scholarly journals Dentin Bonding of TheraCal LC Calcium Silicate Containing an Acidic Monomer: An In Vitro Study

Materials ◽  
2020 ◽  
Vol 13 (2) ◽  
pp. 293 ◽  
Author(s):  
Kim ◽  
Hong ◽  
Kwon
Keyword(s):  
Mechanical Properties ◽  
Calcium Ions ◽  
Calcium Ion ◽  
Shear Bond Strength ◽  
In Vitro Study ◽  
The Other ◽  
Water Contact ◽  
Dentin Bonding ◽  
Pulp Capping

The purpose of this study was to evaluate whether the incorporation of an acidic monomer into the pulp-capping material TheraCal LC, which has a weak dentin bonding, increases the shear bond strength (SBS) to dentin. Di-2-hydroxyethyl methacryl hydrogenphosphate was incorporated into the material at 0.0 (TL0, control), 5.0 (TL5), and 10.0 (TL10) wt%. The water contact angle (CA) and mechanical properties for each material were also studied (n = 6). Debonding was performed at two different times (immediate and after 24 h) (n = 12). Hydroxyl and calcium ion releases in water at 37 °C were monitored up to 28 days (n = 6). The addition of the acidic monomer decreased the CAs (p < 0.001) and increased the flexural moduli (p < 0.001). The debonding time did not significantly affect the SBS values (p = 0.600). The TL10 group exhibited the highest SBS values, followed by the TL5 group. The TL10 group released significantly more calcium ions than the other two groups from 3 days (p < 0.05). The incorporation of the acidic monomer at 10.0 wt% into TheraCal LC enhanced bonding to dentin, while not negatively affecting the mechanical properties and ion-leaching capacity of the material.

scholarly journals Effect of Salivary Contamination on the Bond Strength of Total-etch and Self-etch Adhesive Systems: An in vitro Study

2012 ◽  
Vol 13 (5) ◽  
pp. 655-660 ◽  
Author(s):  
LM Ranganath ◽  
AG Rajesh ◽  
Robert M Justin ◽  
Hemalatha Paranthaman ◽  
Ranjith P Varghese
Keyword(s):  
Bond Strength ◽  
Shear Bond Strength ◽  
In Vitro Study ◽  
Single Bond ◽  
Adhesive Systems ◽  
Bonding Agents ◽  
Dentin Bonding ◽  
Etched Surface ◽  
Self Etch

ABSTRACT Aim To evaluate the influence of salivary contamination during dentin bonding procedures on shear bond strength and to investigate the effect of contaminant-removing treatments on the recovery of bond strength for two dentin-bonding agents. Materials and methods Seventy-seven human maxillary and mandibular molars were randomly divided into two groups for total-etch adhesive (Single bond-3M ESPE, USA) and self-etch primer (UniFil Bond-GC, Tokyo, Japan) and subjected to contamination with saliva. The data for each group were subjected to one-way analysis of variance (ANOVA) followed by the Student Newman-Keuls test to make comparisons among the groups (p < 0.05). Results Salivary contamination had less adverse effect on the shear bond strength of single bond total-etch adhesive when it was blot dried or washed. UniFil bond was tolerant of salivary contamination, except when contamination occurred after application of the primer. Conclusion In single bond adhesive, when the etched surface is contaminated by saliva, blotting the surface and applying the primer can recover the bond strength. Complete drying of the salivary contaminated surface should be avoided. In the UniFil bond groups, the repriming treatment (UF-V and UF-VI) resulted in the recovery of shear bond strength in the specimens contaminated after priming. Clinical significance The results of this study showed that total- etch adhesive (single bond) was not affected by salivary contamination on the etched surface when the bonding surface was kept moist. Self-etch adhesive (UniFil bond) also tolerated salivary contamination except when the contamination occurred after application of the primer. How to cite this article Justin RM, Paranthaman H, Rajesh AG, Varghese RP, Ranganath LM. Effect of Salivary Contamination on the Bond Strength of Total-etch and Selfetch Adhesive Systems: An in vitro Study. J Contemp Dent Pract 2012;13(5):655-660.

