scholarly journals THE STABILIZING OF ANATASE AEROGEL AT HIGH TEMPERATURE

2010 ◽  
Vol 4 (2) ◽  
pp. 110-116 ◽  
Author(s):  
Silvester Tursiloadi ◽  
Hiroshi Hirashima
Keyword(s):  
Specific Surface ◽  
Surface Area ◽  
Specific Surface Area ◽  
Pore Volume ◽  
Anatase Phase ◽  
Total Pore Volume ◽  
Average Pore ◽  
Amorphous Sio2 ◽  
Bet Specific Surface Area ◽  
Sio2 Aerogel

Stable anatase is attractive to its notable functions for photo catalysis and photon-electron transfer.   Stable anatase TiO­2 containing amorphous SiO2 aerogel was prepared by hydrolysis of Ti (OC3H7)4 and Si (OC3H7)4 in a 2-propanol solution with acid catalyst. The solvent in wet gels was supercritically extracted in CO2 at 60 oC and 22 Mpa. Thermal evolutions of the microstructure of the gels were evaluated by TGA-DTA, N2 adsorption and XRD. A stable anatase TiO2 containing amorphous SiO2 aerogel with a BET specific surface area of 365 m2/g and a total pore volume of 0.20 cm3/g was obtained as prepared condition. The anatase phase was stable after calcination up to 1000 oC, and BET specific surface area, total pore volume and average pore diameter did not change significantly after calcination up to 900 oC.   Keywords: Supercritical extraction, sol-gel, aerogel, stable anatase structure

scholarly journals PREPARATION OF MESOPOROUS TITANIA-SILICA AEROGELS BY CO2 SUPERCRITICAL EXTRACTION

2010 ◽  
Vol 7 (2) ◽  
pp. 121-127
Author(s):  
Silvester Tursiloadi ◽  
Dinie Mansur ◽  
Yeny Meliana ◽  
Ruslan Efendi
Keyword(s):  
Specific Surface ◽  
Surface Area ◽  
Specific Surface Area ◽  
Thermal Evolution ◽  
Anatase Phase ◽  
Sol Gel ◽  
Total Pore Volume ◽  
Acid Catalyst ◽  
Supercritical Extraction ◽  
Average Pore

Stable anatase is attractive because of its notable functions for photocatalysis and photon-electron transfer.  TiO2-nanoparticles dispersed SiO2 wet gels were prepared by hydrolysis of Ti(OC4H9n)4 and Si(OC2H5)4 in a 2-propanol solution with acid catalyst.  The solvent in the wet gels was supercritically extracted using CO2 at 60 oC and 22 Mpa in one-step.  Thermal evolution of the microstructure of the extracted gels (aerogels) was evaluated by XRD measurements, TEM and N2 adsorption measurements. The as-extracted aerogel with a large specific surface area, more than 365 m2g-1, contained anatase nanoparticles, about 5 nm in diameter.  The anatase phase was stable after calcinations at temperatures up to 1000 oC, and BET specific surface area, total pore volume and average pore diameter did not change significantly after calcinations at temperature up to 800 oC.   Keywords: Stable anatase, sol-gel, CO2 supercritical extraction.

Optimization of Experimental Conditions for the Preparation of High Specific Surface Area Bamboo-Based Activated Carbon

2015 ◽  
Vol 1090 ◽  
pp. 154-159
Author(s):  
Sheng Zhou Zhang ◽  
Hong Ying Xia ◽  
Li Bo Zhang ◽  
Jin Hui Peng ◽  
Jian Wu ◽  
...  
Keyword(s):  
Activated Carbon ◽  
Specific Surface ◽  
Surface Area ◽  
Specific Surface Area ◽  
Pore Volume ◽  
Total Pore Volume ◽  
High Specific Surface Area ◽  
Raw Material ◽  
Experimental Conditions ◽  
Average Pore

