Microstructure and mechanical properties of laser-welded joints of Ti-22Al-25Nb/Ti-6Al-4V dissimilar titanium alloys

2018 ◽  
Vol 30 (3) ◽  
pp. 032412
Author(s):  
Lingda Xiong ◽  
Gaoyang Mi ◽  
Chunming Wang
Keyword(s):  
Mechanical Properties ◽  
Titanium Alloys ◽  
Welded Joints ◽  
Microstructure And Mechanical Properties

MICROSTRUCTURE AND MECHANICAL PROPERTIES OF DIFFUSION CONNECTIONS FROM Ti6Al4V AND Ti6.5Al2Zr1Mo1V TITANIUM ALLOYS

Metallurg ◽  
2021 ◽  
pp. 61-66
Author(s):  
A.Ya. Travyanov ◽  
P.V. Petrovsky ◽  
V.V. Cheverikin ◽  
A.O. Lagutin ◽  
M.G. Khomutov ◽  
...  
Keyword(s):  
Mechanical Properties ◽  
Titanium Alloys ◽  
Microstructure And Mechanical Properties

Investigation on the microstructure and mechanical properties of Ti6Al4V titanium alloy electron beam welding joint

2022 ◽  
pp. 095440622110329
Author(s):  
Xilong Zhao ◽  
Xinhong Lu ◽  
Kun Wang ◽  
Feng He
Keyword(s):  
Mechanical Properties ◽  
Titanium Alloy ◽  
Electron Beam ◽  
Penetration Depth ◽  
Welding Speed ◽  
Welded Joints ◽  
Electron Beam Welding ◽  
Martensite Phase ◽  
Ti6al4v Titanium Alloy ◽  
Microstructure And Mechanical Properties

Electron beam welding (EBW) is a fusion joining process particularly suitable for welding titanium plates. In the present work, 2.5 mm thickness Ti6Al4V titanium alloy plates were butt-welded together with backing plates by EBW. The detailed procedures of experiments were used to investigate the microstructure and mechanical properties of welded joints. The optimum welding speed was determined by microstructure examinations, microhardness tests, X-Ray diffraction tests, shear punch tests (SPT) and stress simulation calculations. The results showed that all microstructure of welded metal (WM) was martensite phase under the different welding speeds. In the heat-affected zone (HAZ), the martensite phase gradually evolved to be small and equiaxed. It can be seen that the microstructure of each region in welded joints did not change significantly. When the welding speed is between 8 mm/s and 14 mm/s, it can be seen from the macroscopic appearance of the joints that there was no utterly fused penetration between the butt plate and substrate. Finite element simulation was carried out for the no-penetration depth under different welding conditions, and it was found that the stress suffered by the small no-penetration depth was the smallest. Using different welding parameters shows that the engineering stress in WM was higher than other areas, and BM was the lowest. As welding speed increases from 8 mm/s to 14 mm/s, the variation of microhardness distribution was not evident.

Microstructure and mechanical properties of as cast titanium alloys with high elastic modulus

2014 ◽  
Vol 18 (sup4) ◽  
pp. S4-212-S4-214
Author(s):  
Y. L. Qi ◽  
L. Y. Zeng ◽  
Z. M. Hou ◽  
Q. Hong ◽  
S. B. Liu ◽  
...  
Keyword(s):  
Mechanical Properties ◽  
Elastic Modulus ◽  
Titanium Alloys ◽  
High Elastic Modulus ◽  
Microstructure And Mechanical Properties
Sign in / Sign up

Export Citation Format

Share Document