scholarly journals Effect of Aromatic Petroleum Resin on Damping Properties of Polybutyl Methacrylate

Polymers ◽  
2020 ◽  
Vol 12 (3) ◽  
pp. 543
Author(s):  
Songhan Wan ◽  
Saisai Zhou ◽  
Xing Huang ◽  
Songbo Chen ◽  
Shuwei Cai ◽  
...  
Keyword(s):  
Mechanical Analysis ◽  
Damping Properties ◽  
Scanning Calorimetry ◽  
Sem Images ◽  
Dynamical Mechanical Analysis ◽  
Petroleum Resin ◽  
The Matrix ◽  
Higher Temperature ◽  
Dsc Curves ◽  
Positive Effect

The damping properties of polybutyl methacrylate (PBMA)/aromatic petroleum resin (C9) composite were investigated in this work. In particular, a trace of styrene (St) was introduced to copolymerize with PBMA to improve the compatibility between C9 and matrix. The structure of the copolymer, P(BMA-co-St), was characterized by FTIR and 1HNMR. The P(BMA-co-St)/C9 composites were tested by differencial scanning calorimetry (DSC), scanning electron microscopy (SEM) and dynamical mechanical analysis (DMA). DSC curves of all P(BMA-co-1wt%St)/C9 composites expressed only one glass transition temperature (Tg). SEM images showed that C9 had good compatibility with the matrix after St was introduced. DMA curves indicated that the addition of C9 had a positive effect on the damping properties of PBMA. The loss tangent (tanδ) peak moved to a higher temperature with the increment content of C9, and the effective damping temperature range increased significantly. The influence of aromatic resin C9 and aliphatic resin (C5) on PBMA damping performance was compared. It was further shown that C9 with benzene ring effectively improved the damping performance of PBMA.

Effect of graphene nano-platelets on mechanical and impact characteristics of carbon/Kevlar reinforced epoxy hybrid nanocomposites

2021 ◽  
pp. 095440622110168
Author(s):  
Mohamad Alsaadi ◽  
Bashar Younus ◽  
Ahmet Erklig ◽  
Mehmet Bulut ◽  
Omer Bozkurt ◽  
...  
Keyword(s):  
Impact Test ◽  
Charpy Impact ◽  
Hybrid Nanocomposites ◽  
Matrix Composites ◽  
Sem Images ◽  
The Matrix ◽  
Impact Characteristics ◽  
Positive Effect ◽  
Hybrid Carbon ◽  
Composite Samples

The influence of various graphene nano-platelets (GNPs) content on the tensile, flexural and Charpy impact characteristics of carbon, Kevlar and hybrid carbon/Kevlar fibers reinforced epoxy matrix composites was investigated. Both of composite configurations as carbon and Kevlar at outer and core skins were experimentally tested. The SEM images for flexural specimens were taken to observe the adhesion mechanism of GnPs particles with fiber/epoxy system. It is found that hybridization with Kevlar layers is contributed a positive effect on the hybrid carbon/Kevlar laminate structures in terms of tensile, flexural and impact behaviour. The incorporation of GnPs particles in hybrid and non-hybrid composite samples results in significant improvements in tensile, flexural and impact properties, and the greatest improvement occurs within the GnPs particle content of 0.1 and 0.25 wt%, indicating that the interfacial bonding between the matrix and the fibers is better due to the large surface area of the GnPs and the good entanglement between the GnPs layers and the matrix chains. The samples of impact test are experimented for edgewise and flatwise directions.

MICROSTRUCTURAL EVOLUTION OF Al-Cu-Mg-Ag ALLOY WITH TRACE Zr ADDITION DURING TWO-STEP HOMOGENIZATION

2009 ◽  
Vol 23 (06n07) ◽  
pp. 855-862 ◽  
Author(s):  
FEIYUE MA ◽  
ZHIYI LIU
Keyword(s):  
Melting Point ◽  
Grain Boundaries ◽  
Microstructural Evolution ◽  
Cast Alloy ◽  
Scanning Calorimetry ◽  
Zr Addition ◽  
Homogenization Time ◽  
The Matrix ◽  
Higher Temperature ◽  
Lower Temperature

The microstructural evolution in an Al - Cu - Mg - Ag alloy with trace Zr addition during homogenization treatment was characterized by Differential Scanning Calorimetry (DSC), Scanning Electron Microscopy (SEM) and Energy-dispersive X-ray Spectroscopy (EDS). It was shown that the low-melting-point phase segregating toward grain boundaries is Al 2 Cu , with a melting point of 523.52°C. A two-step homogenization process was employed to optimize the microstructure of the as-cast alloy, during which the alloy was first homogenized at a lower temperature, then at a higher temperature. After homogenized at 420°C for 6 h, Al 3 Zr particles were finely formed in the matrix. After that, when the alloy was homogenized at an elevated temperature for a longer time, i.e., 515°C for 24 h, most of the precipates at the grain boundaries were removed. Furthermore, the dispersive Al 3 Zr precipitates were retained, without coarsening greatly in the final homogenization step. A kinetics model is employed to predict the optimal homogenization time at a given temperature theoretically, and it confirms the result in present study, which is 420°C/6h+515°C/24h.

