On the potential of organoclay with respect to conventional fillers (carbon black, silica) for epoxidized natural rubber compatibilized natural rubber vulcanizates

2004 ◽  
Vol 94 (6) ◽  
pp. 2438-2445 ◽  
Author(s):  
P. L. Teh ◽  
Z. A. Mohd Ishak ◽  
A. S. Hashim ◽  
J. Karger-Kocsis ◽  
U. S. Ishiaku
Keyword(s):  
Carbon Black ◽  
Natural Rubber ◽  
Epoxidized Natural Rubber ◽  
Natural Rubber Vulcanizates

Effect of Surface Oxidation of Carbon Black on Its Bonding with Epoxidized Natural Rubber in the Presence of Silane Coupling Agent

1999 ◽  
Vol 72 (2) ◽  
pp. 398-409 ◽  
Author(s):  
Ajay K. Manna ◽  
P. P. De ◽  
D. K. Tripathy ◽  
S. K. De ◽  
M. K. Chatterjee
Keyword(s):  
Carbon Black ◽  
Natural Rubber ◽  
Coupling Agent ◽  
Silane Coupling Agent ◽  
Surface Oxidation ◽  
Spectroscopic Studies ◽  
Epoxidized Natural Rubber ◽  
Silyl Ether ◽  
Silane Coupling ◽  
Swelling Studies

Abstract Results of bound rubber determination, Monsanto rheometry, solvent swelling studies and measurement of physical properties reveal that high temperature molding of epoxidized natural rubber (ENR) filled with intermediate super abrasion furnace (ISAF) carbon black and surface oxidized ISAF carbon black, in the presence of silane coupling agent, namely, N-(4-vinylbenzyl)-N′-[3-(trimethoxysilyl)propyl]ethane-1,2-diamine monoHCl salt, results in crosslinking of the rubber phase, even in the absence of the vulcanizing agents. Infrared spectroscopic studies show formation of silyl ether, in the case of ISAF carbon black, whereas the oxidized grade forms both silyl ether as well as silyl ester and amide linkage. Oxidation of ISAF carbon black causes an increase in the extent of coupling bond formation.

Structural Characterization of Filled Vulcanizates Part 1. Determination of the Concentration of Chemical Crosslinks in Natural Rubber Vulcanizates Containing High Abrasion Furnace Black

1967 ◽  
Vol 40 (3) ◽  
pp. 866-882 ◽  
Author(s):  
M. Porter
Keyword(s):  
Carbon Black ◽  
Natural Rubber ◽  
Volume Fraction ◽  
Exponential Relationship ◽  
Furnace Black ◽  
Simple Linear Relationship ◽  
Chemical Crosslinks ◽  
Natural Rubber Vulcanizates

Abstract The degree to which HAF black restricts the swelling of natural rubber vulcanizates in n-decane has been determined using a vulcanizing system in which the stoichiometry of crosslinking is unaffected by the carbon black. The dependence of the degree of restriction, as measured by the ratio of the volume fractions of rubber in the filled and unfilled vulcanizates swollen to equilibrium, on the concentration of carbon black follows an exponential relationship previously proposed by Lorenz and Parks. This is found to be equivalent to a simple linear relationship between the apparent and actual crosslink concentrations: napparent/nactual=1+Kϕ, where K is a constant characteristic of the filler and φ is its volume fraction in the vulcanizate. The relation has been used to determine actual crosslink concentrations in filled natural rubber vulcanizates. HAF black is found to cause increases of up to 25 per cent in the yield of polymer to polymer crosslinks in conventional sulfur vulcanizing systems, accompanied by changes in rate of cure and of crosslink reversion. All these are small compared with the effect of the filler on many physical properties.

Effect of Crosslink Density on Cut Growth in Black-Filled Natural Rubber Vulcanizates

2002 ◽  
Vol 75 (5) ◽  
pp. 935-942 ◽  
Author(s):  
G. R. Hamed ◽  
N. Rattanasom
Keyword(s):  
Carbon Black ◽  
Natural Rubber ◽  
Crack Growth ◽  
Crosslink Density ◽  
Longitudinal Crack ◽  
Test Pieces ◽  
Filled Rubber ◽  
Longitudinal Cracks ◽  
Natural Rubber Vulcanizates ◽  
High Crosslink Density

Abstract Tensile strengths, σb, of gum and N115-filled natural rubber test pieces, with and without edge pre-cuts, have been determined. At low crosslink density, the regular (uncut) σb of filled and gum vulcanizates is similar. However, at high crosslink density, the gum NR becomes brittle, while the corresponding filled rubber remains strong and resistant to cut growth. It is proposed that the tightly linked gum does not strain-crystallize appreciably during stretching, but that its filled counterpart does. Carbon black appears capable of inducing crystallization in a network that alone remains amorphous during extension. Filled vulcanizates of various crosslink densities have similar normal tensile strengths ( ≈ 30 MPa), but strengths differ, sometimes more than twofold, if a pre-cut is present. Lightly crosslinked specimens containing a small cut have strengths that depend very weakly on cut size, c. Furthermore, these develop long longitudinal cracks from which catastrophic rupture initiates. With larger cuts, strength decreases more rapidly with increasing c, there is less longitudinal crack growth, and rupture initiates near the original cut tip. In contrast, the strength of a highly crosslinked vulcanizate is sensitive to small cuts and test pieces exhibit minimal longitudinal cracking before failure.