scholarly journals Poly(∊-Caprolactone) Reinforced with Sol-Gel Synthesized Organic-Inorganic Hybrid Fillers as Composite Substrates for Tissue Engineering

2010 ◽  
Vol 8 (3) ◽  
pp. 146-152 ◽  
Author(s):  
Teresa Russo ◽  
Antonio Gloria ◽  
Vincenzo D'Antò ◽  
Ugo D'Amora ◽  
Gianluca Ametrano ◽  
...  
Keyword(s):  
Tissue Engineering ◽  
Sol Gel ◽  
Inorganic Hybrid ◽  
Hybrid Fillers ◽  
Composite Substrates ◽  
Poly Caprolactone

UV Curable Organic-Inorganic Hybrid Materials

2000 ◽  
Vol 628 ◽  
Author(s):  
Guang-Way Jang ◽  
Ren-Jye Wu ◽  
Yuung-Ching Sheen ◽  
Ya-Hui Lin ◽  
Chi-Jung Chang
Keyword(s):  
Hybrid Materials ◽  
Colloidal Silica ◽  
Sol Gel ◽  
Solution Ph ◽  
Uv Curable ◽  
Inorganic Hybrid ◽  
Degradation Temperature ◽  
Sol Gel Process ◽  
The Stability ◽  
Thermal Degradation Temperature

This work successfully prepared an UV curable organic-inorganic hybrid material consisting of organic modified colloidal silica. Applications of UV curable organic-inorganic hybrid materials include abrasion resistant coatings, photo-patternable thin films and waveguides. Colloidal silica containing reactive functional groups were also prepared by reacting organic silane and tetraethyl orthosilicate (TEOS) using sol-gel process. In addition, the efficiency of grafting organic moiety onto silica nanoparticles was investigated by applying TGA and FTIR techniques. Experimental results indicated a strong interdependence between surface modification efficiency and solution pH. Acrylate-SiO2 hybrid formation could result in a shifting of thermal degradation temperature of organic component from about 200°C to near 400°C. In addition, the stability of organic modified colloidal silica in UV curable formula and the physical properties of resulting coatings were discussed. Furthermore, the morphology of organic modified colloidal silica was investigated by performing TEM and SEM studies‥

scholarly journals A Proposed Fabrication Method of Novel PCL-GEL-HAp Nanocomposite Scaffolds for Bone Tissue Engineering Applications

2010 ◽  
Vol 19 (4) ◽  
pp. 096369351001900 ◽  
Author(s):  
A. Hamlekhan ◽  
M. Mozafari ◽  
N. Nezafati ◽  
M. Azami ◽  
H. Hadipour
Keyword(s):  
Tissue Engineering ◽  
Bone Tissue Engineering ◽  
Bone Tissue ◽  
Mechanical Test ◽  
Fibroblast Cell ◽  
Mouse Fibroblast ◽  
Fabrication Method ◽  
Engineering Applications ◽  
Poly Caprolactone

In this study, poly(∊-caprolactone) (PCL), gelatin (GEL) and nanocrystalline hydroxyapatite (HAp) was applied to fabricate novel PCL-GEL-HAp nanaocomposite scaffolds through a new fabrication method. With the aim of finding the best fabrication method, after testing different methods and solvents, the best method and solvents were found, and the nanocomposites were prepared through layer solvent casting combined with freeze-drying. Acetone and distillated water were used as the PCL and GEL solvents, respectively. The mechanical test showed that the increasing of the PCL weight through the scaffolds caused the improvement of the final nanocomposite mechanical behavior due to the increasing of the ultimate stress, stiffness and elastic modulus (8 MPa for 0% wt PCL to 23.5 MPa for 50% wt PCL). The biomineralization investigation of the scaffolds revealed the formation of bone-like apatite layers after immersion in simulated body fluid (SBF). In addition, the in vitro cytotoxity of the scaffolds using L929 mouse fibroblast cell line (ATCC) indicated no sign of toxicity. These results indicated that the fabricated scaffold possesses the prerequisites for bone tissue engineering applications.

scholarly journals Preparation and Electrochemical Characterization of Organic–Inorganic Hybrid Poly(Vinylidene Fluoride)-SiO2 Cation-Exchange Membranes by the Sol-Gel Method Using 3-Mercapto-Propyl-Triethoxyl-Silane

Materials ◽  
2019 ◽  
Vol 12 (19) ◽  
pp. 3265 ◽  
Author(s):  
Li ◽  
Li ◽  
Li ◽  
Guan ◽  
Zheng ◽  
...  
Keyword(s):  
Membrane Potential ◽  
Oxidative Stability ◽  
Water Uptake ◽  
Polyvinylidene Fluoride ◽  
Vinylidene Fluoride ◽  
Sol Gel ◽  
Synthesis Method ◽  
Co2 Production ◽  
Inorganic Hybrid ◽  
Poly Vinylidene Fluoride