scholarly journals Evaluation of Thermal Properties of Composites Prepared from Pistachio Shell Particles Treated Chemically and Polypropylene

Molecules ◽  
2022 ◽  
Vol 27 (2) ◽  
pp. 426
Author(s):  
Beatriz Adriana Salazar-Cruz ◽  
María Yolanda Chávez-Cinco ◽  
Ana Beatriz Morales-Cepeda ◽  
Claudia Esmeralda Ramos-Galván ◽  
José Luis Rivera-Armenta
Keyword(s):  
Thermal Properties ◽  
Mechanical Analysis ◽  
Scanning Calorimetry ◽  
Melt Mixing ◽  
Pistachio Shell ◽  
Nucleation Effect ◽  
Chemically Treated ◽  
Naoh Solution ◽  
Shell Particles ◽  
Positive Effect

The purpose of the present work was to prepare polypropylene (PP) matrix composited filled with chemically treated pistachio shell particles (PTx), and evaluate their effect on the composites’ thermal properties. PP-PTx composites were formulated in different PTx content (from 2 to 10 phr) in a mixing chamber, using the melt-mixing process. The PTx were chemically treated using a NaOH solution and infrared spectroscopy (FTIR). According to thermogravimetric analysis (TGA), the treatment of pistachio shell particles resulted in the remotion of lignin and hemicellulose. The thermal stability was evaluated by means of TGA, where the presence of PTx in composites showed a positive effect compared with PP pristine. Thermal properties such as crystallization temperature (Tc), crystallization enthalpy (∆Hc), melting temperature (Tm) and crystallinity were determinate by means differential scanning calorimetry (DSC); these results suggest that the PTx had a nucleation effect on the PP matrix, increasing their crystallinity. Dynamic mechanical analysis (DMA) showed that stiffness of the composites increase compared with that PP pristine, as well as the storage modulus, and the best results were found at a PTx concentration of 4 phr. At higher concentrations, the positive effect decreased; however, they were better than the reference PP.

Fine structure formation and physical properties of poly(butylene terephthalate) fibres in high-speed melt spinning

e-Polymers ◽  
2003 ◽  
Vol 3 (1) ◽  
Author(s):  
Hee Lee Sun ◽  
Hou Kim Kyoung ◽  
Kikutani Takeshi ◽  
Hok Cho Hyun
Keyword(s):  
Fine Structure ◽  
Physical Properties ◽  
Structure Formation ◽  
High Speed ◽  
Melt Spinning ◽  
Mechanical Analysis ◽  
Scanning Calorimetry ◽  
Butylene Terephthalate ◽  
Initial Modulus ◽  
Higher Temperature

Abstract Poly(butylene terephthalate) (PBT) fibres were obtained by high-speed melt spinning up to a take-up velocity of 8 km/min. Fine structure formation and physical properties of these fibres were investigated. The increase of take-up velocity caused raises in both density and birefringence. In wide-angle X-ray diffraction equatorial profiles, the increase of take-up velocity can be observed in the (010) and (100) reflections of β-crystals; the reflection peaks are the sharpest at a take-up velocity of 6 km/min. The initial modulus of the fibres arises when the fraction of β-crystals is increased, while the tenacity depends more on the fraction of α-crystals, i.e., the total crystallinity. Thermal properties of high-speed spun PBT fibres were measured with differential scanning calorimetry, dynamic mechanical and thermo-mechanical analysis, etc. Endothermic curves become sharper with increasing take-up velocity, and endothermic melting peaks are shifted to higher temperature. Crystal structures are well developed in fibres obtained at higher take-up velocities. The tan δ peaks of PBT fibres tend to shift to higher temperature and the peak intensity is decreased with increasing take-up velocity, i.e., the packing density of PBT fibres is high when the take-up velocity and thus the orientation of amorphous regions is increased. The shrinkage has a tendency to decrease with increasing take-up velocity.

scholarly journals Biocomposites from Rice Straw Nanofibers: Morphology, Thermal and Mechanical Properties

Materials ◽  
2020 ◽  
Vol 13 (9) ◽  
pp. 2138 ◽  
Author(s):  
José Carlos Alcántara ◽  
Israel González ◽  
M. Mercè Pareta ◽  
Fabiola Vilaseca
Keyword(s):  
Rice Straw ◽  
Mechanical Performance ◽  
Cellulose Nanofibers ◽  
Nucleating Agent ◽  
Mechanical Analysis ◽  
Nanocomposite Films ◽  
Chemical Extraction ◽  
Poly Vinyl Alcohol ◽  
Scanning Calorimetry ◽  
The Matrix

