Coupled Effects of Activator Type/Concentration and Curing Temperature on the Unconfined Compressive Strength of Alkali-Activated Slag-Based Cemented Paste Backfill

2021 ◽  
Author(s):  
Haiqiang Jiang ◽  
Lei Ren ◽  
Qi Zhang ◽  
Jingru Zheng ◽  
Liang Cui
Keyword(s):  
Compressive Strength ◽  
Unconfined Compressive Strength ◽  
Curing Temperature ◽  
Cemented Paste Backfill ◽  
Alkali Activated Slag ◽  
Paste Backfill ◽  
Activated Slag ◽  
Alkali Activated

scholarly journals Strengthening Behavior of Cemented Paste Backfill Using Alkali-Activated Slag Binders and Bottom Ash Based on the Response Surface Method

Materials ◽  
2020 ◽  
Vol 13 (4) ◽  
pp. 855
Author(s):  
Qi Sun ◽  
Xueda Wei ◽  
Tianlong Li ◽  
Lu Zhang
Keyword(s):  
Response Surface ◽  
Bottom Ash ◽  
Hydration Product ◽  
Cemented Paste Backfill ◽  
Alkali Activated Slag ◽  
Surface Method ◽  
Optimal Mix ◽  
Paste Backfill ◽  
Activated Slag ◽  
Alkali Activated

A new type of cemented paste backfill (CPB) was prepared by using the bottom ash (BA) from a thermal power plant as an aggregate, alkali-activated slag as a binder, and an air-entraining agent as an admixture. Based on the central composite design (CCD) response surface method, the mix ratio was optimized, and scanning electron microscopy-energy dispersive spectroscopy (SEM-EDS) was performed on the optimal mix ratio. ImageJ software was utilized to determine the porosity of the experimental samples at various curing ages. The results indicate that the optimal mix ratio of the aggregate-binder ratio is 3.28, the alkali dosage is 3%, the solid content is 67.44%, and the air-entraining agent dosage is 0.1%. As the curing age increases, the porosity of CPB gradually decreases. A calcium aluminosilicate hydrate (C-A-S-H) gel is the main hydration product of alkali-activated slag. At the beginning of the hydration reaction, the slag gradually dissolves, and the C-A-S-H product binds the BA together. At 14 d, complete calcium hydroxide (CH) crystals appeared in the hydration product. Finally, the degree of C-A-S-H crystallization increased further to form a dense structure.

scholarly journals Rheological Properties of Cemented Paste Backfill with Alkali-Activated Slag

Minerals ◽  
2020 ◽  
Vol 10 (3) ◽  
pp. 288 ◽  
Author(s):  
Yunpeng Kou ◽  
Haiqiang Jiang ◽  
Lei Ren ◽  
Erol Yilmaz ◽  
Yuanhui Li
Keyword(s):  
Yield Stress ◽  
Rheological Behavior ◽  
Plastic Viscosity ◽  
Molar Ratio ◽  
Cemented Paste Backfill ◽  
Lower Yield Stress ◽  
Alkali Activated Slag ◽  
Paste Backfill ◽  
Activated Slag ◽  
Alkali Activated

This study investigates the time-dependent rheological behavior of cemented paste backfill (CPB) that contains alkali-activated slag (AAS) as a binder. Rheological measurements with the controlled shear strain method have been conducted on various AAS-CPB samples with different binder contents, silicate modulus (Ms: SiO2/Na2O molar ratio), fineness of slag and curing temperatures. The Bingham model afforded a good fit to all of the CPB mixtures. The results show that AAS-CPB samples with high binder content demonstrate a more rapid rate of gain in yield stress and plastic viscosity. AAS-CPB also shows better rheological behavior than CPB samples made up of ordinary Portland cement (OPC) at identical binder contents. It is found that increasing Ms yields lower yield stress and plastic viscosity and the rate of gain in these parameters. Increases in the fineness of slag has an adverse effect on rheological behavior of AAS-CPB. The rheological behavior of both OPC- and AAS-CPB samples is also strongly enhanced at higher temperatures. AAS-CPB samples are found to be more sensitive to the variation in curing temperatures than OPC-CPB samples with respect to the rate of gain in yield stress and plastic viscosity. As a result, the findings of this study will contribute to well understand the flow and transport features of fresh CPB mixtures under various conditions and their changes with time.

scholarly journals Strength and Drying Shrinkage of Alkali-Activated Slag Paste and Mortar

2012 ◽  
Vol 2012 ◽  
pp. 1-7 ◽  
Author(s):  
Mao-chieh Chi ◽  
Jiang-jhy Chang ◽  
Ran Huang
Keyword(s):  
Tensile Strength ◽  
Compressive Strength ◽  
Portland Cement ◽  
Liquid Slag ◽  
Drying Shrinkage ◽  
Curing Temperature ◽  
Alkali Activated Slag ◽  
Cement Mortars ◽  
Activated Slag ◽  
Alkali Activated

