The Influence of Surface Standardization of Lithium Disilicate Glass Ceramic on Bond Strength to a Dual Resin Cement

2011 ◽  
Vol 36 (5) ◽  
pp. 478-485 ◽  
Author(s):  
R Brum ◽  
R Mazur ◽  
J Almeida ◽  
G Borges ◽  
D Caldas
Keyword(s):  
Silicon Carbide ◽  
Bond Strength ◽  
Hydrofluoric Acid ◽  
Shear Bond Strength ◽  
Resin Cement ◽  
The Other ◽  
Ceramic Surfaces ◽  
Post Hoc ◽  
Diamond Paste

SUMMARY In vitro studies to assess bond strength between resins and ceramics have used surfaces that have been ground flat to ensure standardization; however, in patients, ceramic surfaces are irregular. The effect of a polished and unpolished ceramic on bond strength needs to be investigated. Sixty ceramic specimens (20×5×2 mm) were made and divided into two groups. One group was ground with 220- to 2000-grit wet silicon carbide paper and polished with 3-, 1-, and ¼-μm diamond paste; the other group was neither ground nor polished. Each group was divided into three subgroups: treated polished controls (PC) and untreated unpolished controls (UPC), polished (PE) and unpolished specimens (UPE) etched with hydrofluoric acid, and polished (PS) and unpolished specimens (UPS) sandblasted with alumina. Resin cement cylinders were built over each specimen. Shear bond strength was measured, and the fractured site was analyzed. Analysis of variance (ANOVA) and Tukey post hoc tests were performed. PE (44.47 ± 5.91 MPa) and UPE (39.70 ± 5.46 MPa) had the highest mean bond strength. PS (31.05 ± 8.81 MPa), UPC (29.11 ± 8.11 MPa), and UPS (26.41 ± 7.31 MPa) were statistically similar, and PC (24.96 ± 8.17 MPa) was the lowest. Hydrofluoric acid provides the highest bond strength regardless of whether the surface is polished or not.

scholarly journals Effect of surface treatment on the shear bond strength of a resin-based cement to porcelain

2006 ◽  
Vol 17 (4) ◽  
pp. 290-295 ◽  
Author(s):  
Marcos Paulo Nagayassu ◽  
Luciana Keiko Shintome ◽  
Eduardo Shigueyuki Uemura ◽  
José Eduardo Junho de Araújo
Keyword(s):  
Bond Strength ◽  
Surface Treatment ◽  
Hydrofluoric Acid ◽  
Shear Bond Strength ◽  
In Vitro Study ◽  
Resin Cement ◽  
Vitro Study ◽  
Acid Etching ◽  
And Control

The purpose of this in vitro study was to evaluate the effect of different surface treatments on the shear bond strength of a resin-based cement to porcelain. Sixty pairs of 50% aluminous porcelain discs were fabricated. In each pair, one disc measured 6 mm in diameter X 3 mm thickness (A) and the other measured 3 mm in diameter X 3mm thickness (B). The specimens were randomly assigned to 6 groups (n=10 pairs of discs), according to the surface treatment: etching with 10% hydrofluoric acid for 2 or 4min (G1 and G2); 50-µm particle aluminum oxide sandblasting for 5 s (G3); sandblasting followed by etching for 2 or 4min (G4 and G5) and control - no treatment (G6). A silane agent was applied to the treated surface of both discs of each pair. Bistite II DC dual-cure resin cement was applied and the B discs were bonded to their respective A discs. Specimens were stored in distilled water at 37ºC for 24 h and were tested in shear strength at a crosshead speed of 2 mm/min. Means in MPa were: G1: 14.21 ± 4.68; G2: 8.92 ± 3.02; G3: 10.04 ± 2.37; G4: 12.74 ± 5.15; G5: 10.99 ± 3.35; G6: 6.09 ± 1.84. Data were compared by one-way ANOVA and Tukey's test at 5% significance level. Bond strength recorded after 2-min acid etching was significantly higher than 4-min etching (p<0.05) and control (p<0.05), but did not differ significantlyfrom sandblasting alone (p>0.05) or followed by etching for 2 or 4 min (p>0.05). Within the limitations of an in vitro study, it may be concluded that 2-min hydrofluoric acid etching produced a favorable micromechanical retention that enhanced resin cement bond strength to porcelain.

