scholarly journals Mechanical Properties and Uniaxial Compression Stress—Strain Relation of Recycled Coarse Aggregate Concrete after Carbonation

Materials ◽  
2021 ◽  
Vol 14 (9) ◽  
pp. 2215
Author(s):  
Tian-Wen Chen ◽  
Jin Wu ◽  
Guo-Qing Dong
Keyword(s):  
Elastic Modulus ◽  
Coarse Aggregate ◽  
Concrete Structures ◽  
Peak Stress ◽  
Peak Strain ◽  
Stress Strain ◽  
Carbonation Depth ◽  
Aggregate Concrete ◽  
Recycled Coarse Aggregate ◽  
Stress Strain Relation

The application of recycled coarse aggregate (RCA) made from waste concrete to replace natural coarse aggregate (NCA) in concrete structures can essentially reduce the excessive consumption of natural resources and environmental pollution. Similar to normal concrete structures, recycled concrete structures would also suffer from the damage of carbonation, which leads to the deterioration of durability and the reduction of service life. This paper presents the experimental results of the cubic compressive strength, the static elastic modulus and the stress–strain relation of recycled coarse aggregate concrete (RAC) after carbonation. The results show that the cubic compressive strength and the static elastic modulus of carbonated RAC gradually increased with the carbonation depth. The uncarbonated and fully carbonated RAC show smaller static elastic modulus than natural aggregate concrete (NAC). As the carbonation depth increased, the peak stress increased, while the peak strain decreased and the descending part of the curves gradually became steeper. As the content of RCA became larger, the peak stress decreased, while the peak strain increased and the descending part of the curves gradually became steeper. An equation for stress–strain curves of RAC after carbonation was proposed, and it was in good agreement with the test results.

Experimental Research on Mechanical Properties of Recycled Aggregate Concrete under Uniaxial Loading

2013 ◽  
Vol 671-674 ◽  
pp. 1736-1740
Author(s):  
Xue Yong Zhao ◽  
Mei Ling Duan
Keyword(s):  
Elastic Modulus ◽  
Coarse Aggregate ◽  
Strain Curve ◽  
Recycled Concrete ◽  
Recycled Aggregate Concrete ◽  
Recycled Aggregate ◽  
Peak Strain ◽  
Stress Strain ◽  
Aggregate Concrete ◽  
Recycled Coarse Aggregate

The complete stress-strain curves of recycled aggregate concrete with different recycled coarse aggregate replacement percentages were tested and investigated. An analysis was made of the influence of varying recycled coarse aggregate contents on the complete stress-strain curve, peak stress, peak strain and elastic modulus etc. The elastic modulus of RC is lower than natural concrete (NC), and with the recycled coarse aggregate contents increase, it reduces. While with the increase of water-cement ratio (W/C), recycled concrete compressive strength and elastic modulus improve significantly. In addition, put forward a new equation on the relationship between Ec and fcu of the RC.

scholarly journals Axial Stress-Strain Performance of Recycled Aggregate Concrete Reinforced with Macro-Polypropylene Fibres

2021 ◽  
Vol 13 (10) ◽  
pp. 5741
Author(s):  
Muhammad Junaid Munir ◽  
Syed Minhaj Saleem Kazmi ◽  
Yu-Fei Wu ◽  
Xiaoshan Lin ◽  
Muhammad Riaz Ahmad
Keyword(s):  
Axial Stress ◽  
Peak Stress ◽  
Polypropylene Fibre ◽  
Recycled Aggregate Concrete ◽  
Recycled Aggregate ◽  
Recycled Aggregates ◽  
Peak Strain ◽  
Stress Strain ◽  
Polypropylene Fibres ◽  
Aggregate Concrete

