scholarly journals Improving Mechanical Properties of 18%Mn TWIP Steels by Cold Rolling and Annealing

Metals ◽  
2019 ◽  
Vol 9 (7) ◽  
pp. 776 ◽  
Author(s):  
Vladimir Torganchuk ◽  
Andrey Belyakov ◽  
Rustam Kaibyshev
Keyword(s):  
Mechanical Properties ◽  
Tensile Strength ◽  
Ultimate Tensile Strength ◽  
Cold Rolling ◽  
Large Strain ◽  
Total Elongation ◽  
Fine Grained ◽  
Average Grain Size ◽  
Twip Steels ◽  
Cold Rolling And Annealing

The microstructures and mechanical properties of Fe-0.4C-18Mn and Fe-0.6C-18Mn steels subjected to large strain cold rolling followed by annealing were studied. Cold rolling with a total reduction of 86% resulted in substantial strengthening at expense of plasticity. The yield strength and the ultimate tensile strength of above 1400 MPa and 1600 MPa, respectively, were achieved in both steels, whereas total elongation decreased below 30%. Subsequent annealing at temperatures above 600 °C was accompanied with the development of recrystallization leading to fine-grained microstructures with an average grain size of about 1 μm in both steels. The fine-grained steels exhibited remarkable improved mechanical properties with a product of ultimate tensile strength by total elongation in the range of 50 to 70 GPa %. The fine-grained steel with relatively high carbon content of 0.6%C was characterized by ultimate tensile strength well above 1400 MPa that was remarkably higher than that of about 1200 MPa in the steel with 0.4%C.

Ultrafine-Grained Structure and Mechanical Properties of a High-Mn Twinning Induced Plasticity Steel

2016 ◽  
Vol 838-839 ◽  
pp. 392-397 ◽  
Author(s):  
Pavel Kusakin ◽  
Andrey Belyakov ◽  
Rustam Kaibyshev ◽  
Dmitri Molodov
Keyword(s):  
Mechanical Properties ◽  
Grain Size ◽  
Tensile Strength ◽  
Ultimate Tensile Strength ◽  
Yield Strength ◽  
Cold Rolling ◽  
Twip Steel ◽  
True Strain ◽  
Total Elongation ◽  
Recrystallization Annealing

The influence of thermo-mechanical treatment consisting of cold rolling followed by recrystallization annealing on the grain size and mechanical properties of a high-Mn TWIP steel was studied. An Fe-23Mn-0.3C-1.5Al TWIP steel (wt. %) was subjected to extensive cold rolling with a reduction of 80% (true strain of ∼1.6) and then annealed in the temperature interval ranging from 400 to 900 °C during 20 minutes. Recovery processes took place below 500 °C, partial recrystallization was evident at ~550°C and fully recrystallized structure evolved after annealing at 600 °C and higher. The static recovery resulted in a slight decrease in the yield strength from 1400 MPa to 1250 MPa and the ultimate tensile strength from 1540 MPa to 1400 MPa whereas the total elongation of 4% did not changed. The recrystallization development led to a drastic drop of strength and an increase in ductility. The yield strength of 225 MPa, the ultimate tensile strength of 700 MPa and the total elongation of 79% was obtained after annealing at 900 °C. Correspondingly, the grain size increased from 0.2 μm to 6.2 μm with increase in anneal temperature from 550 to 900°C.

Vibratory weld conditioning during gas tungsten arc welding of al 5052 alloy on the mechanical and micro-structural behavior

2020 ◽  
Vol 17 (6) ◽  
pp. 831-836
Author(s):  
M. Vykunta Rao ◽  
Srinivasa Rao P. ◽  
B. Surendra Babu
Keyword(s):  
Mechanical Properties ◽  
Grain Size ◽  
Tensile Strength ◽  
Ultimate Tensile Strength ◽  
Welded Joints ◽  
Great Influence ◽  
Welding Process ◽  
Microstructural Characterization ◽  
Content Type ◽  
Average Grain Size

