scholarly journals Influence of the Energy Density for Selective Laser Melting on the Microstructure and Mechanical Properties of Stainless Steel

Metals ◽  
2020 ◽  
Vol 10 (7) ◽  
pp. 919 ◽  
Author(s):  
Črtomir Donik ◽  
Jakob Kraner ◽  
Irena Paulin ◽  
Matjaž Godec
Keyword(s):  
Mechanical Properties ◽  
Stainless Steel ◽  
Energy Density ◽  
Selective Laser Melting ◽  
Process Parameters ◽  
Material Properties ◽  
Beam Diameter ◽  
Laser Melting ◽  
Microstructure And Mechanical Properties ◽  
The Impact

We have investigated the impact of the process parameters for the selective laser melting (SLM) of the stainless steel AISI 316L on its microstructure and mechanical properties. Properly selected SLM process parameters produce tailored material properties, by varying the laser’s power, scanning speed and beam diameter. We produced and systematically studied a matrix of samples with different porosities, microstructures, textures and mechanical properties. We identified a combination of process parameters that resulted in materials with tensile strengths up to 711 MPa, yield strengths up to 604 MPa and an elongation up to 31%, while the highest achieved hardness was 227 HV10. The correlation between the average single-cell diameter in the hierarchical structure and the laser’s input energy is systematically studied, discussed and explained. The same energy density with different SLM process parameters result in different material properties. The higher energy density of the SLM produces larger cellular structures and crystal grains. A different energy density produces different textures with only one predominant texture component, which was revealed by electron-backscatter diffraction. Furthermore, three possible explanations for the origin of the dislocations are proposed.

Main Defects Observed in Titanium GRADE II and 316L Stainless Steel Elements Obtained by Selective Laser Melting

2020 ◽  
Vol 308 ◽  
pp. 33-50
Author(s):  
Anna Woźniak ◽  
Marcin Adamiak
Keyword(s):  
Stainless Steel ◽  
Energy Density ◽  
Selective Laser Melting ◽  
Process Parameters ◽  
Defect Formation ◽  
Pure Titanium ◽  
Parameters Optimization ◽  
Laser Melting ◽  
Grade Ii ◽  
Titanium Grade

Selective Laser Melting SLM is one of the most popular three dimensional printing methods, which can be used for manufactured real elements (with high geometrical complexity) in many application, such as medicine, automotive or aerospace industries. The SLM final parts are characterized by high mechanical properties and satisfactory physicochemical properties. However, the properties of parts depend of process parameters optimization. In this paper, effects of processing parameters, such as laser power P, scanning speed SP, layer thickness t or point distance PD on defect formation and relative densities of manufactured elements are explored. For the purpose the stainless steel 316L and pure titanium Grade II are used. The process optimization were carried out according to the formula of energy density, which is delivered to the powder material. The stainless steel samples were divided into 12 groups, depends of the energy density. The titanium parts were printed at the same value of energy, and the process parameters are changed. The microscope observation and relative density measurements were carried out. Based on the obtained results, it can be confuted that the SLM parameters have a significant effect on the samples properties and the mechanism formed defect in both material are similar.

scholarly journals Microstructure and mechanical properties relationship of additively manufactured 316L stainless steel by selective laser melting

2019 ◽  
Vol 5 ◽  
pp. 23 ◽  
Author(s):  
Anne-Helene Puichaud ◽  
Camille Flament ◽  
Aziz Chniouel ◽  
Fernando Lomello ◽  
Elodie Rouesne ◽  
...  
Keyword(s):  
Mechanical Properties ◽  
Stainless Steel ◽  
Selective Laser Melting ◽  
316L Stainless Steel ◽  
Hot Isostatic Pressing ◽  
Tensile Tests ◽  
Industrial Applications ◽  
Added Value ◽  
Laser Melting ◽  
Microstructure And Mechanical Properties

Additive manufacturing (AM) is rapidly expanding in many industrial applications because of the versatile possibilities of fast and complex fabrication of added value products. This manufacturing process would significantly reduce manufacturing time and development cost for nuclear components. However, the process leads to materials with complex microstructures, and their structural stability for nuclear application is still uncertain. This study focuses on 316L stainless steel fabricated by selective laser melting (SLM) in the context of nuclear application, and compares with a cold-rolled solution annealed 316L sample. The effect of heat treatment (HT) and hot isostatic pressing (HIP) on the microstructure and mechanical properties is discussed. It was found that after HT, the material microstructure remains mostly unchanged, while the HIP treatment removes the materials porosity, and partially re-crystallises the microstructure. Finally, the tensile tests showed excellent results, satisfying RCC-MR code requirements for all AM materials.

Sign in / Sign up

Export Citation Format

Share Document