Stress Corrosion Cracking of Type 304 Stainless Steel under Residual Stress

Michinori Takano; Hiroshi Takaku

doi:10.5006/1.3622157

Stress Corrosion Cracking of Type 304 Stainless Steel under Residual Stress

CORROSION ◽

10.5006/1.3622157 ◽

1981 ◽

Vol 37 (3) ◽

pp. 142-146 ◽

Cited By ~ 3

Author(s):

Michinori Takano ◽

Hiroshi Takaku

Keyword(s):

Residual Stress ◽

Stainless Steel ◽

Stress Corrosion ◽

Stress Corrosion Cracking ◽

Corrosion Cracking ◽

304 Stainless Steel ◽

Type 304 ◽

Type 304 Stainless Steel

Download Full-text

Effect of Hydrogen Peroxide on Stress Corrosion Cracking of Type 304 Stainless Steel

Corrosion engineering digest ◽

10.3323/jcorr1974.33.1_33 ◽

1984 ◽

Vol 33 (1) ◽

pp. 33-36

Author(s):

Eiji Kikuchi ◽

Noriyuki Ohnaka ◽

Akira Minato

Keyword(s):

Hydrogen Peroxide ◽

Stainless Steel ◽

Stress Corrosion ◽

Stress Corrosion Cracking ◽

Corrosion Cracking ◽

304 Stainless Steel ◽

Type 304 ◽

Type 304 Stainless Steel

Download Full-text

Fractographic Observations on Chloride Stress Corrosion Cracking of Type 304 Stainless Steel under Salt Crust / Fraktographische Untersuchung der chloridinduzierten Spannungsrißkorrosion von Typ 304-Stahl unter einer Salzkruste

Practical Metallography ◽

10.1515/pm-1996-330807 ◽

1996 ◽

Vol 33 (8) ◽

pp. 421-430

Author(s):

Nurhan Cansever ◽

Ali Fuat Çakır ◽

Mustafa Ürgen

Keyword(s):

Stainless Steel ◽

Stress Corrosion ◽

Stress Corrosion Cracking ◽

Corrosion Cracking ◽

304 Stainless Steel ◽

Salt Crust ◽

Type 304 ◽

Type 304 Stainless Steel ◽

Chloride Stress Corrosion Cracking

Download Full-text

On the Influence of Thermo-Mechanical Process History on Stress Corrosion Cracking of Solution Annealed Type 304 Stainless Steel

Contributed Papers from MS&T17 ◽

10.7449/2018/mst_2018_738_745 ◽

2018 ◽

Author(s):

O. Al Yousif

Keyword(s):

Stainless Steel ◽

Stress Corrosion ◽

Stress Corrosion Cracking ◽

Corrosion Cracking ◽

304 Stainless Steel ◽

Mechanical Process ◽

Type 304 ◽

Type 304 Stainless Steel

Download Full-text

Effect of Specimen Width on Stress Corrosion Cracking of Type 304 Stainless Steel

CORROSION ◽

10.5006/1.3316002 ◽

1993 ◽

Vol 49 (10) ◽

pp. 796-801 ◽

Cited By ~ 10

Author(s):

R. Nishimura

Keyword(s):

Stainless Steel ◽

Stress Corrosion ◽

Stress Corrosion Cracking ◽

Corrosion Cracking ◽

304 Stainless Steel ◽

Specimen Width ◽

Type 304 ◽

Type 304 Stainless Steel

Download Full-text

On the Influence of Thermo-Mechanical Process History on Stress Corrosion Cracking of Solution Annealed Type 304 Stainless Steel

Contributed Papers from MS&T17 ◽

10.7449/2018mst/2018/mst_2018_738_745 ◽

2018 ◽

Author(s):

O. Al Yousif

Keyword(s):

Stainless Steel ◽

Stress Corrosion ◽

Stress Corrosion Cracking ◽

Corrosion Cracking ◽

304 Stainless Steel ◽

Mechanical Process ◽

Type 304 ◽

Type 304 Stainless Steel

Download Full-text

On the Influence of Thermo-Mechanical Process History on Stress Corrosion Cracking of Solution Annealed Type 304 Stainless Steel

Contributed Papers from MS&T17 ◽

10.7449/2018mst/2018/mst_2018_1406_1413 ◽

2018 ◽

Author(s):

O. Al Yousif

Keyword(s):

Stainless Steel ◽

Stress Corrosion ◽

Stress Corrosion Cracking ◽

Corrosion Cracking ◽

304 Stainless Steel ◽

Mechanical Process ◽

Type 304 ◽

Type 304 Stainless Steel

Download Full-text

The amount of chlorine contamination for prevention of stress corrosion cracking in sensitized type 304 stainless steel

Corrosion Science ◽

10.1016/0010-938x(85)90015-0 ◽

1985 ◽

Vol 25 (8-9) ◽

pp. 837-844 ◽

Cited By ~ 4

Author(s):

Moriyasu Tokiwai ◽

Hideo Kimura ◽

Hideo Kusanagi

Keyword(s):

Stainless Steel ◽

Stress Corrosion ◽

Stress Corrosion Cracking ◽

Corrosion Cracking ◽

304 Stainless Steel ◽

Type 304 ◽

Type 304 Stainless Steel

Download Full-text

Stress Corrosion Cracking of Austenitic Type 304 Stainless Steel in Solutions of Hydrochloric Acid + Sodium Chloride at Ambient Temperature

CORROSION ◽

10.5006/1.3293477 ◽

1994 ◽

Vol 50 (11) ◽

pp. 873-878 ◽

Cited By ~ 7

Author(s):

Z. Fang ◽

Y. Wu ◽

R. Zhu ◽

B. Cao ◽

F. Xiao

Keyword(s):

Stainless Steel ◽

Sodium Chloride ◽

Hydrochloric Acid ◽

Ambient Temperature ◽

Stress Corrosion ◽

Stress Corrosion Cracking ◽

Corrosion Cracking ◽

304 Stainless Steel ◽

Type 304 ◽

Type 304 Stainless Steel

Download Full-text

Stress corrosion cracking of sensitized Type 304 stainless steel in thiosulfate solution: I. Fate of the coupling current

Corrosion Science ◽

10.1016/s0010-938x(02)00219-6 ◽

2003 ◽

Vol 45 (7) ◽

pp. 1455-1471 ◽

Cited By ~ 28

Author(s):

Monika Gomez-Duran ◽

Digby D Macdonald

Keyword(s):

Stainless Steel ◽

Stress Corrosion ◽

Stress Corrosion Cracking ◽

Corrosion Cracking ◽

304 Stainless Steel ◽

Coupling Current ◽

Type 304 ◽

Type 304 Stainless Steel

Download Full-text

Effect of Sensitization on the Probability Distribution of Stress Corrosion Cracking Failure Times of Type 304 Stainless Steel

Corrosion engineering digest ◽

10.3323/jcorr1974.35.2_83 ◽

1986 ◽

Vol 35 (2) ◽

pp. 83-89

Author(s):

Toshio Shibata ◽

Jun Horikawa ◽

Junji Nakata

Keyword(s):

Stainless Steel ◽

Probability Distribution ◽

Stress Corrosion ◽

Stress Corrosion Cracking ◽

Corrosion Cracking ◽

304 Stainless Steel ◽

Failure Times ◽

Distribution Of Stress ◽

Type 304 ◽

Type 304 Stainless Steel

Download Full-text