scholarly journals Influences of Waste Concrete Powder on the Strength Development and Hydration Products of Mortar Containing Fly Ash

2021 ◽  
Author(s):  
Huashan YANG ◽  
Yujun CHE
Keyword(s):  
Fly Ash ◽  
Portland Cement ◽  
Cement Mortar ◽  
Setting Time ◽  
Flow Index ◽  
Strength Development ◽  
Test Results ◽  
Hydration Products ◽  
Waste Concrete ◽  
Time Flow

During recycling waste concrete, a large amount of waste concrete powder (WCP) is generated. However, efficient utilization of WCP remains an unresolved issue. This paper investigates the influences of WCP on the properties and hydration products of cement mortar containing fly ash (FA). This study used two different types of WCPs. One was made from an ordinary Portland cement mortar, and the other was derived from a Portland cement mortar. WCP replaced 10%, 20%, and 30% of FA. The water requirement, setting time, flow index, strength, hydration products, and microstructure of FA mortar incorporating WCP were investigated. Test results indicate that the WCP has no significant influence on the performances and hydration products of FA mortar. By adequately combining WCP and FA, the FA mortar with required performances could be reached.

The Effect on Cement Mortar and Concrete by Admixture of Spray Drying Absorption Products

1989 ◽  
Vol 178 ◽  
Author(s):  
Kirsten G. Jeppesen
Keyword(s):  
Grain Size ◽  
Fly Ash ◽  
Cement Mortar ◽  
Setting Time ◽  
Mineralogical Composition ◽  
Cement Clinker ◽  
Strength Development ◽  
Fall Meeting ◽  
Freeze Thaw ◽  
Spray Dried

AbstractSpray dried absorption products (SDA) having special characteristics are used as substitutes for cement in the preparation of mortars; the qualities of the resulting mixed mortars are described. Conditions are described for mortar mixes, data for which were presented at the MRS Fall Meeting 1987.The influence of the composition of the SDA on water requirement and setting time has been studied. A full scale project involving 3 precast, reinforced concrete front-elements containing 20 and 30 wt.% SDA is described. Strength development, mineralogical composition and corrosion were monitored for two years.A non-standard freeze-thaw experiment was performed which compares mortars containing SDA and fly ash (FA) and also shows the effect of superplasticizer.The possibility of improving the SDA by grinding has been tested and a limited improvement has been found. The strength of the mixed mortars seems slightly influenced by the grain size of SDAGypsum (CaSO4·2H2O), synthetic calcium-sulphite (CaSO3·½H2O) and 2 SDAs have been used as retarders for cement clinker. Mortar test prisms have been cast and comparative strengths after curing for 3 years are reported

scholarly journals Influence of Mechanical and Mineralogical Activation of Biomass Fly Ash on the Compressive Strength Development of Cement Mortars

Materials ◽  
2021 ◽  
Vol 14 (21) ◽  
pp. 6654
Author(s):  
Jakub Popławski ◽  
Małgorzata Lelusz
Keyword(s):  
Compressive Strength ◽  
Fly Ash ◽  
Silica Fume ◽  
Cement Mortar ◽  
Setting Time ◽  
Green Energy ◽  
Biomass Combustion ◽  
Strength Development ◽  
Compressive Strength Development ◽  
Biomass Fly Ash

Biomass combustion is a significant new source of green energy in the European Union. The adequate utilization of byproducts created during that process is a growing challenge for the energy industry. Biomass fly ash could be used in cement composite production after appropriate activation of that material. This study had been conducted to assess the usefulness of mechanical and physical activation methods (grinding and sieving), as well as activation through the addition of active silica in the form of silica fume, as potential methods with which to activate biomass fly ash. Setting time, compressive strength, water absorption and bulk density tests were performed on fresh and hardened mortar. While all activation methods influenced the compressive strength development of cement mortar with fly ash, sieving of the biomass fly ash enhanced the early compressive strength of cement mortar. The use of active silica in the form of silica fume ensured higher compressive strength results than those of control specimens throughout the entire measurement period.

scholarly journals Effects of Highly Crystalized Nano C-S-H Particles on Performances of Portland Cement Paste and Its Mechanism

Crystals ◽  
2020 ◽  
Vol 10 (9) ◽  
pp. 816
Author(s):  
Yuli Wang ◽  
Huijuan Lu ◽  
Junjie Wang ◽  
Hang He
Keyword(s):  
Portland Cement ◽  
Cement Paste ◽  
Setting Time ◽  
Tricalcium Silicate ◽  
Strength Development ◽  
Early Age ◽  
Hydration Products ◽  
X Ray ◽  
Early Strength ◽  
Portland Cement Paste

