scholarly journals Influence of Short-Term Heat Treatment on the Mechanical Properties of Al–Mg–Si Profiles

Metals ◽  
2018 ◽  
Vol 8 (9) ◽  
pp. 664 ◽  
Author(s):  
Sandra Kernebeck ◽  
Sebastian Weber
Keyword(s):  
Mechanical Properties ◽  
Heat Treatment ◽  
Tensile Strength ◽  
Automotive Industry ◽  
Measurement Method ◽  
Natural Aging ◽  
Hot Extrusion ◽  
Tensile Tests ◽  
Short Term ◽  
Aluminum Profiles

Aluminum profiles—for instance, profiles made of precipitation-hardenable alloys—are increasingly used for decorative details in the automotive industry. Typically, after hot extrusion and at least two to three days of natural aging (NA), the aluminum profiles are artificially aged. A commercial EN AW-6060 alloy of high purity was used for this investigation. Tensile tests were used as the main measurement method. This article focuses on the effect of short-term heat treatment on the point in time at which a significant increase of the ultimate tensile strength (UTS) during NA can be measured. Short-term heat treatment is shown to delay this point in time by almost four days, but it increases the variation of UTS. A heterogeneous temperature profile during short-term heat treatment was identified as one reason for this result. Finally, a strategy for minimizing variations in mechanical properties of artificially-aged aluminum alloys was developed, based on the experimental results of this study.

scholarly journals Effects of Different Solid Solution Temperatures on Microstructure and Mechanical Properties of the AA7075 Alloy After T6 Heat Treatment

2019 ◽  
Vol 38 (2019) ◽  
pp. 892-896 ◽  
Author(s):  
Süleyman Tekeli ◽  
Ijlal Simsek ◽  
Dogan Simsek ◽  
Dursun Ozyurek
Keyword(s):  
Mechanical Properties ◽  
Heat Treatment ◽  
Solid Solution ◽  
Tensile Strength ◽  
Tensile Tests ◽  
Solution Temperature ◽  
T6 Heat Treatment ◽  
Microstructure And Mechanical Properties ◽  
Different Temperatures

AbstractIn this study, the effect of solid solution temperature on microstructure and mechanical properties of the AA7075 alloy after T6 heat treatment was investigated. Following solid solution at five different temperatures for 2 hours, the AA7075 alloy was quenched and then artificially aged at 120∘C for 24 hours. Hardness measurements, microstructure examinations (SEM+EDS, XRD) and tensile tests were carried out for the alloys. The results showed that the increased solid solution temperature led to formation of precipitates in the microstructures and thus caused higher hardness and tensile strength.

Mechanical properties of heat-treated cellulose nanofiber-reinforced polyvinyl alcohol nanocomposite

2016 ◽  
Vol 51 (14) ◽  
pp. 1971-1977 ◽  
Author(s):  
NH Noor Mohamed ◽  
Hitoshi Takagi ◽  
Antonio N Nakagaito
Keyword(s):  
Electron Microscopy ◽  
Mechanical Properties ◽  
Heat Treatment ◽  
Tensile Strength ◽  
Polyvinyl Alcohol ◽  
Tensile Tests ◽  
Cellulose Nanofiber ◽  
Heat Treated ◽  
Scanning Electron ◽  
Polyvinyl Alcohol Films

The mechanical properties of cellulose nanofiber-reinforced polyvinyl alcohol composite were studied. Neat polyvinyl alcohol films, cellulose nanofiber sheets, and their nanocomposites containing cellulose nanofiber weight ratios of 5, 15, 30, 40, 45, 50 and 80 wt% were fabricated. Heat treatment by hot pressing at 180℃ was conducted on the specimens to study its effect to the mechanical properties and the results were compared with the non heat-treated specimens. Morphology of the composites was studied by scanning electron microscopy and the mechanical properties were evaluated by means of tensile tests. The results showed that increase of cellulose nanofiber content from 5 wt% to 80 wt% has increased the tensile strength of the composites up to 180 MPa, with cellulose nanofiber content higher than 40 wt% yielding higher tensile strength. The heat-treated specimens exhibited higher tensile strength compared to those of untreated specimens.

