Theoretical Study of CO Adsorption and Activation on Orthorhombic Fe7C3(001) Surfaces for Fischer–Tropsch Synthesis Using Density Functional Theory Calculations

Fischer–Tropsch synthesis (FTS), which converts CO and H2 into useful hydrocarbon products, has attracted considerable attention as an efficient method to replace crude oil resources. Fe-based catalysts are mainly used in industrial FTS, and Fe7C3 is a common carbide phase in the FTS reaction. However, the intrinsic catalytic properties of Fe7C3 are theoretically unknown. Therefore, as a first attempt to understand the FTS reaction on Fe7C3, direct CO* dissociation on orthorhombic Fe7C3(001) (o-Fe7C3(001)) surfaces was studied using density functional theory (DFT) calculations. The surface energies of 14 terminations of o-Fe7C3(001) were first compared, and the results showed that (001)0.20 was the most thermodynamically stable termination. Furthermore, to understand the effect of the surface C atom coverage on CO* activation, C–O bond dissociation was performed on the o-Fe7C3(001)0.85, (001)0.13, (001)0.20, (001)0.09, and (001)0.99 surfaces, where the surface C atom coverages were 0.00, 0.17, 0.33, 0.33, and 0.60, respectively. The results showed that the CO* activation linearly decreased as the surface C atom coverage increased. Therefore, it can be concluded that the thermodynamic and kinetic selectivity toward direct CO* dissociation increased when the o-Fe7C3(001) surface had more C* vacancies.