scholarly journals Aging Mechanisms and Non-Destructive Aging Indicators of XLPE/CSPE Unshielded LV Nuclear Power Cables Subjected to Simultaneous Radiation-Mechanical Aging

Polymers ◽  
2021 ◽  
Vol 13 (18) ◽  
pp. 3033
Author(s):  
Ramy S. A. Afia ◽  
Ehtasham Mustafa ◽  
Zoltán Ádám Tamus
Keyword(s):  
Mechanical Properties ◽  
Nuclear Power ◽  
Power Plants ◽  
Low Voltage ◽  
Voltage Response ◽  
Power Cables ◽  
Mechanical Parameters ◽  
Electrical Parameters ◽  
Cable Systems ◽  
Non Destructive

Low-voltage cable systems in nuclear power plants are key components that have a crucial role in the safe operation of nuclear facilities. Thus, the aging management of cable systems is of utmost importance as they cannot easily or economically be replaced or upgraded. Therefore, there is a continuous need to develop reliable non-destructive condition monitoring techniques, mostly based on the measurement of the dielectric properties of cable insulation. This paper introduces the changing of dielectric and mechanical properties of XLPE insulated and CSPE jacketed unshielded low-voltage nuclear power plant power cable in case of simultaneous mechanical and radiation aging. The cable samples were bent and exposed to 400 kGy gamma irradiation with a 0.5 kGy/hr dose rate. Dielectric response (real and imaginary permittivity) in the 0.1 Hz−1 kHz frequency range, extended voltage response (EVR), and the Shore D hardness test techniques were measured to track aging. The electrical and mechanical parameters have increased monotonically with aging, except the imaginary permittivity, which increased only at frequencies higher than 10 Hz. Furthermore, different quantities were deducted based on the frequency and permittivity data. The electrical parameters and deducted quantities correlation with aging and mechanical parameters were investigated. Since the deducted quantities and the electrical parameters are strongly correlated with absorbed dose and mechanical properties, the electrical measurements can be applied as a non-destructive aging indicator for XLPE/CSPE unshielded low-voltage nuclear power cables.

scholarly journals Implementation of Non-Destructive Electrical Condition Monitoring Techniques on Low-Voltage Nuclear Cables: I. Irradiation Aging of EPR/CSPE Cables

Energies ◽  
2021 ◽  
Vol 14 (16) ◽  
pp. 5139
Author(s):  
Ehtasham Mustafa ◽  
Ramy S. A. Afia ◽  
Oumaima Nouini ◽  
Zoltán Ádám Tamus
Keyword(s):  
Condition Monitoring ◽  
Nuclear Power ◽  
Power Plants ◽  
Low Voltage ◽  
Research Work ◽  
Life Extension ◽  
Voltage Response ◽  
Elongation At Break ◽  
Monitoring Technique ◽  
Non Destructive

In a nuclear power plant environment, low-voltage cables experience different stresses during their service life which challenge their integrity. A non-destructive and reliable condition monitoring technique is desired to determine the state of these low-voltage cables during service and for the life extension of nuclear power plants. Hence, in this research work, an EPR/CSPE-based low-voltage cable was exposed to γ-rays for five different absorbed doses. The overall behavior of the cable under stress was characterized by frequency and time domain electrical measurements (capacitance, tan δ, and Extended Voltage Response) and a mechanical measurement (elongation at break). Significant variations in the electrical parameters were observed, as was a decline in the elongation at break values. A strong correlation between the measurement methods was observed, showing the ability of the electrical methods to be adopted as a non-destructive condition monitoring technique.

scholarly journals Broadband Dielectric Spectroscopy: A Viable Technique for Aging Assessment of Low-Voltage Cable Insulation Used in Nuclear Power Plants

Polymers ◽  
2021 ◽  
Vol 13 (4) ◽  
pp. 494
Author(s):  
Davide Fabiani ◽  
Simone Vincenzo Suraci
Keyword(s):  
Mechanical Properties ◽  
Nuclear Power ◽  
Power Plants ◽  
Low Voltage ◽  
Irradiation Effect ◽  
Cable Insulation ◽  
Dose Rates ◽  
Broadband Dielectric Spectroscopy ◽  
Long Time ◽  
Nuclear Environment

This paper deals with the study of a non-destructive technique to detect the aging state of cable insulation used in a nuclear environment subjected to radiation and temperature aging. Cable samples were aged under dose rates ranging from 0.42 and 1.06 kGy/h at 55 and 85 °C. The imaginary part of the permittivity at 100 kHz is found to correlate well with mechanical properties, such as elongation at break, which is typically used to diagnose cable insulation, but it is a destructive property and cannot be used on field. It has been demonstrated also that a post-irradiation effect occurs even years after aging is stopped, increasing the imaginary permittivity and worsening mechanical properties due to the slow conversion of radicals into oxidized species. The main consequence is that when cable insulation is subjected to a nuclear accident, releasing a huge amount of radiation, the health of cable insulation must be followed also for a long time after the accident occurred, since aging due to oxidation progresses even when the radiation source is switched off.

scholarly journals Dielectric loss and extended voltage response measurements for low-voltage power cables used in nuclear power plant: potential methods for aging detection due to thermal stress

2020 ◽  
Author(s):  
Ehtasham Mustafa ◽  
Ramy S. A. Afia ◽  
Zoltán Ádám Tamus
Keyword(s):  
Thermal Stress ◽  
Power Plant ◽  
Nuclear Power Plant ◽  
Nuclear Power ◽  
Low Voltage ◽  
Voltage Response ◽  
Insulation Material ◽  
Power Cables ◽  
Response Measurement ◽  
Low Frequencies

