scholarly journals The Effect of Multilevel Carbon Reinforcements on the Fire Performance, Conductivity, and Mechanical Properties of Epoxy Composites

Polymers ◽  
2019 ◽  
Vol 11 (2) ◽  
pp. 303 ◽  
Author(s):  
Andrea Toldy ◽  
Gábor Szebényi ◽  
Kolos Molnár ◽  
Levente Tóth ◽  
Balázs Magyar ◽  
...  
Keyword(s):  
Mechanical Properties ◽  
Thermal Conductivity ◽  
Flame Retardant ◽  
Epoxy Resin ◽  
Impact Resistance ◽  
Fire Performance ◽  
Multiwalled Carbon ◽  
Peak Heat Release Rate ◽  
Flame Retarded ◽  
The Impact

We studied the effect of a multilevel presence of carbon-based reinforcements—a combination of conventional load-bearing unidirectional carbon fiber (CF) with multiwalled carbon nanotubes (CNT) and conductive CNT-containing nonwoven carbon nanofabric (CNF(CNT))—on the fire performance, thermal conductivity, and mechanical properties of reference and flame-retarded epoxy resin (EP) composites. The inclusion of carbon fibers and flame retardant reduced the peak heat release rate (pHRR) of the epoxy resins. The extent to which the nanoreinforcements reduced the pHRR depended on their influence on thermal conductivity. Specifically, high thermal conductivity is advantageous at the early stages of degradation, but after ignition it may lead to more intensive degradation and a higher pHRR; especially in the reference samples without flame retardant. The lowest pHRR (130 kW/m2) and self-extinguishing V-0 UL-94 rating was achieved in the flame-retarded composite containing all three levels of carbon reinforcement (EP + CNF(CNT) + CNT + CF FR). The plasticizing effect of the liquid flame retardant impaired both the tensile and flexural properties; however, it significantly enhanced the impact resistance of the epoxy resin and its composites.

scholarly journals Properties of epoxy-thiokol materials based on the products of the preliminary reaction of thioetherification

2021 ◽  
pp. 128-136
Author(s):  
K.M. Sukhyy ◽  
◽  
E.A. Belyanovskaya ◽  
A.N. Nosova ◽  
M.K. Sukhyy ◽  
...  
Keyword(s):  
Mechanical Properties ◽  
Epoxy Resin ◽  
Adhesive Strength ◽  
Impact Resistance ◽  
Maximum Level ◽  
Scanning Calorimetry ◽  
Mechanical Mixtures ◽  
The Impact ◽  
Fracture Work ◽  
Specific Impact

In order to improve the adhesive and physical-mechanical properties of epoxy-thiocol compositions cured without heat treatment, we propose to carry out the reaction of interaction between thiokol mercaptan groups and oxirane cycles of epoxy resin at an elevated temperature before introducing a curing agent, and then use the product of this thioetherification reaction for curing at room temperature. The temperature range of the thioetherification reaction (90–1800С) was determined by the method of differential scanning calorimetry. The optimal temperature (1600С) and duration of the preliminary thioetherification reaction (2 hours) were determined, which ensure the maximum level of adhesive strength and physical-mechanical properties. It was shown that composite materials based on the products of the thioetherification reaction significantly outperform analogs based on mechanical mixtures of epoxy resin and thiokol in terms of cohesive and adhesive strength, deformation capacity, fracture work and specific impact strength. The impact resistance and shear strength of adhesive joints are especially significantly increased during the curing of the compositions without external heat supply.

scholarly journals Environmentally Friendly Flame-Retardant and Its Application in Rigid Polyurethane Foam

2014 ◽  
Vol 2014 ◽  
pp. 1-7 ◽  
Author(s):  
Yongjun Chen ◽  
Zhixin Jia ◽  
Yuanfang Luo ◽  
Demin Jia ◽  
Bin Li
Keyword(s):  
Mechanical Properties ◽  
Thermal Stability ◽  
Flame Retardant ◽  
Polyurethane Foam ◽  
Thermal Effects ◽  
Oxygen Index ◽  
Rigid Polyurethane Foam ◽  
Limiting Oxygen Index ◽  
Peak Heat Release Rate ◽  
The Impact