The addition of macro-polypropylene fibres improves the stress-strain performance of natural aggregate concrete (NAC). However, limited studies focus on the stress-strain performance of macro-polypropylene fibre-reinforced recycled aggregate concrete (RAC). Considering the variability of coarse recycled aggregates (CRA), more studies are needed to investigate the stress-strain performance of macro-polypropylene fibre-reinforced RAC. In this study, a new type of 48 mm long BarChip macro-polypropylene fibre with a continuously embossed surface texture is used to produce BarChip fibre-reinforced NAC (BFNAC) and RAC (BFRAC). The stress-strain performance of BFNAC and BFRAC is studied for varying dosages of BarChip fibres. Results show that the increase in energy dissipation capacity (i.e., area under the curve), peak stress, and peak strain of samples is observed with an increase in fibre dosage, indicating the positive effect of fibre addition on the stress-strain performance of concrete. The strength enhancement due to the addition of fibres is higher for BFRAC samples than BFNAC samples. The reduction in peak stress, ultimate strain, toughness and specific toughness of concrete samples due to the utilisation of CRA also reduces with the addition of fibres. Hence, the negative effect of CRA on the properties of concrete samples can be minimised by adding BarChip macro-polypropylene fibres. The applicability of the stress-strain model previously developed for macro-synthetic and steel fibre-reinforced NAC and RAC to BFNAC and BFRAC is also examined.

scholarly journals Carbonization Durability of Two Generations of Recycled Coarse Aggregate Concrete with Effect of Chloride Ion Corrosion

2020 ◽  
Vol 12 (24) ◽  
pp. 10544
Author(s):  
Chunhong Chen ◽  
Ronggui Liu ◽  
Pinghua Zhu ◽  
Hui Liu ◽  
Xinjie Wang
Keyword(s):  
Compressive Strength ◽  
Coarse Aggregate ◽  
Chloride Ion ◽  
Total Porosity ◽  
Recycled Concrete ◽  
Carbonation Depth ◽  
Aggregate Concrete ◽  
Recycled Coarse Aggregate ◽  
Carbonation Resistance ◽  
Two Generations

Carbonation durability is an important subject for recycled coarse aggregate concrete (RAC) applied to structural concrete. Extensive studies were carried out on the carbonation resistance of RAC under general environmental conditions, but limited researches investigated carbonation resistance when exposed to chloride ion corrosion, which is an essential aspect for reinforced concrete materials to be adopted in real-world applications. This paper presents a study on the carbonation durability of two generations of 100% RAC with the effect of chloride ion corrosion. The quality evolution of recycled concrete coarse aggregate (RCA) with the increasing recycling cycles was analyzed, and carbonation depth, compressive strength and the porosity of RAC were measured before and after chloride ion corrosion. The results show that the effect of chloride ion corrosion negatively affected the carbonation resistance of RAC, and the negative effect was more severe with the increasing recycling cycles of RCA. Chloride ion corrosion led to a decrease in compressive strength, while an increase in carbonation depth and the porosity of RAC. The equation of concrete total porosity and carbonation depth was established, which could effectively judge the deterioration of carbonation resistance of RAC.

Experimental Study on Stress-Strain Curve of Recycled Coarse Aggregate Concrete under Uniaxial Compression

2013 ◽  
Vol 357-360 ◽  
pp. 1415-1419 ◽  
Author(s):  
Zhi Heng Deng ◽  
Li Chen ◽  
Jian Qian ◽  
Chao Lou Meng
Keyword(s):  
Coarse Aggregate ◽  
Strain Curve ◽  
Recycled Concrete ◽  
Peak Strain ◽  
Stress Strain Curve ◽  
Stress Strain ◽  
Recycled Coarse Aggregate ◽  
Rational Expression ◽  
The Difference ◽  
Two Stages

In order to study the mechanical properties of recycled concrete with the same strength, three kinds of recycled concrete have been made which their intensities reached C25, C30, C35 at the recycled coarse aggregate replacement ratios (0%, 50%, 100%), and severally completed the stress-strain curve test on the same strength of recycled concrete, separately analyzed the variance about failure pattern and peak strain, elastic modulus that all belonged to recycled concrete under the condition of the same strength. Studies have shown that the overall shape of recycled concretes stress-strain curves is similar to normal concretes under the same strength, and the difference is small, modulus of elasticity decreases with the increase of recycled coarse aggregate replacement ratio, while the peak strain basicly remains unchanged. Their curves can be used two stages respectively and also be represented by three fitting polynomial and rational expression, their descent stages steepened gradually with the increase of recycled coarse aggregate replacement rate.