Purpose Vibratory weld conditioning parameters have a great influence on the improvement of mechanical properties of weld connections. The purpose of this paper is to understand the influence of vibratory weld conditioning on the mechanical and microstructural characterization of aluminum 5052 alloy weldments. An attempt is made to understand the effect of the vibratory tungsten inert gas (TIG) welding process parameters on the hardness, ultimate tensile strength and microstructure of Al 5052-H32 alloy weldments. Design/methodology/approach Aluminum 5052 H32 specimens are welded at different combinations of vibromotor voltage inputs and time of vibrations. Voltage input is varied from 50 to 230 V at an interval of 10 V. At each voltage input to the vibromotor, there are three levels of time of vibration, i.e. 80, 90 and 100 s. The vibratory TIG-welded specimens are tested for their mechanical and microstructural properties. Findings The results indicate that the mechanical properties of aluminum alloy weld connections improved by increasing voltage input up to 160 V. Also, it has been observed that by increasing vibromotor voltage input beyond 160 V, mechanical properties were reduced significantly. It is also found that vibration time has less influence on the mechanical properties of weld connections. Improvement in hardness and ultimate tensile strength of vibratory welded joints is 16 and 14%, respectively, when compared without vibration, i.e. normal weld conditions. Average grain size is measured as per ASTM E 112–96. Average grain size is in the case of 0, 120, 160 and 230 is 20.709, 17.99, 16.57 and 20.8086 µm, respectively. Originality/value Novel vibratory TIG welded joints are prepared. Mechanical and micro-structural properties are tested.

Influence of Cold Rolling Reduction on Microstructure and Mechanical Properties in 204C2 Austenitic Stainless Steel

2019 ◽  
Vol 944 ◽  
pp. 193-198
Author(s):  
Tian Yi Wang ◽  
Ren Bo Song ◽  
Heng Jun Cai ◽  
Jian Wen ◽  
Yang Su
Keyword(s):  
Mechanical Properties ◽  
Tensile Strength ◽  
Stainless Steel ◽  
Austenitic Stainless Steel ◽  
Ultimate Tensile Strength ◽  
Yield Strength ◽  
Cold Rolling ◽  
Stainless Steels ◽  
Rolling Reduction ◽  
Cold Rolling Reduction

The present study investigated the effect of cold rolling reduction on microstructure and mechanical properties of a 204C2 Cr–Mn austenitic stainless steel which contained 16%Cr, 2%Ni, 9%Mn and 0.083 %C). The 204C2 austenitic stainless steels were cold rolled at multifarious thickness reductions of 10%, 20%, 30%,40% and 50%, which were compared with the solution-treated one. Microstructure of them was investigated by means of optical microscopy, X-ray diffraction technique and scanning electron microscopy. For mechanical properties investigations, hardness and tensile tests were carried out. Results shows that the cold rolling reduction induced the martensitic transformation (γ→α ́) in the structure of the austenitic stainless steel. With the increase of the rolling reduction, the amount of strain-induced martensite increased gradually. Hardness, ultimate tensile strength and yield strength increased with the incremental rolling reduction in 204C2 stainless steels, while the elongation decreased. At the thickness reduction of 50%, the specimen obtained best strength and hardness. Hardness of 204C2 stain steel reached 679HV. Ultimate tensile strength reached 1721 MPa. Yield strength reached 1496 MPa.

scholarly journals Effect of Heat Treatment on Mechanical Properties and Microstructure Morphology of Low-Alloy High-Strength Steel

2016 ◽  
Vol 61 (2) ◽  
pp. 475-480
Author(s):  
K. Bolanowski
Keyword(s):  
Mechanical Properties ◽  
Heat Treatment ◽  
Grain Size ◽  
Tensile Strength ◽  
Ultimate Tensile Strength ◽  
Yield Strength ◽  
High Strength Steel ◽  
High Strength ◽  
Strengthening Phase ◽  
Average Grain Size

Abstract The paper analyzes the influence of different heat treatment processes on the mechanical properties of low-alloy high-strength steel denoted by Polish Standard (PN) as 10MnVNb6. One of the findings is that, after aging, the mechanical properties of rolled steel are high: the yield strength may reach > 600 MPa, and the ultimate tensile strength is > 700 MPa. These properties are largely dependent on the grain size and dispersion of the strengthening phase in the ferrite matrix. Aging applied after hot rolling contributes to a considerable rise in the yield strength and ultimate tensile strength. The process of normalization causes a decrease in the average grain size and coalescence (reduction of dispersion) of the strengthening phase. When 10MnVNb6 steel was aged after normalization, there was not a complete recovery in its strength properties.

