scholarly journals Moisture Absorption Effects on Mode II Delamination of Carbon/Epoxy Composites

Polymers ◽  
2020 ◽  
Vol 12 (9) ◽  
pp. 2162
Author(s):  
King Jye Wong ◽  
Mahzan Johar ◽  
Seyed Saeid Rahimian Koloor ◽  
Michal Petrů ◽  
Mohd Nasir Tamin
Keyword(s):  
Fracture Toughness ◽  
Moisture Content ◽  
Composite Structures ◽  
Moisture Absorption ◽  
Peak Load ◽  
Epoxy Composites ◽  
Mode Ii ◽  
Damage Initiation ◽  
Residual Properties ◽  
Mode Ii Fracture Toughness

It is necessary to consider the influence of moisture damage on the interlaminar fracture toughness for composite structures that are used for outdoor applications. However, the studies on the progressive variation of the fracture toughness as a function of moisture content M (%) is rather limited. In this regard, this study focuses on the characterization of mode II delamination of carbon/epoxy composites conditioned at 70 °C/85% relative humidity (RH). End-notched flexure test is conducted for specimens aged at various moisture absorption levels. Experimental results reveal that mode II fracture toughness degrades with the moisture content, with a maximum of 23% decrement. A residual property model is used to predict the variation of the fracture toughness with the moisture content. Through numerical simulations, it is found that the approaches used to estimate the lamina and cohesive properties are suitable to obtain reliable simulation results. In addition, the damage initiation is noticed during the early loading stage; however, the complete damage is only observed when the numerical peak load is achieved. Results from the present research could serve as guidelines to predict the residual properties and simulate the mode II delamination behavior under moisture attack.

scholarly journals Displacement Rate Effects on the Mode II Shear Delamination Behavior of Carbon Fiber/Epoxy Composites

Polymers ◽  
2021 ◽  
Vol 13 (11) ◽  
pp. 1881
Author(s):  
Kean Ong Low ◽  
Mahzan Johar ◽  
Haris Ahmad Israr ◽  
Khong Wui Gan ◽  
Seyed Saeid Rahimian Koloor ◽  
...  
Keyword(s):  
Fracture Toughness ◽  
Peak Load ◽  
Epoxy Composites ◽  
Displacement Rate ◽  
Interface Debonding ◽  
Mode Ii ◽  
Scanning Electron Micrographs ◽  
Unstable Crack ◽  
Mode Ii Fracture ◽  
Mode Ii Fracture Toughness

This paper studies the influence of displacement rate on mode II delamination of unidirectional carbon/epoxy composites. End-notched flexure test is performed at displacement rates of 1, 10, 100 and 500 mm/min. Experimental results reveal that the mode II fracture toughness GIIC increases with the displacement, with a maximum increment of 45% at 100 mm/min. In addition, scanning electron micrographs depict that fiber/matrix interface debonding is the major damage mechanism at 1 mm/min. At higher speeds, significant matrix-dominated shear cusps are observed contributing to higher GIIC. Besides, it is demonstrated that the proposed rate-dependent model is able to fit the experimental data from the current study and the open literature generally well. The mode II fracture toughness measured from the experiment or deduced from the proposed model can be used in the cohesive element model to predict failure. Good agreement is found between the experimental and numerical results, with a maximum difference of 10%. The numerical analyses indicate crack jump occurs suddenly after the peak load is attained, which leads to the unstable crack propagation seen in the experiment.

scholarly journals Mixed-Mode Interlaminar Fracture Toughness of Glass and Carbon Fibre Powder Epoxy Composites—For Design of Wind and Tidal Turbine Blades

Materials ◽  
2021 ◽  
Vol 14 (9) ◽  
pp. 2103
Author(s):  
Christophe Floreani ◽  
Colin Robert ◽  
Parvez Alam ◽  
Peter Davies ◽  
Conchúr M. Ó. Brádaigh
Keyword(s):  
Fracture Toughness ◽  
Carbon Fibre ◽  
Composite Structures ◽  
Mixed Mode ◽  
Epoxy Composites ◽  
Mode I ◽  
Mode Ii ◽  
Pure Mode ◽  
Interlaminar Fracture Toughness ◽  
Interlaminar Fracture

