scholarly journals Setting, Strength, and Autogenous Shrinkage of Alkali-Activated Fly Ash and Slag Pastes: Effect of Slag Content

Materials ◽  
2018 ◽  
Vol 11 (11) ◽  
pp. 2121 ◽  
Author(s):  
Marija Nedeljković ◽  
Zhenming Li ◽  
Guang Ye
Keyword(s):  
Fly Ash ◽  
Setting Time ◽  
Experimental Studies ◽  
Autogenous Shrinkage ◽  
Engineering Properties ◽  
Engineering Practice ◽  
Granulated Blast Furnace Slag ◽  
Alkali Activated

The engineering properties of alkali activated materials (AAMs) mainly depend on the constituent materials and their mixture proportions. Despite many studies on the characterization of AAMs, guidelines for mixture design of AAMs and their applications in engineering practice are not available. Extensive experimental studies are still necessary for the investigation of the role of different constituents on the properties of AAMs. This paper focuses on the development of alkali-activated fly ash (FA) and ground granulated blast furnace slag (GBFS) paste mixtures in order to determine their suitability for making concretes. In particular, the influence of the GBFS/FA ratio and liquid-to-binder (l/b) ratio on the slump, setting, strength, and autogenous shrinkage of the alkali activated pastes is studied.It is shown that fresh properties largely depend on the type of precursor (GBFS or FA). The slump and setting time of GBFS-rich pastes was significantly reduced. These pastes also have higher compressive strength than FA-rich pastes. The study identifies important practical challenges for application of the studied mixtures, such as the behavior of their flexural strength and high amplitudes of autogenous shrinkage of GBFS-rich mixtures. Finally, the optimum GBFS/FA ratio for their future use in concretes is recommended.

scholarly journals Effect of Internal Curing by Super Absorbent Polymer on the Autogenous Shrinkage of Alkali-Activated Slag Mortars

Materials ◽  
2020 ◽  
Vol 13 (19) ◽  
pp. 4318
Author(s):  
Pengju Wang ◽  
Haiming Chen ◽  
Peiyuan Chen ◽  
Jin Pan ◽  
Yangchen Xu ◽  
...  
Keyword(s):  
Compressive Strength ◽  
Setting Time ◽  
Autogenous Shrinkage ◽  
Internal Curing ◽  
Engineering Properties ◽  
Super Absorbent Polymer ◽  
Alkali Activated Slag ◽  
Activated Slag ◽  
Absorbent Polymer ◽  
Alkali Activated

Alkali activated slag (AAS) mortar is becoming an increasingly popular green building material because of its excellent engineering properties and low CO2 emissions, promising to replace ordinary Portland cement (OPC) mortar. However, AAS’s high shrinkage and short setting time are the important reasons to limit its wide application in engineering. This paper was conducted to investigate the effect of internal curing(IC) by super absorbent polymer (SAP) on the autogenous shrinkage of AAS mortars. For this, an experimental study was carried out to evaluate the effect of SAP dosage on the setting time, autogenous shrinkage, compressive strength, microstructure, and pore structure. The SAP were incorporated at different dosage of 0, 0.05, 0.1, 0.2, 0.3, 0.4, and 0.5 percent by weight of slag. The workability, physical (porosity), mechanical, and shrinkage properties of the mortars were evaluated, and a complementary study on microstructure was made. The results indicated that the setting time increased with an increase of SAP dosage due to the additional activator released by SAP. Autogenous shrinkage decreased with an increase of SAP dosage, and was mitigated completely when the dosage of SAP ≥ 0.2% wt of slag. Although IC by means of SAP reduced the compressive strength, this reduction (23% at 56 days for 0.2% SAP) was acceptable given the important role that it played on mitigating autogenous shrinkage. In the research, the 0.2% SAP dosage was the optimal content. The results can provide data and basis for practical application of AAS mortar.

The Role of Fly Ash in the Granulated Blast Furnace Slag-Based Geopolymer

2013 ◽  
Vol 405-408 ◽  
pp. 2760-2766
Author(s):  
Cheng Xu Wu ◽  
Hua Jun Zeng
Keyword(s):  
Fly Ash ◽  
Heat Release ◽  
Setting Time ◽  
Cementitious Materials ◽  
Inorganic Polymers ◽  
Strength Limit ◽  
Granulated Blast Furnace Slag ◽  
Rate Of Heat Release ◽  
Short Setting Time

Inorganic polymers using slag as cementitious materials have the advantage of a short setting time, high early strength, but the sensitivity of the reaction rate to temperature and the likelihood to subsequently crack, which leads to reduction of strength, limit its application. This article, by configuring different proportion of fly ash and slag, studied its dry shrinkage with the different kinds of activator, the effects of fly ash on the hydration heat release curves, differences of setting time and strength with different configuration, and then explored the effect of fly-ash in inorganic polymer. Experiments had shown that through rational configuration, the addition of fly ash can effectively reduce the rate of heat release and the amount of heat, meanwhile can solve the problem about short setting time of alkali-activated cementitious materials without reducing its strength.

scholarly journals The Hydration, Mechanical, Autogenous Shrinkage, Durability, and Sustainability Properties of Cement–Limestone–Slag Ternary Composites