scholarly journals Comparison of Shear Bond Strength of Metal Brackets Bonded to Porcelain Surface using Different Surface Conditioning Methods: An in vitro Study

2012 ◽  
Vol 13 (4) ◽  
pp. 487-493 ◽  
Author(s):  
PV Girish ◽  
Uma Dinesh ◽  
CS Ramachandra Bhat ◽  
Pradeep Chandra Shetty
Keyword(s):  
Bond Strength ◽  
Hydrofluoric Acid ◽  
Shear Bond Strength ◽  
Orthodontic Brackets ◽  
Control Group ◽  
Ceramic Surface ◽  
Bond Failure ◽  
Surface Conditioning ◽  
Ceramic Surfaces

ABSTRACT Aim To evaluate and compare the shear bond strength of metal brackets bonded to ceramic surfaces using different conditioning methods and to assess the site of bond failure after debonding. Materials and methods A total of 70 ceramic surfaces were produced with uniform shape, size and composition. The samples were divided into 7 groups (each of 10 samples). Group 1 was the control group (untreated surface); in group 2 the surface were roughened with a diamond bur; in group 3 the surface were etched with hydrofluoric acid; in group 4 the surfaces were sandblasted; in group 5 the surfaces roughened with bur and silane applied; in group 6 the surfaces were etched with hydrofluoric acid and silane applied and in group 7 the surfaces were sandblasted and silane applied. To all the above groups, metal orthodontic brackets were bonded with light cure adhesive. The brackets were later stored in artificial saliva and incubated at 37°C (24 hours). The samples were then subjected to shear bond strength test using an Instron universal testing machine. The debonded porcelain surfaces were then studied under stereomicroscope to assess site of bond failure. Results Sandblasting the ceramic surface and silane application showed the highest bond strength. Stereomicroscope examination after debonding showed that the bond failure is at bracket-adhesive interface in four groups namely hydrofluoric acid, sandblasting, hydrofluoric acid with silane and sandblasting with silane. Conclusion Sandblasting with silane combination produced the highest shear bond strength, so it is a clinically suitable method for bonding orthodontic metal brackets onto ceramic surface. Clinical relevance Bonding orthodontic brackets to ceramic crowns of patients has been a tough task. In this study, different conditioning methods were used to treat the ceramic surfaces before bonding. The results showed that sandblasting the ceramic surface prior to application of silane produced the highest shear bond strength which is clinically suitable to reduce bond failures. How to cite this article Girish PV, Dinesh U, Bhat CSR, Shetty PC. Comparison of Shear Bond Strength of Metal Brackets Bonded to Porcelain Surface using Different Surface Conditioning Methods: An in vitro Study. J Contemp Dent Pract 2012;13(4):487-493.

scholarly journals Influence of different treatments of the ceramic surface and thermal cycling on the bond strength of brackets to ceramic

2017 ◽  
Vol 46 (3) ◽  
pp. 179-183
Author(s):  
Fernando Guerra SÁEZ ◽  
Ana Rosa COSTA ◽  
Adriana Simoni LUCATO ◽  
Ana Paula Terossi de GODOI ◽  
Lourenço CORRER-SOBRINHO ◽  
...  
Keyword(s):  
Bond Strength ◽  
Thermal Cycling ◽  
Hydrofluoric Acid ◽  
Shear Bond Strength ◽  
Deionized Water ◽  
Acid Etching ◽  
Ceramic Surface ◽  
Thermal Cycler ◽  
Post Hoc

