scholarly journals The Influence of Chosen Plant Fillers in PHBV Composites on the Processing Conditions, Mechanical Properties and Quality of Molded Pieces

Polymers ◽  
2021 ◽  
Vol 13 (22) ◽  
pp. 3934
Author(s):  
Wiesław Frącz ◽  
Grzegorz Janowski ◽  
Robert Smusz ◽  
Marek Szumski
Keyword(s):  
Mechanical Properties ◽  
Current Trend ◽  
Natural Fibers ◽  
Injection Molding Process ◽  
Molding Process ◽  
Hemp Fibers ◽  
Technical Parameters ◽  
Flax Fibers ◽  
Positive Effect

This work is inspired by the current European policies that aim to reduce plastic waste. This is especially true of the packaging industry. The biocomposites developed in the work belong to the group of environmentally friendly plastics that can reduce the increasing costs of environmental fees in the future. Three types of short fibers (flax, hemp and wood) with a length of 1 mm each were selected as fillers (30% mass content in PHBV). The biocomposites were extruded and then processed by the injection molding process with the same technical parameters. The samples obtained in this way were tested for mechanical properties and quality of the molded pieces. A significant improvement of some mechanical properties of biocomposites containing hemp and flax fibers and quality of molded pieces was obtained in comparison with pure PHBV. Only in the case of wood–PHBV biocomposites was no significant improvement of properties obtained compared to biocomposites with other fillers used in this research. The use of natural fibers, in particular hemp fibers as a filler in the PHBV matrix, in most cases has a positive effect on improving the mechanical properties and quality of molded pieces. In addition, it should be remembered that the obtained biocomposites are of natural origin and are fully biodegradable, which are interesting and desirable properties that are a part of the current trend regarding the production and commercialization of modern biomaterials.

scholarly journals The Structure and Mechanical Properties of Hemp Fibers-Reinforced Poly(ε-Caprolactone) Composites Modified by Electron Beam Irradiation

2021 ◽  
Vol 11 (12) ◽  
pp. 5317
Author(s):  
Rafał Malinowski ◽  
Aneta Raszkowska-Kaczor ◽  
Krzysztof Moraczewski ◽  
Wojciech Głuszewski ◽  
Volodymyr Krasinskyi ◽  
...  
Keyword(s):  
Mechanical Properties ◽  
Tensile Strength ◽  
Electron Beam ◽  
Impact Strength ◽  
Flexural Modulus ◽  
Natural Fibers ◽  
High Energy ◽  
Electron Radiation ◽  
Elongation At Break ◽  
Hemp Fibers

The need for the development of new biodegradable materials and modification of the properties the current ones possess has essentially increased in recent years. The aim of this study was the comparison of changes occurring in poly(ε-caprolactone) (PCL) due to its modification by high-energy electron beam derived from a linear electron accelerator, as well as the addition of natural fibers in the form of cut hemp fibers. Changes to the fibers structure in the obtained composites and the geometrical surface structure of sample fractures with the use of scanning electron microscopy were investigated. Moreover, the mechanical properties were examined, including tensile strength, elongation at break, flexural modulus and impact strength of the modified PCL. It was found that PCL, modified with hemp fibers and/or electron radiation, exhibited enhanced flexural modulus but the elongation at break and impact strength decreased. Depending on the electron radiation dose and the hemp fibers content, tensile strength decreased or increased. It was also found that hemp fibers caused greater changes to the mechanical properties of PCL than electron radiation. The prepared composites exhibited uniform distribution of the dispersed phase in the polymer matrix and adequate adhesion at the interface between the two components.

The Effect of Heat Treatment on Mechanical Properties of Car Interior Fabric Used for Injection Molding

2012 ◽  
Vol 532-533 ◽  
pp. 234-237
Author(s):  
Wei Lai Chen ◽  
Ding Hong Yi ◽  
Jian Fu Zhang
Keyword(s):  
Mechanical Properties ◽  
Heat Treatment ◽  
High Temperature ◽  
Injection Molding ◽  
High Temperatures ◽  
Material Properties ◽  
Injection Molding Process ◽  
Molding Process ◽  
Composite Fabrics

The purpose of this paper is to study the effect of high temperature in injection molding process on mechanical properties of the warp-knitted and nonwoven composite fabrics (WNC)used in car interior. Tensile, tearing and peeling properties of WNC fabrics were tested after heat treatment under120, 140,160,180°C respectively. It was found that, after 140°C heat treatment, the breaking and tearing value of these WNC fabrics are lower than others. The results of this study show that this phenomenon is due to the material properties of fabrics. These high temperatures have no much effect on peeling properties of these WNC fabrics. It is concluded that in order to preserve the mechanical properties of these WNC fabrics, the temperature near 140°C should be avoided possibly during injection molding process.

