HIGHLY WATER-REPELLENT FILM ON CORROSION PROTECTION OF CARBON EFFECT OF (STYRENE-VINYL ACETATE) COPOLYMERS AS STEEL PETROLEUM PIPELINES

2019 ◽  
Vol 34 (12) ◽  
pp. 268-286
Author(s):  
Fadia Sultan
Keyword(s):  
Vinyl Acetate ◽  
Corrosion Protection ◽  
Water Repellent ◽  
Petroleum Pipelines

Water repellent also absorbs

Nature ◽  
2003 ◽  
Author(s):  
Philip Ball
Keyword(s):  
Water Repellent

CVD mullite and mullite-alumina corrosion protection coatings for silicon based ceramics

2001 ◽  
Vol 11 (PR3) ◽  
pp. Pr3-861-Pr3-867 ◽  
Author(s):  
S. M. Zemskova ◽  
J. A. Haynes ◽  
K. M. Cooley
Keyword(s):  
Corrosion Protection ◽  
Silicon Based

EIS study of the corrosion behavior of an organic coating applied on Algerian oil tanker

2020 ◽  
Vol 117 (6) ◽  
pp. 610
Author(s):  
Nadia Hammouda ◽  
Kamel Belmokre
Keyword(s):  
Corrosion Protection ◽  
Electrochemical Impedance ◽  
Paint Film ◽  
Organic Coating ◽  
Diffusion Resistance ◽  
Double Layer Capacitance ◽  
Carbon Steel Surface ◽  
Chloride Environment ◽  
Oil Tanker ◽  
Epoxy Paint

Organic coatings are widely employed in the corrosion protection of most metal surfaces, particularly steel. They provide a barrier against corrosive species present in the environment, due to their high resistance to oxygen, water and ions transport. This study focuses on the evaluation of corrosion protection performance of epoxy paint on the carbon steel surface in chloride environment (3% NaCl) by Electrochemical Impedance Spectroscopy (EIS). The electrochemical behavior of painted surface was estimated by EIS parameters that contained paint film resistance, paint film capacitance and double layer capacitance. On the basis of calculation using EIS spectrums it was observed that pore resistance (Rpore) decreased with the appearance of doubled layer capacitance (Cdl) due to the electrolyte penetration through the film. This was further confirmed by the decrease of diffusion resistance (Rd) which was also the indicator of the deterioration of paint film protectiveness. Microscopic analyses have shown that oxidation dominates the corroded surfaces.

Inhibition of Radical-Initiated Vinyl Acetate Polymerisation by Tobacco Smoke Fractions

1974 ◽  
Vol 7 (5) ◽  
Author(s):  
M.A. Nisbet ◽  
S. Schmeller
Keyword(s):  
Benzoyl Peroxide ◽  
Vinyl Acetate ◽  
Tobacco Smoke ◽  
Boiling Point ◽  
Water Bath ◽  
Measuring Time ◽  
Time Required

AbstractBoth the vapour and particulate phases of tobacco smoke have been shown to retard benzoyI-peroxide-initiated polymerisation of vinyl acetate by interception of the radicals involved in the polymerisation process. The extent of inhibition of polymerisation by test compounds is estimated by measuring time taken for a mixture of monomer and benzoyl peroxide, immersed in a water-bath at 70°C, to reach a spontaneous boil and comparing it with the time required for a similar mixture with added retarder to reach boiling point. Units are expressed as minutes of inhibition per part per million of inhibitor × 10

Sign in / Sign up

Export Citation Format

Share Document