Bamboo as the raw material is carbonized to prepare high specific surface area activated carbon by microwave heating under nitrogen atmosphere in our present work. Influences of activation agents on the preparation of activated carbon are studied. The results show that activation agents have a significant influence on the preparation of activated carbon. Under the heating time of 15 min, the adsorption capacity of the activated carbon prepared utilizing KOH as activation agent is the best. When the KOH/C ratio is 4, the iodine number and yield of activated carbon are 2298 mg/g and 39.82%, respectively. The BET specific surface area, total pore volume and average pore diameter of activated carbon are 3441 m2/g, 2.093 ml/g and 2.434 nm, respectively. The micropore volume of 1.304 ml/g is 62.30% of total pore volume, indicating that the activated carbon is microporous activated carbon.

scholarly journals Synthesis of 9-phenylcarbazole hyper-cross-linked polymers in different conditions and adsorption behavior for carbon dioxide

2019 ◽  
Author(s):  
Dandan Fang ◽  
Xiaodong Li ◽  
Meishuai Zou ◽  
Xiaoyan Guo ◽  
Aijuan Zhang
Keyword(s):  
Specific Surface ◽  
Surface Area ◽  
Specific Surface Area ◽  
Reaction Temperature ◽  
Pore Volume ◽  
High Surface ◽  
Total Pore Volume ◽  
Synthesis Conditions ◽  
Bet Specific Surface Area ◽  
Cross Linker

To systematically explore the effects of the synthesis conditions on the porosity of hyper-cross-linked polymers (HCPs), a series of 9-phenylcarbazole HCPs (P1-P11) have been made by changing the dosage of cross-linker, the reaction temperature, catalyst usage and solvent dosage. Fourier transform infrared spectroscopy is utilized to characterize the structure of the obtained polymers. The TG analysis shows a high thermal stability of the HCPs. More importantly, comparative studies on the porous properties reveals that: molar ration of cross-linker and building block is the main factor of BET specific surface area; Improving reaction temperature or the usage of catalyst could increase the total pore volume greatly but sacrifice part of BET specific surface area; Fortunately changing solvent dosage could remedy this situation, that is slightly changing solvent dosage could simultaneously obtain high surface area and high total pore volume. The BET specific surface areas of P3 is up to 769 m2g-1 with narrow pore size distribution and the CO2 adsorption capacity of P11 is up to 52.4 cm3g-1 (273 K/1.00 bar).

scholarly journals Carbazole-functionalized hyper-cross-linked polymers for CO2 uptake based on Friedel–Crafts polymerization on 9-phenylcarbazole

2019 ◽  
Vol 15 ◽  
pp. 2856-2863 ◽  
Author(s):  
Dandan Fang ◽  
Xiaodong Li ◽  
Meishuai Zou ◽  
Xiaoyan Guo ◽  
Aijuan Zhang
Keyword(s):  
Specific Surface ◽  
Surface Area ◽  
Specific Surface Area ◽  
Reaction Temperature ◽  
Pore Volume ◽  
Total Pore Volume ◽  
Molar Ratio ◽  
Co2 Uptake ◽  
Bet Specific Surface Area ◽  
Cross Linker

To systematically explore the effects of the synthesis conditions on the porosity of hyper-cross-linked polymers (HCPs), a series of 9-phenylcarbazole (9-PCz) HCPs (P1–P11) has been made by changing the molar ratio of cross-linker to monomer, the reaction temperature T 1, the used amount of catalyst and the concentration of reactants. Fourier transform infrared spectroscopy was utilized to characterize the structure of the obtained polymers. The TG analysis of the HCPs showed good thermal stability. More importantly, a comparative study on the porosity revealed that: the molar ratio of cross-linker to monomer was the main influence factor of the BET specific surface area. Increasing the reaction temperature T 1 or changing the used amount of catalyst could improve the total pore volume greatly but sacrificed a part of the BET specific surface area. Fortunately changing the concentration of reactants could remedy this situation. Slightly changing the concentration of reactants could simultaneously obtain a high surface area and a high total pore volume. The BET specific surface areas of P3 was up to 769 m2 g−1 with narrow pore size distribution and the CO2 adsorption capacity of P11 was up to 52.4 cm3 g−1 (273 K/1.00 bar).

scholarly journals Evaluation of coal and shale reservoir in Permian coal-bearing strata for development potential: A case study from well LC-1# in the northern Guizhou, China