Experimental Investigation of Heat-Treated Aluminum Profiles

2015 ◽  
Vol 651-653 ◽  
pp. 59-64
Author(s):  
Marion Merklein ◽  
Matthias Graser ◽  
Michael Lechner
Keyword(s):  
Mechanical Properties ◽  
Heat Treatment ◽  
Experimental Investigation ◽  
Material Flow ◽  
Material Characterization ◽  
Process Window ◽  
Short Term ◽  
Property Distribution ◽  
Heat Treated ◽  
Aluminum Profiles

Tailor Heat Treated Profiles (THTP) are profiles that exhibit local different mechanical properties optimized for a subsequent forming operation. The property distribution is realized by short term heat treatment before a forming operation. Based on the interaction of soft and hard areas the material flow can be improved and the formability can be enhanced. Prerequisite for a successful application of the technology is a comprehensive material characterization. Therefore, within this paper the influence of short term heat treatment on the mechanical properties of profiles will be presented. In particular, different heating technologies based on heat conduction and laser radiation are compared. Based on the results, a process window will be derived. All investigations were performed using the precipitation hardenable aluminum alloy EN AW 6060.

The effect of heat treatment temperature on the mechanical properties of copper M1.

2015 ◽  
Vol 2015 (3) ◽  
pp. 94-97
Author(s):  
Юлия Гусева ◽  
Yuliya Guseva ◽  
Владимир Сакало ◽  
Vladimir Sakalo ◽  
Татьяна Иншакова ◽  
...  
Keyword(s):  
Mechanical Properties ◽  
Heat Treatment ◽  
Tensile Strength ◽  
Heat Treatment Temperature ◽  
Tensile Tests ◽  
Treatment Temperature ◽  
Condi Tions ◽  
Solid Copper

Tensile tests of specimens made from solid copper M1 had been conducted. Samples were subjected to heat treatment by heating to temperatures of 200 to 900°C and were cooled in water or air. Values of tensile strength and relative residual elongation were defined. The condi-tions under which solid copper acquires the properties of soft copper installed.

scholarly journals The Effect of Solid-State Processes and Heat Treatment on the Properties of AA7075 Aluminum Waste Recycling Nanocomposite

Materials ◽  
2021 ◽  
Vol 14 (21) ◽  
pp. 6667
Author(s):  
Huda Mohammed Sabbar ◽  
Zulkiflle Leman ◽  
Shazarel Shamsudin ◽  
Suraya Mohd Tahir ◽  
Che Nor Aiza Jaafar ◽  
...  
Keyword(s):  
Mechanical Properties ◽  
Heat Treatment ◽  
Tensile Strength ◽  
Solid State ◽  
Volume Fraction ◽  
Hot Extrusion ◽  
Waste Recycling ◽  
Heat Treatment Condition ◽  
Zro2 Nanoparticles ◽  
Compression Pressure

Direct solid-states, such as hot extrusion and equal channel angular pressing (ECAP), are alternative and efficient solid-state processes for use in recycling aluminium scrap. These processes utilise less energy and are eco-friendly. Ceramic particles such as ZrO2 are suggested as alternatives in the production of metal composites. This study investigated and optimised the effects of various parameters of reinforced ZrO2 nanoparticles on the mechanical and physical properties via response surface methodology (RSM). These parameters were the volume fraction (VF), preheating temperature (T), and preheating time (t). The effects of these parameters were examined before and after the heat treatment condition and ECAP. Each parameter was evaluated at varying magnitudes, i.e., 450, 500, and 550 °C for T, 1, 2, and 3 h for t, and 1, 3, and 5% for VF. The effect that process variables had on responses was elucidated using the factorial design with centre point analysis. T and VF were crucial for attaining the optimum ultimate tensile strength (UTS) and microhardness. Reducing VF increased the mechanical properties to 1 vol% of oxide. The maximum hardness of 95 HV was attained at 550 °C, 1.6 h, and 1 vol% ZrO2 with a density of 2.85 g/cm3 and tensile strength of 487 MPa. UTS, density, and microhardness were enhanced by 14%, 1%, and 9.5%, respectively. Additionally, the hot extrusion parameters and ECAP followed by heat treatment strengthened the microhardness by 64% and density by 3%. Compression pressure and extrusion stress produced in these stages were sufficient to eliminate voids that increased the mechanical properties.

