scholarly journals Melt Rheology and Mechanical Characteristics of Poly(Lactic Acid)/Alkylated Graphene Oxide Nanocomposites

Polymers ◽  
2020 ◽  
Vol 12 (10) ◽  
pp. 2402
Author(s):  
In Hye Park ◽  
Jae Yoon Lee ◽  
Seung Jae Ahn ◽  
Hyoung Jin Choi
Keyword(s):  
Graphene Oxide ◽  
Lactic Acid ◽  
Flow Characteristics ◽  
Poly Lactic Acid ◽  
Rheological Analysis ◽  
Elongation At Break ◽  
Solution Blending ◽  
Reinforcing Agent ◽  
The Matrix ◽  
Filler Network

Poly(lactic acid) (PLA) nanocomposites were synthesized by a solution blending and coagulation method using alkylated graphene oxide (AGO) as a reinforcing agent. Turbiscan confirmed that the alkylation of GO led to enhanced compatibility between the matrix and the filler. The improved dispersity of the filler resulted in superior interfacial adhesion between the PLA chains and AGO basal plane, leading to enhanced mechanical and rheological properties compared to neat PLA. The tensile strength and elongation at break, i.e., ductility, increased by 38% and 42%, respectively, at the same filler content nanocomposite (PLA/AGO 1 wt %) compared to nonfiller PLA. Rheological analysis of the nanocomposites in the molten state of the samples was performed to understand the filler network formed inside the matrix. The storage modulus increased significantly from PLA/AGO 0.5 wt % (9.6 Pa) to PLA/AGO 1.0 wt % (908 Pa). This indicates a percolation threshold between the two filler contents. A steady shear test was performed to examine the melt flow characteristics of PLA/AGO nanocomposites at 170 °C, and the viscosity was predicted using the Carreau−Yasuda model.

Polylactic Acid/Impact Modifier Blends

2012 ◽  
Vol 486 ◽  
pp. 406-411 ◽  
Author(s):  
Nantharat Phruksaphithak ◽  
Cholticha Noomhorm
Keyword(s):  
Lactic Acid ◽  
Phase Separation ◽  
Tensile Properties ◽  
Interfacial Adhesion ◽  
Poly Lactic Acid ◽  
Elongation At Break ◽  
Solution Blending ◽  
Impact Modifier ◽  
Poly Ethylene ◽  
Poly Acrylonitrile

The effects of four impact modifiers: natural rubber (NR), poly (cis-1,4-isoprene) (IR), poly (acrylonitrile-co-butadiene) (NBR) and poly (ethylene-co-vinyl acetate) (PEVA), on the morphology, thermal and tensile properties by solution blending of poly (lactic acid) and 5 and 10 wt% impact modifier were investigated. Results showed that Youngs modulus and T.S. at break decreased in all PLA/impact modifier blends. In addition, Youngs modulus in all blends and T.S. at break in PLA/NR, PLA/IR and PLA/NBR blends was not significantly affected by the type and content of impact modifiers in the blends, but T.S. at break in PLA/PEVA blends was decreased by increasing the PVEA content from 5 wt% to 10 wt%. By contrast, the elongation at break significantly increased in all PLA/impact modifier blends and only PLA/NBR blends was affected by the content of impact modifier. Finally, the increase in ductility of all PLA/impact modifier blends confirmed the toughening capability of all impact modifiers. Thus, it is evident from tensile properties obtained indicated that PLA/impact modifier blends exhibit greater flexibility with all impact modifiers. Phase separation morphology of dispersion of impact modifier in PLA matrix indicating poor interfacial adhesion was observed. Tgand Tmof PLA/impact modifier blends exhibited almost the same as pure PLA, this suggested that there was no molecular interaction between PLA and impact modifiers, therefore, the PLA/impact modifier blends were immiscible.