In order to improve the early age strength of ordinary Portland cement-based materials, many early strength agents were applied in different conditions. Different from previous research, the nano calcium silicate hydrate (C-S-H) particles used in this study were synthesized through the chemical reaction of CaO, SiO2, and H2O under 120 °C using the hydrothermal method, and the prepared nano C-S-H particles were highly crystalized. The influences of different amounts of nano C-S-H particles (0%, 0.5%, 1%, 2% and 3% by weight of cement) on the setting time, compressive strength, and hydration heat of cement paste were studied. The hydration products and microstructure of the cement paste with different additions of nano C-S-H particles were investigated through thermogravimetry-differential thermal analysis (TG-DTA), X-ray powder diffraction (XRD), and scanning electron microscope (SEM) tests. The results show that the nano C-S-H particles could be used as an early strength agent, and the early strength of cement paste can be increased by up to 43% through accelerating the hydration of tricalcium silicate (C3S). However, the addition of more than 2% nano C-S-H particles was unfavorable to the later strength development due to more space being left during the initial accelerated hydration process. It is suggested that the suitable content of the nano C-S-H particles is 0.5%−1% by weight of cement.

scholarly journals Effect of Fly Ash Belite Cement on Hydration Performance of Portland Cement

Crystals ◽  
2021 ◽  
Vol 11 (7) ◽  
pp. 740
Author(s):  
Yongfan Gong ◽  
Jianming Yang ◽  
Haifeng Sun ◽  
Fei Xu
Keyword(s):  
Fly Ash ◽  
Portland Cement ◽  
Setting Time ◽  
Hydration Heat ◽  
Hydration Reaction ◽  
Term Strength ◽  
Hydration Products ◽  
Composite Cement ◽  
Belite Cement

Fly ash belite cement is a green, low carbon cementitious material, mainly composed of hydraulic minerals of dicalcium silicate and calcium aluminate. In this study, we used fly ash belite cement to control the setting time, hydration heat, strength, composition and microstructure of hydration products in Portland cement. Results showed that incorporating fly ash belite cement into Portland cement can shorten the setting time, accelerate hydration reaction speed, enhance early hydration heat release rate of silicate minerals and reduce total hydration heat. Moreover, replacing composite cement with 30% FABC causes the 90 d compressive strength of pastes and mortars to reach 107 and 46.2 MPa, respectively. The mechanical properties can meet the requirements of P·F 42.5 cement. During the hydration reaction process, clinker and Portland cement have a synergistic hydration effect. Notably, hydration of fly ash belite cement promotes the formation of C-S-H gel, Ettringite and calcium hydroxide, thereby significantly enhancing long-term strength. With the increase of FABC contents, the long-term strength would be improved with the densification of hydration products. The porosity has a great influence on the strength, and the high porosity was the main cause of the low early strength of FABC pastes. FABC and its composite cement show promise for mass concrete applications and can be applied as a setting agent for Portland cement.

scholarly journals Strength Development and Elemental Distribution of Dolomite/Fly Ash Geopolymer Composite under Elevated Temperature

Materials ◽  
2020 ◽  
Vol 13 (4) ◽  
pp. 1015 ◽  
Author(s):  
Emy Aizat Azimi ◽  
Mohd Mustafa Al Bakri Abdullah ◽  
Petrica Vizureanu ◽  
Mohd Arif Anuar Mohd Salleh ◽  
Andrei Victor Sandu ◽  
...  
Keyword(s):  
Elevated Temperature ◽  
Fly Ash ◽  
Portland Cement ◽  
Ordinary Portland Cement ◽  
Raw Materials ◽  
Liquid Sodium ◽  
Strength Development ◽  
Elemental Distribution ◽  
Distribution Analysis ◽  
Geopolymer Composites

A geopolymer has been reckoned as a rising technology with huge potential for application across the globe. Dolomite refers to a material that can be used raw in producing geopolymers. Nevertheless, dolomite has slow strength development due to its low reactivity as a geopolymer. In this study, dolomite/fly ash (DFA) geopolymer composites were produced with dolomite, fly ash, sodium hydroxide, and liquid sodium silicate. A compression test was carried out on DFA geopolymers to determine the strength of the composite, while a synchrotron Micro-Xray Fluorescence (Micro-XRF) test was performed to assess the elemental distribution in the geopolymer composite. The temperature applied in this study generated promising properties of DFA geopolymers, especially in strength, which displayed increments up to 74.48 MPa as the optimum value. Heat seemed to enhance the strength development of DFA geopolymer composites. The elemental distribution analysis revealed exceptional outcomes for the composites, particularly exposure up to 400 °C, which signified the homogeneity of the DFA composites. Temperatures exceeding 400 °C accelerated the strength development, thus increasing the strength of the DFA composites. This appears to be unique because the strength of ordinary Portland Cement (OPC) and other geopolymers composed of other raw materials is typically either maintained or decreases due to increased heat.