Abstract This paper discusses the effect of thermal stress on the electrical properties, conduction and polarization, of low-voltage CSPE/XLPE-based power cables used in a nuclear power plant. The cables were subjected to an accelerated thermal stress at 120°C for an equivalent service period of 20, 40, 60 and 80 years. The capacitance, tanδ, resistivity at different frequencies and extended voltage response were the methods used for the investigation. A significant variation in the values of tanδ at low frequency, i.e., at 100 Hz, was observed. For the extended voltage response measurement, the decay voltage slope increased, showing the increase in the conduction particles inside the insulation material. While the decrease in return voltage slope showed that the slow polarization processes occurring at very low frequencies were decreased with aging. A strong correlation between the tanδ and decay voltage slope was also observed, which increased as the insulation aging increased. The results showed that the methods could be used for the in situ measurement of conduction and polarization phenomenon in the low-voltage cables, and hence helping in the assessment of the condition of cable insulation.

Human reliability in non-destructive inspections of nuclear power plant components: modeling and analysis

2019 ◽  
Vol 7 (2B) ◽  
Author(s):  
Vanderley Vasconcelos ◽  
Wellington Antonio Soares ◽  
Raissa Oliveira Marques ◽  
Silvério Ferreira Silva Jr ◽  
Amanda Laureano Raso
Keyword(s):  
Power Plant ◽  
Nuclear Power Plant ◽  
Human Factors ◽  
Nuclear Power ◽  
Power Plants ◽  
Failure Modes ◽  
Cooling System ◽  
Human Reliability ◽  
Non Destructive ◽  
Plant Components

Non-destructive inspection (NDI) is one of the key elements in ensuring quality of engineering systems and their safe use. This inspection is a very complex task, during which the inspectors have to rely on their sensory, perceptual, cognitive, and motor skills. It requires high vigilance once it is often carried out on large components, over a long period of time, and in hostile environments and restriction of workplace. A successful NDI requires careful planning, choice of appropriate NDI methods and inspection procedures, as well as qualified and trained inspection personnel. A failure of NDI to detect critical defects in safety-related components of nuclear power plants, for instance, may lead to catastrophic consequences for workers, public and environment. Therefore, ensuring that NDI is reliable and capable of detecting all critical defects is of utmost importance. Despite increased use of automation in NDI, human inspectors, and thus human factors, still play an important role in NDI reliability. Human reliability is the probability of humans conducting specific tasks with satisfactory performance. Many techniques are suitable for modeling and analyzing human reliability in NDI of nuclear power plant components, such as FMEA (Failure Modes and Effects Analysis) and THERP (Technique for Human Error Rate Prediction). An example by using qualitative and quantitative assessesments with these two techniques to improve typical NDI of pipe segments of a core cooling system of a nuclear power plant, through acting on human factors issues, is presented.

The application efficiency of intumescent coatings for power cables of safety systems of nuclear power plants under fire conditions

2021 ◽  
Vol 30 (4) ◽  
pp. 36-47
Author(s):  
O. S. Lebedchenko ◽  
S. V. Puzach ◽  
V. I. Zykov
Keyword(s):  
Outer Surface ◽  
Nuclear Power ◽  
Power Plants ◽  
Nuclear Power Plants ◽  
Fire Retardant ◽  
Insulation Material ◽  
Power Cables ◽  
Fire Retardants ◽  
Safety Systems ◽  
Fire Conditions

Introduction. The reliable operation of safety systems, that allows for the failure of no more than one safety system component, entails the safe shutdown and cool-down of an NPP reactor in the event of fire. However, the co-authors have not assessed the loss of performance by an insulating material, treated by intumescent compositions and used in the power cables of the above safety systems exposed to the simultaneous effect of various modes of fire and current loads.Goals and objectives. The purpose of the article is the theoretical assessment of the application efficiency of intumescent fire-retardant coatings in power cables used in the safety systems of nuclear power plants having water-cooled and water-moderated reactors under fire conditions. To achieve this goal, the temperature of the outer surface of the insulation and the intumescent fire-retardant coating was analyzed depending on the mode of fire. Theoretical foundations. A non-stationary one-dimensional heat transfer equation is solved to identify the temperature distribution inside the multilayered insulation and the fire-protection layer of a conductive core.Results and their discussion. The co-authors have identified dependences between the temperature of the outer surface of the insulation and the fire retarding composition of the three-core cable VVGng (A)-LS 3x2.5-0.66, on the one hand, and the temperature of the indoor gas environment for three standard modes of fire and one real fire mode. It is found that before the initiation of the process of destruction of the insulation material, the intumescence of the fire-retardant coating occurs only in case of a hydrocarbon fire. Under real fire conditions, the maximal insulation melting time before the initiation of intumescence of the fire-retardant coating at the minimal temperature of intumescence is 4.75 minutes, while the maximal time period from the initiation of destruction of the insulation material to the moment of the insulation melting is 6.0 minutes.Conclusions. An experimental or theoretical substantiation of parameters of intumescent fire retardants, performed using standard modes of fire, has proven the potential loss of operational properties by insulating materials of power cables, used in the safety systems of nuclear power plants, in case of a real fire. Therefore, it is necessary to establish a scientific rationale for the efficient use of fire retardants in the above cables with regard for the conditions of a real fire.

Sign in / Sign up

Export Citation Format

Share Document