The Effect of Specimen Thickness Upon the Fatigue Crack Growth Rate of A516-60 Pressure Vessel Steel

1977 ◽  
Vol 99 (2) ◽  
pp. 248-252 ◽  
Author(s):  
A. M. Sullivan ◽  
T. W. Crooker
Keyword(s):  
Growth Rate ◽  
Fatigue Crack ◽  
Crack Growth Rate ◽  
Fatigue Crack Growth ◽  
Crack Growth ◽  
Fatigue Crack Growth Rate ◽  
Pressure Vessel ◽  
Specimen Thickness ◽  
Pressure Vessel Steel ◽  
Vessel Steel

Fatigue crack growth rate studies on A516-60 pressure vessel steel indicate no effect of specimen thickness in stress-relieved specimens ranging in thickness from 0.25 to 2.0 in. (6.35 to 50.8 mm). A regression curve equation for all thicknesses relating cyclic crack growth rate (da/dN) to crack-tip stress-intensity factor range (ΔK) is obtained. The significance of these results is discussed in the light of current engineering practice and previous studies on size effects in fatigue crack propagation.

Influence of reactor water of nominal parameters on fatigue crack growth rate in 15Kh2NMFA steel

1985 ◽  
Vol 21 (2) ◽  
pp. 130-133
Author(s):  
V. I. Pokhmurskii ◽  
A. S. Zubchenko ◽  
A. A. Popov ◽  
I. P. Gnyp ◽  
V. M. Timonin ◽  
...  
Keyword(s):  
Growth Rate ◽  
Fatigue Crack ◽  
Crack Growth Rate ◽  
Fatigue Crack Growth ◽  
Crack Growth ◽  
Fatigue Crack Growth Rate ◽  
Reactor Water ◽  
15Kh2nmfa Steel
Sign in / Sign up

Export Citation Format

Share Document