2018 ◽  
Vol 37 (1) ◽  
pp. 194-218 ◽  
Author(s):  
Hongjie Xu ◽  
Shuxun Sang ◽  
Jingfen Yang ◽  
Jun Jin ◽  
Huihu Liu ◽  
...  
Keyword(s):  
Specific Surface ◽  
Pore Size ◽  
Surface Area ◽  
Specific Surface Area ◽  
Shale Gas ◽  
Pore Volume ◽  
Coalbed Methane ◽  
Total Pore Volume ◽  
Gas Content ◽  
Bet Specific Surface Area

Indentifying reservoir characteristics of coals and their associated shales is very important in understanding the co-exploration and co-production potential of unconventional gases in Guizhou, China. Accordingly, comprehensive experimental results of 12 core samples from well LC-1# in the northern Guizhou were used and analyzed in this paper to better understand their vertical reservoir study. Coal and coal measured shale, in Longtan Formation, are rich in organic matter, with postmature stage of approximately 3.5% and shales of type III kerogen with dry gas generation. All-scale pore size analysis indicates that the pore size distribution of coal and shale pores is mainly less than 20 nm and 100 nm, respectively. Pore volume and area of coal samples influenced total gas content as well as desorbed gas and lost gas content. Obvious relationships were observed between residual gas and BET specific surface area and BJH total pore volume (determined by nitrogen adsorption). For shale, it is especially clear that the desorbed gas content is negatively correlated with BET specific surface area, BJH total pore volume and clay minerals. However, the relationships between desorbed gas and TOC (total organic carbon) as well as siderite are all well positive. The coals and shales were shown to have similar anoxic conditions with terrestrial organic input, which is beneficial to development of potential source rocks for gas. However, it may be better to use a low gas potential assessment for shales in coal-bearing formation because of their low S1+S2 values and high thermal evolution. Nevertheless, the coalbed methane content is at least 10 times greater than the shale gas content with low desorbed gases, indicating that the main development unconventional natural gas should be coalbed methane, or mainly coalbed methane with supplemented shale gas.

Fuels Desulphurisation by Adsorbtion on Fe / Bentonite

2017 ◽  
Vol 68 (3) ◽  
pp. 483-486
Author(s):  
Constantin Sorin Ion ◽  
Mihaela Bombos ◽  
Gabriel Vasilievici ◽  
Dorin Bombos
Keyword(s):  
Specific Surface ◽  
Surface Area ◽  
Specific Surface Area ◽  
Pore Volume ◽  
Pore Diameter ◽  
Adsorption Process ◽  
Continuous System ◽  
Gas Oil ◽  
Average Pore ◽  
Atmospheric Distillation

Desulfurisation of atmospheric distillation gasoline and gas oil was performed by adsorption process on Fe/ bentonite. The adsorbent was characterized by determining the adsorption isotherms, specific surface area, pore volume and average pore diameter. Adsorption experiments of atmospheric distillation gasoline and gas oil were performed in continuous system at 280�320oC, 5 atm and volume hourly space velocities of 1�2 h-1. The efficiency of adsorption on Fe / bentonite was better at desulphurisation of gasoline versus gas oil.

scholarly journals Nanometer Pore Structure Characterization of Taiyuan Formation Shale in the Lin-Xing Area Based on Nitrogen Adsorption Experiments

Minerals ◽  
2021 ◽  
Vol 11 (3) ◽  
pp. 298
Author(s):  
Chenlong Ding ◽  
Jinxian He ◽  
Hongchen Wu ◽  
Xiaoli Zhang
Keyword(s):  
Specific Surface ◽  
Pore Structure ◽  
Surface Area ◽  
Specific Surface Area ◽  
Shale Gas ◽  
Pore Volume ◽  
Ordos Basin ◽  
Total Pore Volume ◽  
Nitrogen Adsorption ◽  
Taiyuan Formation

