scholarly journals The Effects of Grain Size, Dendritic Structure and Crystallographic Orientation on Fatigue Crack Propagation in IN713C Nickel-Based Superalloy

2019 ◽  
Author(s):  
G. Liu ◽  
S. Winwood ◽  
K. Rhodes ◽  
S. Birosca
Keyword(s):  
Grain Size ◽  
Fatigue Crack ◽  
Crack Propagation ◽  
Fatigue Crack Propagation ◽  
Crystallographic Orientation ◽  
Dendritic Structure ◽  
Nickel Based Superalloy

50-Fold Difference in Region-II Fatigue Crack Propagation Resistance of Titanium Alloys: A Grain-Size Effect

1979 ◽  
Vol 101 (1) ◽  
pp. 86-90 ◽  
Author(s):  
G. R. Yoder ◽  
L. A. Cooley ◽  
T. W. Crooker
Keyword(s):  
Grain Size ◽  
Fatigue Crack ◽  
Crack Propagation ◽  
Crack Growth ◽  
Fatigue Crack Propagation ◽  
Load Ratio ◽  
Plastic Zone Size ◽  
Crack Propagation Resistance ◽  
Order Of Magnitude ◽  
Region Ii

Fatigue crack growth rates (da/dN) in ambient laboratory air have been determined for a wide variety of materials from four basic α + β titanium alloy systems. Each material was cyclically loaded with a haversine waveform and a load ratio, R = 0.10. The results indicate that, at a constant value of stress-intensity range (ΔK), the width of the da/dN data band exceeds an order of magnitude. For example, at ΔK = 21 MPa·m1/2, a 50-fold difference in fatigue crack propagation rates is observed. Analysis of the crack growth rate data at this point indicates a systematic dependence on grain size (l), viz. that da/dN decreases with increasing l. An interpretation of this effect is offered in terms of reversed (cyclic) plastic zone size considerations.