Hydrogen Assisted Stress Corrosion Cracking Related Material Properties of Service-Applied Landing Gear Ultra-High Strength Steels

Thomas Boellinghaus; Benjamin R. Steffens; Michael Rhode; Gregory A. Shoales

doi:10.5006/3028

Hydrogen Assisted Stress Corrosion Cracking Related Material Properties of Service-Applied Landing Gear Ultra-High Strength Steels

CORROSION ◽

10.5006/3028 ◽

2019 ◽

Vol 75 (5) ◽

pp. 513-524

Author(s):

Thomas Boellinghaus ◽

Benjamin R. Steffens ◽

Michael Rhode ◽

Gregory A. Shoales

Keyword(s):

Stress Corrosion ◽

Stress Corrosion Cracking ◽

Material Properties ◽

High Strength Steels ◽

High Strength ◽

Landing Gear ◽

Corrosion Cracking ◽

Related Material ◽

Ultra High Strength Steels

Download Full-text

EFFECT OF METALLURGY ON STRESS CORROSION CRACKING AND HYDROGEN EMBRITTLEMENT OF ULTRA/HIGH STRENGTH STEELS

The Physical Metallurgy of Fracture ◽

10.1016/b978-0-08-022138-0.50046-0 ◽

1978 ◽

pp. 255-259

Author(s):

M. Tvrd ◽

V. Suchánek ◽

L. Hyspecká ◽

K. Mazanec

Keyword(s):

Hydrogen Embrittlement ◽

Stress Corrosion ◽

Stress Corrosion Cracking ◽

High Strength Steels ◽

High Strength ◽

Corrosion Cracking ◽

Ultra High Strength Steels

Download Full-text

Stress Corrosion Cracking of High Strength Steels

10.21236/ada375902 ◽

1995 ◽

Author(s):

Eun U. Lee ◽

Henry Sanders ◽

Bhaskar Sarkar

Keyword(s):

Stress Corrosion ◽

Stress Corrosion Cracking ◽

High Strength Steels ◽

High Strength ◽

Corrosion Cracking

Download Full-text

Effects of high temperature austenitization on fracture, fatigue and stress corrosion cracking behavior of cast and forged high strength steels I: Monotonic fracture behavior

Materials Science and Engineering A ◽

10.1016/0921-5093(89)90166-4 ◽

1989 ◽

Vol 110 ◽

pp. 151-164 ◽

Cited By ~ 2

Author(s):

Wei-Di Cao ◽

Xiao-Ping Lu

Keyword(s):

High Temperature ◽

Stress Corrosion ◽

Stress Corrosion Cracking ◽

Fracture Behavior ◽

High Strength Steels ◽

High Strength ◽

Corrosion Cracking ◽

Cracking Behavior

Download Full-text

LITERATURE SURVEY OF STRESS-CORROSION CRACKING AND HYDROGEN EMBRITTLEMENT IN HIGH STRENGTH STEELS.

10.2172/4708564 ◽

1971 ◽

Author(s):

J.L. Briggs

Keyword(s):

Hydrogen Embrittlement ◽

Stress Corrosion ◽

Stress Corrosion Cracking ◽

High Strength Steels ◽

High Strength ◽

Corrosion Cracking ◽

Literature Survey

Download Full-text

Stress Corrosion Cracking of High Strength Steels and Titanium Al in Chloride Solutions at Ambient Temperature

CORROSION ◽

10.5006/0010-9312-23.5.142 ◽

1967 ◽

Vol 23 (5) ◽

pp. 142-148 ◽

Cited By ~ 50

Author(s):

M. H. PETERSON ◽

B. F. BROWN ◽

R. L. NEWBEGIN ◽

R. E. GROOVER

Keyword(s):

Ambient Temperature ◽

Stress Corrosion ◽

Stress Corrosion Cracking ◽

High Strength Steels ◽

High Strength ◽

Corrosion Cracking ◽

Chloride Solutions

Download Full-text

Influence of Experimental Variables on the Measurement of Stress Corrosion Cracking Properties of High-Strength Steels

Environmentally Assisted Cracking: Science and Engineering ◽

10.1520/stp24078s ◽

2009 ◽

pp. 410-410-13 ◽

Cited By ~ 1

Author(s):

RW Judy ◽

WE King ◽

JA Hauser ◽

TW Crooker

Keyword(s):

Stress Corrosion ◽

Stress Corrosion Cracking ◽

High Strength Steels ◽

High Strength ◽

Corrosion Cracking

Download Full-text

THE INVESTIGATION OF STRESS CORROSION CRACKING OF HIGH STRENGTH STEELS

10.21236/ad0434247 ◽

1964 ◽

Author(s):

R. B. Setterlund

Keyword(s):

Stress Corrosion ◽

Stress Corrosion Cracking ◽

High Strength Steels ◽

High Strength ◽

Corrosion Cracking

Download Full-text

Exploratory stress-corrosion cracking tests on some low-alloy high-strength steels

10.4095/299997 ◽

1969 ◽

Author(s):

G J Biefer

Keyword(s):

Stress Corrosion ◽

Stress Corrosion Cracking ◽

High Strength Steels ◽

High Strength ◽

Corrosion Cracking

Download Full-text

The study of influence organic and inorganic corrosion inhibitors on the stress-corrosion cracking high-strength steels

Proceedings of VIAM ◽

10.18577/2307-6046-2017-0-6-12-12 ◽

2017 ◽

pp. 12-12

Author(s):

T.M. Rakova ◽

◽

A.A. Kozlova ◽

N.I. Nefedov ◽

A.B. Laptev ◽

...

Keyword(s):

Stress Corrosion ◽

Stress Corrosion Cracking ◽

Corrosion Inhibitors ◽

High Strength Steels ◽

High Strength ◽

Corrosion Cracking

Download Full-text

A study on fractal dimension of fracture surface created by stress corrosion cracking in high strength steels

Scripta Metallurgica et Materialia ◽

10.1016/0956-716x(92)90077-r ◽

1992 ◽

Vol 27 (10) ◽

pp. 1319-1324 ◽

Cited By ~ 4

Author(s):

Q.Y. Long ◽

Jun Chen ◽

Jizhi Chen ◽

Z.Q. Mu ◽

C.W. Lung

Keyword(s):

Fractal Dimension ◽

Fracture Surface ◽

Stress Corrosion ◽

Stress Corrosion Cracking ◽

High Strength Steels ◽

High Strength ◽

Corrosion Cracking

Download Full-text