Direct Observations of Stress Corrosion Crack Tips of Type 304 Stainless Steel in a Boiling 42% MgCl2Solution

Takenori Nakayama; Michinori Takano

doi:10.5006/1.3577275

Direct Observations of Stress Corrosion Crack Tips of Type 304 Stainless Steel in a Boiling 42% MgCl2Solution

CORROSION ◽

10.5006/1.3577275 ◽

1981 ◽

Vol 37 (4) ◽

pp. 226-231 ◽

Cited By ~ 24

Author(s):

Takenori Nakayama ◽

Michinori Takano

Keyword(s):

Stainless Steel ◽

Stress Corrosion ◽

Stress Corrosion Crack ◽

304 Stainless Steel ◽

Direct Observations ◽

Crack Tips ◽

Type 304 ◽

Type 304 Stainless Steel

Download Full-text

Intergranular Stress Corrosion Crack Growth of Sensitized Type 304 Stainless Steel in a Simulated Boiling-Water Reactor Environment

CORROSION ◽

10.5006/1.3280472 ◽

1997 ◽

Vol 53 (4) ◽

pp. 306-311 ◽

Cited By ~ 13

Author(s):

E. Kikuchi ◽

M. ltow ◽

J. Kuniya ◽

H. Sakamoto ◽

M. Yamamoto ◽

...

Keyword(s):

Stainless Steel ◽

Stress Corrosion ◽

Stress Corrosion Crack ◽

Crack Growth ◽

Boiling Water ◽

304 Stainless Steel ◽

Intergranular Stress Corrosion ◽

Water Reactor ◽

Type 304 ◽

Type 304 Stainless Steel

Download Full-text

AE response of type 304 stainless steel during stress corrosion crack propagation

Corrosion Science ◽

10.1016/j.corsci.2008.08.028 ◽

2008 ◽

Vol 50 (12) ◽

pp. 3382-3388 ◽

Cited By ~ 28

Author(s):

M.G. Alvarez ◽

P. Lapitz ◽

J. Ruzzante

Keyword(s):

Stainless Steel ◽

Crack Propagation ◽

Stress Corrosion ◽

Stress Corrosion Crack ◽

304 Stainless Steel ◽

Type 304 ◽

Type 304 Stainless Steel

Download Full-text

ChemInform Abstract: MORPHOLOGY OF TRANSGRANULAR STRESS CORROSION CRACK IN TYPE 304 STAINLESS STEEL TESTED IN PH 2,5 H2SO4 AT 289 DEGREES

Chemischer Informationsdienst ◽

10.1002/chin.197448058 ◽

1974 ◽

Vol 5 (48) ◽

Author(s):

DAVID A. VERMILYEA

Keyword(s):

Stainless Steel ◽

Stress Corrosion ◽

Stress Corrosion Crack ◽

304 Stainless Steel ◽

Type 304 ◽

Type 304 Stainless Steel

Download Full-text

Morphology of Transgranular Stress Corrosion Crack in Type 304 Stainless Steel Tested in pH 2.5 H[sub 2]SO[sub 4] at 289°C

Journal of The Electrochemical Society ◽

10.1149/1.2402008 ◽

1974 ◽

Vol 121 (9) ◽

pp. 1190 ◽

Cited By ~ 8

Author(s):

David A. Vermilyea

Keyword(s):

Stainless Steel ◽

Stress Corrosion ◽

Stress Corrosion Crack ◽

304 Stainless Steel ◽

Type 304 ◽

Type 304 Stainless Steel

Download Full-text

Effect of Hydrogen Peroxide on Stress Corrosion Cracking of Type 304 Stainless Steel

Corrosion engineering digest ◽

10.3323/jcorr1974.33.1_33 ◽

1984 ◽

Vol 33 (1) ◽

pp. 33-36

Author(s):

Eiji Kikuchi ◽

Noriyuki Ohnaka ◽

Akira Minato

Keyword(s):

Hydrogen Peroxide ◽

Stainless Steel ◽

Stress Corrosion ◽

Stress Corrosion Cracking ◽

Corrosion Cracking ◽

304 Stainless Steel ◽

Type 304 ◽

Type 304 Stainless Steel

Download Full-text

Fractographic Observations on Chloride Stress Corrosion Cracking of Type 304 Stainless Steel under Salt Crust / Fraktographische Untersuchung der chloridinduzierten Spannungsrißkorrosion von Typ 304-Stahl unter einer Salzkruste

Practical Metallography ◽

10.1515/pm-1996-330807 ◽

1996 ◽

Vol 33 (8) ◽

pp. 421-430

Author(s):

Nurhan Cansever ◽

Ali Fuat Çakır ◽

Mustafa Ürgen

Keyword(s):

Stainless Steel ◽

Stress Corrosion ◽

Stress Corrosion Cracking ◽

Corrosion Cracking ◽

304 Stainless Steel ◽

Salt Crust ◽

Type 304 ◽

Type 304 Stainless Steel ◽

Chloride Stress Corrosion Cracking

Download Full-text

Acoustic emission characteristics of stress corrosion cracks in a type 304 stainless steel tube

Nuclear Engineering and Technology ◽

10.1016/j.net.2015.04.001 ◽

2015 ◽

Vol 47 (4) ◽

pp. 454-460 ◽

Cited By ~ 11

Author(s):

Woonggi Hwang ◽

Seunggi Bae ◽

Jaeseong Kim ◽

Sungsik Kang ◽

Nogwon Kwag ◽

...

Keyword(s):

Stainless Steel ◽

Acoustic Emission ◽

Stress Corrosion ◽

Steel Tube ◽

304 Stainless Steel ◽

Stainless Steel Tube ◽

Emission Characteristics ◽

Type 304 ◽

Type 304 Stainless Steel

Download Full-text

On the Influence of Thermo-Mechanical Process History on Stress Corrosion Cracking of Solution Annealed Type 304 Stainless Steel

Contributed Papers from MS&T17 ◽

10.7449/2018/mst_2018_738_745 ◽

2018 ◽

Author(s):

O. Al Yousif

Keyword(s):

Stainless Steel ◽

Stress Corrosion ◽

Stress Corrosion Cracking ◽

Corrosion Cracking ◽

304 Stainless Steel ◽

Mechanical Process ◽

Type 304 ◽

Type 304 Stainless Steel

Download Full-text

Effect of Specimen Width on Stress Corrosion Cracking of Type 304 Stainless Steel

CORROSION ◽

10.5006/1.3316002 ◽

1993 ◽

Vol 49 (10) ◽

pp. 796-801 ◽

Cited By ~ 10

Author(s):

R. Nishimura

Keyword(s):

Stainless Steel ◽

Stress Corrosion ◽

Stress Corrosion Cracking ◽

Corrosion Cracking ◽

304 Stainless Steel ◽

Specimen Width ◽

Type 304 ◽

Type 304 Stainless Steel

Download Full-text

On the Influence of Thermo-Mechanical Process History on Stress Corrosion Cracking of Solution Annealed Type 304 Stainless Steel

Contributed Papers from MS&T17 ◽

10.7449/2018mst/2018/mst_2018_738_745 ◽

2018 ◽

Author(s):

O. Al Yousif

Keyword(s):

Stainless Steel ◽

Stress Corrosion ◽

Stress Corrosion Cracking ◽

Corrosion Cracking ◽

304 Stainless Steel ◽

Mechanical Process ◽

Type 304 ◽

Type 304 Stainless Steel

Download Full-text