scholarly journals Stress Corrosion and Corrosion Fatigue of Biodegradable Mg-Zn-Nd-Y-Zr Alloy in In-Vitro Conditions

Metals ◽  
2020 ◽  
Vol 10 (6) ◽  
pp. 791
Author(s):  
Lilach Elkaiam ◽  
Orly Hakimi ◽  
Eli Aghion
Keyword(s):  
Mechanical Properties ◽  
Stress Corrosion ◽  
Corrosion Fatigue ◽  
Secondary Phases ◽  
Accelerated Corrosion ◽  
Premature Failure ◽  
Corrosion Susceptibility ◽  
T Phase ◽  
Zn Alloy

Mg alloys are attractive as a structural material for biodegradable implants due to their mechanical properties, biocompatibility and degradation capability in physiological environments. However, their accelerated corrosion degradation, coupled with their inherent sensitivity to stress corrosion, can cause premature failure and consequently loss of mechanical integrity. This study aims to evaluate the potential of a Mg-5% Zn alloy with up to 3% Nd as an implant material in terms of stress corrosion performance in in vitro conditions. Stress corrosion behavior was evaluated under static loading conditions using slow strain rate testing (SSRT) analysis and under low cycle corrosion fatigue (LCCF). Both the SSRT analysis and LCCF testing were carried out in a simulated physiological environment in the form of a phosphate-buffered saline (PBS) solution. The obtained results indicate that the addition of up to 3% Nd to Mg-5% Zn alloy did not have any substantial influence on the stress corrosion susceptibility, beyond the inherent different mechanical properties of the tested alloys. This was attributed to the limited effect of the Nd on the passivation layer and due to the fact that the secondary phases produced by the Nd additions—W-phase (Mg3(Nd,Y)2Zn3) and T-phase (Mg4(Nd,Y)Zn2)—did not create any substantial micro-galvanic effect.

scholarly journals Stress Corrosion Analysis and Direct Cell Viability of Biodegradable Zn-Fe-Ca Alloy in In-Vitro Conditions

Metals ◽  
2022 ◽  
Vol 12 (1) ◽  
pp. 76
Author(s):  
Orit Avior ◽  
Noa Ben Ghedalia-Peled ◽  
Tomer Ron ◽  
Jeremy Goldman ◽  
Razi Vago ◽  
...  
Keyword(s):  
Cell Viability ◽  
Stress Corrosion ◽  
Alloy Surface ◽  
Biodegradable Implants ◽  
Biodegradable Implant ◽  
Cyclic Potentiodynamic Polarization ◽  
Direct Cell ◽  
Phosphate Buffered Saline ◽  
Zn Alloy

Due to the excellent biocompatibility of Zn and Zn-based alloys, researchers have shown great interest in developing biodegradable implants based on zinc. Furthermore, zinc is an essential component of many enzymes and proteins. The human body requires ~15 mg of Zn per day, and there is minimal concern for systemic toxicity from a small zinc-based cardiovascular implant, such as an arterial stent. However, biodegradable Zn-based implants have been shown to provoke local fibrous encapsulation reactions that may isolate the implant from its surrounding environment and interfere with implant function. The development of biodegradable implants made from Zn-Fe-Ca alloy was designed to overcome the problem of fibrous encapsulation. In a previous study made by the authors, the Zn-Fe-Ca system demonstrated a suitable corrosion rate that was higher than that of pure Zn and Zn-Fe alloy. The Zn-Fe-Ca system also showed adequate mechanical properties and a unique microstructure that contained a secondary Ca-reach phase. This has raised the promise that the tested alloy could serve as a biodegradable implant metal. The present study was conducted to further evaluate this promising Zn alloy. Here, we assessed the material’s corrosion performance in terms of cyclic potentiodynamic polarization analysis and stress corrosion behavior in terms of slow strain rate testing (SSRT). We also assessed the ability of cells to survive on the alloy surface by direct cell culture test. The results indicate that the alloy develops pitting corrosion, but not stress corrosion under phosphate-buffered saline (PBS) and air environment. The direct cell viability test demonstrates the successful adherence and growth of cells on the alloy surface.

