scholarly journals Preliminary Study on the Application of Concentrated Solar Power in Metallurgy of Titanium

2019 ◽  
Vol 3 (4) ◽  
pp. 84 ◽  
Author(s):  
Jaroslav Kováčik ◽  
Natália Mináriková ◽  
Tomáš Dvorák ◽  
Jose Rodríguez ◽  
Inmaculada Cañadas ◽  
...  
Keyword(s):  
Titanium Powder ◽  
Solar Power ◽  
Titanium Sponge ◽  
Processing Parameters ◽  
Yttria Stabilized Zirconia ◽  
Solar Furnace ◽  
Concentrated Solar Power ◽  
Stabilized Zirconia ◽  
Experimental Works ◽  
Preliminary Study

The applicability of concentrated solar power for metallurgy of titanium is discussed based on preliminary experimental works performed at Plataforma Solar de Almeria Spain, using solar furnace SF40 under protective argon atmosphere. As a starting material, titanium powder was used. The possibility of melting titanium compacts on yttria stabilized zirconia mat was investigated, and the effect of density and size of different green compacts was studied. It was observed that the time to achieve melting point is very short when concentrated solar power is used. The obtained results are expected to be similar for titanium sponge from which titanium powder is processed. After optimization of processing parameters, this will probably lead to a significant decrease of carbon footprint in the titanium ingots and castings production.

Preparation of Pb(Zr0.54Ti0.46)O3 Thin Films on (100)Si Using Textured YBa2Cu3O7−δ and Yttria-Stabilized Zirconia Buffer Layers by Laser Physical Vapor Deposition Technique

1992 ◽  
Vol 285 ◽  
Author(s):  
P. Tiwari ◽  
T. Zheleva ◽  
A. Morimoto ◽  
V.N. Shukla ◽  
J. Narayan
Keyword(s):  
Thin Films ◽  
Physical Vapor Deposition ◽  
Ferroelectric Properties ◽  
Processing Parameters ◽  
Yttria Stabilized Zirconia ◽  
Buffer Layers ◽  
Stabilized Zirconia ◽  
Vapor Deposition Technique ◽  
Pzt Films ◽  
Physical Vapor Deposition Technique

ABSTRACTWe have fabricated high-quality <001> textured Pb(Zr0.54Ti0.46)O3 (PZT) thin films on (001)Si with interposing <001> textured YBa2Cu3O7−δ (YBCO) and yttria-stabilized zirconia (YSZ) buffer layers using pulsed laser deposition (KrF excimer laser, λ=248 nm, τ=20 nanoseconds). The YBCO layer provides a seed for PZT growth and can also act as an electrode for the PZT films, whereas YSZ provides a diffusion barrier as well as a seed for the growth of YBCO films on (001)Si. These heterostructures were characterized using X-ray diffraction, high-resolution transmission electron microscopy and Rutherford backscattering techniques. The YSZ films were deposited in oxygen ambient (∼9X10−4 torr) at 775°C on (001)Si substrate having <001>YSZ// <001>Si texture. The YBCO thin films were deposited in-situ in oxygen ambient (200 mtorr) at 650°C. Temperature and oxygen ambient for the PZT deposition were optimized to be 530°C and 0.4–0.6 torr, respectively. The laser fluence to deposit this multistructure was 2.5–5.0 J/cm2. The <001> textured perovskite PZT films showed a dielectric constant of 800–1000, a saturation polarization of 37.81 μC/cm2, remnant polarization of 24.38 μC/cm2 and a coersive field of 125 kV/cm. The effects of processing parameters on microstructure and ferroelectric properties of PZT films and device implications of these structures are discussed.

scholarly journals Characterization of Solar-Aged Porous Silicon Carbide for Concentrated Solar Power Receivers

Materials ◽  
2021 ◽  
Vol 14 (16) ◽  
pp. 4627
Author(s):  
Inmaculada Cañadas ◽  
Victor M. Candelario ◽  
Giulia De Aloysio ◽  
Jesús Fernández ◽  
Luca Laghi ◽  
...  
Keyword(s):  
Silicon Carbide ◽  
Porous Silicon ◽  
Thermal Stresses ◽  
Solar Power ◽  
Ultrasonic Inspection ◽  
Solar Furnace ◽  
Accelerated Ageing ◽  
Flash Method ◽  
Concentrated Solar Power ◽  
Porous Silicon Carbide