Agricultural residues are major potential resources for biomass and for material production. In this work, rice straw residues were used to isolate cellulose nanofibers of different degree of oxidation. Firstly, bleached rice fibers were produced from the rice straw residues following chemical extraction and bleaching processes. Oxidation of rice fibers mediated by radical 2,2,6,6-tetramethylpiperidine 1-oxyl (TEMPO) at pH 10 was then applied to extract rice cellulose nanofibers, with diameters of 3–11 nm from morphological analysis. The strengthening capacity of rice nanofibers was tested by casting nanocomposite films with poly(vinyl alcohol) polymer. The same formulations with eucalyptus nanofibers were produced as comparison. Their thermal and mechanical performance was evaluated using thermogravimetry, differential scanning calorimetry, dynamic mechanical analysis and tensile testing. The glass transition of nanocomposites was shifted to higher temperatures with respect to the pure polymer by the addition of rice cellulose nanofibers. Rice nanofibers also acted as a nucleating agent for the polymer matrix. More flexible eucalyptus nanofibers did not show these two phenomena on the matrix. Instead, both types of nanofibers gave similar stiffening (as Young’s modulus) to the matrix reinforced up to 5 wt.%. The ultimate tensile strength of nanocomposite films revealed significant enhancing capacity for rice nanofibers, although this effect was somehow higher for eucalyptus nanofibers.

scholarly journals Mechanical and Thermal Characterization of Natural Intralaminar Hybrid Composites Based on Sisal

Polymers ◽  
2020 ◽  
Vol 12 (4) ◽  
pp. 866 ◽  
Author(s):  
Alexandre L. Pereira ◽  
Mariana D. Banea ◽  
Jorge S.S. Neto ◽  
Daniel K.K. Cavalcanti
Keyword(s):  
Thermal Properties ◽  
Natural Fiber ◽  
Hybrid Composites ◽  
Thermal Characterization ◽  
Mechanical And Thermal Properties ◽  
Scanning Calorimetry ◽  
Sem Images ◽  
The Matrix ◽  
American Society ◽  
Curaua Fibers

The main objective of this work was to investigate the effect of hybridization on the mechanical and thermal properties of intralaminar natural fiber-reinforced hybrid composites based on sisal. Ramie, sisal and curauá fibers were selected as natural fiber reinforcements for the epoxy matrix based composites, which were produced by the hand lay-up technique. Tensile, flexural and impact tests were carried out according to American society for testing and materials (ASTM) standards to characterize the hybrid composites, while differential scanning calorimetry (DSC) and thermogravimetric analysis (TGA) were used to evaluate the thermal properties. It was found that the mechanical properties are improved by hybridization of sisal based composites. The thermal analysis showed that the hybridization did not significantly affect the thermal stability of the composites. A scanning electron microscopy (SEM) was used to examine the fracture surface of the tested specimens. The SEM images showed a brittle fracture of the matrix and fiber breakage near the matrix.

Preparation and Characterization of Multiwalled Carbon Nanotubes-Reinforced pCBT by Ring-Opening Polymerization of Cyclic Butylene Terephthalate

2016 ◽  
Vol 848 ◽  
pp. 125-131
Author(s):  
Yin He Su ◽  
Jun Rong Yu
Keyword(s):  
Carbon Nanotubes ◽  
Multiwalled Carbon Nanotubes ◽  
Ring Opening ◽  
Ring Opening Polymerization ◽  
Scanning Calorimetry ◽  
Multiwalled Carbon ◽  
Butylene Terephthalate ◽  
Cyclic Butylene Terephthalate ◽  
The Matrix ◽  
Higher Temperature

Multiwalled carbon nanotubes (MWCNT)-reinforced polymerized cyclic butylene terephthalate (pCBT) nanocomposites were prepared by in situ ring opening polymerization of cyclic butylene terephthalate oligomers (CBT). The results of differential scanning calorimetry (DSC) indicated that the melting peak located at the low temperature (Tm1) increased and that at higher temperature (Tm2) decreased with the increasing of content of the MWCNT. During the cooling the MWCNT served as nucleation points from where crystallization can start. The more the MWCNT in the system the earlier the crystallization starts. The Morphological investigations performed by scanning electron microscopy (SEM) shown that the MWCNT were embedded in the matrix and held tightly by the matrix. The modulus and strength increased with MWCNT concentration in the nanocomposites, however, the elongation at break, absorbed energy at break and impact strength were decreased with the increasing of MWCNT content.