A novel Flame-Retardant N-(P,P′-diphenyl) phosphorus-based-(3-triethoxysilicon) propylamine (DPTP) was synthesized in this study. The impact of DPTP on the mechanical properties, thermal stability, and flame retardancy of rigid polyurethane foam (RPUF) was studied. The addition of DPTP to RPUF can significantly reduce the undesirable thermal effects and smoke density during combustion, as well as increasing the limiting oxygen index. Compared with pure RPUF, the peak heat release rate of RPUF containing 10 phr of DPTP decreased by 39.4%, while its peak smoke production rate decreased by 49.9%. However, it was also found that the addition of DPTP reduced the compressive strength of RPUF.

Effect of combined drink cans and steel fibers on the impact resistance and mechanical properties of concrete

2020 ◽  
Vol 14 (2) ◽  
pp. 6734-6742
Author(s):  
A. Syamsir ◽  
S. M. Mubin ◽  
N. M. Nor ◽  
V. Anggraini ◽  
S. Nagappan ◽  
...  
Keyword(s):  
Mechanical Properties ◽  
Tensile Strength ◽  
Compressive Strength ◽  
Reinforced Concrete ◽  
Impact Resistance ◽  
Fiber Reinforced Concrete ◽  
Steel Fibers ◽  
Fiber Reinforced ◽  
Indirect Tensile ◽  
The Impact

This study investigated the combine effect of 0.2 % drink cans and steel fibers with volume fractions of 0%, 0.5%, 1%, 1.5%, 2%, 2.5% and 3% to the mechanical properties and impact resistance of concrete. Hooked-end steel fiber with 30 mm and 0.75 mm length and diameter, respectively was selected for this study.  The drinks cans fiber were twisted manually in order to increase friction between fiber and concrete. The results of the experiment showed that the combination of steel fibers and drink cans fibers improved the strength performance of concrete, especially the compressive strength, flexural strength and indirect tensile strength. The results of the experiment showed that the combination of steel fibers and drink cans fibers improved the compressive strength, flexural strength and indirect tensile strength by 2.3, 7, and 2 times as compare to batch 1, respectively. Moreover, the impact resistance of fiber reinforced concrete has increase by 7 times as compared to non-fiber concretes. Moreover, the impact resistance of fiber reinforced concrete consistently gave better results as compared to non-fiber concretes. The fiber reinforced concrete turned more ductile as the dosage of fibers was increased and ductility started to decrease slightly after optimum fiber dosage was reached. It was found that concrete with combination of 2% steel and 0.2% drink cans fibers showed the highest compressive, split tensile, flexural as well as impact strength.    

scholarly journals Effect of SWCNT-Tuball Paper on the Lightning Strike Protection of CFRPs and Their Selected Mechanical Properties

Materials ◽  
2021 ◽  
Vol 14 (11) ◽  
pp. 3140
Author(s):  
Kamil Dydek ◽  
Anna Boczkowska ◽  
Rafał Kozera ◽  
Paweł Durałek ◽  
Łukasz Sarniak ◽  
...  
Keyword(s):  
Mechanical Properties ◽  
Carbon Nanotubes ◽  
Electrical Conductivity ◽  
Copper Foil ◽  
Impact Resistance ◽  
Mechanical Analysis ◽  
Lightning Strike ◽  
Single Wall Carbon Nanotubes ◽  
Carbon Fibre Reinforced Polymer ◽  
The Impact

