scholarly journals AN EXPERIMENTAL STUDY ON ELECTROMAGNETIC SHIELDING EFFECT OF CARBON FIBER REINFORCED MORTAR (CFRM) AND ELECTROLYTIC CORROSION OF REBARS PLACED IN CFRM UNDER LONG-TERM EXPOSURE

2012 ◽  
Vol 77 (672) ◽  
pp. 161-169
Author(s):  
Makoto YAMAGUCHI ◽  
Kiyoshi MURAKAMI ◽  
Koji TAKEDA ◽  
Yoshiyuki MITSUI ◽  
Tadatsugu KAGE ◽  
...  
Keyword(s):  
Experimental Study ◽  
Carbon Fiber ◽  
Electromagnetic Shielding ◽  
Shielding Effect ◽  
Fiber Reinforced ◽  
Electrolytic Corrosion ◽  
Carbon Fiber Reinforced

Effects of high pressure on the crystallization of carbon fiber reinforced polyetheretherketone (CF/PEEK) laminate composites

1990 ◽  
Vol 48 (4) ◽  
pp. 876-877
Author(s):  
Hong-Ming Lin ◽  
C. H. Liu ◽  
R. F. Lee
Keyword(s):  
High Pressure ◽  
Carbon Fiber ◽  
Sample Surface ◽  
High Yield ◽  
Fiber Reinforced ◽  
Laminate Composites ◽  
Peek Composite ◽  
Continuous Carbon Fiber ◽  
Carbon Fiber Reinforced

Polyetheretherketone (PEEK) is a crystallizable thermoplastic used as composite matrix materials in application which requires high yield stress, high toughness, long term high temperature service, and resistance to solvent and radiation. There have been several reports on the crystallization behavior of neat PEEK and of CF/PEEK composite. Other reports discussed the effects of crystallization on the mechanical properties of PEEK and CF/PEEK composites. However, these reports were all concerned with the crystallization or melting processes at or close to atmospheric pressure. Thus, the effects of high pressure on the crystallization of CF/PEEK will be examined in this study.The continuous carbon fiber reinforced PEEK (CF/PEEK) laminate composite with 68 wt.% of fibers was obtained from Imperial Chemical Industry (ICI). For the high pressure experiments, HIP was used to keep these samples under 1000, 1500 or 2000 atm. Then the samples were slowly cooled from 420 °C to 60 °C in the cooling rate about 1 - 2 degree per minute to induce high pressure crystallization. After the high pressure treatment, the samples were scanned in regular DSC to study the crystallinity and the melting temperature. Following the regular polishing, etching, and gold coating of the sample surface, the scanning electron microscope (SEM) was used to image the microstructure of the crystals. Also the samples about 25mmx5mmx3mm were prepared for the 3-point bending tests.