Effect of Bi on Microstructure and Mechanical Properties of Extruded AZ80-2Sn Magnesium Alloy

2018 ◽  
Vol 37 (1) ◽  
pp. 97-103 ◽  
Author(s):  
Hansong Xue ◽  
Xinyu Li ◽  
Weina Zhang ◽  
Zhihui Xing ◽  
Jinsong Rao ◽  
...  
Keyword(s):  
Mechanical Properties ◽  
Grain Size ◽  
Tensile Strength ◽  
Magnesium Alloy ◽  
Ultimate Tensile Strength ◽  
Yield Strength ◽  
Microstructure And Mechanical Properties ◽  
Average Grain Size

AbstractThe effects of Bi on the microstructure and mechanical properties of AZ80-2Sn alloy were investigated. The results show that the addition of Bi within the as-cast AZ80-2Sn alloy promotes the formation of Mg3Bi2 phase, which can refine the grains and make the eutectic phases discontinuous. The addition of 0.5 % Bi within the as-extruded AZ80-2Sn alloy, the average grain size decreases to 12 μm and the fine granular Mg17Al12 and Mg3Bi2 phases are dispersed in the α-Mg matrix. With an increase in Bi content, the Mg17Al12 and Mg3Bi2 phases become coarsened and the grain size increases. The as-extruded AZ80-2Sn-0.5 %Bi alloy has the optimal properties, and the ultimate tensile strength, yield strength and elongation are 379.6 MPa, 247.1 MPa and 14.8 %, respectively.

Influence of Grain Size on Mechanical Properties of AZX311 Alloy

2013 ◽  
Vol 753 ◽  
pp. 473-476 ◽  
Author(s):  
Naoto Sakai ◽  
Kunio Funami ◽  
Masafumi Noda ◽  
Hisashi Mori ◽  
Kenji Fujino
Keyword(s):  
Mechanical Properties ◽  
Grain Size ◽  
Tensile Strength ◽  
Ultimate Tensile Strength ◽  
Yield Strength ◽  
Total Elongation ◽  
Growth Behavior ◽  
Rolled Material ◽  
Annealing Temperatures ◽  
Grain Growth Behavior

In the present study, the grain refinement, grain growth behavior, and tensile properties of rolled and annealed AZX311 Mg alloys were investigated. The yield strength and ultimate tensile strength of the rolled material were 360 MPa and 370 MPa, respectively, and the total elongation was 5%. When annealing was performed at 423 K for 1hr, the yield strength and ultimate tensile strength were unchanged, but the elongation increased to 10%. Furthermore, the strength and elongation did not change for annealing temperatures of 473–673 K owing to Al2Ca precipitations.

Microstructure and Mechanical Properties of Mg96Y3Zn1 Alloy Processed by Equal Channel Angular Pressing

2011 ◽  
Vol 682 ◽  
pp. 49-54
Author(s):  
Bin Chen ◽  
Chen Lu ◽  
Dong Liang Lin ◽  
Xiao Qin Zeng
Keyword(s):  
Mechanical Properties ◽  
Grain Size ◽  
Tensile Strength ◽  
Ultimate Tensile Strength ◽  
Yield Strength ◽  
Tensile Test ◽  
Equal Channel Angular Pressing ◽  
Ultrafine Grains ◽  
Angular Pressing ◽  
Average Grain Size

The Mg96Y3Zn1 alloy processed by equal channel angular pressing has been investigated. It was found that the Mg96Y3Zn1 alloy processed by ECAP obtained ultrafine grains and exhibits excellent mechanical properties. After ECAP, the average grain size of Mg96Y3Zn1 alloy refined to about 400 nm. The highest strengths with yield strength of 381.45MPa and ultimate tensile strength of 438.33MPa were obtained after 2 passes at 623K. It was found that cracks were preferentially initiated and propagated in the interior of X-phase during the tensile test. As a result, the elongation of alloy is decreased with pass number increasing.

scholarly journals Effect of True Strains in Isothermal abc Pressing on Mechanical Properties of Ti49.8Ni50.2 Alloy