Physical Properties of Cement Mortar Containing Waste Ash

2015 ◽  
Vol 804 ◽  
pp. 129-132
Author(s):  
Sumrerng Rukzon ◽  
Prinya Chindaprasirt
Keyword(s):  
Compressive Strength ◽  
Fly Ash ◽  
Rice Husk ◽  
Rice Husk Ash ◽  
Cement Mortar ◽  
Ash Content ◽  
Water Requirement ◽  
Test Results ◽  
Pozzolanic Material ◽  
Materials Used

This research studies the potential for using waste ash from industrial and agricultural by-products as a pozzolanic material. Classified fly ash (FA) and ground rice husk ash (RA) were the materials used. Water requirement, compressive strength and porosity of cement mortar were investigated. Test results indicated that FA and RA (waste ash) have a high potential to be used as a good pozzolanic material. The water requirement of mortar mix decreases with the increases in fly ash content. For ground rice husk ash (RA), the water requirement of mortar mix increases with the increases in rice husk ash content. In addition, the reduction in porosity was associated with the increase in compressive strength.

Utilization of Circulating Fluidized Bed Combustion (CFBC) Fly Ash and Coal-Fired Fly Ash in Portland Cement

2014 ◽  
Vol 629-630 ◽  
pp. 306-313 ◽  
Author(s):  
Mao Chieh Chi ◽  
Ran Huang ◽  
Te Hsien Wu ◽  
Toun Chun Fou
Keyword(s):  
Fly Ash ◽  
Portland Cement ◽  
Fluidized Bed ◽  
Building Materials ◽  
Circulating Fluidized Bed ◽  
Setting Time ◽  
Fluidized Bed Combustion ◽  
Initial Setting Time ◽  
Cfbc Fly Ash ◽  
Circulating Fluidized Bed Combustion

Circulating fluidized bed combustion (CFBC) fly ash is a promising admixture for construction and building materials due to its pozzolanic activity and self-cementitious property. In this study, CFBC fly ash and coal-fired fly ash were used in Portland cement to investigate the pozzolanic and cementitious characteristics of CFBC fly ash and the properties of cement-based composites. Tests show that CFBC fly ash has the potential instead of cementing materials and as an alternative of pozzolan. In fresh specimens, the initial setting time of mortars increases with the increasing amount of cement replacement by CFBC fly ash and coal-fire fly ash. In harden specimens, adding CFBC fly ash to replace OPC reduces the compressive strength. Meanwhile, CFBC fly ash would results in a higher length change when adding over 30%. Based on the results, the amount of CFBC fly ash replacement cement was recommended to be limited below 20%.

Setting Behaviour of Phosphate Cement

2011 ◽  
Vol 194-196 ◽  
pp. 853-857
Author(s):  
Zhong Hua Li ◽  
He Fei Gao ◽  
Shu Rong Feng ◽  
Chao Su
Keyword(s):  
Fly Ash ◽  
Portland Cement ◽  
Influencing Factors ◽  
Setting Time ◽  
Repair Material ◽  
Rapid Repair ◽  
Binder Ratio

For the situation that concrete engineering required rapid and timely repair after nature disaster, setting time and influencing factors of phosphate rapid repair material were studied in this paper. The results showed that setting time of phosphate rapid repair material increased a little with increase of water and binder ratio but the setting time was short. When water and binder ratio was less than 0.20 setting time was less than 3min. Setting time was shorted with reducing of P/M. Setting time was from 2min30s to 5min when P/M was reduced from 1:0.6 to 1:4. Setting time of phosphate cement increase a little mixed with fly ash, slag or portland cement but effect of their content on setting time was little. Setting time of phosphate rapid repair material increased with increase of B/M. When content was greated than 12% the setting time was longer than 20min. Fly ash, slag and portland cement can reduce setting time of phosphate cement with borax obviously.