scholarly journals Influence of Cooking Oil on the Mitigation of Autogenous Shrinkage of Alkali-Activated Slag Concrete

Materials ◽  
2020 ◽  
Vol 13 (21) ◽  
pp. 4907
Author(s):  
Jinguang Huang ◽  
Jiachuan Yan ◽  
Kaihua Liu ◽  
Bin Wei ◽  
Chaoying Zou
Keyword(s):  
Surface Tension ◽  
Setting Time ◽  
Autogenous Shrinkage ◽  
Carbonation Depth ◽  
Alkali Activated Slag ◽  
Cooking Oil ◽  
Carbonation Resistance ◽  
Activated Slag ◽  
Alkali Activated ◽  
Shrinkage Reducing Agent

This paper reports an investigation into the autogenous shrinkage, mechanical, and durability performances of alkali-activated slag concrete (AASC) with emulsified cooking oil (ECO). Properties of AASC including flowability, setting time, compressive strength, autogenous shrinkage, and carbonation depth are tested to clarify the effects of the ECO. Commercially available expansion agent (EA) and shrinkage reducing agent (SRA) are also applied on AASC to compare with ECO. Experimental results show that the utilization of ECO could significantly decrease the autogenous shrinkage of alkali-activated slag concrete owing to the reduction of surface tension and the denser internal structure. It also shows that cooking oil after emulsification could have better performances than that of plain cooking oil when applied on AASC. Setting time and carbonation resistance ability are also improved with the utilization of ECO. The application of ECO is considered a cheap and easy way to overcome the limitation of AASC.

scholarly journals Effect of Internal Curing by Super Absorbent Polymer on the Autogenous Shrinkage of Alkali-Activated Slag Mortars

Materials ◽  
2020 ◽  
Vol 13 (19) ◽  
pp. 4318
Author(s):  
Pengju Wang ◽  
Haiming Chen ◽  
Peiyuan Chen ◽  
Jin Pan ◽  
Yangchen Xu ◽  
...  
Keyword(s):  
Compressive Strength ◽  
Setting Time ◽  
Autogenous Shrinkage ◽  
Internal Curing ◽  
Engineering Properties ◽  
Super Absorbent Polymer ◽  
Alkali Activated Slag ◽  
Activated Slag ◽  
Absorbent Polymer ◽  
Alkali Activated

Alkali activated slag (AAS) mortar is becoming an increasingly popular green building material because of its excellent engineering properties and low CO2 emissions, promising to replace ordinary Portland cement (OPC) mortar. However, AAS’s high shrinkage and short setting time are the important reasons to limit its wide application in engineering. This paper was conducted to investigate the effect of internal curing(IC) by super absorbent polymer (SAP) on the autogenous shrinkage of AAS mortars. For this, an experimental study was carried out to evaluate the effect of SAP dosage on the setting time, autogenous shrinkage, compressive strength, microstructure, and pore structure. The SAP were incorporated at different dosage of 0, 0.05, 0.1, 0.2, 0.3, 0.4, and 0.5 percent by weight of slag. The workability, physical (porosity), mechanical, and shrinkage properties of the mortars were evaluated, and a complementary study on microstructure was made. The results indicated that the setting time increased with an increase of SAP dosage due to the additional activator released by SAP. Autogenous shrinkage decreased with an increase of SAP dosage, and was mitigated completely when the dosage of SAP ≥ 0.2% wt of slag. Although IC by means of SAP reduced the compressive strength, this reduction (23% at 56 days for 0.2% SAP) was acceptable given the important role that it played on mitigating autogenous shrinkage. In the research, the 0.2% SAP dosage was the optimal content. The results can provide data and basis for practical application of AAS mortar.

scholarly journals Internal Curing Effect of Pre-Soaked Zeolite Sand on the Performance of Alkali-Activated Slag

Materials ◽  
2021 ◽  
Vol 14 (4) ◽  
pp. 718
Author(s):  
Guang-Zhu Zhang ◽  
Han-Seung Lee ◽  
Xiao-Yong Wang ◽  
Yi Han
Keyword(s):  
Compressive Strength ◽  
Electrical Resistivity ◽  
Natural Zeolite ◽  
Setting Time ◽  
Autogenous Shrinkage ◽  
Internal Curing ◽  
Alkali Activated Slag ◽  
Activated Slag ◽  
Two Stages ◽  
Alkali Activated

This study clarifies the effects of pre-soaked zeolite sand as an internal curing material on the hydration, strength, autogenous shrinkage, and durability of alkali-activated slag (AAS) mortars. The liquid-to-binder ratio (L/b) of all of the AAS mortars was 0.55. Sodium hydroxide solution was used as an alkali activator and an internal curing liquid. Calcined zeolite and natural zeolite sand replaced the standard sand at 15% and 30%, respectively. The setting time, autogenous shrinkage, compressive strength, ultrasonic pulse velocity, and surface electrical resistivity were tested. The following conclusions were drawn: (1) The addition of zeolite significantly reduces the autogenous shrinkage of AAS mortar. Compared with the control group, 30% calcined zeolite reduced the autogenous shrinkage by 96.4%. Moreover, the autogenous shrinkage of the AAS mortars was noticed in two stages (a variable temperature stage and an ambient temperature stage), and the two stages split at one day of age. (2) The compressive strength of all of the specimens increased as the zeolite sand content increased, and the highest compressive strength was obtained for AAS combined with 30% natural zeolite sand. (3) Internal curing accelerated the formation of the second peak of heat flow and reduced the accumulated heat release. (4) Calcined zeolite sand delayed the setting time of the AAS mortars. (5) The addition of zeolite significantly reduced the surface electrical resistivity of the AAS mortars. In summary, zeolite sand is extremely useful as an internal curing agent to reduce autogenous shrinkage and to increase the compressive strength of AAS mortars.

