Studies at the Pacific Northwest National Laboratory in Richland, Washington, are being conducted to evaluate nondestructive examination approaches for inspecting butt fusion joints in high density polyethylene (HDPE) pipe for lack of fusion (LOF). The work provides information to the United States Nuclear Regulatory Commission on the effectiveness and need for volumetric inspection techniques of HDPE butt fusion joints in Section III, Division 1, Class 3, buried piping systems in nuclear power plants. This paper describes results from preliminary assessments using ultrasonic nondestructive techniques and high-speed tensile impact testing for determining joint integrity. A series of butt joints were fabricated in 3408, 12-inch IPS DR-11 material by varying the fusion parameters in attempts to provide good joints and joints containing LOF. These butt joints were visually examined and volumetrically examined with time-of-flight diffraction (TOFD) and phased-array (PA) ultrasound. A limited subset of pipe joint material was destructively analyzed by either slicing through the joint and visually examining the surface or by employing a standard high-speed tensile impact test. Initial correlation of the fusion parameters, nondestructive, and destructive evaluations have shown that areas with gross LOF were detected with both TOFD and PA ultrasound and that the tensile impact test showed a brittle failure at the joint. There is still some ambiguity in results from the less obvious LOF conditions. Current work is targeted on assessing the sensitivity of the ultrasonic volumetric examinations and validating the results with a destructive analysis. It is expected that on-going and future work will lead to quantifying the ultrasonic responses in terms of joint integrity.
Nylon-6/rubber blends: 6. Notched tensile impact testing of nylon-6/(ethylene-propylene rubber) blends