Ordos Basin is an important continental shale gas exploration site in China. The micropore structure of the shale reservoir is of great importance for shale gas evaluation. The Taiyuan Formation of the lower Permian is the main exploration interval for this area. To examine the nanometer pore structures in the Taiyuan Formation shale reservoirs in the Lin-Xing area, Northern Shaanxi, the microscopic pore structure characteristics were analyzed via nitrogen adsorption experiments. The pore structure parameters, such as specific surface area, pore volume, and aperture distribution, of shale were calculated; the significance of the pore structure for shale gas storage was analyzed; and the main controlling factors of pore development were assessed. The results indicated the surface area and hole volume of the shale sample to be 0.141–2.188 m2/g and 0.001398–0.008718 cm3/g, respectively. According to the IUPAC (International Union of Pure and Applied Chemistry) classification, mesopores and macropores were dominant in the pore structure, with the presence of a certain number of micropores. The adsorption curves were similar to the standard IV (a)-type isotherm line, and the hysteresis loop type was mainly similar to H3 and H4 types, indicating that most pores are dominated by open type pores, such as parallel plate-shaped pores and wedge-shaped slit pores. The micropores and mesopores provide the vast majority of the specific surface area, functioning as the main area for the adsorption of gas in the shale. The mesopores and macropores provide the vast majority of the pore volume, functioning as the main storage areas for the gas in the shale. Total organic carbon had no notable linear correlation with the total pore volume and the specific surface area. Vitrinite reflectance (Ro) had no notable correlation with the specific surface area, but did have a low “U” curve correlation with the total pore volume. There was no relationship between the quartz content and specific surface area and total pore volume. In addition, there was no notable correlation between the clay mineral content and total specific surface area and total pore volume.

scholarly journals Structural and fractal characterization of adsorption pores of middle–high rank coal reservoirs in western Yunnan and eastern Guizhou: An experimental study of coals from the Panguan syncline and Laochang anticline

2018 ◽  
Vol 37 (1) ◽  
pp. 251-272 ◽  
Author(s):  
Junjian Zhang ◽  
Chongtao Wei ◽  
Gaoyuan Yan ◽  
Guanwen Lu
Keyword(s):  
Specific Surface ◽  
Surface Area ◽  
Specific Surface Area ◽  
Pore Volume ◽  
Pore Diameter ◽  
Structural Parameters ◽  
Total Pore Volume ◽  
Type A ◽  
Type B ◽  
Type C

To better understand the structural characteristic of adsorption pores (pore diameter < 100 nm) of coal reservoirs around the coalbed methane production areas of western Yunnan and eastern Guizhou, we analyzed the structural and fractal characteristics of pore size range of 0.40–2.0 nm and 2–100 nm in middle–high rank coals ( Ro,max = 0.93–3.20%) by combining low-temperature N2/CO2 adsorption tests and surface/volume fractal theory. The results show that the coal reservoirs can be divided into three categories: type A ( Ro,max < 2.15%), type B (2.15% <  Ro,max <2.50%), and type C ( Ro,max > 2.15%). The structural parameters of pores in the range from 2 to 100 nm are influenced by the degree of coal metamorphism and the compositional parameters (e.g., ash and volatile matter). The dominant diameters of the specific surface areas are 10–50 nm, 2–50 nm, and 2–10 nm, respectively. The pores in the range from <2 nm provide the largest proportion of total specific surface area (97.22%–99.96%) of the coal reservoir, and the CO2-specific surface area and CO2-total pore volume relationships show a positive linear correlation. The metamorphic degree has a much greater control on the pores (pore diameter less than 2 nm) structural parameters than those of the pore diameter ranges from 2 to 100 nm. Dv1 and Dv2 can characterize the structure of 2–100 nm adsorption pores, and Dv1 (volume heterogeneity) has a positive correlation with the pore structural parameters such as N2-specific surface area and N2-total pore volume. This parameter can be used to characterize volume heterogeneity of 2–10 nm pores. Dv2 (surface heterogeneity) showed type A > type B > type C and was mainly affected by the metamorphism degree. Ds2 can be used to characterize the pore surface heterogeneity of micropores in the range of 0.62–1.50 nm. This parameter has a good correlation with the pore parameters (CO2-total pore volume, CO2-specific surface area, and average pore size) and is expressed as type C < type B < type A. In conclusion, the heterogeneity of the micropores is less than that of the meso- and macropores (2–100 nm). Dv1, Dv2, and Ds2 can be used as effective parameters to characterize the pore structure of adsorption pores. This result can provide a theoretical basis for studying the pore structure compatibility of coal reservoirs in the region.