Mechanical Properties of Bamboo Charcoal (BC)/Poly(Lactic) Acid (PLA) Composites

2019 ◽  
Vol 801 ◽  
pp. 121-126
Author(s):  
Rapeeporn Srisuk ◽  
Laongdaw Techawinyutham ◽  
Wantana Koetniyom ◽  
Rapeephun Dangtungee
Keyword(s):  
Mechanical Properties ◽  
Tensile Strength ◽  
Lactic Acid ◽  
Shear Viscosity ◽  
Tensile Modulus ◽  
Poly Lactic Acid ◽  
Bamboo Charcoal ◽  
Elongation At Break ◽  
The Matrix

The influence of bamboo charcoal (BC) in Poly (lactic) acid (PLA) matrix as masterbatch was studied on mechanical 40:60, 50:50 and 60:40 of masterbatch. BC MBs were diluted at 1 phr, 3 phr, and 5 phr. BC showed even distribution in PLA matrix; however,, it decreased compatibility in the matrix. The infusion of BC in PLA matrix enhanced the tensile modulus; however, there was a reduction in the tensile strength and the elongation at break. It could also be ascertained that there is no signification difference in the hardness of BC/PLA composites compared with neat PLA. The addition of BC slightly decreased shear viscosity of the composites. The optimal BC content in the composites was found to be 2.82wt.% (5 phr 60:40).

Mechanical, Thermal, and Morphological Properties of Thermoplastic Starch/Poly(lactic acid/Poly(butylene adipate-co-terephthalate) Blends

2014 ◽  
Vol 970 ◽  
pp. 312-316
Author(s):  
Sujaree Tachaphiboonsap ◽  
Kasama Jarukumjorn
Keyword(s):  
Lactic Acid ◽  
Impact Strength ◽  
Interfacial Adhesion ◽  
Tensile Modulus ◽  
Thermoplastic Starch ◽  
Morphological Properties ◽  
Poly Lactic Acid ◽  
Melt Blending ◽  
Elongation At Break ◽  
Blending Method

Thermoplastic starch (TPS)/poly (lactic acid) (PLA) blend and thermoplastic starch (TPS)/poly (lactic acid) (PLA)/poly (butylene adipate-co-terephthalate) (PBAT) blend were prepared by melt blending method. PLA grafted with maleic anhydride (PLA-g-MA) was used as a compatibilizer to improve the compatibility of the blends. As TPS was incorporated into PLA, elongation at break was increased while tensile strength, tensile modulus, and impact strength were decreased. Tensile properties and impact properties of TPS/PLA blend were improved with adding PLA-g-MA indicating the enhancement of interfacial adhesion between PLA and TPS. With increasing PBAT content, elongation at break and impact strength of TPS/PLA blends were improved. The addition of TPS decreased glass transition temperature (Tg), crystallization temperature (Tc), and melting temperature (Tm) of PLA. Tgand Tcof TPS/PLA blend were decreased by incorporating PLA-g-MA. However, the presence of PBAT reduced Tcof TPS/PLA blend. Thermal properties of TPS/PLA/PBAT blends did not change with increasing PBAT content. SEM micrographs revealed that the compatibilized TPS/PLA blends exhibited finer morphology when compared to the uncompatibilized TPS/PLA blend.

Tensile and water absorption properties of solvent cast biofilms of sugarcane leaves fibre-filled poly(lactic) acid

2018 ◽  
Vol 33 (3) ◽  
pp. 289-304 ◽  
Author(s):  
Kuhananthan Nanthakumar ◽  
Chan Ming Yeng ◽  
Koay Seong Chun
Keyword(s):  
Tensile Strength ◽  
Lactic Acid ◽  
Water Absorption ◽  
Young’S Modulus ◽  
Young's Modulus ◽  
Poly Lactic Acid ◽  
Infrared Analysis ◽  
Absorption Properties ◽  
Elongation At Break ◽  
Bleaching Treatment