Cytocompatibility and Material Properties of Poly-carbonate Urethane/Carbon Nanofiber Composites for Neural Applications

2003 ◽  
Vol 774 ◽  
Author(s):  
Janice L. McKenzie ◽  
Michael C. Waid ◽  
Riyi Shi ◽  
Thomas J. Webster
Keyword(s):  
Mechanical Properties ◽  
Carbon Nanofibers ◽  
Material Properties ◽  
Carbon Nanofiber ◽  
Scar Tissue ◽  
Tissue Response ◽  
Positive Interactions ◽  
Weight Percentage ◽  
Poly Carbonate

AbstractCarbon nanofibers possess excellent conductivity properties, which may be beneficial in the design of more effective neural prostheses, however, limited evidence on their cytocompatibility properties exists. The objective of the present in vitro study was to determine cytocompatibility and material properties of formulations containing carbon nanofibers to predict the gliotic scar tissue response. Poly-carbonate urethane was combined with carbon nanofibers in varying weight percentages to provide a supportive matrix with beneficial bulk electrical and mechanical properties. The substrates were tested for mechanical properties and conductivity. Astrocytes (glial scar tissue-forming cells) were seeded onto the substrates for adhesion. Results provided the first evidence that astrocytes preferentially adhered to the composite material that contained the lowest weight percentage of carbon nanofibers. Positive interactions with neurons, and, at the same time, limited astrocyte functions leading to decreased gliotic scar tissue formation are essential for increased neuronal implant efficacy.

scholarly journals Anti-Inflammatory Properties of Injectable Betamethasone-Loaded Tyramine-Modified Gellan Gum/Silk Fibroin Hydrogels

Biomolecules ◽  
2020 ◽  
Vol 10 (10) ◽  
pp. 1456
Author(s):  
Isabel Matos Oliveira ◽  
Cristiana Gonçalves ◽  
Myeong Eun Shin ◽  
Sumi Lee ◽  
Rui Luis Reis ◽  
...  
Keyword(s):  
Rheumatoid Arthritis ◽  
Mechanical Properties ◽  
Silk Fibroin ◽  
Therapeutic Efficacy ◽  
Composite Structures ◽  
Gelation Time ◽  
Polymeric Materials ◽  
Gellan Gum ◽  
Traditional Use

Rheumatoid arthritis is a rheumatic disease for which a healing treatment does not presently exist. Silk fibroin has been extensively studied for use in drug delivery systems due to its uniqueness, versatility and strong clinical track record in medicine. However, in general, natural polymeric materials are not mechanically stable enough, and have high rates of biodegradation. Thus, synthetic materials such as gellan gum can be used to produce composite structures with biological signals to promote tissue-specific interactions while providing the desired mechanical properties. In this work, we aimed to produce hydrogels of tyramine-modified gellan gum with silk fibroin (Ty–GG/SF) via horseradish peroxidase (HRP), with encapsulated betamethasone, to improve the biocompatibility and mechanical properties, and further increase therapeutic efficacy to treat rheumatoid arthritis (RA). The Ty–GG/SF hydrogels presented a β-sheet secondary structure, with gelation time around 2–5 min, good resistance to enzymatic degradation, a suitable injectability profile, viscoelastic capacity with a significant solid component and a betamethasone-controlled release profile over time. In vitro studies showed that Ty–GG/SF hydrogels did not produce a deleterious effect on cellular metabolic activity, morphology or proliferation. Furthermore, Ty–GG/SF hydrogels with encapsulated betamethasone revealed greater therapeutic efficacy than the drug applied alone. Therefore, this strategy can provide an improvement in therapeutic efficacy when compared to the traditional use of drugs for the treatment of rheumatoid arthritis.

scholarly journals Mechanical Properties, Corrosion Resistance and Bioactivity of Oxide Layers Formed by Isothermal Oxidation of Ti-6Al-7Nb Alloy