Abstract Objective To evaluate in vitro the effect of different treatments of the ceramic surface and thermal cycling on the shear bond strength (SBS) of metallic brackets bonded to feldspathic ceramic. Material and method Ceramic cylinders were divided into four groups (n=4) according to the treatment of ceramic surface: G1-Clearfil Ceramic Primer silane and Transbond XT (CCPT); G2-etched with 10% hydrofluoric acid (HFA) for 60 s, CCP and Transbond XT (ACCPT); G3-etched with 10% HFA for 60 s, Ambar Adhesive and Transbond XT (AAAT); and, G4 - etched with 10% HFA for 60 s, RelyX Ceramic Primer silane -RCP, adhesive primer Transbond and Transbond XT (ACPPT). Brackets were bonded to the cylinders with Transbond XT and light-activated for 40 s with LED Radii Plus. All specimens were stored in deionized water at 37 °C for 24 h, and two cylinders from each group were subject to 7,000 thermal cycles in a thermal cycler (5 °C/55 °C). After storage and thermal cycling, the SBS test was performed at a crosshead speed of 1 mm/min. Data were subjected to two-way ANOVA and Tukey’s post hoc test (α=0.05). Result The SBS of ACCPT was significantly higher than the other groups (p<0.05). The specimens submitted to thermal cycling showed significantly lower SBS than those without thermal cycling (p<0.05), regardless the ceramic surface treatment. The ARI showed predominance of score 0 for all groups. Conclusion Acid etching, CCP silane and Transbond XT method obtained the best results for bracket bonding. Thermal cycling reduced SBS for all groups. Score 0 was predominant for ARI in all groups.

scholarly journals Influence of adhesive and thermal cycling on the bond strength of ceramic brackets to dental ceramic

2017 ◽  
Vol 15 (2) ◽  
pp. 176
Author(s):  
Patricia de Fátima Fraga ◽  
Ana Paula Terossi de Godoi ◽  
Ana Rosa Costa ◽  
Lourenço Correr-Sobrinho ◽  
Mario Vedovello Filho ◽  
...  
Keyword(s):  
Bond Strength ◽  
Thermal Cycling ◽  
Hydrofluoric Acid ◽  
Shear Bond Strength ◽  
In Vitro Study ◽  
Single Bond ◽  
Adhesive Remnant Index ◽  
Ceramic Brackets ◽  
Post Hoc

Aim: This in vitro study investigated the effect of the application of an adhesive, silane and thermal cycling (TC) on the shear bond strength (SBS) of ceramic brackets to feldspathic ceramic. Methods: 16 cylinders of feldspathic ceramic were etched with hydrofluoric acid and divided into four groups (n=4): G1 - silane, without TC; G2 – silane, with TC; G3 - adhesive, without TC; G4 - adhesive, with TC. One layer of silane was applied on the surface of cylinders in G1 and G2 e one layer of photo-activated adhesive Single Bond Universal was used in G3 and G4. Ceramic brackets were bonded using Transbond XT. The SBS data were subjected to two-way ANOVA and Tukey’s post hoc test (α=0.05). The Adhesive Remnant Index (ARI) was evaluated at 40× magnification. Results: Silane was more effective than adhesive on the SBS of the brackets to ceramic (p<0.05). TC decreased significantly the SBS values compared with the groups without TC (p<0.05). The ARI results showed predominance of score 0. Conclusions: Groups with silane showed higher SBS than groups with adhesive. TC influence significantly on the bond strength. Regarding ARI, score 0 predominated in all groups.

scholarly journals Influence of irradiation with Er:YAG laser on the shear bond strength of a resin cement to feldspathic ceramic - in vitro study

Cerâmica ◽  
2015 ◽  
Vol 61 (358) ◽  
pp. 244-250 ◽  
Author(s):  
M. C. Loffredo ◽  
F. S. Hanashiro ◽  
W. Steagall Júnior ◽  
M. N. Youssef ◽  
W. C. de Souza-Zaroni
Keyword(s):  
Bond Strength ◽  
Hydrofluoric Acid ◽  
Shear Bond Strength ◽  
Er:Yag Laser ◽  
In Vitro Study ◽  
Surface Treatments ◽  
Resin Cement ◽  
Air Abrasion ◽  
Yag Laser

