scholarly journals Structure and Properties of High-Strength Ti Grade 4 Prepared by Severe Plastic Deformation and Subsequent Heat Treatment

Materials ◽  
2020 ◽  
Vol 13 (5) ◽  
pp. 1116
Author(s):  
Alena Michalcová ◽  
Dalibor Vojtěch ◽  
Jaroslav Vavřík ◽  
Kristína Bartha ◽  
Přemysl Beran ◽  
...  
Keyword(s):  
Mechanical Properties ◽  
Heat Treatment ◽  
Plastic Deformation ◽  
Severe Plastic Deformation ◽  
High Strength ◽  
Ultimate Tensile Stress ◽  
Internal Stresses ◽  
In Situ Xrd ◽  
Microstructure Observation

Severe plastic deformation represented by three passes in Conform SPD and subsequent rotary swaging was applied on Ti grade 4. This process caused extreme strengthening of material, accompanied by reduction of ductility. Mechanical properties of such material were then tuned by a suitable heat treatment. Measurements of in situ electrical resistance, in situ XRD and hardness indicated the appropriate temperature to be 450 °C for the heat treatment required to obtain desired mechanical properties. The optimal duration of annealing was stated to be 3 h. As was verified by neutron diffraction, SEM and TEM microstructure observation, the material underwent recrystallization during this heat treatment. That was documented by changes of the grain shape and evaluation of crystallite size, as well as of the reduction of internal stresses. In annealed state, the yield stress and ultimate tensile stress decreased form 1205 to 871 MPa and 1224 to 950 MPa, respectively, while the ductility increased from 7.8% to 25.1%. This study also shows that mechanical properties of Ti grade 4 processed by continual industrially applicable process (Conform SPD) are comparable with those obtained by ECAP.

The Influence of Severe Plastic Deformation Process on Structure and Properties of AZ 31 Alloy after Selected Heat Treatment

2018 ◽  
Vol 275 ◽  
pp. 134-146
Author(s):  
Stanislav Rusz ◽  
Ondřej Hilšer ◽  
Stanislav Tylšar ◽  
Lubomír Čížek ◽  
Tomasz Tański ◽  
...  
Keyword(s):  
Mechanical Properties ◽  
Heat Treatment ◽  
Plastic Deformation ◽  
Severe Plastic Deformation ◽  
Structure Refinement ◽  
Hardness Measurement ◽  
Az31 Alloy ◽  
Strength Properties ◽  
Aviation Industry ◽  
Initial State

The technology of structure refinement in materials with the aim of achieving substantial mechanical properties and maintaining the required plasticity level is becoming increasingly useful in industrial practice. Magnesium alloys are very progressive materials for utilization in practice thanks to their high strength-to-weight ratios (tensile strength/density). The presented paper analyses the effect of the input heat treatment of the AZ31 alloy on the change of structure and strength properties through the process of severe plastic deformation (SPD), which finds an increasing utilization, especially in the automotive and aviation industry. For the study of the influence of the SPD process (ECAP method) on the properties of the AZ31 alloy, two types of thermal treatment of the initial state of the structure were selected. The analysis of the structure of the AZ31 alloy was performed in the initial state without heat treatment and subsequently after heat treatment. In the next part, the influence of the number of passes on the strengthening curves was evaluated. Mechanical properties of the AZ31 alloy after ECAP were evaluated by hardness measurement and completed by structure analysis.

Characterization of Microstructure and Mechanical Properties of 6060 Aluminum Alloy Processed by ECAP

2018 ◽  
Vol 275 ◽  
pp. 81-88
Author(s):  
Monika Karoń ◽  
Marcin Adamiak
Keyword(s):  
Mechanical Properties ◽  
Heat Treatment ◽  
Plastic Deformation ◽  
Aluminum Alloy ◽  
Internal Stresses ◽  
Refined Grains ◽  
Angular Pressing ◽  
Heat Treated ◽  
Evolution Of Microstructure

The purpose of this paper is to present the microstructure and mechanical behavior of 6060 aluminum alloy after intense plastic deformation. Equal Channel Angular Pressing (ECAP) was used as a method of severe plastic deformation. Before ECAP part of the samples were heat treated to remove internal stresses in the commercially available aluminium alloy. The evolution of microstructure and tensile strength were tested after 1, 3, 6 and 9 ECAP passes in annealed and non annealed states. It was found that intensely plastically deformed refined grains were present in the tested samples and exhibited increased mechanical properties. Differences were noted between samples without and after heat treatment

scholarly journals Microstructure and Mechanical Properties of High Vacuum Die-Cast AlSiMgMn Alloys at as-Cast and T6-Treated Conditions

