scholarly journals On the Anti-Corrosion Property of Dry-Gel-Conversion-Grown MFI Zeolite Coating on Aluminum Alloy

Materials ◽  
2020 ◽  
Vol 13 (20) ◽  
pp. 4595
Author(s):  
Shang-Tien Tsai ◽  
Wen-Chyuan ChangJean ◽  
Lin-Yi Huang ◽  
Tseng-Chang Tsai
Keyword(s):  
Fumed Silica ◽  
Thick Layer ◽  
Surface Hydrophobicity ◽  
Corrosion Property ◽  
Mfi Zeolite ◽  
Dry Gel Conversion ◽  
Zeolite Film ◽  
Protection Property ◽  
Strong Barrier ◽  
Zeolite Coating

MFI zeolite film coated on AA6061 alloy was prepared from fumed silica modified with/without n-octyldecyltrimethoxysilane (ODS) by means of dry gel conversion (DGC) method. The DGC-grown MFI zeolite film could form a strong barrier to protect AA6061 surface against the corrosion from NaCl solution. By using fumed silica as a starting material, the hydrophilicity and anti-corrosion capability of the MFI zeolite film declined with increasing humidity in the DGC synthesis. By silanization with ODS, the surface hydrophobicity of the MFI zeolite film increased, leading to substantial enhancement in anti-corrosion capability. On the other hand, MFI film grown from ODS-modified fumed silica exhibited low hydrophilicity and a much improved anti-corrosion protection property by four orders of magnitude, even stronger than the ODS post-treated MFI film. The strong anti-corrosion capability is attributed to the “thick layer” surface hydrophobicity of zeolite crystal.

scholarly journals Whole pH range anti-corrosion property of aluminium alloy coated with MFI zeolite film

2018 ◽  
Vol 53 (sup1) ◽  
pp. 34-38 ◽  
Author(s):  
Shang-Tien Tsai ◽  
Wen-Chyuan ChangJean ◽  
Pei-Hsiun Chao ◽  
Shang-Yuan Fu ◽  
Tseng-Chang Tsai
Keyword(s):  
Aluminium Alloy ◽  
Corrosion Property ◽  
Mfi Zeolite ◽  
Zeolite Film ◽  
Ph Range

TPA+-Mediated Conversion of Silicon Wafer into Preferentially-Oriented MFI Zeolite Film under Steaming

2007 ◽  
Vol 19 (17) ◽  
pp. 4120-4122 ◽  
Author(s):  
Watcharop Chaikittisilp ◽  
Mark E. Davis ◽  
Tatsuya Okubo
Keyword(s):  
Silicon Wafer ◽  
Mfi Zeolite ◽  
Zeolite Film

Corrosion Property Analysis of Coating Formulated Using Acrylic Polyol and Silicone Resin Hybrid Systems

2013 ◽  
Vol 746 ◽  
pp. 363-368
Author(s):  
S.K.M. Jamaria ◽  
K. Rameshb ◽  
B. Vengadaesvaranc ◽  
S. Rameshd ◽  
S.R. Raue ◽  
...  
Keyword(s):  
Differential Scanning Calorimetry ◽  
Corrosion Resistance ◽  
Electrochemical Impedance ◽  
Corrosion Property ◽  
Cross Linking ◽  
Silicone Resin ◽  
Scanning Calorimetry ◽  
Maximum Value ◽  
Infra Red ◽  
Protection Property

Coating systems consist of acrylic polyol resin and silicone intermediate resins were tested for their corrosion resistance properties. The corrosion protection property of the coating was evaluated by using Electrochemical Impedance Spectroscopy (EIS) which showed that system with 70 % of acrylic has the highest corrosion resistance. The maximum value of corrosion resistance obtained was found to be 1.40 x 109Ω on the 30thday for the 70 % of acrylic sample. The glass transition temperature (Tg) obtained using the Differential Scanning Calorimetry (DSC) were in the range of 23 °C to 65 °C. It showed that all samples are suitable for decorative paints, general industrial coatings and floor care coatings. The functional groups and also the cross-linking between the organic resins were analyzed using Fourier Transform Infra-Red Spectroscopy.

Synthesis of mesoporous MFI zeolite by dry gel conversion with ZnO particles and the catalytic activity on TMB cracking

2015 ◽  
Vol 23 (2) ◽  
pp. 311-316 ◽  
Author(s):  
Koji Miyake ◽  
Mayuka Yamada ◽  
Yusuke Sugiura ◽  
Yuichiro Hirota ◽  
Yoshiaki Uchida ◽  
...  
Keyword(s):  
Catalytic Activity ◽  
Mfi Zeolite ◽  
Dry Gel Conversion ◽  
Zno Particles

Growth of MFI zeolite film as corrosion protection layer of aluminum alloy

2015 ◽  
Vol 217 ◽  
pp. 71-80 ◽  
Author(s):  
Lin-Yi Huang ◽  
Yuan-Chung Hao ◽  
WenChyuan ChangJean ◽  
Mei-Jhu Wang ◽  
Anthony S.T. Chiang ◽  
...  
Keyword(s):  
Aluminum Alloy ◽  
Corrosion Protection ◽  
Mfi Zeolite ◽  
Zeolite Film ◽  
Protection Layer

scholarly journals MFI zeolite coating with intrazeolitic aluminum (acidic) gradient supported on SiC foams to improve the methanol-to-propylene (MTP) reaction

2018 ◽  
Vol 559 ◽  
pp. 1-9 ◽  
Author(s):  
Yilai Jiao ◽  
Shaojun Xu ◽  
Chunhai Jiang ◽  
Michal Perdjon ◽  
Xiaolei Fan ◽  
...  
Keyword(s):  
Mfi Zeolite ◽  
Zeolite Coating

Thermal processing of zeolite seed layers for the fabrication of compact oriented MFI zeolite films

CrystEngComm ◽  
2018 ◽  
Vol 20 (32) ◽  
pp. 4531-4535 ◽  
Author(s):  
Yong Peng ◽  
Ruilan Xu ◽  
Xinde Jiang ◽  
Sheng Xu ◽  
Zhengbao Wang
Keyword(s):  
Thermal Processing ◽  
Seed Layer ◽  
Mfi Zeolite ◽  
Covalent Linkage ◽  
Zeolite Film ◽  
Zeolite Films ◽  
Seed Layers

The formation of a close-packed oriented MFI zeolite film through thermal processing created a strong covalent linkage between the seed layer and the substrate.

scholarly journals Dynamic Hydrothermal Synthesis of a b-Oriented MFI Zeolite Film

2011 ◽  
Vol 32 (1-2) ◽  
pp. 217-223 ◽  
Author(s):  
Xianming LI ◽  
Zhengbao WANG ◽  
Jie ZHENG ◽  
Shiqun SHAO ◽  
Yinchao WANG ◽  
...  
Keyword(s):  
Hydrothermal Synthesis ◽  
Mfi Zeolite ◽  
Zeolite Film
Sign in / Sign up

Export Citation Format

Share Document