Powder epoxy composites have several advantages for the processing of large composite structures, including low exotherm, viscosity and material cost, as well as the ability to carry out separate melting and curing operations. This work studies the mode I and mixed-mode toughness, as well as the in-plane mechanical properties of unidirectional stitched glass and carbon fibre reinforced powder epoxy composites. The interlaminar fracture toughness is studied in pure mode I by performing Double Cantilever Beam tests and at 25% mode II, 50% mode II and 75% mode II by performing Mixed Mode Bending testing according to the ASTM D5528-13 test standard. The tensile and compressive properties are comparable to that of standard epoxy composites but both the mode I and mixed-mode toughness are shown to be significantly higher than that of other epoxy composites, even when comparing to toughened epoxies. The mixed-mode critical strain energy release rate as a function of the delamination mode ratio is also provided. This paper highlights the potential for powder epoxy composites in the manufacturing of structures where there is a risk of delamination.

Fracture Properties and Characteristics of Sisal Textile Reinforced Epoxy Composites

2006 ◽  
Vol 312 ◽  
pp. 167-172
Author(s):  
Yan Li ◽  
Yiu Wing Mai ◽  
Lin Ye
Keyword(s):  
Fracture Toughness ◽  
Surface Treatment ◽  
Fiber Surface ◽  
Epoxy Composites ◽  
Mode I ◽  
Mode Ii ◽  
Fracture Properties ◽  
Pull Out ◽  
Mode Ii Fracture Toughness ◽  
Fiber Surface Treatment

In this paper, double cantilever beam (DCB) and end notch flexural (ENF) tests were performed to study mode I and mode II interlaminar fracture toughness of sisal textile reinforced epoxy composites. Two kinds of fiber surface treatment methods were used to improve the interfacial bonding properties between sisal fiber and the epoxy resin. Effect of fiber surface treatments on mode I and mode II fracture toughness was analyzed with the aid of microobservation and single fiber pull-out test. It was concluded that proper fiber surface treatment could improve the fracture properties of this kind of Eco-composite.

scholarly journals Environmental effects on mode II fracture toughness of unidirectional E-glass/vinyl ester laminated composites

2021 ◽  
Vol 28 (1) ◽  
pp. 382-393
Author(s):  
Mazaher Salamt-Talab ◽  
Fatemeh Delzendehrooy ◽  
Alireza Akhavan-Safar ◽  
Mahdi Safari ◽  
Hossein Bahrami-Manesh ◽  
...  
Keyword(s):  
Fracture Toughness ◽  
Sulfuric Acid ◽  
Vinyl Ester ◽  
Cohesive Zone Model ◽  
Flexural Modulus ◽  
Mode Ii ◽  
Zone Model ◽  
Sharp Drop ◽  
Mode Ii Fracture ◽  
Mode Ii Fracture Toughness

Abstract In this article, mode II fracture toughness ( G IIc {G}_{\text{IIc}} ) of unidirectional E-glass/vinyl ester composites subjected to sulfuric acid aging is studied at two different temperatures (25 and 90°C). Specimens were manufactured using the hand lay-up method with the [ 0 ] 20 {{[}0]}_{20} stacking sequence. To study the effects of environmental conditions, samples were exposed to 30 wt% sulfuric acid at room temperature (25°C) for 0, 1, 2, 4, and 8 weeks. Some samples were also placed in the same solution but at 90°C and for 3, 6, 9, and 12 days to determine the interlaminar fracture toughness at different aging conditions. Fracture tests were conducted using end notched flexure (ENF) specimens according to ASTM D7905. The results obtained at 25°C showed that mode II fracture toughness increases for the first 2 weeks of aging and then it decreases for the last 8 weeks. It was also found that the flexural modulus changes with the same trend. Based on the results of the specimens aged at 90°C, a sharp drop in fracture toughness and flexural modulus with a significant decrease in maximum load have been observed due to the aging. Finite element simulations were performed using the cohesive zone model (CZM) to predict the global response of the tested beams.

Sign in / Sign up

Export Citation Format

Share Document