Coatings ◽  
2021 ◽  
Vol 11 (5) ◽  
pp. 505
Author(s):  
Krzysztof Aniołek ◽  
Bożena Łosiewicz ◽  
Julian Kubisztal ◽  
Patrycja Osak ◽  
Agnieszka Stróż ◽  
...  
Keyword(s):  
Mechanical Properties ◽  
Corrosion Resistance ◽  
Contact Potential Difference ◽  
Isothermal Oxidation ◽  
Potential Method ◽  
Open Circuit ◽  
Kelvin Probe ◽  
Contact Potential ◽  
Oxide Layers

Titanium and its alloys are among the most promising biomaterials for medical applications. In this work, the isothermal oxidation of Ti-6Al-7Nb biomedical alloy towards improving its mechanical properties, corrosion resistance, and bioactivity has been developed. The oxide layers were formed at 600, 700, and 800 °C for 72 h. Scanning electron microscopy (SEM), energy dispersive spectroscopy (EDS), 3D profilometry, and microindentation test, were used to characterize microstructure, surface geometrical structure, and the hardness of the diphase (α + β) Ti-6Al-7Nb alloy after oxidation, respectively. In vitro corrosion resistance tests were carried out in a saline solution at 37 °C using the open-circuit potential method and potentiodynamic measurements. Electronic properties in the air were studied using the Scanning Kelvin Probe (SKP) technique. The bioactivity test was conducted by soaking the alkali- and heat-treated samples in simulated body fluid for 7 days. The presence of apatite was confirmed using SEM/EDS and Fourier Transform Infrared Spectroscopy (FTIR) studies. The thickness of oxide layers formed increased with the temperature growth from 0.25 to 5.48 µm. It was found that with increasing isothermal oxidation temperature, the surface roughness, hardness, corrosion resistance, and contact potential difference increased. The Ti-6Al-7Nb alloy after oxidation revealed the HAp-forming ability in a biological environment.

scholarly journals Development of Biopolymeric Hybrid Scaffold-Based on AAc/GO/nHAp/TiO2 Nanocomposite for Bone Tissue Engineering: In-Vitro Analysis

Nanomaterials ◽  
2021 ◽  
Vol 11 (5) ◽  
pp. 1319
Author(s):  
Muhammad Umar Aslam Khan ◽  
Wafa Shamsan Al-Arjan ◽  
Mona Saad Binkadem ◽  
Hassan Mehboob ◽  
Adnan Haider ◽  
...  
Keyword(s):  
Mechanical Properties ◽  
Tissue Engineering ◽  
Bone Tissue Engineering ◽  
Bone Tissue ◽  
Guar Gum ◽  
Porous Scaffolds ◽  
Vitro Assay ◽  
Vitro Analysis ◽  
Nanocomposite Scaffolds

Bone tissue engineering is an advanced field for treatment of fractured bones to restore/regulate biological functions. Biopolymeric/bioceramic-based hybrid nanocomposite scaffolds are potential biomaterials for bone tissue because of biodegradable and biocompatible characteristics. We report synthesis of nanocomposite based on acrylic acid (AAc)/guar gum (GG), nano-hydroxyapatite (HAp NPs), titanium nanoparticles (TiO2 NPs), and optimum graphene oxide (GO) amount via free radical polymerization method. Porous scaffolds were fabricated through freeze-drying technique and coated with silver sulphadiazine. Different techniques were used to investigate functional group, crystal structural properties, morphology/elemental properties, porosity, and mechanical properties of fabricated scaffolds. Results show that increasing amount of TiO2 in combination with optimized GO has improved physicochemical and microstructural properties, mechanical properties (compressive strength (2.96 to 13.31 MPa) and Young’s modulus (39.56 to 300.81 MPa)), and porous properties (pore size (256.11 to 107.42 μm) and porosity (79.97 to 44.32%)). After 150 min, silver sulfadiazine release was found to be ~94.1%. In vitro assay of scaffolds also exhibited promising results against mouse pre-osteoblast (MC3T3-E1) cell lines. Hence, these fabricated scaffolds would be potential biomaterials for bone tissue engineering in biomedical engineering.

Sign in / Sign up

Export Citation Format

Share Document