends on the cement paste quality and on the characteristics of the aggregates. The former is controlled by the water to cement ratio, while the properties of the aggregate, in general, cannot be manipulated as it is customary to employ the ones available near the construction site. In many regions rocks with no desirable properties are employed as aggregates. Therefore, the aim of this study was to answer the question about what would that be the maximum compressive strength attainable in concrete made with a specific type of aggregate obtained from crushed limestone of high absorption. Concrete mixtures involved six water to cement ratios and two sizes of coarse aggregate. It was concluded that with this type of aggregate it is possible to made concrete with compressive strength up to 500 k/cm2 of f’c.Key words: Absorption; compressive strength; concrete; limestone aggregate; water/cement ratio.

scholarly journals Effects of Disparate Zones of Sand on the Compressive Strength of Concrete

2021 ◽  
Vol 9 (11) ◽  
pp. 1368-1375
Author(s):  
Suhaib Bakshi
Keyword(s):  
Compressive Strength ◽  
Coarse Aggregate ◽  
Testing Machine ◽  
Concrete Compressive Strength ◽  
Research Papers ◽  
Concrete Material ◽  
Cement Ratio ◽  
Water Cement Ratio ◽  
Concrete Mix ◽  
Compressive Strength Of Concrete

Abstract: Compressive strength of concrete is the capacity of concrete to bear loads of materials or structure sans breaking or being deformed. Specimen under compression shrinks in size whilst under tension the size elongates. Compressive strength essentially gives concept about the properties of concrete. Compressive strength relies on many aspects such as water-cement ratio, strength of cement, calidad of concrete material. Specimens are tested by compression testing machine after the span of 7 or 28 days of curing. Compressive strength of the concrete is designated by the load on the area of specimen. In this research various proportions of such aggregate mixed in preparing M 30 grade and M 40 grade of Concrete mix and the effect is studied on its compressive strength . Several research papers have been assessed to analyze the compressive strength of concrete and the effect of different zones of sand on compressive strength are discussed in this paper. Keywords: Sand, Gradation, Coarse aggregate, Compressive strength

scholarly journals The relationship between the compressive strength and ultrasonic pulse velocity concrete with fibers exposed to high temperatures

2018 ◽  
Vol 3 (1) ◽  
pp. 31
Author(s):  
Belaribi Hassiba ◽  
Mellas Mekki ◽  
Rahmani Fraid
Keyword(s):  
Compressive Strength ◽  
Ultrasonic Velocity ◽  
High Temperatures ◽  
Ultrasonic Pulse Velocity ◽  
Ultrasonic Pulse ◽  
Pulse Velocity ◽  
Cement Ratio ◽  
Compressive Strength Of Concrete ◽  
The Relationship ◽  
The Waves

The paper analyses the effects of high temperatures on the concrete residual strength using ultrasonic velocity (UPV). An experimental investigation was conducted to study the relationship between UPV residual data and compressive strength of concrete with different mixture proportions, cubic specimens with water-cement ratio of 0.35. They were heated in an electric furnace at temperatures ranging from 200°C to 600°C. In this experiment a comparison was made between the four groups which include two types of fibers steel 0,19%, 0,25% and 0,5%, polypropylene: 0,05%, 0,11% 0,16 % by volume. Cube specimens were tested in order to determine ultrasonic velocity. The compressive strength was tested too. According to the results, relations were established between ultrasonic velocity in the specimens and the compressive strength at different temperature and the range of the velocity of the waves were also determined for this kind of concrete. Result of the test showed that UPV test can be successfully used in order to verify the consistency of structures damaged by fire.