scholarly journals Intrinsic Ferroelectricity in Charge-Ordered Magnetite

Crystals ◽  
2019 ◽  
Vol 9 (11) ◽  
pp. 546
Author(s):  
Manuel Angst ◽  
Shilpa Adiga ◽  
Semen Gorfman ◽  
Michael Ziolkowski ◽  
Jörg Strempfer ◽  
...  
Keyword(s):  
Low Temperatures ◽  
Time Window ◽  
Bragg Reflection ◽  
Relaxor Ferroelectric ◽  
Threshold Field ◽  
Diffraction Experiment ◽  
Time Resolved ◽  
Switchable Polarization ◽  
Ordered State

Single crystalline magnetite Fe 3 O 4 was investigated at low temperatures in the charge ordered state by electric measurements and time-resolved diffraction with voltage applied in-situ. Dielectric spectroscopy indicates relaxor ferroelectric characteristics, with polarization switching observably only at sufficiently low temperatures and in a suitably chosen time-window. PUND measurements with a ms time scale indicate a switchable polarization of about 0 . 6 μ C / cm 2 . Significant switching occurs only above a threshold field of about 3 kV / mm , and it occurs with a time delay of about 20 μ s . The time-resolved diffraction experiment yields, for sufficiently high voltage pulses, a systematic variation by about 0 . 1 % of the intensity of the ( 2 , 2 ¯ , 10 ¯ ) Bragg reflection, which is attributed to structural switching of domains of the non-centrosymmetric C c structure to its inversion twins, providing proof of intrinsic ferroelectricity in charge ordered magnetite.

In situ Tensile Experiments at Low Temperatures on Niobium Single Crystals by H.V.E.M.

1975 ◽  
Vol 33 ◽  
pp. 58-59
Author(s):  
F. H. Louchet ◽  
L. P. Kubin
Keyword(s):  
Electron Microscope ◽  
Transition Temperature ◽  
Low Temperature ◽  
Slip System ◽  
Low Temperatures ◽  
Tensile Axis ◽  
Image Intensifier ◽  
Screw Dislocations ◽  
Source Operation

Experiments have been carried out on the 3 MeV electron microscope in Toulouse. The low temperature straining holder has been previously described Images given by an image intensifier are recorded on magnetic tape.The microtensile niobium samples are cut in a plane with the two operative slip directions [111] and lying in the foil plane. The tensile axis is near [011].Our results concern:- The transition temperature of niobium near 220 K: at this temperature and below an increasing difference appears between the mobilities of the screw and edge portions of dislocations loops. Source operation and interactions between screw dislocations of different slip system have been recorded.

“In-Situ Raman Spectroscopy of Electronic Processes in Fullerene Thin Films

2002 ◽  
Vol 725 ◽  
Author(s):  
S.B. Phelan ◽  
B.S. O'Connell ◽  
G. Farrell ◽  
G. Chambers ◽  
H.J. Byrne
Keyword(s):  
Thin Film ◽  
Indium Tin Oxide ◽  
Low Temperatures ◽  
In Situ Raman Spectroscopy ◽  
State Reduction ◽  
In Situ Raman ◽  
Linear Behavior ◽  
Current Voltage ◽  
Solid State Reduction

AbstractThe current voltage characteristics of C60 thin film sandwich structures fabricated by vacuum deposition on indium tin oxide (ITO) with an aluminium top electrode are presented and discussed. A strongly non-linear behavior and a sharp increase in the device conductivity was observed at relatively low voltages (∼2V), at both room and low temperatures (20K). At room temperature the system is seen to collapse, and in situ Raman measurements indicate a solid state reduction of the fullerene thin film to form a polymeric state. The high conductivity state was seen to be stable at elevated voltages and low temperatures. This state is seen to be reversible with the application of high voltages. At these high voltages the C60 film was seen to sporadically emit white light at randomly localized points analogous to the much documented Electroluminescence in single crystals.

Exciton dynamics in thick GaN MOVPE epilayers deposited on sapphire.