Porous silicon carbide is a promising material for ceramic receivers in next-generation concentrated solar power receivers. To investigate its tolerance to thermal shock, accelerated ageing of large coupons (50 × 50 × 5 mm) was conducted in a solar furnace to investigate the effects of thermal cycling up to 1000 °C, with gradients of up to 22 °C/mm. Non-destructive characterization by computed X-ray tomography and ultrasonic inspection could detect cracking from thermal stresses, and this informed the preparation of valid specimens for thermophysical characterization. The effect of thermal ageing on transient thermal properties, as a function of temperature, was investigated by using the light-flash method. The thermophysical properties were affected by increasing the severity of the ageing conditions; thermal diffusivity decreased by up to 10% and specific heat by up to 5%.

Microstructural examination of modified yttria stabilized zirconia by EM analytical techniques

1986 ◽  
Vol 44 ◽  
pp. 842-843
Author(s):  
W. W. Davison ◽  
R. C. Buchanan
Keyword(s):  
Mechanical Properties ◽  
Analytical Techniques ◽  
Yttria Stabilized Zirconia ◽  
Stabilized Zirconia ◽  
Transmission Microscopy ◽  
Sintering Aid ◽  
Densification Temperature ◽  
Chemical Inertness ◽  
Scanning Transmission ◽  
Microstructural Examination

Yttria stabilized zirconia (YSZ) has become a significant technological material due to its high ionic conductivity, chemical inertness, and good mechanical properties. Temperatures on the order of 1700°C are required, however, to densify YSZ to the degree necessary for good electrical and mechanical properties. A technique for lowering the densification temperature is the addition of small amounts of material which facilitate the formation of a liquid phase at comparatively low temperatures. In this study, sintered microstructures obtained from the use of Al2O3 as a sintering aid were examined with scanning, transmission, and scanning transmission microscopy (SEM, TEM, and STEM).

CONCENTRATED SOLAR POWER (CSP) PLANT PROPOSAL FOR BRAZIL

2017 ◽  
Vol 8 (4) ◽  
pp. 1-19
Author(s):  
Oliveira Helio Marques de ◽  
◽  
Giacaglia Giorgio Eugenio Oscare ◽  
Keyword(s):  
Solar Power ◽  
Concentrated Solar Power

Characterizations of Synthetic 8mol% YSZ with Comparison to 3mol %YSZ for HT-SOFC

2020 ◽  
Vol 38 (4A) ◽  
pp. 491-500
Author(s):  
Abeer F. Al-Attar ◽  
Saad B. H. Farid ◽  
Fadhil A. Hashim
Keyword(s):  
Ionic Conductivity ◽  
Electrochemical Impedance ◽  
Structural Information ◽  
Impedance Analysis ◽  
High Energy ◽  
Yttria Stabilized Zirconia ◽  
X Ray Diffraction ◽  
Stabilized Zirconia ◽  
Powder Morphology ◽  
X Ray

In this work, Yttria (Y2O3) was successfully doped into tetragonal 3mol% yttria stabilized Zirconia (3YSZ) by high energy-mechanical milling to synthesize 8mol% yttria stabilized Zirconia (8YSZ) used as an electrolyte for high temperature solid oxide fuel cells (HT-SOFC). This work aims to evaluate the densification and ionic conductivity of the sintered electrolytes at 1650°C. The bulk density was measured according to ASTM C373-17. The powder morphology and the microstructure of the sintered electrolytes were analyzed via Field Emission Scanning Electron Microscopy (FESEM). The chemical analysis was obtained with Energy-dispersive X-ray spectroscopy (EDS). Also, X-ray diffraction (XRD) was used to obtain structural information of the starting materials and the sintered electrolytes. The ionic conductivity was obtained through electrochemical impedance spectroscopy (EIS) in the air as a function of temperatures at a frequency range of 100(mHz)-100(kHz). It is found that the 3YSZ has a higher density than the 8YSZ. The impedance analysis showed that the ionic conductivity of the prepared 8YSZ at 800°C is0.906 (S.cm) and it was 0.214(S.cm) of the 3YSZ. Besides, 8YSZ has a lower activation energy 0.774(eV) than that of the 3YSZ 0.901(eV). Thus, the prepared 8YSZ can be nominated as an electrolyte for the HT-SOFC.

Sign in / Sign up

Export Citation Format

Share Document