Effect of Forward Extrusion and Heat Treatment on Microstructure and Mechanical Properties of as-Cast ZK60 Magnesium Alloy

2010 ◽  
Vol 148-149 ◽  
pp. 332-337 ◽  
Author(s):  
Yong Xue ◽  
Zhi Min Zhang ◽  
Li Hui Lang
Keyword(s):  
Mechanical Properties ◽  
Heat Treatment ◽  
Tensile Strength ◽  
Magnesium Alloy ◽  
Tensile Tests ◽  
Extrusion Process ◽  
Extrusion Ratio ◽  
Forward Extrusion ◽  
Zk60 Alloy ◽  
Zk60 Magnesium Alloy

In the present research, the influences of different extrusion ratios (15, 30, 45, 60, and 75), extrusion temperatures (300 , 340 , 380 , 420 , and 460 ), and subsequent heat treatment on the mechanical properties and microstructure of as-cast ZK60 magnesium alloy have been investigated through the tensile tests and via metallographic observation. The results show that forward extrusion process can refine the microstructure of as-cast ZK60 alloy effectively. If as-cast ZK60 alloys have been extruded with the extrusion ratio 45 at 380 ,420 and 460 , respectively, and then post-heat treatment was conducted, the ZK60 alloy’s strength is higher under T5 than T6 treatment. For as-cast ZK60 alloy processed by extrusion and T5 method, the most appropriate temperature for extrusion processing is 300 , at which its tensile strength are highest provided the extrusion ratio is 30 but yet its plasticity is best provided the extrusion ratio is 45. If forward extrusions were conducted at 380 , mechanical properties of ZK60 alloy have little difference as the extrusion ratio varies. When T6 treatment was conducted for the extruded bars, their mechanical properties were improved little, moreover, the bigger the extrusion ratio is, the higher the tensile strength and elongation of the extruded bars become.

Tailored Heat Treated Profiles - Enhancement of the Forming Limit of Aluminum Profiles under Bending Load

2012 ◽  
Vol 504-506 ◽  
pp. 375-380 ◽  
Author(s):  
Marion Merklein ◽  
Michael Lechner ◽  
Thomas Schneider ◽  
Raoul Plettke
Keyword(s):  
Mechanical Properties ◽  
Heat Treatment ◽  
Tensile Tests ◽  
Local Heat ◽  
Forming Limit ◽  
Cold Bending ◽  
Heat Treated ◽  
Bending Load ◽  
Local Modification ◽  
Aluminum Profiles

Aluminum profiles are well-established components in lightweight constructions. However, these profiles have a small forming capability in comparison to steel profiles, which leads to a limitation in their application. Within this paper a new and innovative approach for the enhancement of the forming limit of aluminum profiles under bending load called Tailored Heat Treated Profiles (THTP) is presented. With THTP the mechanical properties of the material are locally modified by a short-term heat treatment. By this local modification the material flow during the following cold bending operation can be influenced. For the design of the heat treatment layout, the correlation between the heat treatment parameters and the material properties has to be investigated. Tensile specimens were cut out of the profile and were subsequently completely heat treated with a laser. The changes of the mechanical properties caused by the heat treatment were analyzed by tensile tests. However, with a complete softening of the profile, the formability could not be improved. To increase the formability a local heat treatment, which leads to partial softening of the profile, has to be investigated. In order to characterize the heat-affected zone (HAZ) of the laser treatment, thermal camera and microhardness measurements were carried out. Appropriate heat treatment layouts have to be found to enhance the forming limit. Different layout strategies were developed and afterwards validated by the heat treatment and forming of profiles. This paper will present the findings of this investigation and show that THTP can be used to improve the formability of aluminum profiles for bending operations.