<p>Although several conventional surface treatments have been used on feldspathic ceramic, a few studies investigated the effects of the irradiation with Er: YAG laser using different parameters. The aim of this in vitro study was to evaluate the shear bond strength of a resin cement to feldspathic ceramic, after the application of different surface treatments, especially the irradiation with Er:YAG laser. Forty-two discs made of a feldspathic ceramic were divided into six groups (n = 7): G1: control group - 10% hydrofluoric acid (HF), G2: Air abrasion with Al2O3 + HF; G3: Er: YAG laser with 500 mJ/4Hz, G4: Er: YAG laser with 500 mJ/4Hz: + HF; G5: Er: YAG laser with 400 mJ/6Hz and G6: Er:YAG laser with 400 mJ/6Hz + HF. After this, all the specimens were treated with silane, and then a resin cement cylinder was built on the treated ceramic surface. After 24 h at 37 oC, specimens were submitted to the shear bond strenght test and stereoscopic evaluation to determine the type of failure. The mean bond strength values (MPa) obtained were: G1 - 17.55, G2 - 18.80, G3 - 21.80, G4 - 12.62, G5 - and 15.81 G6- 11.59. After performing the ANOVA and Tukey's test, it was concluded that the group irradiated with Er:YAG laser at 500mJ/4Hz performed similarly to the groups that received the conventional treatments, such as hydrofluoric acid etching and the combination of air abrasion plus hydrofluoric acid, and was higher than the other groups irradiated with Er:YAG laser.</p>

scholarly journals Effects of Universal Adhesive on Shear Bond Strength of Resin Cement to Zirconia Ceramic with Different Surface Treatments

2021 ◽  
Vol 2021 ◽  
pp. 1-6
Author(s):  
Zohreh Moradi ◽  
Farnoosh Akbari ◽  
Sara Valizadeh
Keyword(s):  
Bond Strength ◽  
Shear Bond Strength ◽  
Testing Machine ◽  
In Vitro Study ◽  
Surface Treatments ◽  
Resin Cement ◽  
Zirconia Ceramic ◽  
Single Bond ◽  
Universal Adhesive

Aim. This study aimed to assess shear bond strength (SBS) of resin cement to zirconia ceramic with different surface treatments by using Single Bond Universal. Methods. In this in vitro study, 50 zirconia discs (2 × 6 mm) were divided into 5 groups of (I) sandblasting with silica-coated alumina (CoJet)  + silane + Single Bond 2, (II) sandblasting with CoJet + Single Bond Universal, (III) sandblasting with alumina + Single Bond Universal, (IV) sandblasting with alumina + Z-Prime Plus, and (V) Single Bond Universal with no surface treatment. Resin cement was applied in plastic tubes (3 × 5 mm2), and after 10,000 thermal cycles, the SBS was measured by a universal testing machine. The mode of failure was determined under a stereomicroscope at × 40 magnification. Data were analyzed using one-way ANOVA. Results. The maximum (6.56 ± 4.29 MPa) and minimum (1.94 ± 1.96 MPa) SBS values were noted in groups III and I, respectively. Group III had the highest frequency of mixed failure (60%). Group V had the maximum frequency of adhesive failure (100%). Conclusion. Single Bond Universal + sandblasting with alumina or silica-coated alumina particles is an acceptable method to provide a strong SBS between resin cement and zirconia.

scholarly journals Effects of different etching methods and bonding procedures on shear bond strength of orthodontic metal brackets applied to different CAD/CAM ceramic materials

2017 ◽  
Vol 88 (2) ◽  
pp. 221-226 ◽  
Author(s):  
S. Kutalmış Buyuk ◽  
Ahmet Serkan Kucukekenci
Keyword(s):  
Bond Strength ◽  
Hydrofluoric Acid ◽  
Shear Bond Strength ◽  
Ceramic Materials ◽  
Ceramic Surface ◽  
Bonding Agents ◽  
Ceramic Surfaces ◽  
Different Types ◽  
Cad Cam ◽  
Hybrid Ceramic