Materials ◽  
2019 ◽  
Vol 12 (13) ◽  
pp. 2065
Author(s):  
Fei Liu ◽  
Haidong Zhao ◽  
Runsheng Yang ◽  
Fengzhen Sun
Keyword(s):  
Mechanical Properties ◽  
Heat Treatment ◽  
Failure Modes ◽  
High Vacuum ◽  
High Strength ◽  
Thin Wall ◽  
T6 Heat Treatment ◽  
Die Cast ◽  
Strength And Ductility

Al–Si–Mg based alloys can provide high strength and ductility to satisfy the increasing demands of thin wall castings for automotive applications. This study has investigated the effects of T6 heat-treatment on the microstructures, the local mechanical properties of alloy phases and the fracture behavior of high vacuum die-cast AlSiMgMn alloys using in-situ scanning electron microscopy (SEM) in combination with nano-indentation testing. The microstructures of the alloys at as-cast and T6 treated conditions were compared and analyzed. It is found that the T6 heat treatment plays different roles in affecting the hardness and the Young’s modulus of alloy phases. This study also found that the T6 heat treatment would influence the failure modes of the alloys. The mechanisms of crack propagation in the as-cast and T6 treated alloys were also analyzed and discussed.

Influence of Severe Plastic Deformation on Mechanical Properties of an AA5024 Alloy

2016 ◽  
Vol 879 ◽  
pp. 1317-1322 ◽  
Author(s):  
Anna Mogucheva ◽  
Diana Yuzbekova ◽  
Tatiana Lebedkina ◽  
Mikhail Lebyodkin ◽  
Rustam Kaibyshev
Keyword(s):  
Mechanical Properties ◽  
Plastic Deformation ◽  
Severe Plastic Deformation ◽  
High Strength ◽  
Coarse Grained ◽  
Type B ◽  
Angular Pressing ◽  
Ultrafine Grained ◽  
Elongation To Failure ◽  
Dislocation Strengthening

The paper reports on the effect of severe plastic deformation on mechanical properties of an Al-4.57Mg-0.35Mn-0.2Sc-0.09Zr (in wt. pct.) alloy processed by equal channel angular pressing followed by cold rolling (CR). The sheets of the 5024 alloy with coarse grained (CG) structure exhibited a yield stress (YS) near 410 MPa and an ultimate tensile strength (UTS) of 480 MPa, while the YS and UTS of this material with ultrafine-grained (UFG) structure increased to 530 and 560 MPa, respectively. On the other hand, the elongation to failure decreased by a factor of 2 and 4 after CR and CR following ECAP, respectively. It was shown that dislocation strengthening attributed to extensive CR plays a major role in achieving high strength of this alloy. Besides these macroscopic characteristics, jerky flow caused by the Portevin-Le Chatelier (PLC) instability of plastic deformation was examined. The formation of UFG structure results in a transition from mixed type A+B to pure type B PLC serrations. No such effect on the serrations type was observed after CR.

Equal Channel Angular Pressing of Al Alloy AA2219

2009 ◽  
Vol 67 ◽  
pp. 53-58
Author(s):  
V. Anil Kumar ◽  
M.K. Karthikeyan ◽  
Rohit Kumar Gupta ◽  
P. Ramkumar ◽  
P.P. Sinha
Keyword(s):  
Mechanical Properties ◽  
Plastic Deformation ◽  
Severe Plastic Deformation ◽  
Grain Refinement ◽  
Equal Channel Angular Pressing ◽  
High Strength ◽  
Dark Field ◽  
Grain Structure ◽  
Al Alloy ◽  
Angular Pressing

