scholarly journals Effect of the molecular weight of polycarbonate on the impact resistance of continuous carbon fiber reinforced polycarbonate composites

2014 ◽  
Author(s):  
K. Tanaka ◽  
H. Koriyama ◽  
S. Isshiki ◽  
T. Katayama ◽  
M. Shinohara
Keyword(s):  
Molecular Weight ◽  
Carbon Fiber ◽  
Impact Resistance ◽  
Fiber Reinforced ◽  
Continuous Carbon Fiber ◽  
Carbon Fiber Reinforced ◽  
The Impact

STUDY OF THE POSSIBILITY OF INCREASING THE IMPACT RESISTANCE OF THIN-SHEETED CARBON FIBER-REINFORCED PLASTICS DUE TO CLADING WITH ARAMID ORGANOPLASTICS

2021 ◽  
pp. 35-42
Author(s):  
G.F. Zhelezina ◽  
◽  
N.A. Solovieva ◽  
G.S. Kulagina ◽  
P.M. Shuldeshova ◽  
...  
Keyword(s):  
Carbon Fiber ◽  
Impact Resistance ◽  
Fiber Reinforced ◽  
Technical Literature ◽  
Carbon Fiber Reinforced Plastics ◽  
Reinforced Plastics ◽  
Fiber Reinforced Plastics ◽  
Carbon Fiber Reinforced ◽  
The Impact ◽  
Specific Impact

The article provides the analysis of the scientific and technical literature and the effectiveness of the use of organoplastics in aircraft structures as screens and coatings that provide protection of carbon parts from damage caused by shock and erosion. The paper examined the mechanical properties and the nature of impact fracture of carbon fiber-reinforced plastics samples without a cladding layer. It is shown that it is possible to increase the specific impact strength in bending by 22 % due to cladding of CFRP, and to reduce the area of damage by 30 % upon impact with a kinetic energy of 30 J.

Effects of high pressure on the crystallization of carbon fiber reinforced polyetheretherketone (CF/PEEK) laminate composites

1990 ◽  
Vol 48 (4) ◽  
pp. 876-877
Author(s):  
Hong-Ming Lin ◽  
C. H. Liu ◽  
R. F. Lee
Keyword(s):  
High Pressure ◽  
Carbon Fiber ◽  
Sample Surface ◽  
High Yield ◽  
Fiber Reinforced ◽  
Laminate Composites ◽  
Peek Composite ◽  
Continuous Carbon Fiber ◽  
Carbon Fiber Reinforced

Polyetheretherketone (PEEK) is a crystallizable thermoplastic used as composite matrix materials in application which requires high yield stress, high toughness, long term high temperature service, and resistance to solvent and radiation. There have been several reports on the crystallization behavior of neat PEEK and of CF/PEEK composite. Other reports discussed the effects of crystallization on the mechanical properties of PEEK and CF/PEEK composites. However, these reports were all concerned with the crystallization or melting processes at or close to atmospheric pressure. Thus, the effects of high pressure on the crystallization of CF/PEEK will be examined in this study.The continuous carbon fiber reinforced PEEK (CF/PEEK) laminate composite with 68 wt.% of fibers was obtained from Imperial Chemical Industry (ICI). For the high pressure experiments, HIP was used to keep these samples under 1000, 1500 or 2000 atm. Then the samples were slowly cooled from 420 °C to 60 °C in the cooling rate about 1 - 2 degree per minute to induce high pressure crystallization. After the high pressure treatment, the samples were scanned in regular DSC to study the crystallinity and the melting temperature. Following the regular polishing, etching, and gold coating of the sample surface, the scanning electron microscope (SEM) was used to image the microstructure of the crystals. Also the samples about 25mmx5mmx3mm were prepared for the 3-point bending tests.

