scholarly journals The granulating process as an effective way to increase demand for high calcium fly ash of a thermal power plant

2014 ◽  
Author(s):  
I. Domanskaya ◽  
F. Kapustin ◽  
V. Ufimtsev ◽  
V. Oleynik
Keyword(s):  
Fly Ash ◽  
Power Plant ◽  
Thermal Power Plant ◽  
Thermal Power ◽  
High Calcium ◽  
High Calcium Fly Ash

FLY ASH FROM THERMAL POWER PLANT, RAW MATERIAL FOR GLASS-CERAMIC

2013 ◽  
Vol 12 (2) ◽  
pp. 337-342 ◽  
Author(s):  
Firuta Goga ◽  
Roxana Dudric ◽  
Calin Cormos ◽  
Florica Imre ◽  
Liliana Bizo ◽  
...  
Keyword(s):  
Fly Ash ◽  
Power Plant ◽  
Glass Ceramic ◽  
Thermal Power Plant ◽  
Thermal Power ◽  
Raw Material ◽  
Plant Raw Material

scholarly journals THE USE OF ASH FROM THERMAL POWER PLANT DUMPS IN THE PRODUCTION OF PORTLAND CEMENT

2022 ◽  
Vol 1 (15) ◽  
pp. 171-174
Author(s):  
Andrey Savenkov ◽  
Viktorya Kolomiets
Keyword(s):  
Fly Ash ◽  
Power Plant ◽  
Portland Cement ◽  
Thermal Power Plant ◽  
Energy Intensity ◽  
Thermal Power ◽  
Technical Solution

The article considers a technical solution for the introduction of pozzolan additives into the cement after grinding clinker. Such additives are the fly ash of the CHP and ash from the ash dump. The use of ash in the composition of cement reduces its cost and energy intensity of its production

scholarly journals Reactivity of fly ashes milled in different milling devices

2019 ◽  
Vol 58 (1) ◽  
pp. 179-188 ◽  
Author(s):  
Yong-Sik Chu ◽  
Batmunkh Davaabal ◽  
Dae-Sung Kim ◽  
Sung-Kwan Seo ◽  
Yoo Kim ◽  
...  
Keyword(s):  
Particle Size ◽  
Fly Ash ◽  
Surface Area ◽  
Thermal Power ◽  
Chemical Properties ◽  
Particle Size Reduction ◽  
Attrition Mill ◽  
High Calcium ◽  
High Calcium Fly Ash ◽  
Physical And Chemical

Abstract The effect of two different milling devices, namely attrition mill versus vibration mill, on the reactivity of fly ash was studied. High calcium fly ash from 4th Thermal power station of Ulaanbaatar (Mongolia) was used for the experiments. The raw and processed samples were characterized by XRD, SEM, Particle size distribution, BET, Blaine surface area and density measurements. The efficiency of 1 hour milling was evaluated with the Blaine surface area set to be more than 5000 cm2/g. The physical and chemical properties of the attrition milled fly ash changed not much compared to the vibration milled samples. For example the d50 particle size became reduced from 29 µm to 6 µm by attrition milling and in vibration milled fly ash it was reduced to 7 µm. The density increased from 2.44 g/cm3 of raw fly ash to 2.84 g/cm3 and 2.79 g/cm3 in attrition and vibration milled samples, respectively. Mechanical milling revealed not only a particle size reduction but also the formation of a denser microstructure. As a result the vibration milled fly ash showed a weaker interaction with the alkaline solution (8 M NaOH used here) compared to the attrition milled fly ash. Consequently, compressive strength of the binder prepared using the attrition milled fly ash was higher, 61 MPa, while for vibration milled fly ash it was 49 MPa. For comparison unmilled fly ash, it was 21 MPa.

Sign in / Sign up

Export Citation Format

Share Document