scholarly journals Effect of Ordinary Portland Cement and Water Glass on the Properties of Alkali Activated Fly Ash Concrete

Minerals ◽  
2019 ◽  
Vol 10 (1) ◽  
pp. 40 ◽  
Author(s):  
Vytautas Bocullo ◽  
Danutė Vaičiukynienė ◽  
Ramūnas Gečys ◽  
Mindaugas Daukšys
Keyword(s):  
Compressive Strength ◽  
Fly Ash ◽  
Portland Cement ◽  
Water Glass ◽  
Ordinary Portland Cement ◽  
Reference Sample ◽  
Freeze And Thaw ◽  
Naoh Solution ◽  
Increased Strength ◽  
Alkali Activated

This research presents the influence of ordinary Portland cement (OPC) and/or water glass addition on fly ash alkali-activated mortar and concrete. The results show that fly ash (FA) concrete activated with a NaOH solution and water glass mixture had better resistance to freeze and thaw, carbonation, alkali-silica reaction (ASR) and developed higher compressive strength and static elastic modulus compared with the FA concrete activated only with an NaOH solution. The addition of OPC contributes to the development of a denser microstructure of alkali activated concrete (AAC) samples. In the presence of water glass and OPC, the compressive strength (52.60 MPa) of the samples increased more than two times as compared with the reference sample (21.36 MPa) without OPC and water glass. The combination of OPC and water glass showed the increased strength and enhanced durability of AAC. The samples were more resistant to freeze and thaw, ASR, and carbonation.

scholarly journals Effect of Elevated Temperature on Alkali Activated Slag and Fly Ash based Geopolymer Concrete

2020 ◽  
Vol 9 (4) ◽  
pp. 1241-1250
Keyword(s):  
Compressive Strength ◽  
Elevated Temperature ◽  
Fly Ash ◽  
Flexural Strength ◽  
Portland Cement ◽  
Ordinary Portland Cement ◽  
Geopolymer Concrete ◽  
Base Materials ◽  
Activated Slag ◽  
Alkali Activated

Activated Slag (AAS) and Fly Ash (FA) based geopolymer concrete a new blended alkali-activated concrete that has been progressively studied over the past years because of its environmental benefits superior engineering properties. Geopolymer has many favorable characteristics in comparison to Ordinary Portland Cement. Many base materials could be utilized to make geopolymer with the convenient concentration of activator solution. In this study, the experimental program composed of two phases; phase on divided into four groups; Group one deliberated the effect of sodium hydroxide molarity and different curing condition on compressive strength. Group two studied the effect of alkali activated solution (NaOH and Na2SiO3) content on compressive strength and workability. The effect of sand replacement with slag on compressive strength and workability was explained in group three. Group four studied the effect of slag replacement with several base materials Fly Ash (FA), Ordinary Portland Cement (OPC), pulverized Red Brick (PRB), and Meta Kaolin (MK). Phase two contains three mixtures from phase one which had the highest compressive strength. For each mixture, the fresh concrete test was air content. In addition the hardened concrete tests were the compressive strength at 3, 7, 28, 90, 180, and 365 days, the flexural strength at 28, 90, and 365 days, and the young's modulus at 28, 90, and 365 days. Moreover; the three mixtures were exposed to elevated temperature at 100oC, 300oC, and 600oC to study the effect of elevated temperature on compressive and flexural strength.

scholarly journals Alkali-Activated Hybrid Cements Based on Fly Ash and Construction and Demolition Wastes Using Sodium Sulfate and Sodium Carbonate

Molecules ◽  
2021 ◽  
Vol 26 (24) ◽  
pp. 7572
Author(s):  
William Valencia-Saavedra ◽  
Rafael Robayo-Salazar ◽  
Ruby Mejía de Gutiérrez
Keyword(s):  
Compressive Strength ◽  
Fly Ash ◽  
Portland Cement ◽  
Sodium Carbonate ◽  
Sodium Sulfate ◽  
Room Temperature ◽  
Ordinary Portland Cement ◽  
Mechanical Performance ◽  
Construction And Demolition Wastes ◽  
Alkali Activated

