scholarly journals Low-temperature tension properties of glass-epoxy composite materials

2005 ◽  
pp. 123-134
Author(s):  
Slavisa Putic ◽  
Marina Stamenovic ◽  
Branislav Bajceta ◽  
Predrag Stajcic ◽  
Srdjan Bosnjak
Keyword(s):  
Tensile Strength ◽  
Composite Material ◽  
Composite Materials ◽  
Room Temperature ◽  
Epoxy Composite ◽  
Epoxy Composites ◽  
Tension Properties ◽  
Different Temperatures ◽  
Stereo Microscope

The aim of this paper was to present the determination of tensile strength Rm and modulus of elasticity Et of glass-epoxy composites at two different temperatures (at room temperature t=20?C, and at t =?50?C). Standard mechanical testing was carried out on glass woven-epoxy composite material with different structures (two specific weights of reinforcement, 210 g/m2 and 550 g/m2) and orientations (0?/90? and ?45?). Micromechanical analysis of failure was performed on a stereo microscope and SEM in order to determine real models and mechanisms of crack.

scholarly journals Tension mechanical properties of recycled glass-epoxy composite material

2012 ◽  
pp. 189-198 ◽  
Author(s):  
Jelena Petrovic ◽  
Darko Ljubic ◽  
Marina Stamenovic ◽  
Ivana Dimic ◽  
Slavisa Putic
Keyword(s):  
Mechanical Properties ◽  
Tensile Strength ◽  
Composite Material ◽  
Composite Materials ◽  
Modulus Of Elasticity ◽  
Epoxy Composite ◽  
Raw Materials ◽  
Mechanical Tests ◽  
Recycled Glass ◽  
Before And After

The significance of composite materials and their applications are mainly due to their good properties. This imposes the need for their recycling, thus extending their lifetime. Once used composite material will be disposed as a waste at the end of it service life. After recycling, this kind of waste can be used as raw materials for the production of same material, which raises their applicability. This indicates a great importance of recycling as a method of the renowal of composite materials. This study represents a contribution to the field of mechanical properties of the recycled composite materials. The tension mechanical properties (tensile strength and modulus of elasticity) of once used and disposed glass-epoxy composite material were compared before and after the recycling. The obtained results from mechanical tests confirmed that the applied recycling method was suitable for glass-epoxy composite materials. In respect to the tensile strength and modulus of elasticity it can be further assessed the possibility of use of recycled glass-epoxy composite materials.

scholarly journals The influence of high and low temperatures on the impact properties of glass-epoxy composites

2007 ◽  
Vol 72 (7) ◽  
pp. 713-722 ◽  
Author(s):  
Slavisa Putic ◽  
Marina Stamenovic ◽  
Branislav Bajceta ◽  
Predrag Stajcic ◽  
Srdjan Bosnjak
Keyword(s):  
Low Temperatures ◽  
Composite Structures ◽  
Room Temperature ◽  
Epoxy Composite ◽  
Epoxy Composites ◽  
Temperature Influence ◽  
Impact Properties ◽  
Different Temperatures ◽  
High And Low Temperatures ◽  
The Impact

The aim of this paper is to present the influence of high and low temperatures on the impact properties glass-epoxy composites. The impact strength an is presented for four different glass-epoxy composite structures at three different temperatures, i.e., at room temperature t=20?C, at an elevated temperature t=+50?C and at a low temperature t=-50?C. Standard mechanical testing was carried out on the composite materials with specific masses of reinforcement of 210 g m-2 and 550 g m-2 and orientations 0?/90? and ?45?. Micromechanical analysis of the failure was performed in order to determine real models and mechanisms of crack and temperature influence on the impact properties. .

The Estimation of Thermal Conductivity for Alumina-Epoxy Composite Material with High Filling Volume Fraction

2014 ◽  
Vol 918 ◽  
pp. 21-26
Author(s):  
Chen Kang Huang ◽  
Yun Ching Leong
Keyword(s):  
Thermal Conductivity ◽  
Composite Material ◽  
Composite Materials ◽  
Physical Model ◽  
Electron Scattering ◽  
Volume Fraction ◽  
Epoxy Composite ◽  
The Matrix ◽  
Transport Theorem ◽  
Good Agreement

In this study, the transport theorem of phonons and electrons is utilized to create a model to predict the thermal conductivity of composite materials. By observing or assuming the dopant displacement in the matrix, a physical model between dopant and matrix can be built, and the composite material can be divided into several regions. In each region, the phonon or electron scattering caused by boundaries, impurities, or U-processes was taken into account to calculate the thermal conductivity. The model is then used to predict the composite thermal conductivity for several composite materials. It shows a pretty good agreement with previous studies in literatures. Based on the model, some discussions about dopant size and volume fraction are also made.

scholarly journals The Influence of Composite Polymeric Materials Topology Over the Shearing Modulus Using Virtual Instruments