1997 ◽  
Vol 2 ◽  
Author(s):  
J. Allègre ◽  
P. Lefebvre ◽  
J. Camassel ◽  
B. Beaumont ◽  
Pierre Gibart
Keyword(s):  
Layer Thickness ◽  
Buffer Layers ◽  
Rate Equations ◽  
Time Resolved ◽  
Versus Layer ◽  
Level Model ◽  
Shallow Impurities ◽  
Aln Buffer ◽  
Time Resolved Photoluminescence

Time-resolved photoluminescence spectra have been recorded on three GaN epitaxial layers of thickness 2.5 μm, 7 μm and 16 μm, at various temperatures ranging from 8K to 300K. The layers were deposited by MOVPE on (0001) sapphire substrates with standard AlN buffer layers. To achieve good homogeneities, the growth was in-situ monitored by laser reflectometry. All GaN layers showed sharp excitonic peaks in cw PL and three excitonic contributions were seen by reflectivity. The recombination dynamics of excitons depends strongly upon the layer thickness. For the thinnest layer, exponential decays with τ ~ 35 ps have been measured for both XA and XB free excitons. For the thickest layer, the decay becomes biexponential with τ1 ~ 80 ps and τ2 ~ 250 ps. These values are preserved up to room temperature. By solving coupled rate equations in a four-level model, this evolution is interpreted in terms of the reduction of density of both shallow impurities and deep traps, versus layer thickness, roughly following a L−1 law.

Monitoring Polymer-Assisted Mechanochemical Cocrystallisation Through in Situ X-Ray Powder Diffraction

2020 ◽  
Author(s):  
Luzia S. Germann ◽  
Sebastian T. Emmerling ◽  
Manuel Wilke ◽  
Robert E. Dinnebier ◽  
Mariarosa Moneghini ◽  
...  
Keyword(s):  
Molecular Weight ◽  
Powder Diffraction ◽  
Reaction Rate ◽  
Polymer Additives ◽  
Time Resolved ◽  
X Ray

Time-resolved mechanochemical cocrystallisation studies have so-far focused solely on neat and liquid-assisted grinding. Here, we report the monitoring of polymer-assisted grinding reactions using <i>in situ</i> X-ray powder diffraction, revealing that reaction rate is almost double compared to neat grinding and independent of the molecular weight and amount of used polymer additives.<br>

In situ Time-Resolved Small-Angle X-ray Scattering Reveals the Formation Kinetics of Polyelectrolyte Complex Micelles

2019 ◽  
Author(s):  
Hao Wu ◽  
Jeffrey Ting ◽  
Siqi Meng ◽  
Matthew Tirrell
Keyword(s):  
Small Angle ◽  
Self Assembly ◽  
Electrostatic Interactions ◽  
Polyelectrolyte Complex ◽  
Time Resolved ◽  
X Ray ◽  
X Ray Scattering ◽  
Kinetics Of ◽  
Ray Scattering

We have directly observed the <i>in situ</i> self-assembly kinetics of polyelectrolyte complex (PEC) micelles by synchrotron time-resolved small-angle X-ray scattering, equipped with a stopped-flow device that provides millisecond temporal resolution. This work has elucidated one general kinetic pathway for the process of PEC micelle formation, which provides useful physical insights for increasing our fundamental understanding of complexation and self-assembly dynamics driven by electrostatic interactions that occur on ultrafast timescales.

Dependence of the intrinsic phase structure of Bi2O3 catalysts on photocatalytic CO2 reduction

2021 ◽  
Vol 11 (6) ◽  
pp. 2021-2025
Author(s):  
Liujin Wei ◽  
Guan Huang ◽  
Yajun Zhang
Keyword(s):  
Fourier Transform ◽  
Infrared Spectroscopy ◽  
Fourier Transform Infrared Spectroscopy ◽  
Phase Structure ◽  
Co2 Reduction ◽  
Fourier Transform Infrared ◽  
Time Resolved ◽  
Dependent Activity

The combination of time-resolved transient photoluminescence with in-situ Fourier transform infrared spectroscopy has been conducted to investigate the intrinsic phase structure-dependent activity of Bi2O3 catalyst for CO2 reduction.

Sign in / Sign up

Export Citation Format

Share Document