ABSTRACT Objective: To investigate the shear bond strength (SBS) of orthodontic metal brackets applied to different types of ceramic surfaces treated with different etching procedures and bonding agents. Materials and Methods: Monolithic CAD/CAM ceramic specimens (N = 120; n = 40 each group) of feldspathic ceramic Vita Mark II, resin nanoceramic Lava Ultimate, and hybrid ceramic Vita Enamic were fabricated (14 × 12 × 3 mm). Ceramic specimens were separated into four subgroups (n = 10) according to type of surface treatment and bonding onto the ceramic surface. Within each group, four subgroups were prepared by phosphoric acid, hydrofluoric acid, Transbond XT primer, and Clearfill Ceramic primer. Mandibular central incisor metal brackets were bonded with light-cure composite. The SBS data were analyzed using three-way analysis of variance (ANOVA) and Tukey HSD tests. Results: The highest SBS was found in the Vita Enamic group, which is a hybrid ceramic, etched with hydrofluoric acid and applied Transbond XT Adhesive primer (7.28 ± 2.49 MPa). The lowest SBS was found in the Lava Ultimate group, which is a resin nano-ceramic etched with hydrofluoric acid and applied Clearfill ceramic primer (2.20 ± 1.21 MPa). Conclusions: CAD/CAM material types and bonding procedures affected bond strength (P &lt; .05), but the etching procedure did not (P &gt; .05). The use of Transbond XT as a primer bonding agent resulted in higher SBS.

scholarly journals Shear Bond Strength Comparison between Two Orthodontic Adhesives and Self-Ligating and Conventional Brackets

2007 ◽  
Vol 77 (4) ◽  
pp. 701-706 ◽  
Author(s):  
Rodney G. Northrup ◽  
David W. Berzins ◽  
Thomas Gerard Bradley ◽  
William Schuckit
Keyword(s):  
Bond Strength ◽  
Shear Bond Strength ◽  
Orthodontic Adhesives ◽  
Significant Difference ◽  
Conventional Brackets ◽  
Group 3 ◽  
Group 2 ◽  
Post Hoc ◽  
Group 1

Abstract Objective: To evaluate and compare the shear bond strengths of two adhesives using two types of brackets: a conventional and a self-ligating bracket system. Materials and Methods: Sixty extracted human premolars were collected. The premolars were randomly divided into three groups of 20 teeth. All three groups were direct bonded. Groups 1 and 2 used light-cured adhesive and primer (Transbond XT) with a conventional (Orthos) and a self-ligating bracket (Damon 2), respectively. Group 3 used a light-cured primer (Orthosolo) and a light-cured adhesive (Blūgloo) with a self-ligating bracket (Damon 2). The specimens were stored in distilled water at 37°C for 40 ± 2 hours, after which they were debonded and inspected for Adhesive Remnant Index (ARI) scoring. Results: The mean shear bond strength was 15.2 MPa for group 1, 23.2 MPa for group 2, and 24.8 MPa for group 3. A one-way analysis of variance and post hoc Tukey test showed significant differences in bond strength (P &lt; .001) between group 1 and groups 2 and 3 but no significant difference (P &gt; .05) between groups 2 and 3. A Weibull analysis demonstrated that all three groups provided sufficient bond strength with over 90% survival rate at normal masticatory and orthodontic force levels. A Kruskal-Wallis test showed no significant difference (P &gt; .05) in ARI scores among all three groups. Conclusions: All three groups demonstrated clinically acceptable bond strength. The Damon 2 self-ligating bracket exhibited satisfactory in vitro bond strength with both adhesive systems used.

scholarly journals The Effect of Hydrofluoric Acid Concentration and Heat on the Bonding to Lithium Disilicate Glass Ceramic

2016 ◽  
Vol 27 (6) ◽  
pp. 727-733 ◽  
Author(s):  
Daniel Sundfeld ◽  
Lourenço Correr-Sobrinho ◽  
Núbia Inocêncya Pavesi Pini ◽  
Ana Rosa Costa ◽  
Renato Herman Sundfeld ◽  
...  
Keyword(s):  
Bond Strength ◽  
Glass Ceramic ◽  
Hydrofluoric Acid ◽  
Lithium Disilicate ◽  
Resin Cement ◽  
Glassy Matrix ◽  
Etching Time ◽  
Sem Images ◽  
Matrix Removal ◽  
Post Hoc