2018 ◽  
Vol 55 (4) ◽  
pp. 524-530
Author(s):  
Marinela Marinescu ◽  
Larisa Butu ◽  
Claudia Borda ◽  
Delicia Arsene ◽  
Mihai Butu
Keyword(s):  
Composite Material ◽  
Composite Materials ◽  
Virtual Instrument ◽  
Mechanical Characteristics ◽  
Polymeric Materials ◽  
Mechanical Impedance ◽  
Impedance Analysis ◽  
Cross Linking ◽  
Labview Software ◽  
Different Temperatures

This study presents research regarding the calculation of the mechanical characteristics of composite polymeric materials. By using LabVIEW� software a virtual instrument was created used for monitoring in real time the process of cross-linking the composite polymeric materials. The experiments were realized based on composite materials containing epoxy/fiberglass resin of different topologies. By means of the virtual instrument and of a sensor created based on the mechanical impedance analysis, implanted in the composite material, it was determined the G shearing module of the composite material at different temperatures.

scholarly journals Pengaruh Campuran dan Rasio Bahan Pembentuk Komposit terhadap Karakteristik Komposit Bioplastik

2021 ◽  
Vol 9 (2) ◽  
pp. 157
Author(s):  
Syah Banu Putra Sitepu ◽  
Bambang Admadi Harsojuwono ◽  
Amna Hartiati
Keyword(s):  
Tensile Strength ◽  
Composite Material ◽  
Composite Materials ◽  
Design Method ◽  
Block Design ◽  
Elongation At Break ◽  
Factor I ◽  
Method Factor ◽  
Randomized Block Design ◽  
Multiple Comparison Test

This research aims to determine the effect of the mixture and the ratio of the composites and their interactions to the characteristics of the bioplastic composites and to determine the mix and ratio of the composites that produce the best characteristics of the bioplastic composites. The experimental design of this study used a randomized block design method. Factor I is a mixture of composite materials consisting of maizena-glucomannan, maizena-chitosan, and maizena-carrageenan. The second factor is the ratio of the composite material mixture which consists of 5 levels, namely 100: 0, 75:25, 50:50, 25:75 and 0: 100. The experiment resulted in 15 treatment combinations and were grouped into 2 groups when the process of making bioplastic composites was obtained, so that 30 experimental units were obtained. Data were analyzed for their diversity and continued with Duncan's multiple comparison test. The observed variables which tensile strength, elongation at break, modulus young, swelling, and biodegradation time. The results showed that the mixture and the ratio of the composites forming a very significant effect on tensile strength, elongation at break, elasticity, and swelling. The interaction has a very significant effect on tensile strength, elasticity and swelling and significantly affects the elongation at break of bioplastic composites. Meanwhile, the mixture and the ratio of the ingredients to form the composites had no significant effect on the biodegradation time. Maizena:glucomannan composite with ratio (25:75) produced the best characteristics of bioplastic composites with tensile strength values of 6.99 MPa, elongation at break of 16.5%, elasticity 42.39 MPa, swelling 78.78% and biodegradable time of 7 days. There are 2 variables that have met the standard, namely: elongation at break of bioplastic composites that meet the plastic Standard SNI 7188.7: 2016 and biodegradation time has met the international plastic standard ASTM 5336 and 3 variables that do not meet the standards, namely: Tensile strength (6,99 MPa) and elasticity (42,39 MPa) do not meet the Plastic Standard SNI 7188.7: 2016 and swelling (39,1%) does not meet international plastic standards (EN 317). Keywords : bioplastic composites, maizena, glucomannan, chitosan, carrageenan

scholarly journals Experimental and Numerical Study on the Effect of Creep Behavior on Epoxy Composites Reinforced with Yttrium Oxide Powder

2020 ◽  
Vol 25 (4) ◽  
pp. 203-213
Author(s):  
B.H. Abed ◽  
K.J. Jadee ◽  
A.A. Battawi
Keyword(s):  
Mechanical Properties ◽  
Composite Material ◽  
Elasticity Modulus ◽  
Epoxy Composite ◽  
Numerical Study ◽  
Creep Behaviour ◽  
Weight Ratio ◽  
Volume Ratio ◽  
Epoxy Composites ◽  
Creep Characteristics

AbstractThe creep test is one of the important approaches to determining some mechanical properties of composite materials. This study was carried out to investigate the creep behaviour of an epoxy composite material that was reinforced with Y2O3 powder at weight ratios of 2%, 7%, 12%, 17% and 22%. Each volume ratio was subjected to five loads over the range of 1N to5N at a constant temperature of 16 ± 2°C. In this work, creep behaviour, stress and elasticity modulus were studied through experimental and numerical analyses. Results showed that increasing the weight ratio of Y2O3 powder enhanced creep characteristics.

