scholarly journals Optimizing Viscoelastic Properties of Rubber Compounds for Ballistic Applications

2020 ◽  
Vol 10 (21) ◽  
pp. 7840
Author(s):  
Janis Karl ◽  
Franziska Kirsch ◽  
Norbert Faderl ◽  
Leonhard Perko ◽  
Teresa Fras
Keyword(s):  
Glass Transition ◽  
Transition Temperature ◽  
Glass Transition Temperature ◽  
Mechanical Stress ◽  
Mechanical Load ◽  
Superposition Principle ◽  
Dynamic Mechanical Properties ◽  
Mechanical Analysis ◽  
Ballistic Impact ◽  
Dynamic Mechanical

Using interlayers of rubber adds a positive effect to the synergy of disruptor–absorber armors. Emerging from its viscoelasticity the material is able to transform mechanical stress into heat. The dynamic mechanical properties of elastomers depend on both ambient temperature and frequency of an applied mechanical load. The damping shows a maximum in the glass transition area. If the frequency of the glass transition is in the magnitude of the mechanical stress rate applied by ballistic impact, the elastomer will undergo the transition and thus show maximized damping. An ideal material for ballistic protection against small calibers is developed by making use of dynamic mechanical analysis and the time–temperature superposition principle. The material is later analyzed by ballistic experiments and compared to other nonideal rubbers with regard to glass transition temperature, hardness and damping. It is shown that by choosing a material correctly with certain glass transition temperature and hardness, the ballistic properties of a steel–rubber–aluminum armor can be enhanced. The chosen material (butyl rubber) with a hardness of 50 °ShA is able to enhance energy absorption during ballistic impact by around 8%, which is twice as good as other rubber with non-optimized properties.

Effects of Nano-Silica Addition and Reactive Diluent Addition on Dynamic Mechanical Properties of Epoxy Nanocomposites

2013 ◽  
Vol 853 ◽  
pp. 46-52
Author(s):  
Huey Ling Chang ◽  
Chih Ming Chen
Keyword(s):  
Glass Transition ◽  
Transition Temperature ◽  
Glass Transition Temperature ◽  
Storage Modulus ◽  
Loss Modulus ◽  
Dynamic Mechanical Properties ◽  
Mechanical Analysis ◽  
Reactive Diluent ◽  
Dynamic Mechanical ◽  
Silica Nanopowder

Epoxy resin nanocomposite samples containing 0~3wt.% reactive diluent and 0~3wt.% silica nanopowder are prepared. The preparation process is presented for solvent-free and greenmanufacturing. The storage modulus, loss modulus and glass transition temperature of the various samples are then evaluated via Dynamic Mechanical Analysis (DMA). For samples containing 0wt.% and 3wt.% reactive diluent, respectively, 3wt.% nanoSiO2 addition is found to increase the storage modulus by 51.06 % and 22.22 %, respectively. In addition, it is found that the loss modulus is determined principally by the level of SiO2 addition, whereas the glass transition temperature is determined mainly by the level of reactive diluent addition.

Dynamic mechanical behaviour of kevlar and carbon-kevlar hybrid fibre reinforced polymer composites

2020 ◽  
pp. 095440622097060
Author(s):  
Pragati Priyanka ◽  
Harlal Singh Mali ◽  
Anurag Dixit
Keyword(s):  
Glass Transition ◽  
Transition Temperature ◽  
Glass Transition Temperature ◽  
Dynamic Mechanical Analysis ◽  
Storage Modulus ◽  
Composite Laminates ◽  
Mechanical Analysis ◽  
Textile Composites ◽  
Elastic Behaviour ◽  
Dynamic Mechanical

Comprehensive experimental results of dynamic mechanical analysis (DMA) of polymer reinforced textile composites are presented in the current investigation. Plain and 2x2 twill woven multilayer fabrics of monolithic kevlar and hybrid carbon-kevlar (C-K) are reinforced into the thermoset polymer matrix. Kevlar/epoxy and C-K/epoxy composite laminates are fabricated using an in-house facility of the vacuum-assisted resin infusion process. Variation of the visco-elastic behaviour (storage modulus, damping factor and glass transition temperature, Tg) along with time, temperature and frequency is studied for the composites. Dynamic mechanical analysis is performed under temperature sweep with frequency ranging from 1-50 Hz. Results depict the effect of inter yarn hybridisation of carbon with kevlar yarns on the storage modulus, damping performance, and creep behaviour of dry textile composites. Temperature swept dynamic characterisation is also performed to evaluate the degradation and damping performance of the composite laminates soaked in the deionised water at glass transition temperature Tg, ½ Tg, and ¾ Tg. The morphological study has been performed post the dynamic mechanical analysis using field emission scanning electron microscope.

Dynamic Mechanical Analysis of Nanosilica Filled Epoxy Nanocomposites

2014 ◽  
Vol 699 ◽  
pp. 239-244 ◽  
Author(s):  
Nurhidayah R. Zamani ◽  
Aidah Jumahat ◽  
Rosnadiah Bahsan
Keyword(s):  
Glass Transition ◽  
Transition Temperature ◽  
Glass Transition Temperature ◽  
Epoxy Polymer ◽  
Loss Modulus ◽  
Matrix Material ◽  
Mechanical Analysis ◽  
Dynamic Mechanical ◽  
Mechanical Stirring ◽  
Tan Δ

In this study, Dynamic Mechanical Analyzer (DMA) was used to study the effect of nanoparticles, which is nanosilica, on glass transition temperature (Tg) of epoxy polymer. A series of epoxy based nanosilica composite with 5-25 wt% nanosilica content was prepared using mechanical stirring method. The weight fractions of nanosilica in epoxy were 5 wt%, 13 wt% and 25 wt%. 30mm x 10mm x 3mm size specimens were tested using DMA machine from room temperature up to 180oC at 2°C/min heating rate. From the analysis of the results, dynamic modulus and glass transition temperature of pure polymer and nanosilica filled polymer were obtained. The glass transition of a polymer composite is a temperature-induced change in the matrix material from the glassy to the rubbery state during heating or cooling. Glass transition temperature Tg was determined using several method: storage modulus onset, loss modulus peak, and tan δ peak. The results showed that the presence of nanosilica reduced Tg of epoxy polymer.