Flame retardancy and thermal properties of poly(butylene succinate)/ nano‐boehmite composites prepared via in situ polymerization

2020 ◽  
Vol 60 (9) ◽  
pp. 2262-2271 ◽  
Author(s):  
Saman Kahkesh ◽  
Mehdi Rafizadeh
Keyword(s):  
Thermal Properties ◽  
Flame Retardancy ◽  
In Situ Polymerization ◽  
Butylene Succinate

Synthesis and Characterizations of Poly(Butylene Succinate) Copolyester

2014 ◽  
Vol 1015 ◽  
pp. 381-384
Author(s):  
Li Liu ◽  
Li Hai Cai ◽  
Dan Liu ◽  
Jun Xu ◽  
Bao Hua Guo
Keyword(s):  
Mechanical Properties ◽  
Polymer Matrix ◽  
Crystallization Temperature ◽  
In Situ Polymerization ◽  
Nucleating Agent ◽  
Single Fiber ◽  
Butylene Succinate ◽  
Crystallization Behaviors ◽  
Polymerization Method

The poly (butylene succinate) (PBS) and 3 wt% attapulgite (ATP) reinforced PBS/ATP nanocomposites with 1,6-hexanediol were fabricated using an in situ polymerization method. The crystallization behaviors indicated that ATP had effectively acted as nucleating agent, resulting in the enhancement on the crystallization temperature. The SEM results showed a superior interfacial linkage between ATP and PBS. Also, ATP could disperse as a single fiber and embed in the polymer matrix, which resulted in the improved mechanical properties.

scholarly journals Structural, morphological and thermal properties of nanocomposites poly(GMA)/clay prepared by ultrasound and in-situ polymerization

2018 ◽  
Vol 48 ◽  
pp. 188-198 ◽  
Author(s):  
Zakaria Cherifi ◽  
Bouhadjar Boukoussa ◽  
Aniss Zaoui ◽  
Mohammed Belbachir ◽  
Rachid Meghabar
Keyword(s):  
Thermal Properties ◽  
In Situ Polymerization

Fabrication Polyurethane/Expanded Graphite Powder Composite Antistatic Sponge by In Situ Polymerization

2012 ◽  
Vol 479-481 ◽  
pp. 395-398
Author(s):  
Dan Qing Chen
Keyword(s):  
Mechanical Properties ◽  
Thermal Properties ◽  
In Situ Polymerization ◽  
Expanded Graphite ◽  
Graphite Powder ◽  
Polymeric Matrix ◽  
Powder Composite

This document explains and demonstrates how to prepare Polyurethane(PU)/Expanded Graphite powder(EGp) composite antistatic sponge by in situ polymerization. The morphology、mechanical、electrical and thermal properties of the PU/EGp composite antistatic sponge have been investigated. PU/ EGp composite sponge have better mechanical properties than that of CB composite. The resistivity of PU/EGp composite antistatic sponge can reach at about 108Ω•cm at the content around 5wt% of the EGp. EGp can stably exist in PU sponge and has little influence to the polymeric matrix while being heated.

Characterization and Thermal Properties of the Microencapsulated PCM Slurry

2011 ◽  
Vol 284-286 ◽  
pp. 940-944 ◽  
Author(s):  
Yan Lai Zhang ◽  
Zhong Hao Rao ◽  
Shuang Feng Wang ◽  
Hong Zhang ◽  
Li Jun Li ◽  
...  
Keyword(s):  
Thermal Properties ◽  
In Situ Polymerization ◽  
Membrane Thickness ◽  
Fluid Behavior ◽  
Microencapsulated Phase Change Material ◽  
Paraffin Waxes ◽  
Latent Heats ◽  
Change Material ◽  
Polymerization Method

The microencapsulated phase change material (PCM) slurry is a kind of mixture with the PCM microcapsule particles and water. The actual PCM in the microcapsule is composed of several kinds of paraffin waxes (mainly nonadecane), and the membrane is a type of melamine resin. This study is focused on preparation, characterization, and thermal properties of the microencapsulated (PCM) slurry. The microencapsulated PCM particles are prepared by in-situ polymerization method. Four different levels of mass concentration Cm of the PCM will be used such as Cm=10%, 20%, 30% and 40%, respectively. The diameter of the particles is distributed in the range of 0µm~4.5µm, and most (61%) of them occur in the range of 0.5µm~1.5µm. The average volumetric diameter of the PCM microcapsule particle is about 0.78µm. And the average membrane thickness is about 11nm.Thermal properties of the microencapsulated PCM slurry are determined using differential scanning calorimeter (DSC). From DSC analysis, the melting and freezing temperatures and the latent heats of Cm=30% are measured as 38°C and 25°C, and 37.9 kJ/kg, respectively. The rheological properties are measured by a rotating cylinder type of rheometer, which the slurry shows the pseudo plastic non-Newtonian fluid behavior with the power-law fluid index n.

Mechanical and thermal properties of hybrid nanocomposites prepared by in situ polymerization

Polimery ◽  
2016 ◽  
Vol 61 (03) ◽  
pp. 172-180 ◽  
Author(s):  
Sandra Paszkiewicz ◽  
Iwona Pawelec ◽  
Anna Szymczyk ◽  
Zbigniew Roslaniec
Keyword(s):  
Thermal Properties ◽  
In Situ Polymerization ◽  
Hybrid Nanocomposites ◽  
Mechanical And Thermal Properties

The preparation of modified boehmite/PMMA nanocomposites by in situ polymerization and the assessment of their capability for Cu2+ ion removal

2016 ◽  
Vol 40 (4) ◽  
pp. 3612-3621 ◽  
Author(s):  
Gholamhossein Mohammadnezhad ◽  
Mohammad Dinari ◽  
Roozbeh Soltani
Keyword(s):  
Thermal Properties ◽  
Polymer Matrix ◽  
Active Sites ◽  
In Situ Polymerization ◽  
Ion Removal

The addition of nanoboehmite as a nanofiller into the polymer matrix led to the improvement of the thermal properties and increased the active sites of nanocomposites for Cu(ii) removal.