The influence of functionalization time of carbon nanotube on the mechanical properties of the epoxy composites

2017 ◽  
Vol 51 (12) ◽  
pp. 1693-1701 ◽  
Author(s):  
EA Zakharychev ◽  
EN Razov ◽  
Yu D Semchikov ◽  
NS Zakharycheva ◽  
MA Kabina
Keyword(s):  
Mechanical Properties ◽  
Carbon Nanotubes ◽  
Tensile Strength ◽  
Elastic Modulus ◽  
Carbon Nanotube ◽  
Composite Materials ◽  
Polymer Composites ◽  
Epoxy Composites ◽  
Multi Walled Carbon Nanotubes ◽  
Walled Carbon Nanotubes

This paper investigates the structure, length, and percentage of functional groups of multi-walled carbon nanotubes (CNT) depending on the time taken for functionalization in HNO3 and H2SO4 mixture. The carbon nanotube content and influence of functionalization time on mechanical properties of polymer composite materials based on epoxy matrix are studied. The extreme dependencies of mechanical properties of carbon nanotube functionalization time of polymer composites were established. The rise in tensile strength of obtained composites reaches 102% and elastic modulus reaches 227% as compared to that of unfilled polymer. The composites exhibited best mechanical properties by including carbon nanotube with 0.5 h functionalization time.

Investigation of Mechanical Properties of Silk and Epoxy Composite Materials

2021 ◽  
Vol 889 ◽  
pp. 27-31
Author(s):  
Norie A. Akeel ◽  
Vinod Kumar ◽  
Omar S. Zaroog
Keyword(s):  
Mechanical Properties ◽  
Composite Material ◽  
Composite Materials ◽  
Epoxy Composite ◽  
Mechanical Test ◽  
Weight Ratio ◽  
Industrial Applications ◽  
Sem Analysis ◽  
Equivalent Strength ◽  
Test Impact

This research Investigates the new composite materials are fabricated of two or more materials raised. The fibers material from the sources of natural recycled materials provides certain benefits above synthetic strengthening material given that very less cost, equivalent strength, less density, and the slightest discarded difficulties. In the current experiments, silk and fiber-reinforced epoxy composite material is fabricated and the mechanical properties for the composite materials are assessed. New composite materials samples with the dissimilar fiber weight ratio were made utilizing the compression Molding processes with the pressure of 150 pa at a temperature of 80 °C. All samples were exposed to the mechanical test like a tensile test, impact loading, flexural hardness, and microscopy. The performing results are the maximum stress is 33.4MPa, elastic modulus for the new composite material is 1380 MPa, and hardness value is 20.64 Hv for the material resistance to scratch, SEM analysis of the microstructure of new composite materials with different angles of layers that are more strength use in industrial applications.

The study on coffee slag/recycled polystyrene circulation materials and its application on blinds

2020 ◽  
Vol 34 (07n09) ◽  
pp. 2040010
Author(s):  
Hsu-Chiang Kuan ◽  
Chin-Lung Chiang ◽  
Ming-Yuan Shen ◽  
Chen-Feng Kuan
Keyword(s):  
Tensile Strength ◽  
Composite Material ◽  
Composite Materials ◽  
Flexural Strength ◽  
Energy Saving ◽  
Metal Powder ◽  
Carbon Footprint ◽  
Heat Deflection Temperature ◽  
Carbon Footprint Reduction

In this study, we combine the coffee slag, metal powder with recycled petrochemical plastics (polystyrene, PS) to prepare circulation composite materials. It is an energy saving and carbon footprint reduction composite material compared with traditional one. The resulted PS/coffee composite has tensile strength 117.5 kgf/cm2 and flexural strength is 314.2 kgf/cm2. The heat deflection temperature (HDT) is 92[Formula: see text]C and the UV test fits the ASTM G154 requirement. The metal gross composite is with tensile strength 318.8 kgf/cm2 and flexural strength is 581.6 kgf/cm2. The HDT is 91[Formula: see text]C and the UV test fits the ASTM G154 requirement as well. Its reuse ratio can reach 85% for recycled PS. The resultant product has metal texture blinds with metal gross and wood-like blinds with coffee aroma flavor.

scholarly journals Generation of R-Curve from 4ENF Specimens: An Experimental Study

2014 ◽  
Vol 2014 ◽  
pp. 1-10 ◽  
Author(s):  
V. Alfred Franklin ◽  
T. Christopher
Keyword(s):  
Composite Materials ◽  
Fracture Energy ◽  
Epoxy Composite ◽  
Beam Theory ◽  
Fiber Direction ◽  
Crack Growth Resistance Curve ◽  
Aerospace Applications ◽  
Delamination Toughness ◽  
Theory Solution

The experimental determination of the resistance to delamination is very important in aerospace applications as composite materials have superior properties only in the fiber direction. To measure the interlaminar fracture toughness of composite materials, different kinds of specimens and experimental methods are available. This article examines the fracture energy of four-point end-notched flexure (4ENF) composite specimens made of carbon/epoxy and glass/epoxy. Experiments were conducted on these laminates and the mode II fracture energy, GIIC, was evaluated using compliance method and was compared with beam theory solution. The crack growth resistance curve (R-curve) for these specimens was generated and the found glass/epoxy shows higher toughness values than carbon/epoxy composite. From this study, it was observed that R-curve effect in 4ENF specimens is quite mild, which means that the measured delamination toughness, GIIC, is more accurate.