Tribology study of hydroxyapatite (HAp) scaffold blended single based binder via rheology and mechanical properties

2017 ◽  
Vol 69 (3) ◽  
pp. 414-419
Author(s):  
Mimi Azlina Abu Bakar ◽  
Siti Norazlini Abd Aziz ◽  
Muhammad Hussain Ismail
Keyword(s):  
Mechanical Properties ◽  
Injection Molding ◽  
Palm Stearin ◽  
Polymeric Materials ◽  
High Energy ◽  
Single Step ◽  
Injection Molding Process ◽  
Plastic Behavior ◽  
Molding Process ◽  
Content Type

Purpose This paper aims to investigate the vital characteristic of an innovative ceramic injection molding (CIM) process for orthopedic application with controlled porosity and improved tribological and mechanical properties which were affected by complex tribological interactions, whether lubricated like hip implants and other artificial prostheses. The main objective is to maximize the usage of palm stearin as a single based binder as the function of flow properties during injection molding process. Design/methodology/approach The binder used in this present study consists of 100 per cent palm stearin manufactured by Kempas Oil Sdn Bhd and supplied by Vistec Technology Sdn Bhd. The feedstock was prepared by using a Z-blade mixer (Thermo Haake Rheomix OS) and Brabender mixer model R2400. The feedstock prepared was injection molded using a manually operated vertical benchtop machine with an average pressure of about 5-7 bars. The firing step included the temporary holds at intermediate temperatures to burn out organic binders. At this stage, the green molded specimen was de-bound using a single-step wick-debinding method. Findings The maximum content of ceramic material is applied to investigate the efficiencies of net formulation that can be achieved by ceramic materials. The longer the viscosity will change with shear rate, the higher the value of n obtained instead. From the slope of the curves obtained in Figure 3, the value of n for the feedstock was determined to be less than 1, which indicates a pseudoplastic behavior and suitability for the molding process. Moreover, high shear sensitivity is important in producing complex and intrinsic specimens which are leading products in the CIM industry. Originality/value The feedstock containing HAp powder and palm stearin binder was successfully prepared at very low temperature of 70°C, which promoting a required pseudo-plastic behavior during rheological test. The single binder palm stearin should be optimized in other research works carried out, as palm stearin is most preferred compared to other polymeric materials that provided high energy consumption when subjected to the sintering process. Besides the binder is widely available in Malaysia, low cost and harmless effect during debinding process.

Prediction of Elastic Modulus of Glass Short Fiber/Wood Powder/Polypropylene Hybrid Composites

2013 ◽  
Author(s):  
Ying Yu ◽  
Manabu Nomura ◽  
Hiroyuki Hamada
Keyword(s):  
Mechanical Properties ◽  
Elastic Modulus ◽  
Hybrid Composites ◽  
Length Distribution ◽  
Wood Particle ◽  
Short Fiber ◽  
Injection Molding Process ◽  
Orientation Factor ◽  
Wood Powder ◽  
Molding Process

Recent years, thermoplastics incorporated with particulate fillers have been gained high interests. To improve the mechanical properties of the natural particle reinforced polymer plastics, hybrid structure has been applied on the composite combining natural particle with stronger synthetic fibers. However, the reinforcing mechanism of the hybrid composite is quite complicated. Experiments on it may become time consuming and cost prohibitive. Therefore, researchers are interested in studying variable models to predict the elastic properties of the composites. In this study, glass short fiber/wood particle/pp hybrid composites were prepared by injection molding process at a fixed reinforcement to matrix ratio of 51:49. 4 kinds of hybrid specimens with glass fiber/wood particle ratios of 41:10, 31:20, 21:30 and 11:40 were fabricated. The effect of hybridization content on the mechanical properties of the composites was evaluated based on tensile test. Theoretically, the elastic modulus of hybrid composites was predicted by using the rule of hybrid mixtures (RoHM) equation and classical lamination theory (CLT) and the accuracy of the two estimation models has been discussed. Results showed that it can be considered the hybridization of wood powder into glass/PP composite could contribute to a similar high elastic modulus with high green degree. On the other hand, the fiber orientation factor, fiber length distribution factor, powder dispersion factor were very important factors and need to be considered in the prediction model.