Study of a Cu-Al-Mn Shape Memory Alloy Produced by Plasma Melting Followed by Injection Molding

2014 ◽  
Vol 1611 ◽  
pp. 25-30
Author(s):  
Francisco Fernando Roberto Pereira ◽  
Maria Goretti Ferreira Coutinho ◽  
Bruno Moura Miranda ◽  
Carlos José de Araújo
Keyword(s):  
Injection Molding ◽  
Shape Memory ◽  
Shape Recovery ◽  
Permanent Deformation ◽  
Melting Process ◽  
Mechanical Analysis ◽  
Scanning Calorimetry ◽  
Dynamical Mechanical Analysis ◽  
Plasma Melting ◽  
New Applications

ABSTRACTShape Memory Alloys (SMA) are characterized by the capacity to recover a permanent deformation after being heated above a critical temperature called Final Austenite Temperature (Af). The Ni-Ti SMA are the most commercially used, however recent studies showed that the Cu-Al-Mn SMA present significant shape recovery and mechanical properties, showing a strong potential for developing new applications. In this context, the main goal of this work is to manufacture a Cu-Al-Mn SMA through a plasma melting process followed by injection molding of liquid metal and then characterize the samples, using the following techniques: Optical Microscopy (OM), Differential Scanning Calorimetry (DSC), Electrical Resistance as a function of Temperature (ERT) tests, Dynamical Mechanical Analysis (DMA) and Microhardness (MH).

scholarly journals Block Copolymers of Poly(ω-Pentadecalactone) in Segmented Polyurethanes: Novel Biodegradable Shape Memory Polyurethanes

Polymers ◽  
2020 ◽  
Vol 12 (9) ◽  
pp. 1928
Author(s):  
Katalin Czifrák ◽  
Csilla Lakatos ◽  
Marcell Árpád Kordován ◽  
Lajos Nagy ◽  
Lajos Daróczi ◽  
...  
Keyword(s):  
Shape Memory ◽  
Shape Recovery ◽  
Mechanical Analysis ◽  
Attenuated Total Reflectance ◽  
Dibutyltin Dilaurate ◽  
Scanning Calorimetry ◽  
Dynamical Mechanical Analysis ◽  
Good Shape ◽  
Segmented Polyurethanes ◽  
Shape Fixity

In this report, the synthesis of poly(ω-pentadecalactone) (PPDL) (co)polymers and their incorporation into polyurethanes (PUs) are reported. Optimal conditions for the ring-opening polymerization (ROP) of ω-pentadecalactone (PDL) using dibutyltin dilaurate catalyst were established. For the synthesis of linear and crosslinked PUs, 50 kDa poly(ε-caprolactone) (PCL) and 1,6-hexamethylenediisocyanate (HDI) were used. The obtained polyurethanes were characterized by Attenuated Total Reflectance Fourier-Transform Infrared spectroscopy (AT-FTIR), differential scanning calorimetry (DSC), and dynamical mechanical analysis (DMA). The DMA of the selected sample showed a rubbery plateau on the storage modulus versus temperature curve predicting shape memory behavior. Indeed, good shape memory performances were obtained with shape fixity (Rf) and shape recovery (Rr) ratios.

scholarly journals Effect of Phenolic Resin Oligomer Motion Ability on Energy Dissipation of Poly (Butyl Methacrylate)/Phenolic Resins Composites

Polymers ◽  
2020 ◽  
Vol 12 (2) ◽  
pp. 490
Author(s):  
Xing Huang ◽  
Songbo Chen ◽  
Songhan Wan ◽  
Ben Niu ◽  
Xianru He ◽  
...  
Keyword(s):  
Molecular Weight ◽  
Hydrogen Bonding ◽  
Glass Transition ◽  
Dynamic Mechanical Properties ◽  
Mechanical Analysis ◽  
Butyl Methacrylate ◽  
Scanning Calorimetry ◽  
Phenolic Resins ◽  
Dynamic Mechanical ◽  
The Matrix

Poly (butyl methacrylate) (PBMA) was blended with a series of phenolic resins (PR) to study the effect of PR molecular weight on dynamic mechanical properties of PBMA/PR composites. Differential scanning calorimetry (DSC) and dynamic mechanical analysis (DMA) found a similar variation of glass transition temperature (Tg). The maximum loss peak (tanδmax) improved in all PBMA/PR blends compared with the pure PBMA. However, tanδmax reduced as the molecular weight increased. This is because PR with higher molecular weight is more rigid in the glass transition zone of blends. The hydrogen bonding between PBMA and PR was characterized by Fourier transform infrared spectroscopy (FTIR). Lower molecular weight PR formed more hydrogen bonds with the matrix and it had weaker temperature dependence. Combined with the results from DMA, we studied how molecular weight affected hydrogen bonding and thus further affected tanδmax.