The aim of this study is to investigate the strengths and drying shrinkage of alkali-activated slag paste and mortar. Compressive strength, tensile strength, and drying shrinkage of alkali-activated slag paste and mortar were measured with various liquid/slag ratios, sand/slag ratios, curing ages, and curing temperatures. Experimental results show that the higher compressive strength and tensile strength have been observed in the higher curing temperature. At the age of 56 days, AAS mortars show higher compressive strength than Portland cement mortars and AAS mortars with liquid/slag ratio of 0.54 have the highest tensile strength in all AAS mortars. In addition, AAS pastes of the drying shrinkage are higher than AAS mortars. Meanwhile, higher drying shrinkage was observed in AAS mortars than that observed comparable Portland cement mortars.

scholarly journals Experimental Study of the Mechanical and Microstructure Characteristics of Coal Gangue Road Stabilization Materials Based on Alkali Slag Cementation

Materials ◽  
2021 ◽  
Vol 14 (13) ◽  
pp. 3601
Author(s):  
Changbai Wang ◽  
Junxin Yang ◽  
Shuzhan Xu
Keyword(s):  
Compressive Strength ◽  
Unconfined Compressive Strength ◽  
Coal Gangue ◽  
Hydration Time ◽  
Alkali Activated Slag ◽  
Microstructure Characteristics ◽  
Activated Coal ◽  
Activated Slag ◽  
Activated Coal Gangue ◽  
Alkali Activated

To accelerate the resource utilization of coal gangue and meet the strategic requirements of carbon neutralization, alkali-activated, slag-cemented coal gangue is applied in the preparation of solid waste-based road stabilization materials. Here, the cementation characteristics and microstructure characteristics of alkali-activated, slag-cemented coal gangue road stabilization materials are studied using the alkali equivalent and coal gangue aggregate ratio as experimental variables. The results show that with the increase in alkali equivalent from 1% to 7%, the unconfined compressive strength of the alkali-activated coal gangue road stabilization material initially increases and then decreases, with 3% being the optimal group in terms of stabilization, the aggregate ratio of coal gangue increases from 70% to 85%, and the 7-day unconfined compressive strength of the stabilized material decreases approximately linearly from 8.16 to 1.68 MPa. At the same time, the porosity gradually increases but still meets the requirements of the specification. With the increase in hydration time, a large number of hydration products are formed in the alkali slag cementation system, and they are closely attached to the surface of and interweave with the coal gangue to fill the pores, resulting in the alkali slag slurry and coal gangue being brought closer together.

scholarly journals The Effect of Different Types of Internal Curing Liquid on the Properties of Alkali-Activated Slag (AAS) Mortar

2021 ◽  
Vol 13 (4) ◽  
pp. 2407
Author(s):  
Guang-Zhu Zhang ◽  
Xiao-Yong Wang ◽  
Tae-Wan Kim ◽  
Jong-Yeon Lim ◽  
Yi Han
Keyword(s):  
Mechanical Properties ◽  
Compressive Strength ◽  
Deionized Water ◽  
Internal Curing ◽  
Control Group ◽  
Alkali Activated Slag ◽  
Different Types ◽  
Naoh Solution ◽  
Activated Slag ◽  
Alkali Activated

This study shows the effect of different types of internal curing liquid on the properties of alkali-activated slag (AAS) mortar. NaOH solution and deionized water were used as the liquid internal curing agents and zeolite sand was the internal curing agent that replaced the standard sand at 15% and 30%, respectively. Experiments on the mechanical properties, hydration kinetics, autogenous shrinkage (AS), internal temperature, internal relative humidity, surface electrical resistivity, ultrasonic pulse velocity (UPV), and setting time were performed. The conclusions are as follows: (1) the setting times of AAS mortars with internal curing by water were longer than those of internal curing by NaOH solution. (2) NaOH solution more effectively reduces the AS of AAS mortars than water when used as an internal curing liquid. (3) The cumulative heat of the AAS mortar when using water for internal curing is substantially reduced compared to the control group. (4) For the AAS mortars with NaOH solution as an internal curing liquid, compared with the control specimen, the compressive strength results are increased. However, a decrease in compressive strength values occurs when water is used as an internal curing liquid in the AAS mortar. (5) The UPV decreases as the content of zeolite sand that replaces the standard sand increases. (6) When internal curing is carried out with water as the internal curing liquid, the surface resistivity values of the AAS mortar are higher than when the alkali solution is used as the internal curing liquid. To sum up, both NaOH and deionized water are effective as internal curing liquids, but the NaOH solution shows a better performance in terms of reducing shrinkage and improving mechanical properties than deionized water.