scholarly journals Activated Carbons from Thermoplastic Precursors and Their Energy Storage Applications

Nanomaterials ◽  
2019 ◽  
Vol 9 (6) ◽  
pp. 896 ◽  
Author(s):  
Hye-Min Lee ◽  
Kwan-Woo Kim ◽  
Young-Kwon Park ◽  
Kay-Hyeok An ◽  
Soo-Jin Park ◽  
...  
Keyword(s):  
Electron Microscope ◽  
Specific Surface ◽  
Surface Area ◽  
Field Emission ◽  
Specific Surface Area ◽  
Pore Volume ◽  
Activated Carbons ◽  
Total Pore Volume ◽  
Cross Linking ◽  
Mesopore Volume

In this study, low-density polyethylene (LDPE)-derived activated carbons (PE-AC) were prepared as electrode materials for an electric double-layer capacitor (EDLC) by techniques of cross-linking, carbonization, and subsequent activation under various conditions. The surface morphologies and structural characteristics of the PE-AC were observed by field-emission scanning electron microscope, Cs-corrected field-emission transmission electron microscope, and X-ray diffraction analysis, respectively. The nitrogen adsorption isotherm-desorption characteristics were confirmed by Brunauer–Emmett–Teller, nonlocal density functional theory, and Barrett–Joyner–Halenda equations at 77 K. The results showed that the specific surface area and total pore volume of the activated samples increased with increasing the activation time. The specific surface area, the total pore volume, and mesopore volume of the PE-AC were found to be increased finally to 1600 m2/g, 0.86 cm3/g, and 0.3 cm3/g, respectively. The PE-AC also exhibited a high mesopore volume ratio of 35%. This mesopore-rich characteristic of the activated carbon from the LDPE is considered to be originated from the cross-linking density and crystallinity of precursor polymer. The high specific surface area and mesopore volume of the PE-AC led to their excellent performance as EDLC electrodes, including a specific capacitance of 112 F/g.

The Influence of Sinterng Temperature on the Phase, Microstructure and Textual Properties of Hollow Hydroxyapatite Microspheres

2011 ◽  
Vol 239-242 ◽  
pp. 2274-2279 ◽  
Author(s):  
Ying Chun Wang ◽  
Wen Hai Huang ◽  
Ai Hua Yao ◽  
De Ping Wang
Keyword(s):  
Specific Surface ◽  
Pore Size ◽  
Surface Area ◽  
Specific Surface Area ◽  
Pore Volume ◽  
Sintering Temperature ◽  
Total Pore Volume ◽  
Precipitation Method ◽  
Simple Method ◽  
Air Atmosphere

A simple method to prepare hollow hydroxyapatite (HAP) microspheres with mespores on the surfaces is performed using a precipitation method assisted with Li2O-CaO-B2O3(LCB) glass fabrication process. This research is concerned with the effect of sintering temperature on the microstructure evolution, phase purity, surface morphology, specific surface area, and porosity after sintering process. The microspheres were sintered in air atmosphere at temperatures ranging from 500 to 900 °C. The starting hollow HAP microspheres and the sintered specimens were characterized by scanning electron microscope, X-ray diffractometer, specific surface area analyzer, and Hg porosimetry, respectively. The as-prepared microspheres consisted of calcium deficient hydroxyapatite. The results showed that the as-prepared hollow HAP microspheres had the highest specific surface areas, and the biggest total pore volume. The pore size distribution of the as-prepared hollow HAP microspheres were mainly the mesopores in the range of 2～40 nm. The specific surface area and total pore volume of hollow HAP microspheres decreased with increasing sintering temperature. Whereas the mean pore size increased with increasing sintering temperature. It showed that at 700°C, Ca-dHAP decomposes into a biphasic mixture of HAP and β-calcium phosphate(TCP).

Sign in / Sign up

Export Citation Format

Share Document