Stress Corrosion Cracking and Life Prediction Evaluation of Austenitic Stainless Steels in Calcium Chloride Solution

CORROSION ◽  
1996 ◽  
Vol 52 (5) ◽  
pp. 337-346 ◽  
Author(s):  
H. Leinonen
Keyword(s):  
Stress Corrosion ◽  
Calcium Chloride ◽  
Stress Corrosion Cracking ◽  
Stainless Steels ◽  
Life Prediction ◽  
Chloride Solution ◽  
Austenitic Stainless Steels ◽  
Calcium Chloride Solution ◽  
Corrosion Cracking ◽  
Prediction Evaluation

Effect of Surface Treatment on the Stress Corrosion Cracking of 304 Austenitic Stainless Steels in Acid Chloride Solution

2015 ◽  
Vol 1095 ◽  
pp. 433-436
Author(s):  
Liu Yi Huang ◽  
Si Hai Li ◽  
Huai Qiu Zhu ◽  
Dong Yue Cheng ◽  
Fang Fang Zhang
Keyword(s):  
Stress Corrosion ◽  
Stress Corrosion Cracking ◽  
Acid Chloride ◽  
Stainless Steels ◽  
Chloride Solution ◽  
Austenitic Stainless Steels ◽  
Fracture Morphology ◽  
Corrosion Cracking ◽  
Tensile Tester ◽  
Shock Peening

A slow strain rate tensile (SSRT) test was used to investigate the effect of laser shock peening (LSP) on stress corrosion cracking (SCC) behavior of the 304 austenitic stainless steels (ASSs) in acid chloride solution. Mechanical properties and fracture morphology evolutions of the 304 ASSs were studied as a function of the pulse energies through slow speed tensile tester and scanning electron microscopy (SEM). The results showed that the percentage elongation after fracture increased significantly as the pulse energy rose. Fractographic examination revealed that all the samples appeared a tendency to SCC in the given conditions, but specimens treated by LSP had better resistance to stress corrosion.