Severe plastic deformation processes (SPD) are gaining importance as advanced materials processing techniques and hold immense potential in obtaining ultra fine-grained high strength materials. Among the SPD techniques, Equal channel angular pressing (ECAP) has its own merits to produce materials with ultra fine grains in bulk with better mechanical properties. The material deforms with high level of plastic strain inside the channel resulting in grain refinement of the output material with improvement in mechanical properties. A very viable die configuration was conceptualized and die was made with 1200 channel angle. Processing of 25 mm dia. of Al alloy AA2219 at room temperature was successfully carried out and grain refinement was observed. The mechanism of grain refinement has been studied using optical and transmission electron microscopy (TEM). It was observed that low energy dislocation structure (LEDS) forms concurrently with sub-grain structure due to dislocation rearrangements, which provide stability to the evolving sub-grain structure. Dislocation mobility is hindered by the presence of precipitates and / or intermetallic dispersoids present in the matrix and results in presence of dislocations in grain interiors. The pile up of dislocations at intermetallic dispersoids was confirmed from the dark field TEM micrographs. Present paper describes the experimental procedure and followed to attain severe plastic deformation through ECAP. Increase in hardness as well as refinement in the grain size after 5-passes have been discussed in light of extensive optical and TEM. The mechanisms of grain refinement to achieve nano-grained structure and strengthening accrued from the grain refinement through ECAP has been discussed.

Improvement of mechanical properties of a nanoaluminium alloy by precipitate strengthening

2012 ◽  
Vol 57 (3) ◽  
pp. 877-881 ◽  
Author(s):  
K. Wawer ◽  
M. Lewandowska ◽  
K.J. Kurzydłowski
Keyword(s):  
Mechanical Properties ◽  
Heat Treatment ◽  
Plastic Deformation ◽  
Grain Size ◽  
Severe Plastic Deformation ◽  
Grain Refinement ◽  
Precipitation Strengthening ◽  
Post Processing ◽  
Heat Treated ◽  
Precipitate Strengthening

In the present study, severe plastic deformation (SPD) processing was combined with pre- and post processing heat treatment to investigate the possibility of synergic grain size and precipitation strengthening. Samples of 7475 alloy were solution heat treated and water quenched prior to hydrostatic extrusion (HE) which resulted in a grain refinement by 3 orders of magnitude, from 70 μm to about 70 nm. The extruded samples were subsequently aged at temperatures resulting in formation of nanoprecipitates.

Experimental study of the simultaneous effects of severe plastic deformation and secondary radial strain on copper

2021 ◽  
pp. 095440892110244
Author(s):  
Seyyed Ehsan Eftekhari Shahri ◽  
Mohammad Amin Ranaei ◽  
Hossein Jamshidi ◽  
Elyas Rezaei
Keyword(s):  
Mechanical Properties ◽  
Electrical Conductivity ◽  
Plastic Deformation ◽  
Severe Plastic Deformation ◽  
Copper Wire ◽  
Pure Copper ◽  
Radial Strain ◽  
High Strength ◽  
Homogeneous Structure ◽  
Direct Extrusion

Due to the widespread use of copper wires in electrical power transmission, the need for raw materials with a homogeneous structure and high strength while maintaining their conductive properties is of high importance. The present study investigates the production of copper wire with improved mechanical properties and homogeneous microstructure due to its nanometre-sized structure. Therefore, the commercial pure copper specimens were subjected to severe plastic deformation (SPD) by means of equal channel angular pressing (ECAP) during four steps at ambient temperature. Due to the creation of a structure with elongated grains in the ECAP process, the deformed specimens were subjected to the direct extrusion operations; thus, a more homogeneous structure was created in them due to the appearance of a secondary radial strain. The obtained results indicate that by applying the simultaneous effects of SPD and direct extrusion on the microstructure, the mechanical properties such as strength and hardness have improved significantly, while the electrical conductivity of pure copper decreased slightly. The outcome can be used as an alternative to current methods for producing high-strength copper wires with suitable electrical conductivity properties.

Influence of Annealing on the Structure and Mechanical Properties of Ultrafine-Grained Alloy Ti-6Al-7Nb, Processed by Severe Plastic Deformation

2010 ◽  
Vol 667-669 ◽  
pp. 943-948 ◽  
Author(s):  
Veronika Polyakova ◽  
Irina P. Semenova ◽  
Ruslan Valiev
Keyword(s):  
Mechanical Properties ◽  
Plastic Deformation ◽  
Severe Plastic Deformation ◽  
Equal Channel Angular Pressing ◽  
Human Body ◽  
High Strength ◽  
Point Of View ◽  
Angular Pressing ◽  
Ultrafine Grained ◽  
Strength And Ductility

This work is devoted to enhancement of strength and ductility of the Ti-6Al-7Nb ELI alloy, which is less harmful from medical point of view for human body in comparison to Ti-6Al-4V. It has been demonstrated that formation of an ultrafine-grained structure in the alloy with the help of equal-channel angular pressing in combination with heat and deformation treatments allows reaching high strength (UTS = 1400 MPa) and sufficient ductility (elongation 10 %).