The main aim of this work was the investigation of the possibility of replacing the heavy metallic meshes applied onto the composite structure in airplanes for lightning strike protection with a thin film of Tuball single-wall carbon nanotubes in the form of ultra-light, conductive paper. The Tuball paper studied contained 75 wt% or 90 wt% of carbon nanotubes and was applied on the top of carbon fibre reinforced polymer before fabrication of flat panels. First, the electrical conductivity, impact resistance and thermo-mechanical properties of modified laminates were measured and compared with the reference values. Then, flat panels with selected Tuball paper, expanded copper foil and reference panels were fabricated for lightning strike tests. The effectiveness of lightning strike protection was evaluated by using the ultrasonic phased-array technique. It was found that the introduction of Tuball paper on the laminates surface improved both the surface and the volume electrical conductivity by 8800% and 300%, respectively. The impact resistance was tested in two directions, perpendicular and parallel to the carbon fibres, and the values increased by 9.8% and 44%, respectively. The dynamic thermo-mechanical analysis showed higher stiffness and a slight increase in glass transition temperature of the modified laminates. Ultrasonic investigation after lightning strike tests showed that the effectiveness of Tuball paper is comparable to expanded copper foil.

scholarly journals An Effective Method for Preparation of Liquid Phosphoric Anhydride and Its Application in Flame Retardant Epoxy Resin

Materials ◽  
2021 ◽  
Vol 14 (9) ◽  
pp. 2205
Author(s):  
Qian Li ◽  
Yujie Li ◽  
Yifan Chen ◽  
Qiang Wu ◽  
Siqun Wang
Keyword(s):  
Flame Retardant ◽  
Epoxy Resin ◽  
Epoxy Resins ◽  
Oxygen Index ◽  
Decomposition Temperature ◽  
Ease Of Use ◽  
Limiting Oxygen Index ◽  
Good Thermal Stability ◽  
Low Viscosity ◽  
The Impact

A novel liquid phosphorous-containing flame retardant anhydride (LPFA) with low viscosity was synthesized from 9,10-dihydro-9-oxa-10-phosphaphenanthrene-10-oxide (DOPO) and methyl tetrahydrophthalic anhydride (MeTHPA) and further cured with bisphenol-A epoxy resin E-51 for the preparation of the flame retardant epoxy resins. Both Fourier transform infrared spectroscopy (FT-IR), mass spectrometry (MS) and nuclear magnetic resonance (NMR) measurements revealed the successful incorporation of DOPO on the molecular chains of MeTHPA through chemical reaction. The oxygen index analysis showed that the LPFA-cured epoxy resin exhibited excellent flame retardant performance, and the corresponding limiting oxygen index (LOI) value could reach 31.2%. The UL-94V-0 rating was achieved for the flame retardant epoxy resin with the phosphorus content of 2.7%. With the addition of LPFA, the impact strength of the cured epoxy resins remained almost unchanged, but the flexural strength gradually increased. Meanwhile, all the epoxy resins showed good thermal stability. The glass transition temperature (Tg) and thermal decomposition temperature (Td) of epoxy resin cured by LPFA decreased slightly compared with that of MeTHPA-cured epoxy resin. Based on such excellent flame retardancy, low viscosity at room temperature and ease of use, LPFA showed potential as an appropriate curing agent in the field of electrical insulation materials.

Smoke suppression and thermal conductivity of epoxy resin modified by Al 2 O 3 and hyperbranched flame retardant

2021 ◽  
pp. 51654
Author(s):  
Huawei Qiao ◽  
Xiuhuang Lin ◽  
Wei Zhong ◽  
Jiashui Lan ◽  
Huagui Zhang ◽  
...  
Keyword(s):  
Thermal Conductivity ◽  
Flame Retardant ◽  
Epoxy Resin ◽  
Smoke Suppression

scholarly journals Effect of Secondary Carbon Nanofillers on the Electrical, Thermal, and Mechanical Properties of Conductive Hybrid Composites Based on Epoxy Resin and Graphite

