Three Dimensional Progressive Failure Analysis of Laminated Composite Structures

2015 ◽  
Author(s):  
Arafat I. Khan ◽  
Rakesh K. Kapania ◽  
Romesh C. Batra ◽  
Eric R. Johnson ◽  
Jean-Mathieu Guimard
Keyword(s):  
Failure Analysis ◽  
Composite Structures ◽  
Progressive Failure ◽  
Three Dimensional ◽  
Laminated Composite ◽  
Progressive Failure Analysis ◽  
Laminated Composite Structures

Failure Analysis of Laminated Composites under in-Plane Compressive Loading

2012 ◽  
Vol 476-478 ◽  
pp. 583-586
Author(s):  
Yin Huan Yang
Keyword(s):  
Failure Analysis ◽  
Composite Laminates ◽  
Composite Structures ◽  
Parametric Design ◽  
Laminated Composites ◽  
Progressive Failure ◽  
Compressive Loading ◽  
Laminated Composite ◽  
Progressive Failure Analysis ◽  
Ultimate Failure

Failure prediction of laminated composites is performed by progressive failure analysis method. A modified form of Hashin’s failure criterion by Shokrieh is used to detect the failure, where a sudden degradation model is proposed to reduce engineering material constants. The numerical analysis of composite laminates is implemented in ANSYS Parametric Design Language (APDL) with commercial finite element codes ANSYS. The method can predict the initiation and propagation of local damage and response of laminated composite structures from initial loading and ultimate failure. The model has been validated by comparing numerical results with existing experimental results. And then failure analysis specimen fabricated from M40J/Ag80 and investigation on influence of stacking sequences and fiber orientations under in-plane compressive loading have been performed by the proposed model.

Progressive failure analysis for the interaction of interlaminar and intralaminar failure modes in composite structures with an initial delamination

2013 ◽  
Vol 117 (1187) ◽  
pp. 71-85 ◽  
Author(s):  
W. Ji ◽  
A. M. Waas
Keyword(s):  
Failure Analysis ◽  
Composite Laminates ◽  
Composite Structures ◽  
Failure Modes ◽  
Progressive Failure ◽  
Laminated Composite ◽  
Composite Panel ◽  
Analysis Tool ◽  
Plane Failure ◽  
Progressive Failure Analysis

AbstractThis paper is concerned with the development of a failure initiation and progressive failure analysis (PFA) method for advanced composite structures. The present PFA model is capable of predicting interactive out-of-plane and in-plane failure modes observed in fiber reinforced composite laminates including interlaminar behavior and matrix microdamage at the mesoscale. A probability analysis tool is coupled with the PFA to account for uncertainty in modelling parameters caused by material variability and manufacturing inconsistencies. The progressive damage response of a laminated composite panel with an initial delamination is studied and used to demonstrate the PFA modelling framework that is presented here.

Failure Analysis of Laminate on Influence of the Hole

2012 ◽  
Vol 450-451 ◽  
pp. 590-593
Author(s):  
Yin Huan Yang
Keyword(s):  
Failure Analysis ◽  
Composite Structures ◽  
Parametric Design ◽  
Numerical Study ◽  
Laminated Composites ◽  
Progressive Failure ◽  
Failure Process ◽  
Laminated Composite ◽  
Progressive Failure Analysis ◽  
Ultimate Failure

Failure process of laminated composites is performed by progressive failure analysis method. A modified form of Hashin’s failure criterion by Shokrieh is used to investigate the failure, where a sudden degradation model is proposed to reduce engineering material constants. The numerical study of laminated composites is implemented in ANSYS Parametric Design Language (APDL). The initiation and propagation of local damage and response of laminated composite structures from initial loading and ultimate failure are predicted. The model has been validated by comparing numerical results with existing experimental results. And then failure analysis of specimen fabricated from M40J/Ag80 on influence of the hole has been performed by the proposed model.