scholarly journals Influence of Na2O Content and Ms (SiO2/Na2O) of Alkaline Activator on Workability and Setting of Alkali-Activated Slag Paste

Materials ◽  
2019 ◽  
Vol 12 (13) ◽  
pp. 2072 ◽  
Author(s):  
Sung Choi ◽  
Kwang-Myong Lee
Keyword(s):  
Setting Time ◽  
High Strength ◽  
Abrupt Decrease ◽  
Na2o Content ◽  
Alkali Activated Slag ◽  
Granulated Blast Furnace Slag ◽  
Type Composition ◽  
Activated Slag ◽  
Binary Alkaline ◽  
Alkali Activated

The performance of alkali-activated slag (AAS) paste using activators of strong alkali components is affected by the type, composition, and dosage of the alkaline activators. Promoting the reaction of ground granulated blast furnace slag (GGBFS) by alkaline activators can produce high-strength AAS concrete, but the workability might be drastically reduced. This study is aimed to experimentally investigate the heat release, workability, and setting time of AAS pastes and the compressive strength of AAS mortars considering the Na2O content and the ratio of Na2O to SiO2 (Ms) of binary alkaline activators blended with sodium hydroxide and sodium silicate. The test results indicated that the AAS mortars exhibited a high strength of 25 MPa at 24 h, even at ambient temperature, even though the pastes with an Na2O content of ≥6% and an Ms of ≥1.0 exhibited an abrupt decrease in flowability and rapid setting.

Experimental Study on Alkali-Activated Slag-Lithium Slag-Fly Ash Environmental Concrete

2011 ◽  
Vol 287-290 ◽  
pp. 1237-1240
Author(s):  
Lan Fang Zhang ◽  
Rui Yan Wang
Keyword(s):  
Experimental Study ◽  
Compressive Strength ◽  
Fly Ash ◽  
Setting Time ◽  
Alkali Activated Slag ◽  
Percent Increase ◽  
Compressive Strength Of Concrete ◽  
Activated Slag ◽  
Lithium Slag ◽  
Alkali Activated

The aim of this paper is to study the influence of lithium-slag and fly ash on the workability , setting time and compressive strength of alkali-activated slag concrete. The results indicate that lithium-slag and fly-ash can ameliorate the workability, setting time and improve the compressive strength of alkali-activated slag concrete，and when 40% or 60% slag was replaced by lithium-slag or fly-ash, above 10 percent increase in 28-day compressive strength of concrete were obtained.

scholarly journals Mitigating the Drying Shrinkage and Autogenous Shrinkage of Alkali-Activated Slag by NaAlO2

Materials ◽  
2020 ◽  
Vol 13 (16) ◽  
pp. 3499
Author(s):  
Bin Chen ◽  
Jun Wang ◽  
Jinyou Zhao
Keyword(s):  
Autogenous Shrinkage ◽  
Drying Shrinkage ◽  
Nitrogen Adsorption ◽  
Partial Substitution ◽  
Hydration Reaction ◽  
X Ray Diffraction ◽  
Na2o Content ◽  
Alkali Activated Slag ◽  
Activated Slag ◽  
Alkali Activated

The shrinkage of alkali-activated slag (AAS) is obviously higher than ordinary Portland cement, which limited its application in engineering. In this study, the effects of NaAlO2 in mitigating drying shrinkage and autogenous shrinkage of AAS were studied. To further understand the shrinkage mechanism, the hydration products and microstructures were studied by X-ray diffraction, scanning electron microscopy and nitrogen adsorption approaches. As the partial substitution rate of NaAlO2 for Na2SiO3 increased, the drying shrinkage and autogenous shrinkage reduced significantly. The addition of NaAlO2 could slow down the rate of hydration reaction and reduce the porosity, change the pore diameter and the composition of generated paste and cause more hydrotalcite and tetranatrolite generated—which contributed to reduced shrinkage. Additionally, raising the Na2O content rate caused obvious differences in drying shrinkage and autogenous shrinkage. As the Na2O content elevated, the drying shrinkage decreased and autogenous shrinkage increased. A high Na2O content would cause complete hydration reactions and provoke high autogenous shrinkage. However, incomplete hydration reactions left more water in the paste, and the evaporated water dramatically influenced drying shrinkage. The results indicate that addition of NaAlO2 could greatly mitigate the drying shrinkage and autogenous shrinkage of AAS.

scholarly journals Evaluation of the surfactant leaching from alkali-activated slag-based composites using surface-tension measurements

2019 ◽  
Vol 53 (1) ◽  
pp. 33-38
Author(s):  
V. Bílek Jr. ◽  
L. Kalina ◽  
E. Bartoníčková ◽  
J. Pořízka
Keyword(s):  
Surface Tension ◽  
Alkali Activated Slag ◽  
Activated Slag ◽  
Alkali Activated
Sign in / Sign up

Export Citation Format

Share Document