Materials ◽  
2021 ◽  
Vol 14 (15) ◽  
pp. 4169
Author(s):  
Marcel Zambrzycki ◽  
Krystian Sokolowski ◽  
Maciej Gubernat ◽  
Aneta Fraczek-Szczypta
Keyword(s):  
Mechanical Properties ◽  
Specific Surface ◽  
Epoxy Resin ◽  
Surface Area ◽  
Specific Surface Area ◽  
Hybrid Composites ◽  
Department Of Energy ◽  
Carbon Nanofillers ◽  
The Impact ◽  
Secondary Carbon

In this work, we present a comparative study of the impact of secondary carbon nanofillers on the electrical and thermal conductivity, thermal stability, and mechanical properties of hybrid conductive polymer composites (CPC) based on high loadings of synthetic graphite and epoxy resin. Two different carbon nanofillers were chosen for the investigation—low-cost multi-layered graphene nanoplatelets (GN) and carbon black (CB), which were aimed at improving the overall performance of composites. The samples were obtained by a simple, inexpensive, and effective compression molding technique, and were investigated by the means of, i.a., scanning electron microscopy, Raman spectroscopy, electrical conductivity measurements, laser flash analysis, and thermogravimetry. The tests performed revealed that, due to the exceptional electronic transport properties of GN, its relatively low specific surface area, good aspect ratio, and nanometric sizes of particles, a notable improvement in the overall characteristics of the composites (best results for 4 wt % of GN; σ = 266.7 S cm−1; λ = 40.6 W mK−1; fl. strength = 40.1 MPa). In turn, the addition of CB resulted in a limited improvement in mechanical properties, and a deterioration in electrical and thermal properties, mainly due to the too high specific surface area of this nanofiller. The results obtained were compared with US Department of Energy recommendations regarding properties of materials for bipolar plates in fuel cells. As shown, the materials developed significantly exceed the recommended values of the majority of the most important parameters, indicating high potential application of the composites obtained.

Phase Morphology, Thermal and Mechanical Properties of Compatibilized Nylon12/Natural Rubber Blends Using PS/MNR

2013 ◽  
Vol 844 ◽  
pp. 53-56
Author(s):  
Saravalee Saengthaveep ◽  
Sadhan C. Jana ◽  
Rathanawan Magaraphan
Keyword(s):  
Mechanical Properties ◽  
Natural Rubber ◽  
Moisture Absorption ◽  
Rubber Particle ◽  
Impact Resistance ◽  
Phase Morphology ◽  
Thermal And Mechanical Properties ◽  
Binary Blend ◽  
Polyamide 12 ◽  
The Impact

To produce a tough material for application demanding high impact resistance and low moisture absorption, melt blending of Nylon12 (Polyamide 12, PA12) and natural rubber (NR) was carried out in a brabender plasticorder at 210 °C with rotor speed of 70 rpm in the presence of polystyrene/maleated natural rubber (PS/MNR) blend as a compatibilizer. The effect of compatibilizer content (1, 3, 5, 7 and 10 phr) on phase morphology, thermal, and mechanical properties of [Nylon12/NR]/[PS/MNR] blends was investigated by using SEM, DSC, and Izod impact tester, respectively. The result revealed that PS/MNR blend improved the compatibility of Nylon12/NR blends efficiently due to the presence of amide linkage at the interfaces from the reaction between the reactive groups of MNR and the NH2 end groups of Nylon12 during mixing. A fine phase morphology (good dispersion and small dispersed phase size of NR domains in Nylon12 matrix) of [Nylon12/NR]/[PS/MNR] blends was observed at the optimum compatibilizer content of 7 phr, relating to the improvement of mechanical property. The impact energy of [Nylon12/NR]/[PS/MNR] blends was 503 J/m higher than that of neat Nylon12 (115 J/m) and Nylon12/NR binary blend (241 J/m) due to the toughening effect of rubber and proper morphology. The melting temperature of all blends did not change obviously from thermal analysis. However, the presence of rubber particle obstructed the crystallization of Nylon12 phase, leading to the decreasing of %crystallinity from 93% to around 70%.

Sign in / Sign up

Export Citation Format

Share Document