Influence of Extrusion Temperature on Microstructures and Properties of Cu-17Ni-3Al-X Alloy

2013 ◽  
Vol 749 ◽  
pp. 105-111
Author(s):  
Wei Yan ◽  
Yuan Hui Weng ◽  
Zong Qiang Luo ◽  
Wei Wen Zhang
Keyword(s):  
Mechanical Properties ◽  
Grain Size ◽  
Tensile Strength ◽  
Brinell Hardness ◽  
Cast Alloy ◽  
Hot Extrusion ◽  
Tensile Tests ◽  
Optical Microscope ◽  
Different Temperatures ◽  
Electronic Microscope

The microstructures and mechanical properties of the Cu-17Ni-3Al-X alloy extruded at different temperatures were investigated by hardness and tensile tests, optical microscope and scanning electronic microscope. The experimental results showed that dynamic re-crystallization occured during the hot extrusion at 1000 . The grain size of the extruded alloy was significantly refined and the mechanical properties increased remarkably compared to the as-cast alloy. The alloy extruded at 1075 exhibited good mechanical properties with tensile strength of 994 MPa, Brinell hardness of 296 and elongation of 8.0%, which are 30%, 9% and 285% higher than that of the as-cast alloy.

Microstructure and Tensile Properties of Al-15wt%Mg2Si Composite after Hot Extrusion and Heat Treatment

2011 ◽  
Vol 471-472 ◽  
pp. 1171-1176 ◽  
Author(s):  
A. Bahrami ◽  
A. Razaghian ◽  
M. Emamy ◽  
H.R. Jafari Nodooshan ◽  
G.S. Mousavi
Keyword(s):  
Mechanical Properties ◽  
Heat Treatment ◽  
Tensile Strength ◽  
Tensile Testing ◽  
Solution Treatment ◽  
Hot Extrusion ◽  
Extrusion Ratio ◽  
Primary Mg2si ◽  
Heat Treated ◽  
The Relationship

In this study, the relationship between microstructures and mechanical properties of the extrusion processed Al-15wt.%Mg2Si composite was investigated after applying various extrusion ratios (6:1, 12:1 and 18:1) and solution treatment. Various techniques including metallography, tensile testing and SEM fractography were utilized to characterize the mechanical behavior of the MMC. Results demonstrated that extruded and heat treated composite possesses considerably higher strength and enhanced ductility in comparison with the as-cast samples. It was also found that heat treatment and extrusion processes do not change the primary Mg2Si morphology considerably, but its size increases as extrusion ratio decreased. Heat treatment and extrusion ratio effects on tensile strength, elongation of extruded specimens were also studied in this work.

scholarly journals Heat Treatment Evaluation for the Camshafts Production of ADI Low Alloyed with Vanadium

Metals ◽  
2021 ◽  
Vol 11 (7) ◽  
pp. 1036
Author(s):  
Eduardo Colin García ◽  
Alejandro Cruz Ramírez ◽  
Guillermo Reyes Castellanos ◽  
José Federico Chávez Alcalá ◽  
Jaime Téllez Ramírez ◽  
...  
Keyword(s):  
Mechanical Properties ◽  
Heat Treatment ◽  
Tensile Strength ◽  
Ductile Iron ◽  
Volume Fraction ◽  
Energy Impact ◽  
Treatment Conditions ◽  
Mold Casting ◽  
Grade 3 ◽  
Good Agreement

Ductile iron camshafts low alloyed with 0.2 and 0.3 wt % vanadium were produced by one of the largest manufacturers of the ductile iron camshafts in México “ARBOMEX S.A de C.V” by a phenolic urethane no-bake sand mold casting method. During functioning, camshafts are subject to bending and torsional stresses, and the lobe surfaces are highly loaded. Thus, high toughness and wear resistance are essential for this component. In this work, two austempering ductile iron heat treatments were evaluated to increase the mechanical properties of tensile strength, hardness, and toughness of the ductile iron camshaft low alloyed with vanadium. The austempering process was held at 265 and 305 °C and austempering times of 30, 60, 90, and 120 min. The volume fraction of high-carbon austenite was determined for the heat treatment conditions by XRD measurements. The ausferritic matrix was determined in 90 min for both austempering temperatures, having a good agreement with the microstructural and hardness evolution as the austempering time increased. The mechanical properties of tensile strength, hardness, and toughness were evaluated from samples obtained from the camshaft and the standard Keel block. The highest mechanical properties were obtained for the austempering heat treatment of 265 °C for 90 min for the ADI containing 0.3 wt % V. The tensile and yield strength were 1200 and 1051 MPa, respectively, while the hardness and the energy impact values were of 47 HRC and 26 J; these values are in the range expected for an ADI grade 3.