A new synthesis method for organic–inorganic hybrid Poly(vinylidene fluoride)-SiO2 cation-change membranes (CEMs) is proposed. This method involves mixing tetraethyl orthosilicate (TEOS) and 3-mercapto-propyl-triethoxy-silane (MPTES) into a polyvinylidene fluoride (PVDF) sol-gel solution. The resulting slurry was used to prepare films, which were immersed in 0.01 M HCl, which caused hydrolysis and polycondensation between the MPTES and TEOS. The resulting Si-O-Si polymers chains intertwined and/or penetrated the PVDF skeleton, significantly improving the mechanical strength of the resulting hybrid PVDF-SiO2 CEMs. The -SH functional groups of MPTES oxidized to-SO3H, which contributed to the excellent permeability of these CEMs. The surface morphology, hybrid structure, oxidative stability, and physicochemical properties (IEC, water uptake, membrane resistance, membrane potential, transport number, and selective permittivity) of the CEMs obtained in this work were characterized using scanning electron microscope and Fourier transform infrared spectroscopy, as well as electrochemical testing. Tests to analyze the oxidative stability, water uptake, membrane potential, and selective permeability were also performed. Our organic–inorganic hybrid PVDF-SiO2 CEMs demonstrated higher oxidative stability and lower resistance than commercial Ionsep-HC-C membranes with a hydrocarbon structure. Thus, the synthesis method described in this work is very promising for the production of very efficient CEMs. In addition, the physical and electrochemical properties of the PVDF-SiO2 CEMs are comparable to the Ionsep-HC-C membranes. The electrolysis of the concentrated CoCl2 solution performed using PVDF-SiO2-6 and Ionsep-HC-C CEMs showed that at the same current density, Co2+ production, and current efficiency of the PVDF-SiO2-6 CEM membrane were slightly higher than those obtained using the Ionsep-HC-C membrane. Therefore, our novel membrane might be suitable for the recovery of cobalt from concentrated CoCl2 solutions.

Synthesis and Intermolecularly Mediated Assembly of Organic Pigment in Hybrid Coating Films

1998 ◽  
Vol 519 ◽  
Author(s):  
Y. Yan ◽  
Z. Duan ◽  
D.-G. Chen ◽  
S. Ray Chaudhuri
Keyword(s):  
Sol Gel ◽  
Hybrid Coating ◽  
Hypsochromic Shift ◽  
Hybrid Films ◽  
Coating Films ◽  
Organic Pigment ◽  
Inorganic Hybrid ◽  
Matrix Interactions ◽  
Sol Gel Process

AbstractThe insoluble, strongly hydrogen bonded organic pigment of 3,6-bis-(4-chlorphenyl)-l,4- diketopyrrolo [3,4-c] pyrrole was transiently blocked by adding carbamate groups, and consequently incorporated into organic-inorganic hybrid matrices by a sol-gel process. The homo- (pigment-pigment) and hetero-intermolecular (pigment-matrix) interactions were found to control both the assembly and dispersion of pigment molecules in the hybrid coating films. A weaker interaction between matrices and pigment molecules results in aggregation of the carbamate pigment in the methyl-silicate films. A stronger interaction forms a homogenous dispersion and coloration of the phenyl-silicate films. The as-prepared methyl- and phenylsilicate films doped with the organic pigment were distinguished by a morphology change and a blue (hypsochromic) shift in absorption from 550 to 460 nm. Thermal treatment can remove the carbamate groups and in-situ form the organic pigment in the hybrid films.

A NEW ORGANIC/INORGANIC HYBRID WITH HIGH ELECTRORHEOLOGICAL ACTIVITY

2002 ◽  
Vol 16 (17n18) ◽  
pp. 2454-2460 ◽  
Author(s):  
X. P. ZHAO ◽  
X. DUAN
Keyword(s):  
Activation Energy ◽  
Shear Stress ◽  
Necessary Conditions ◽  
Sol Gel ◽  
Root Temperature ◽  
Sedimentation Stability ◽  
Inorganic Hybrid ◽  
Active Particles ◽  
Static Shear

In-situ sol-gel method to prepare colloidal hybrids of surfactant modified polysucchride and titanium oxide has been presented, and experiments indicated these highly ER active particles exhibited a remarkable ER effect. The static shear stress can be up to 37 k Pa (shear rate 5 S -1) under DC field of 4 kV/mm at root temperature, well above that of simple blends of starch and TiO 2. In the meanwhile, temperature dependence and sedimentation stability were also greatly improved. Based on recent experimental facts, we find that dielectric properties and surface (interface) activity are two necessary conditions fulfilling the requirement of high ER activity. Adequate grinding of particles with oil can effectively enhance the shear stress, which may be owed to the decline of the activation energy needed for restructuring. It has provided us a new horizon for preparation of excellent ER materials and further studies should be continued to make.

Sign in / Sign up

Export Citation Format

Share Document