Manufacturing and High Temperature Mechanical Properties of Inconel 713C by Using Metal Injection Molding

2012 ◽  
Vol 602-604 ◽  
pp. 627-630 ◽  
Author(s):  
Kyu Sik Kim ◽  
Kee Ahn Lee ◽  
Jong Ha Kim ◽  
Si Woo Park ◽  
Kyu Sang Cho
Keyword(s):  
Mechanical Properties ◽  
High Temperature ◽  
Injection Molding ◽  
Room Temperature ◽  
Tensile Tests ◽  
Metal Injection Molding ◽  
Injection Molding Process ◽  
Molding Process ◽  
High Temperature Mechanical Properties ◽  
Inconel 713C

Inconel 713C alloy was tried to manufacture by using MIM(Metal Injection Molding) process. The high-temperature mechanical properties of MIMed Inconel 713C were also investigated. Processing defects such as pores and binders could be observed near the surface. Tensile tests were conducted from room temperature to 900°C. The result of tensile tests showed that this alloy had similar or somewhat higher strengths (YS: 734 MPa, UTS: 968 MPa, elongation: 7.16 % at room temperature) from RT to 700°C than those of conventional Inconel 713C alloys. Above 800°C, however, ultimate tensile strength decreased rapidly with increasing temperature (lower than casted Inconel 713C). Based on the observation of fractography, initial crack was found to have started near the surface defects and propagated rapidly. The superior mechanical properties of MIMed Inconel 713C could be obtained by optimizing the MIM process parameters.

scholarly journals Holding Pressure and Its Influence on Quality in PIM Technology

10.14311/1608 ◽  
2012 ◽  
Vol 52 (4) ◽  
Author(s):  
Pavel Petera
Keyword(s):  
Phase Separation ◽  
Injection Molding ◽  
Density Measurement ◽  
Powder Injection Molding ◽  
New Method ◽  
Powder Injection ◽  
Injection Molding Process ◽  
Molding Process

The PIM (powder injection molding) process consists of several steps in which faults can occur. The quality of the part that is produced usually cannot be seen until the end of the process. It is therefore necessary to find a way to discover the fault earlier in the process. The cause of defects is very often “phase separation” (inhomogeneity in powder distribution), which can also be influenced by the holding pressure. This paper evaluates the powder distribution with a new method based on density measurement. Measurements were made using various holding pressure values.

Process comparison on the microstructure and mechanical properties of fiber-reinforced polyphenylene sulfide using MuCell technology

2018 ◽  
Vol 37 (15) ◽  
pp. 1020-1034 ◽  
Author(s):  
Christoph Lohr ◽  
Björn Beck ◽  
Frank Henning ◽  
Kay André Weidenmann ◽  
Peter Elsner
Keyword(s):  
Mechanical Properties ◽  
High Pressure ◽  
Injection Molding ◽  
Fiber Orientation ◽  
Polyphenylene Sulfide ◽  
Injection Molding Process ◽  
Fiber Reinforced ◽  
Molding Process ◽  
Glass Fiber Reinforced ◽  
Foam Injection Molding

The MuCell process is a special injection molding process which utilizes supercritical gas (nitrogen) to create integral foam sandwiches. The advantages are lower weight, higher specific properties and shorter cycle times. In this study, a series of glass fiber-reinforced polyphenylene sulfide foam blanks are manufactured using the MuCell injection molding process. The different variations of the process (low-pressure also known as structural foam injection molding) and high-pressure foam injection molding (also known as “core back expansion,” “breathing mold,” “precision opening,” decompression molding) are used. The sandwich structure and mechanical properties (tensile strength, bending strength, and impact behavior) of the microcellular and glass fiber-reinforced polyphenylene sulfide foams are systematically investigated and compared to compact material. The results showed that the injection parameters (injection speed, foaming mechanism) played an important role in the relative density of microcellular polyphenylene sulfide foams and the mechanical properties. It could be shown that the specific tensile strength decreased while increasing the degree of foaming which can be explained by the increased number of cells and the resulting cell size. This leads to stress peaks which lower the mechanical properties. The Charpy impact strength shows a significant dependence on the fiber orientation. The specific bending modulus of the high-pressure foaming process, however, surpasses the values of the other two processes showing the potential of this manufacturing variation especially with regard to bending loads. Furthermore, a high dependence of the mechanical properties on the fiber orientation of the tested specimens can be found.

Sign in / Sign up

Export Citation Format

Share Document