Metals ◽  
2020 ◽  
Vol 10 (10) ◽  
pp. 1313
Author(s):  
Oleg Kashin ◽  
Konstantin Krukovskii ◽  
Aleksandr Lotkov ◽  
Victor Grishkov
Keyword(s):  
Mechanical Properties ◽  
Grain Size ◽  
Tensile Strength ◽  
Ultimate Tensile Strength ◽  
True Strain ◽  
Main Idea ◽  
Strain Curve ◽  
Subgrain Structure ◽  
Average Grain Size ◽  
Abc Pressing

The paper analyzes the microstructure and mechanical properties of Ti49.8Ni50.2 alloy (at.%) under uniaxial tension at room temperature after isothermal abc pressing to true strains e = 0.29 − 8.44 at T = 723 K. The analysis shows that as the true strain e is increased, the grain–subgrain structure of the alloy is gradually refined. This leads to an increase in its yield stress σy and strain hardening coefficient θ = dσ/dε at linear stage III of its tensile stress–strain curve according to the Hall–Petch relation. However, the ultimate tensile strength remains invariant to such refinement. The possible mechanism is proposed to explain why the ultimate tensile strength can remain invariant to the average grains size (dav). It is assumed that the sharp increase of the ultimate tensile strength σUTS begins when (dav) is less than the critical average grain size (dav)cr. In our opinion, for the investigated alloy (dav)cr ≈ 0.5 µm. In our study, the attained average grain size is larger the critical one. The main idea of the mechanism is next. In alloys with an average grain size (dav) less than the critical one, a higher external stress is required for the nucleation and propagation of the main crack.

Microstructure and Mechanical Properties of TRIP-Aided Steels with Different Heat Treatments

2015 ◽  
Vol 817 ◽  
pp. 439-443 ◽  
Author(s):  
Rui Dong ◽  
Ai Min Zhao ◽  
Ran Ding ◽  
Jian Guo He ◽  
Han Jiang Hu
Keyword(s):  
Mechanical Properties ◽  
Tensile Strength ◽  
Ultimate Tensile Strength ◽  
Retained Austenite ◽  
Volume Fraction ◽  
Total Elongation ◽  
Heat Treatments ◽  
Second Phase ◽  
Soft Matrix ◽  
Significant Difference

The microstructures, mechanical properties and retained austenite characteristics of TRIP-aided steels with three different heat treatments were studied in this paper. The results indicated that the designed annealing treatments resulted in completely different matrices and the morphologies of second phase, and a significant difference in mechanical properties. The TAM steel was found to have fine annealed martensite lath matrix and inter lath acicular retained austenite, and possessed an excellent combination of strength and elongation which attributed to the highest retained austenite volume fraction and carbon concentration. For TPF steel, the higher instability and lower carbon content of retained austenite and the soft matrix resulted in the lowest ultimate tensile strength and total elongation. While in TBF steel, the stability of retained austenite was lower than that in TAM steel but higher than that in TPF steel. The ultimate tensile strength of TBF was significantly higher than the TAM and TPF steels, but the ductility of TBF steel was lower than TAM steel.

scholarly journals Recrystallization and Mechanical Behavior of High Mn and Low C Cold Rolled and Annealed Steel with TWIP Effect

2012 ◽  
Vol 715-716 ◽  
pp. 579-584 ◽  
Author(s):  
Dagoberto Brandao Santos ◽  
Berenice Mendonça Gonzalez ◽  
Elena V. Pereloma
Keyword(s):  
Mechanical Properties ◽  
Tensile Strength ◽  
Driving Force ◽  
Vickers Microhardness ◽  
Tensile Tests ◽  
Total Elongation ◽  
Strain Hardening Exponent ◽  
Twip Steels ◽  
Cold Rolled ◽  
Annealed Steel

ncreasing demand for automotive vehicles with reduced weight, improved crashworthiness and passengers safety has steamed the research of new Twinning Induced Plasticity (TWIP) steels. In this work the effect of annealing between 400 and 900°C on the microstructure and mechanical properties of hot and cold rolled 0.06C-24Mn-3Al-2Si-1Ni (wt%) steel with TWIP effect was investigated. The results have shown that steel exhibits fast recrystallization kinetics with a low amount of recovery, which results in a high driving force for the former. Mechanical properties were determined using Vickers microhardness and tensile tests. Tensile strength of 670 MPa with 54% of total elongation, and strain hardening exponent of 0.57 were reached after annealing at 900°C.

Sign in / Sign up

Export Citation Format

Share Document