Linear translaminar fracture characterization of additive manufactured continuous carbon fiber reinforced thermoplastic

2021 ◽  
pp. 089270572110214
Author(s):  
Weiller M Lamin ◽  
Flávio LS Bussamra ◽  
Rafael TL Ferreira ◽  
Rita CM Sales ◽  
José E Baldo
Keyword(s):  
Fracture Toughness ◽  
Carbon Fiber ◽  
Fracture Mechanics ◽  
Image Correlation ◽  
Fiber Reinforced ◽  
Fused Filament Fabrication ◽  
Critical Energy Release Rate ◽  
Linear Elastic ◽  
Continuous Carbon Fiber ◽  
Carbon Fiber Reinforced

This work presents the experimental determination of fracture mechanics parameters of composite specimens manufactured by fused filament fabrication (FFF) with continuous carbon fiber reinforced thermoplastic filaments, based on Linear Elastic Fracture Mechanics (LEFM). The critical mode I translaminar fracture toughness (KIc) and the critical energy release rate (GIc) are found for unidirectional and cross-ply laminates. The specimens were submitted to quasi-static tensile testing. Digital Image Correlation (DIC) is used to find the stress field. The stress fields around the crack tip are compared to linear elastic finite element simulations. The results demonstrate the magnitude of fracture toughness is in the same range as for polymers and some metals, depending on lay-up configuration. Besides, fractographic analyses show some typical features as river lines, fiber impression, fiber pulls-out and porosity aspects.

scholarly journals The Micro–Macro Interlaminar Properties of Continuous Carbon Fiber-Reinforced Polyphenylene Sulfide Laminates Made by Thermocompression to Simulate the Consolidation Process in FDM

Polymers ◽  
2022 ◽  
Vol 14 (2) ◽  
pp. 301
Author(s):  
Jiale Hu ◽  
Suhail Mubarak ◽  
Kunrong Li ◽  
Xu Huang ◽  
Weidong Huang ◽  
...  
Keyword(s):  
Carbon Fiber ◽  
3D Printing ◽  
Manufacturing Industry ◽  
Fused Deposition Modeling ◽  
Polyphenylene Sulfide ◽  
Fiber Reinforced ◽  
Continuous Fiber ◽  
Fused Deposition ◽  
Continuous Carbon Fiber ◽  
Carbon Fiber Reinforced

Three-dimensional (3D) printing of continuous fiber-reinforced composites has been developed in recent decades as an alternative means to handle complex structures with excellent design flexibility and without mold forming. Although 3D printing has been increasingly used in the manufacturing industry, there is still room for the development of theories about how the process parameters affect microstructural properties to meet the mechanical requirements of the printed parts. In this paper, we investigated continuous carbon fiber-reinforced polyphenylene sulfide (CCF/PPS) as feedstock for fused deposition modeling (FDM) simulated by thermocompression. This study revealed that the samples manufactured using a layer-by-layer process have a high tensile strength up to 2041.29 MPa, which is improved by 68.8% compared with those prepared by the once-stacked method. Moreover, the mechanical–microstructure characterization relationships indicated that the compactness of the laminates is higher when the stacked CCF/PPS are separated, which can be explained based on both the void formation and the nanoindentation results. These reinforcements confirm the potential of remodeling the layer-up methods for the development of high-performance carbon fiber-reinforced thermoplastics. This study is of great significance to the improvement of the FDM process and opens broad prospects for the aerospace industry and continuous fiber-reinforced polymer matrix materials.

scholarly journals Improvement in Mechanical Properties of Continuous Carbon Fiber Reinforced Polycarbonates by Ozone Oxidation Treatment

2016 ◽  
Vol 42 (5) ◽  
pp. 178-184 ◽  
Author(s):  
Hiroyuki OGUMA ◽  
Tomoya KUMAGAI ◽  
Daisuke SAKAMOTO ◽  
Masahiro SEKINE ◽  
Norio HIRAYAMA ◽  
...  
Keyword(s):  
Mechanical Properties ◽  
Carbon Fiber ◽  
Fiber Reinforced ◽  
Oxidation Treatment ◽  
Ozone Oxidation ◽  
Continuous Carbon Fiber ◽  
Carbon Fiber Reinforced