Atmospheric Corrosion Behavior of Extruded Aluminum Alloy 7075-T6 After Long-Term Field Testing in China

CORROSION ◽  
2011 ◽  
Vol 67 (10) ◽  
pp. 106002-106002-10 ◽  
Author(s):  
S. Hu ◽  
S. Sun ◽  
A. Guo ◽  
X. Jia ◽  
Y. Geng
Keyword(s):  
Aluminum Alloy ◽  
Corrosion Behavior ◽  
Atmospheric Corrosion ◽  
Field Testing ◽  
Aluminum Alloy 7075 ◽  
Term Field

scholarly journals Long-Term Atmospheric Corrosion Behavior of Epoxy Prime Coated Aluminum Alloy 7075-T6 in Coastal Environment

Materials ◽  
2018 ◽  
Vol 11 (6) ◽  
pp. 965 ◽  
Author(s):  
Sheng Zhang ◽  
Yuting He ◽  
Teng Zhang ◽  
Guirong Wang ◽  
Xu Du
Keyword(s):  
Aluminum Alloy ◽  
Corrosion Behavior ◽  
Atmospheric Corrosion ◽  
Coastal Environment ◽  
Aluminum Alloy 7075

Atmospheric Corrosion in Marine Environments

CORROSION ◽  
1978 ◽  
Vol 34 (12) ◽  
pp. 433-437 ◽  
Author(s):  
R. A. LEGAULT ◽  
V. P. PEARSON
Keyword(s):  
Corrosion Behavior ◽  
Atmospheric Corrosion ◽  
Low Alloy Steels ◽  
Marine Environments ◽  
Weight Losses ◽  
Alloy Steels

Abstract It has been demonstrated that the natural atmospheric corrosion behavior of low alloy steels in marine environments can be accurately described by an equation of the form: ΔW = KtN. With this relationship, reliable predictions of long term weight losses can be made from as few as two sets of determinations obtained in relatively short exposures. The reliability of this relationship has also been established for galvanized and aluminized steels.

scholarly journals Atmospheric Corrosion Behavior of 2A12 Aluminum Alloy in a Tropical Marine Environment

2015 ◽  
Vol 2015 ◽  
pp. 1-17 ◽  
Author(s):  
Zhongyu Cui ◽  
Xiaogang Li ◽  
Huan Zhang ◽  
Kui Xiao ◽  
Chaofang Dong ◽  
...  
Keyword(s):  
Mechanical Properties ◽  
Aluminum Alloy ◽  
Corrosion Behavior ◽  
Marine Environment ◽  
Atmospheric Corrosion ◽  
Product Layer ◽  
Barrier Effect ◽  
Corrosion Morphology ◽  
Corrosion Product Layer ◽  
Morphology Changes

Atmospheric corrosion behavior of 2A12 aluminum alloy exposed to a tropical marine environment for 4 years was investigated. Weight loss of 2A12 alloy in the log-log coordinates can be well fitted with two linear segments, attributing to the evolution of the corrosion products. EIS results indicate that the corrosion product layer formed on the specimens exposed for 12 months or longer presents a good barrier effect. Corrosion morphology changes from pitting corrosion to severe intergranular corrosion with the extension of exposure time, resulting in the reduction of the mechanical properties.

scholarly journals The NEWgenerator non-sewered sanitation system: Long-term field testing at an informal settlement community in eThekwini municipality, South Africa

2021 ◽  
Vol 296 ◽  
pp. 112921
Author(s):  
Hsiang-Yang Shyu ◽  
Robert A. Bair ◽  
Cynthia J. Castro ◽  
Lindelani Xaba ◽  
Manuel Delgado-Navarro ◽  
...  
Keyword(s):  
South Africa ◽  
Informal Settlement ◽  
Field Testing ◽  
Term Field
Sign in / Sign up

Export Citation Format

Share Document