This article demonstrates the possibility of producing alkali-activated hybrid cements based on fly ash (FA), and construction and demolition wastes (concrete waste, COW; ceramic waste, CEW; and masonry waste, MAW) using sodium sulfate (Na2SO4) (2–6%) and sodium carbonate (Na2CO3) (5–10%) as activators. From a mixture of COW, CEW, and MAW in equal proportions (33.33%), a new precursor called CDW was generated. The precursors were mixed with ordinary Portland cement (OPC) (10–30%). Curing of the materials was performed at room temperature (25 °C). The hybrid cements activated with Na2SO4 reached compressive strengths of up to 31 MPa at 28 days of curing, and the hybrid cements activated with Na2CO3 yielded compressive strengths of up to 22 MPa. Based on their mechanical performance, the optimal mixtures were selected: FA/30OPC-4%Na2SO4, CDW/30OPC-4%Na2SO4, FA/30OPC-10%Na2CO3, and CDW/30OPC-10%Na2CO3. At prolonged ages (180 days), these mixtures reached compressive strength values similar to those reported for pastes based on 100% OPC. A notable advantage is the reduction of the heat of the reaction, which can be reduced by up to 10 times relative to that reported for the hydration of Portland cement. These results show the feasibility of manufacturing alkaline-activated hybrid cements using alternative activators with a lower environmental impact.

Effects of Fly Ash/Slag Ratio and Liquid/Binder Ratio on Strength of Alkali-Activated Fly Ash/Slag Mortars

2013 ◽  
Vol 377 ◽  
pp. 50-54 ◽  
Author(s):  
Mao Chieh Chi ◽  
Yen Chun Liu
Keyword(s):  
Compressive Strength ◽  
Fly Ash ◽  
Flexural Strength ◽  
Portland Cement ◽  
Ordinary Portland Cement ◽  
The Other ◽  
Factors Influencing ◽  
Binder Ratio ◽  
Alkali Activated ◽  
Significant Factors

The purpose of this study is to investigate the effects of fly ash/slag ratio and liquid/binder ratio on strength of alkali-activated fly ash/slag (AAFS) mortars. Three liquid/binder ratios of 0.35, 0.5 and 0.65 and three fly ash/slag ratios of 100/0, 50/50, and 0/100 were selected as variables to design and produce mixes of AAFS mortars. The compressive strength and flexural strength of alkali-activated fly ash/slag mortars were discussed and compared with reference mortars produced using ordinary Portland cement (OPC) mortars. Based on the results, both fly ash/slag ratio and the liquid/binder ratio are significant factors influencing the strengths of AAFS mortars. The strength of AAFS mortars except alkali-activated fly ash mortars is higher than that of OPC mortars. When the fly ash/slag ratio reaches 50/50, the AAFS mortars possesses the highest strength compared with the other mortars.

A Review of Alkali-Activated Slag as Cement Replacement

2019 ◽  
Vol 803 ◽  
pp. 262-266
Author(s):  
Osama Ahmed Mohamed ◽  
Maadoum M. Mustafa
Keyword(s):  
Compressive Strength ◽  
Portland Cement ◽  
Construction Industry ◽  
Ordinary Portland Cement ◽  
Environmental Footprint ◽  
Alkali Activated Slag ◽  
Cement Replacement ◽  
Activated Slag ◽  
Alkali Activated

Alkali activated slag (AAS) offers opportunities to the construction industry as an alternative to ordinary Portland cement (OPC). The production of OPC and its use contributes significantly to release of CO2 into the atmosphere while AAS is an industrial by-product that contributes much less to the environmental footprint that needs to be recycled if not landfilled. This paper outlines some of the key properties, merits and demerits of AAS when used as alternative to OPC. Competitive compressive strength of AAS concrete is amongst of the advantages of replacing cement with AAS while high shrinkage and carbonation levels are potential disadvantages.

Effect of Alkaline Solution to Fly Ash Ratio on Geopolymer Mortar Properties

2017 ◽  
Vol 733 ◽  
pp. 85-88 ◽  
Author(s):  
Amir Fauzi ◽  
Mohd Fadhil Nuruddin ◽  
Ahmad B. Malkawi ◽  
Mohd Mustafa Al Bakri Abdullah ◽  
Bashar S. Mohammed
Keyword(s):  
Compressive Strength ◽  
Fly Ash ◽  
Portland Cement ◽  
Alkaline Solution ◽  
Similar Pattern ◽  
Ordinary Portland Cement ◽  
Setting Time ◽  
Pozzolanic Reaction

Geopolymer system is new binding materials in concrete industry that is produced by the alkaline solution and materials rich in aluminosilicate such as fly ash. The effect of the alkaline solution to fly ash ratios of 0.3, 0.4 and 0.5 on mortar geopolymer properties was an issue in this study. The results showed that the higher alkaline solution to fly ash ratio improves the workability and brings a longer setting time, whereas the lower alkaline solution to fly ash ratio gains the significant compressive strength. It was a similar pattern with conventional mortar used ordinary Portland cement, which the compressive strength at 7 days was 85%-90% for 28 days compressive strength, whereas conventional mortar is only 65%-75%. This was due to the higher reactivity in geopolymer system that was faster than the pozzolanic reaction.