This research covers the preparation of poly(lactic acid) (PLA)/sugarcane leaves fibre (SLF) biofilms via a solvent-casting method. The results showed that the tensile strength and Young’s modulus of PLA/SLF biofilms increased with the increasing of SLF content. Nevertheless, the elongation at break showed an opposite trend as compared to tensile strength and Young’s modulus of biofilms. Moreover, water absorption properties of PLA/SLF biofilms increased with the increasing of SLF content. In contrast, the tensile strength and Young’s modulus of biofilms were enhanced after bleaching treatment with hydrogen peroxide on SLF, but the elongation at break and water absorption properties of bleached biofilms were reduced due to the improvement of filler–matrix adhesion in biofilms. The tensile and water properties were further discussed using B-factor and Fick’s law, respectively. Furthermore, the functional groups of unbleached and bleached SLF were characterized by Fourier transform infrared analysis.

Effects of walnut shell powders on the morphology and the thermal and mechanical properties of poly(lactic acid)

2019 ◽  
Vol 33 (10) ◽  
pp. 1383-1395
Author(s):  
Hongjuan Zheng ◽  
Zhengqian Sun ◽  
Hongjuan Zhang
Keyword(s):  
Mechanical Properties ◽  
Lactic Acid ◽  
Property Testing ◽  
Walnut Shell ◽  
Poly Lactic Acid ◽  
Thermal And Mechanical Properties ◽  
Scanning Calorimetry ◽  
Elongation At Break ◽  
Heat Distortion Temperature ◽  
Testing Techniques

Poly(lactic acid) (PLA) has good environmental compatibility, however, its high brittleness, slow rate of crystallization, and low heat distortion temperature restrict its widespread use. To overcome these limitations, in this study, PLA was mixed with walnut shell (WS) powders. The effects of WS powders on the morphology and the thermal and mechanical properties of PLA were investigated. The products were characterized by differential scanning calorimetry (DSC), infrared (IR) spectroscopy, polarizing optical microscopy (POM), and various mechanical property testing techniques. The results showed that WS powders had a significant effect on the morphology and the thermal and mechanical properties of PLA. The tensile strength, impact strength, and elongation at break of the PLA/WS composites first increased and then decreased with the increasing addition of WS powders. When the addition of WS powders was about 0.5 wt%, they reached maximum values of 51.2 MPa, 23.3 MPa, and 19.0%, respectively. Compared with neat PLA, the spherulite grain size of the composites could be reduced and many irregular polygons were formed during crystallization. The melting, cold crystallization, and glass-transition temperatures of the composites were lower than those of neat PLA.

scholarly journals Release of Graphene and Carbon Nanotubes from Biodegradable Poly(Lactic Acid) Films during Degradation and Combustion: Risk Associated with the End-of-Life of Nanocomposite Food Packaging Materials

Materials ◽  
2018 ◽  
Vol 11 (12) ◽  
pp. 2346 ◽  
Author(s):  
Stanislav Kotsilkov ◽  
Evgeni Ivanov ◽  
Nikolay Vitanov
Keyword(s):  
Risk Assessment ◽  
Carbon Nanotubes ◽  
Lactic Acid ◽  
Food Packaging ◽  
Safety Concern ◽  
Barrier Properties ◽  
Nanocomposite Films ◽  
Poly Lactic Acid ◽  
Qualitative Risk Assessment ◽  
The Matrix

Nanoparticles of graphene and carbon nanotubes are attractive materials for the improvement of mechanical and barrier properties and for the functionality of biodegradable polymers for packaging applications. However, the increase of the manufacture and consumption increases the probability of exposure of humans and the environment to such nanomaterials; this brings up questions about the risks of nanomaterials, since they can be toxic. For a risk assessment, it is crucial to know whether airborne nanoparticles of graphene and carbon nanotubes can be released from nanocomposites into the environment at their end-life, or whether they remain embedded in the matrix. In this work, the release of graphene and carbon nanotubes from the poly(lactic) acid nanocomposite films were studied for the scenarios of: (i) biodegradation of the matrix polymer at the disposal of wastes; and (ii) combustion and fire of nanocomposite wastes. Thermogravimetric analysis in air atmosphere, transmission electron microscopy (TEM), atomic force microscopy (AFM) and scanning electron microscope (SEM) were used to verify the release of nanoparticles from nanocomposite films. The three factors model was applied for the quantitative and qualitative risk assessment of the release of graphene and carbon nanotubes from nanocomposite wastes for these scenarios. Safety concern is discussed in respect to the existing regulations for nanowaste stream.