2021 ◽  
Vol 13 (4) ◽  
pp. 1881
Author(s):  
Mei-Yu Xuan ◽  
Yi Han ◽  
Xiao-Yong Wang
Keyword(s):  
Compressive Strength ◽  
Electrical Resistivity ◽  
Experimental Studies ◽  
Autogenous Shrinkage ◽  
Ultrasonic Pulse Velocity ◽  
Ultrasonic Pulse ◽  
Pulse Velocity ◽  
Hydration Heat ◽  
Granulated Blast Furnace Slag ◽  
Binder Ratio

This study examines the hydration–mechanical–autogenous shrinkage–durability–sustainability properties of ternary composites with limestone filler (LF) and ground-granulated blast furnace slag (BFS). Four mixtures were prepared with a water/binder ratio of 0.3 and different replacement ratios varying from 0 to 45%. Multiple experimental studies were performed at various ages. The experimental results are summarized as follows: (1) As the replacement levels increased, compressive strength and autogenous shrinkage (AS) decreased, and this relationship was linear. (2) As the replacement levels increased, cumulative hydration heat decreased. At the age of 3 and 7 days, there was a linear relationship between compressive strength and cumulative hydration heat. (3) Out of all mixtures, the ultrasonic pulse velocity (UPV) and electrical resistivity exhibited a rapid increase in the early stages and tended to slow down in the latter stages. There was a crossover of UPV among various specimens. In the later stages, the electrical resistivity of ternary composite specimens was higher than plain specimens. (4) X-ray diffraction (XRD) results showed that LF and BFS have a synergistic effect. (5) With increasing replacement ratios, the CO2 emissions per unit strength reduced, indicating the sustainability of ternary composites.

scholarly journals Influence of Na2O Content and Ms (SiO2/Na2O) of Alkaline Activator on Workability and Setting of Alkali-Activated Slag Paste

Materials ◽  
2019 ◽  
Vol 12 (13) ◽  
pp. 2072 ◽  
Author(s):  
Sung Choi ◽  
Kwang-Myong Lee
Keyword(s):  
Setting Time ◽  
High Strength ◽  
Abrupt Decrease ◽  
Na2o Content ◽  
Alkali Activated Slag ◽  
Granulated Blast Furnace Slag ◽  
Type Composition ◽  
Activated Slag ◽  
Binary Alkaline ◽  
Alkali Activated

The performance of alkali-activated slag (AAS) paste using activators of strong alkali components is affected by the type, composition, and dosage of the alkaline activators. Promoting the reaction of ground granulated blast furnace slag (GGBFS) by alkaline activators can produce high-strength AAS concrete, but the workability might be drastically reduced. This study is aimed to experimentally investigate the heat release, workability, and setting time of AAS pastes and the compressive strength of AAS mortars considering the Na2O content and the ratio of Na2O to SiO2 (Ms) of binary alkaline activators blended with sodium hydroxide and sodium silicate. The test results indicated that the AAS mortars exhibited a high strength of 25 MPa at 24 h, even at ambient temperature, even though the pastes with an Na2O content of ≥6% and an Ms of ≥1.0 exhibited an abrupt decrease in flowability and rapid setting.

scholarly journals Properties of non-standard fly ash – slag cements containing calcareous fly ash

2013 ◽  
Vol 12 (3) ◽  
pp. 215-222
Author(s):  
Katarzyna Synowiec
Keyword(s):  
Fly Ash ◽  
Blast Furnace Slag ◽  
Strength Class ◽  
Setting Time ◽  
Heat Of Hydration ◽  
Initial Setting Time ◽  
Granulated Blast Furnace Slag ◽  
Unfavorable Effect ◽  
Initial Setting ◽  
Furnace Slag

The paper presents the tests results of the properties of non - standard fly ash - slag cements composition. Both natural (unprocessed) and activated by grinding calcareous fly ash was used. It was found that the calcareous fly ash next to the granulated blast furnace slag may be a component of low - clinker cements (ca. 40%). Those cements are characterized by low heat of hydration and overdue of initial setting time in comparison with Ordinary Portland Cement, moreover they have an unfavorable effect on consistency and its upkeep in time. Production of fly ash - slag cements is possible for strength class 32,5 N when the component of cement is raw fly ash, and for strength classes 32,5 N, 32,5 R and 42,5 N when ground fly ash was used. Fly ash activated by grinding was characterized by higher activity.

Experimental Study on Alkali-Activated Slag-Lithium Slag-Fly Ash Environmental Concrete

2011 ◽  
Vol 287-290 ◽  
pp. 1237-1240
Author(s):  
Lan Fang Zhang ◽  
Rui Yan Wang
Keyword(s):  
Experimental Study ◽  
Compressive Strength ◽  
Fly Ash ◽  
Setting Time ◽  
Alkali Activated Slag ◽  
Percent Increase ◽  
Compressive Strength Of Concrete ◽  
Activated Slag ◽  
Lithium Slag ◽  
Alkali Activated

The aim of this paper is to study the influence of lithium-slag and fly ash on the workability , setting time and compressive strength of alkali-activated slag concrete. The results indicate that lithium-slag and fly-ash can ameliorate the workability, setting time and improve the compressive strength of alkali-activated slag concrete，and when 40% or 60% slag was replaced by lithium-slag or fly-ash, above 10 percent increase in 28-day compressive strength of concrete were obtained.