scholarly journals Fire Resistance of High-Volume Fly Ash RC Slab Inclusion with Nano-Silica

Materials ◽  
2021 ◽  
Vol 14 (12) ◽  
pp. 3311
Author(s):  
Mohamed H. Mussa ◽  
Noor Azim Mohd Radzi ◽  
Roszilah Hamid ◽  
Azrul A. Mutalib
Keyword(s):  
Thermal Conductivity ◽  
Compressive Strength ◽  
Fly Ash ◽  
Concrete Slab ◽  
High Volume ◽  
Concrete Cover ◽  
Nano Silica ◽  
Load Curve ◽  
High Volume Fly Ash ◽  
Rc Slab

The study aims to investigate the fire performance of reinforced concrete (RC) slab fabricated from high volume fly ash inclusion with nano-silica (HVFANS) under ISO 834 load curve. The HVFANS concrete slab with dimensions of 1850 mm × 1700 mm × 200 mm was tested via an electrical furnace under an exposing temperature of 1100 °C for 120 min. The slab behaviour was evaluated in terms of residual compressive strength, temperature distribution along its thickness, spalling, and cracks. The results revealed that the slab was capable of maintaining 62.19% of its original compressive strength at room temperature after exposure to the above temperature. Moreover, the distribution of temperature revealed that the temperature of concrete cover and bottom reinforcement was less than 300 °C with a maximum spalling depth of 11 mm within the temperature range of 680 to 840 °C. Furthermore, the thermal conductivity index (K) of the HVFANS concrete was determined, and results indicated that thermal conductivity equalled 0.35 W/mK which is considered low, as compared with other concretes tested in current and previous studies.

Research on the Foamed Concrete with High Volume Fly Ash

2017 ◽  
Vol 727 ◽  
pp. 1062-1066
Author(s):  
Hui Chao Chu ◽  
Xian Jun Lyu ◽  
Yan Zhang
Keyword(s):  
Thermal Conductivity ◽  
Compressive Strength ◽  
Fly Ash ◽  
Water Absorption ◽  
Process Parameters ◽  
High Volume ◽  
Dry Density ◽  
High Volume Fly Ash ◽  
Foamed Concrete

A study has been undertaken to investigate the effects, on the properties of foamed concrete, of replacing large volumes of cement with fly ash. This paper reports the results of the properties of foamed concrete and shows that up to 55% of the cement could be replaced without any significant reduction in compressive strength. Foamed concrete with 55% fly ash and good performance were obtained by optimizing the process parameters. The results showed that the compressive strength, dry density, water absorption and thermal conductivity of foamed concrete with 55% fly ash were 0.71MPa, 244kg/m3, 33%, and 0.045 W/mK respectively.

Effect of Nano Silica and Ultrafine Fly Ash on Compressive Strength of High Volume Fly Ash Mortar

2013 ◽  
Vol 368-370 ◽  
pp. 1061-1065 ◽  
Author(s):  
Steve W.M. Supit ◽  
Faiz U.A. Shaikh ◽  
Prabir K. Sarker
Keyword(s):  
Compressive Strength ◽  
Fly Ash ◽  
High Volume ◽  
Partial Replacement ◽  
Strength Development ◽  
Test Results ◽  
X Ray Diffraction ◽  
Nano Silica ◽  
High Volume Fly Ash ◽  
Class F Fly Ash

This paper evaluates the effect of Ultrafine Fly Ash (UFFA) and nanoSilica (NS) on compressive strength of high volume fly ash (HVFA) mortar at 7 days and 28 days. Three series of mortar mixes are considered in the first part of this study. In the first series the effect of high content of class F fly ash as partial replacement of cement at 40, 50 and 60% (by wt.) are considered. While in the second and third series, the UFFA and NS are used as partial replacement of cement at 5%, 8%, 10%, 12% and 15% and 1%, 2%, 4%, 6% and 8% (by wt.) of cement, respectively. The UFFA and the NS content which exhibited highest compressive strength in the above series are used in the second part where their effects on the compressive strength of HVFA mortars are evaluated. Results show that the mortar containing 10% UFFA as partial replacement of cement exhibited the highest compressive strength at both 7 and 28 days among all UFFA contents. Similarly, the mortar containing 2% NS as partial replacement of cement exhibited the best performance. Interestingly, the use of UFFA in HVFA mortars did not improve the compressive strength. However, the use of 2% and 4% NS showed improvement in the compressive strength of HVFA mortar containing 40% and 50% fly ash at both ages. The effects of NS and UFFA on the hydration and strength development of HVFA mortar is also evaluated through X-Ray Diffraction (XRD) test. Results also show that the UFFA and NS can significantly reduce the calcium hydroxide (CH) in HVFA mortars.

scholarly journals Late Age Dynamic Strength of High-Volume Fly Ash Concrete with Nano-Silica and Polypropylene Fibres