Abstract The aim of this study was to evaluate the effects of hydrofluoric acid (HF) concentration and previous heat treatment (PHT) on the surface morphology and micro-shear bond strength (mSBS) of a lithium disilicate glass ceramic (EMX) to resin cement. One hundred four EMX specimens were randomly assigned to two groups (n=52) according to the HF concentration: 5% and 10%. A new random distribution was made according to the PHTs (n=13): control (no PHT); previously heated HF (70 °C); previously heated EMX surface (85 °C); the combination of heated HF + heated EMX surface. The etching time was set at 20 s. All EMX blocks were silanated and received a thin layer of an unfilled resin. Five resin cement cylinders were made on each EMX surface using Tygon tubes as matrices, and then stored for 24 h at 37 °C. One random etched EMX sample from each group was analyzed using field-emission scanning electron microscopy (FE-SEM). The data were subjected to two-way ANOVA and multiple comparisons were performed using the Tukey post hoc test (a=0.05). For the control groups, 5% HF showed statistically lower mSBS values when compared to 10% HF (p<0.05). PHT increased the mSBS values for 5% HF, yielding statistically similar results to non-PHT 10% HF (p<0.05). FE-SEM images showed increased glassy matrix removal when PHT was applied to HF 5%, but not to the same degree as for 10% HF. PHT has the potential to improve the bond strength of 5% HF concentration on lithium disilicate glass ceramic.

scholarly journals Effect of Acid Etching, Silane and Thermal Cycling on the Bond Strength of Metallic Brackets to Ceramic

2016 ◽  
Vol 27 (6) ◽  
pp. 734-738 ◽  
Author(s):  
Natália Regina Santos de Matos ◽  
Ana Rosa Costa ◽  
Heloísa Cristina Valdrighi ◽  
Américo Bortolazzo Correr ◽  
Silvia Amélia Vedovello ◽  
...  
Keyword(s):  
Bond Strength ◽  
Thermal Cycling ◽  
Surface Treatment ◽  
Hydrofluoric Acid ◽  
Shear Bond Strength ◽  
Deionized Water ◽  
Acid Etching ◽  
Ceramic Surface ◽  
Adhesive Remnant Index ◽  
Post Hoc

Abstract The aim of this study was to evaluate the effect of silanes, thermal cycling and acid etching on the shear bond strength (SBS) of metallic brackets to feldspathic ceramic. Feldspathic ceramic cylinders (Groups 1, 2, 5 and 6) were etched for 60 s with 10% hydrofluoric acid and Groups 3, 4, 7 and 8, without acid etching. Two layers of silane Clearfil Ceramic Primer (CCP, Groups 1 to 4) and two layers of RelyX Ceramic Primer (RCP, groups 5 to 8) were applied and dried for 60 s. Brackets were bonded to the cylinders with Transbond XT and light-activated for 40 s with Bluephase G2. All specimens were stored in deionized water at 37 °C for 24 h, and the specimens of groups 1, 3, 5 and 7 were submitted to 7,000 thermal cycles (5 °C/55 °C). After storage, the SBS test was performed at a crosshead speed of 1 mm/min. Data were subjected to three-way ANOVA and Tukey's post hoc test (α=0.05). The adhesive remnant index (ARI) was evaluated at 8x magnification. The SBS of CCP was significantly greater than of RCP (p<0.05), with or without thermal cycling. Thermal cycling significantly reduced the SBS (p<0.05). The groups submitted to acid etching showed significantly higher SBS than those without acid etching (p<0.05). In conclusion, thermal cycling reduced SBS for all groups. The best ceramic surface treatment for bracket bonding was achieved by acid etching and CCP silane. The ARI results showed predominance of score 0 for all groups.