scholarly journals Effect of Ordinary Portland Cement on Some Properties of Pervious Geopolymer Concrete

2021 ◽  
Vol 39 (4A) ◽  
pp. 668-674
Author(s):  
Wasan I. Khalіl ◽  
Qaіs J. Frayyeh ◽  
Haider Abed
Keyword(s):  
Thermal Conductivity ◽  
Compressive Strength ◽  
Flexural Strength ◽  
Portland Cement ◽  
Ordinary Portland Cement ◽  
Total Content ◽  
Dry Density ◽  
Geopolymer Concrete ◽  
Naoh Solution

In this research, a study is made on the Pervious Geopolymer Concrete (PGC), which is based on localmaterial(Metakaolin). The inclusion of Ordinary Portland Cement (OPC) as a partial substitute for Metakaolin (MK) for the production of (PGCs) has also been investigated. Pervious Geopolymer concrete was outputted from the local Metakaolin (MK), and ordinary Portland cement (OPC) as a partial substitute by weight of MK and silicate of sodium (Na2SiO3) and hydroxide of sodium (NaOH) solution. All PGC samples were cured after 24 hours from casting for five hours at a degree of the temperature of 50 ° C, then the testingafter 28 days. The compressive-strength, total content of voids, the strength of bending, dry-density, and thermal-conductivity of pervious Geopolymer concrete were examined. The mechanicalresults of testing ranged from (11.03 and 2.25) to (14.3 and 2.75) MPa for compressive-strength and flexural strength respectively.

Factors Influencing the Strength of Alkali-Activated Slag Cement

2011 ◽  
Vol 368-373 ◽  
pp. 3240-3245
Author(s):  
Zhi Jun Zhou ◽  
Hui Li ◽  
Qiang Song ◽  
Bao Jing Shen
Keyword(s):  
Compressive Strength ◽  
Fly Ash ◽  
Silica Fume ◽  
Water Glass ◽  
Slag Cement ◽  
Alkali Activated Slag ◽  
Factors Influencing ◽  
Activated Slag ◽  
Alkali Activated

In this paper, water glass was chosen as activator to prepare Alkali-activated slag(AAS) cement. Effects of modulus and dosage of water glass, and admixture (fly ash, slag and silica fume) on the strength of AAS cement was investigated. It was found that the modulus of water glass had great effect on the strength of AAS cement when the mixing amount of water glass was less than 12%. With the incorporation of fly ash or slag, the strength of AAS cement decreased, however the incorporation of silica fume could promote the flexural and compressive strength of AAS cement slightly.

scholarly journals Alkali-Activated Metakaolin and Fly Ash as Unfired Ceramic Bonding Systems

Minerals ◽  
2021 ◽  
Vol 11 (2) ◽  
pp. 197
Author(s):  
Jozef Vlček ◽  
Michaela Topinková ◽  
Miroslava Klárová ◽  
Petra Maierová ◽  
Hana Ovčačíková ◽  
...  
Keyword(s):  
Mechanical Properties ◽  
Compressive Strength ◽  
Fly Ash ◽  
Water Glass ◽  
Raw Materials ◽  
Alkali Activation ◽  
Activation Process ◽  
Laboratory Conditions ◽  
Naoh Solution ◽  
Bonding Systems

Metakaolin (MK) prepared by the calcination of kaolin at 550 °C and fly ash (FA) from the combustion of black coal in a granulating boiler were used to prepare unfired ceramic bonding systems via the alkali activation process. A long-term stability of the mechanical properties of the prepared samples similar to the unfired ceramic systems was observed. The optimal metakaolin and fly ash ratio, the type of the activator (NaOH or water glass) and its concentration were evaluated after the hydration in: a) laboratory conditions; b) hydration box; and c) under the hydrothermal activation. Raw materials and the samples prepared by alkali activation process were characterized by XRD, XRF, TG/DTA, and FTIR methods. The mechanical properties of the prepared samples were tested using a compressive strength test after 2, 28 and 56 days of hydration. The compressive strengths of 16 and 24 MPa after 28 days of hydration were reached for FA samples activated with water glass. The alkali activation of MK was successful in the NaOH solution of the molar concentration above 5 M. The compressive strength values of metakaolin, activated hydrothermally and hydrated at laboratory conditions, reached 11.2 and 5.5 MPa, respectively, for 5 M activator of NaOH.