scholarly journals Improving Interaction at Polymer–Filler Interface: The Efficacy of Wrinkle Texture

Nanomaterials ◽  
2020 ◽  
Vol 10 (2) ◽  
pp. 208 ◽  
Author(s):  
Pietro Russo ◽  
Virginia Venezia ◽  
Fabiana Tescione ◽  
Joshua Avossa ◽  
Giuseppina Luciani ◽  
...  
Keyword(s):  
Lactic Acid ◽  
Effective Properties ◽  
Chemical Properties ◽  
Poly Lactic Acid ◽  
Physical Interaction ◽  
Chemical Surface ◽  
Surface Areas ◽  
Polymer Filler ◽  
The Matrix ◽  
Modified Stöber Method

One of the main issues in preparing polymer-based nanocomposites with effective properties is to achieve a good dispersion of the nanoparticles into the matrix. Chemical interfacial modifications by specific coupling agents represents a good way to reach this objective. Actually, time consuming compatibilization procedures strongly compromise the sustainability of these strategies. In this study, the role of particles’ architectures in their dispersion into a poly-lactic acid matrix and their subsequent influences on physical-chemical properties of the obtained nanocomposites were investigated. Two kinds of silica nanoparticles, “smooth” and “wrinkled,” with different surface areas (≈30 and ≈600 m2/g respectively) were synthesized through a modified Stöber method and used, without any chemical surface pre-treatments, as fillers to produce poly-lactic acid based nanocomposites. The key role played by wrinkled texture in modifying the physical interaction at the polymer-filler interface and in driving composite properties, was investigated and reflected in the final bulk properties. Detailed investigations revealed the presence of wrinkled nanoparticles, leading to (i) an enormous increase of the chain relaxation time, by almost 30 times compared to the neat PLA matrix; (ii) intensification of the shear-thinning behavior at low shear-rates; and (iii) slightly slower thermal degradation of polylactic acid.

scholarly journals Investigation on compatibility of PLA/PBAT blends modified by epoxy-terminated branched polymers through chemical micro-crosslinking

e-Polymers ◽  
2020 ◽  
Vol 20 (1) ◽  
pp. 39-54 ◽  
Author(s):  
Bo Wang ◽  
Yujuan Jin ◽  
Kai’er Kang ◽  
Nan Yang ◽  
Yunxuan Weng ◽  
...  
Keyword(s):  
Lactic Acid ◽  
Glass Transition ◽  
Sem Analysis ◽  
Branched Polymers ◽  
Poly Lactic Acid ◽  
Elongation At Break ◽  
Butylene Terephthalate ◽  
The Difference ◽  
Physical And Chemical ◽  
The Impact

AbstractIn this study, a type of epoxy-terminated branched polymer (ETBP) was used as an interface compati- bilizer to modify the poly lactic acid (PLA)/poly(butylene adipate-co-butylene terephthalate) (PBAT) (70/30) blends. Upon addition of ETBP, the difference in glass transition temperature between PLA and PBAT became smaller. By adding 3.0 phr of ETBP, the elongation at break of the PLA/PBAT blends was found increased from 45.8% to 272.0%; the impact strength increased from 26.2 kJ·m−2 to 45.3 kJ·m−2. In SEM analysis, it was observed that the size of the dispersed PBAT particle decreased with the increasing of ETBP content. These results indicated that the compatibility between PLA and PBAT can be effectively enhanced by using ETBP as the modifier. The modification mechanism was discussed in detail. It proposes that both physical and chemical micro-crosslinking were formed, the latter of which was confirmed by gel content analysis.

Sign in / Sign up

Export Citation Format

Share Document