Shear bond strength of metal/ceramic Interface after different surface treatments: an in vitro study. Resistência ao cisalhamento da interface metal/cerâmica após diferentes tratamentos de superfície: estudo in vitro

2013 ◽  
Author(s):  
Sílvia Fontes Do Amaral Pereira
Keyword(s):  
Bond Strength ◽  
Shear Bond Strength ◽  
In Vitro Study ◽  
Surface Treatments ◽  
Vitro Study ◽  
Metal Ceramic

O objetivo do presente estudo in vitro foi verificar, através de teste de cisalhamento, a resistência de união da liga Wironia®light, à base de níquel-cromo sem berílio, sujeita a diferentes tratamentos de superfície, às cerâmicas Vita VM13 e Noritake. Foram confeccionados oitenta espécimes cilíndricos metálicos, com o auxílio de uma matriz de aço, nas dimensões de 4 mm de diâmetro por 4 mm de altura. Os espécimes foram divididos em oito grupos (n=10), de acordo com o tipo de tratamento superficial aplicado à liga metálica e com o tipo de cerâmica testada. Estes foram avaliados de acordo com os critérios de resistência ao cisalhamento e, com o auxílio de microscopia óptica, foi avaliada a área de cerâmica remanescente aderida ao metal após a fratura. Os corpos-de-prova do G6 (fabricados em Cerâmica Noritake com jateamento-26,401 ± 11,637 MPa) apresentaram maior resistência ao cisalhamento (p> 0,05) enquanto que os menores valores foram registrados no G4 (Cerâmica Vita com utilização de broca-13,440 ± 7,766 MPa). G6 (19425,4 μm2) apresentou a maior área de cerâmica aderida ao metal (p> 0,05) enquanto que o G4 (2310,2 μm2) apresentou a menor área. Concluiu-se que G6 obteve os valores mais altos de resistência ao cisalhamento e de remanescente cerâmico aderido à superfície metálica enquanto que o G4 obteve os valores mais baixos. Descritores: Restaurações metalo-cerâmicas; ligas de níquel-cromo;porcelana dentária.

scholarly journals Shear bond strength evaluation of bonded molar tubes on fluorotic molars

2012 ◽  
Vol 83 (1) ◽  
pp. 152-157 ◽  
Author(s):  
Erika L. Silva-Benítez ◽  
Veronica Zavala-Alonso ◽  
Gabriel A. Martinez-Castanon ◽  
Juan P. Loyola-Rodriguez ◽  
Nuria Patiño-Marin ◽  
...  
Keyword(s):  
Bond Strength ◽  
Shear Bond Strength ◽  
Dental Fluorosis ◽  
In Vitro Study ◽  
Mean Value ◽  
Fixed Appliance ◽  
Adhesive Remnant Index ◽  
The Mean ◽  
Electronic Microscope

Abstract Objective: To study the shear bond strength (SBS), sites of failure, and micromorphology of bonded molar tubes used on teeth affected by dental fluorosis. Materials and Methods: This in vitro study included 140 first molars classified according to Dean's index for dental fluorosis. Samples were divided into seven groups: (1) healthy teeth etched for 15 seconds, (2) teeth with moderate fluorosis (MOF) etched for 15 seconds, (3) teeth with MOF etched for 150 seconds, (4) teeth with MOF microabrasion etched for 15 seconds, (5) teeth with severe fluorosis (SEF) etched for 15 seconds, (6) teeth with SEF etched for 150 seconds, and (7) teeth with SEF microabrasion etched for 15 seconds. All samples were incubated and were then submitted to the SBS test and evaluated with the modified adhesive remnant index (ARI) and analyzed by using a scanning electronic microscope. Results: The SBS mean value for healthy enamel was 20 ± 10.2 MPa. For the group with MOF, the etched 150-second mean value was the highest (19 ± 7.6 MPa); for the group with SEF treated with microabrasion and etched for 15 seconds, the mean value was (13 ± 4.1 MPa). Significant differences (P ≤ .05) were found in the ARI between healthy and fluorosed groups. Conclusions: Fluorotic enamel affects the adhesion of bonded molar tubes. The use of overetching in cases of MOF and the combination of microabrasion and etching in SEF provides a suitable adhesion for fixed appliance therapy.