Resistance welding. Destructive testing of welds. Specimen dimensions and procedure for impact tensile shear test and cross-tension testing of resistance spot and embossed projection welds

2015 ◽  
Keyword(s):  
Shear Test ◽  
Resistance Welding ◽  
Tensile Shear ◽  
Destructive Testing ◽  
Resistance Spot ◽  
Tension Testing ◽  
Cross Tension

Resistance Spot Welding in Non-Combustible Magnesium Alloy

2020 ◽  
Author(s):  
Xuanyi Shao ◽  
Yukio Miyashita ◽  
Duriyathep Panwised ◽  
Rattana Borrisutthekul
Keyword(s):  
Magnesium Alloy ◽  
Resistance Spot Welding ◽  
Spot Welding ◽  
Shear Test ◽  
Dissimilar Materials ◽  
Maximum Load ◽  
Tensile Shear ◽  
Similar Material ◽  
Resistance Spot ◽  
Surface Polishing

Abstract Resistance spot welding (RSW) was applied to non-combustible magnesium alloy, AX41 (Mg-4%Al-1%Ca) to investigate its weldability. The similar material joint of AX41 and dissimilar materials joint between AX41 and aluminum alloy, AA6061 were welded. Tensile shear test was carried out to evaluate joining strength in the similar and dissimilar materials RSW joints. In case of similar material joints, the maximum load obtained with tensile shear test in AX41 similar material joint was higher than that obtained in AA6061 similar material joint. Moreover, higher maximum load was obtained in a similar material joint without surface polishing compared to joint welded with surface polishing in AX41. In case of the dissimilar materials joint, the maximum load obtained was almost comparable with AX41 similar material joint, however scatter in joint strength was large. Weldability of the dissimilar materials joint became poor by applying surface polishing.

Influence of Paint Baking on the Energy Absorption and Failure Mode of Resistance Spot Welds in TRIP1180 Steel

2021 ◽  
Vol 143 (9) ◽  
Author(s):  
D. V. Marshall ◽  
D. Bhattacharya ◽  
J. G. Speer
Keyword(s):  
Energy Absorption ◽  
Failure Mode ◽  
Low Energy ◽  
Interfacial Failure ◽  
Spot Welds ◽  
Resistance Spot ◽  
Pull Out ◽  
Resistance Spot Welds ◽  
Tension Testing ◽  
Cross Tension

Abstract Resistance spot welds (RSWs) in advanced high strength steels frequently exhibit interfacial failure during cross-tension testing: a mode of fracture associated with low-energy absorption. Automotive assembly lines include a paint application and baking cycle after the vehicle assembly and joining processes to cure paint and any adhesives used for assembly. In this article, the effects of a typical baking cycle: 180 °C for 20 min, on the failure mode and energy absorption during cross-tension testing of RSWs made in a TRIP1180 steel are reported. Further, short-time baking cycles of 30 s, 90 s, and 4 min were employed to investigate how quickly these baking effects are activated. RSWs, which exhibited interfacial failure and a low-energy absorption of 30.9 J in the as-welded condition, saw a change in a failure mode to partial interfacial failure and a 260% increase in energy absorption after baking for 30 s. After baking for a longer time (4 min), welds failed by button pull-out and exhibited a 296% increase in energy absorption during cross-tension testing. Baking for the full 20 min resulted in no additional improvement than was observed in the 4 min condition. The mechanisms responsible for the majority of the improvement in weld performance during baking are found to be activated after only 30 s of baking.