Crystals ◽  
2020 ◽  
Vol 10 (4) ◽  
pp. 243 ◽  
Author(s):  
Mohamed H. Mussa ◽  
Ahmed M. Abdulhadi ◽  
Imad Shakir Abbood ◽  
Azrul A. Mutalib ◽  
Zaher Mundher Yaseen
Keyword(s):  
Compressive Strength ◽  
Fly Ash ◽  
Elevated Temperatures ◽  
High Volume ◽  
Nano Silica ◽  
Polypropylene Fibres ◽  
Fly Ash Concrete ◽  
High Volume Fly Ash ◽  
Dynamic Compressive Strength ◽  
Curing Age

The dynamic behaviour of high-volume fly ash concrete with nano-silica (HVFANS) and polypropylene fibres at curing ages of 7 to 90 days was determined by using a split Hopkinson pressure bar (SHPB) machine. At each curing age, the concrete samples were laboratory tested at different temperatures conditions under strain rates reached up to 101.42 s−1. At room temperature, the results indicated that the dynamic compressive strength of plain concrete (PC) was slightly higher than HVFANS concrete at early curing ages of 7 and 28 days, however, a considerable improvement in the strength of HVFANS concrete was noted at a curing age of 90 days and recorded greater values than PC owing to the increase of fly ash reactivity. At elevated temperatures, the HVFANS concrete revealed a superior behaviour than PC even at early ages in terms of dynamic compressive strength, critical strain, damage and toughness due to increase of nano-silica (NS) activity during the heating process. Furthermore, equations were suggested to estimate the dynamic increase factor (DIF) of both concretes under the investigated factors.

scholarly journals Influence of Particle Size Distribution of High Calcium Fly Ash on HVFA Mortar Properties

2018 ◽  
Vol 20 (2) ◽  
pp. 51
Author(s):  
Antoni . ◽  
Hendra Surya Wibawa ◽  
Djwantoro Hardjito
Keyword(s):  
Particle Size ◽  
Compressive Strength ◽  
Fly Ash ◽  
Particle Size Distribution ◽  
Size Distribution ◽  
Setting Time ◽  
High Volume ◽  
High Volume Fly Ash ◽  
High Calcium ◽  
High Calcium Fly Ash

This study evaluates the effect of particle size distribution (PSD) of high calcium fly ash on high volume fly ash (HVFA) mortar characteristics. Four PSD variations of high calcium fly ash used were: unclassified fly ash and fly ash passing sieve No. 200, No. 325 and No. 400, respectively. The fly ash replacement ratio of the cementitious material ranged between 50-70%. The results show that with smaller fly ash particles size and higher levels of fly ash replacement, the workability of the mixture was increased with longer setting time. There was an increase in mortar compressive strength with finer fly ash particle size, compared to those with unclassified ones, with the highest strength was found at those with fly ash passing mesh No. 325. The increase was found due to better compactability of the mixture. Higher fly ash replacement reduced the mortar’s compressive strength, however, the rate was reduced when finer fly ash particles was used.

High Volume Slag and Slag-Fly Ash Blended Cement Pastes Containing Nano Silica

2019 ◽  
Vol 967 ◽  
pp. 205-213
Author(s):  
Faiz U.A. Shaikh ◽  
Anwar Hosan
Keyword(s):  
Compressive Strength ◽  
Fly Ash ◽  
Cement Paste ◽  
Ordinary Portland Cement ◽  
Blended Cement ◽  
High Volume ◽  
Ash Content ◽  
Partial Replacement ◽  
Nano Silica ◽  
Cement Pastes

This paper presents the effect of nanosilica (NS) on compressive strength and microstructure of cement paste containing high volume slag and high volume slag-fly ash blend as partial replacement of ordinary Portland cement (OPC). Results show that high volume slag (HVS) cement paste containing 60% slag exhibited about 4% higher compressive strength than control cement paste, while the HVS cement paste containing 70% slag maintained the similar compressive strength to control cement paste. However, about 9% and 37% reduction in compressive strength in HVS cement pastes is observed due to use of 80% and 90% slag, respectively. The high volume slag-fly ash (HVSFA) cement pastes containing total slag and fly ash content of 60% exhibited about 5%-16% higher compressive strength than control cement paste. However, significant reduction in compressive strength is observed in higher slag-fly ash blends with increasing in fly ash contents. Results also show that the addition of 1-4% NS improves the compressive strength of HVS cement paste containing 70% slag by about 9-24%. However, at higher slag contents of 80% and 90% this improvement is even higher e.g. 11-29% and 17-41%, respectively. The NS addition also improves the compressive strength by about 1-59% and 5-21% in high volume slag-fly ash cement pastes containing 21% fly ash+49%slag and 24% fly ash+56%slag, respectively. The thermogravimetric analysis (TGA) results confirm the reduction of calcium hydroxide (CH) in HVS/HVSFA pastes containing NS indicating the formation of additional calcium silicate hydrate (CSH) gels in the system. By combining slag, fly ash and NS in high volumes e.g. 70-80%, the carbon footprint of cement paste is reduced by 66-76% while maintains the similar compressive strength of control cement paste. Keywords: high volume slag, nanosilica, compressive strength, TGA, high volume slag-fly ash blend, CO2 emission.