Fatigue Crack Growth Rate Behavior in Titanium Alloy Ti-5111 Weld Metal

2004 ◽  
Author(s):  
Amy C. Stauffer ◽  
Ernest J. Czyryca
Keyword(s):  
Growth Rate ◽  
Titanium Alloy ◽  
Fatigue Crack ◽  
Crack Growth Rate ◽  
Fatigue Crack Growth ◽  
Weld Metal ◽  
Crack Growth ◽  
Fatigue Crack Growth Rate ◽  
Rate Behavior

Fatigue and Static Crack Growth Rate of Alloy 718 Under Cathodic Polarization

CORROSION ◽  
10.5006/3572 ◽  
2021 ◽  
Author(s):  
Ramgopal Thodla ◽  
Anand Venkatesh
Keyword(s):  
Growth Rate ◽  
Fatigue Crack ◽  
Crack Growth Rate ◽  
Fatigue Crack Growth ◽  
Crack Growth ◽  
Fatigue Crack Growth Rate ◽  
Cathodic Polarization ◽  
Alloy 718 ◽  
Static Crack ◽  
Rate Behavior

Fatigue crack growth rate was developed on three heats of alloy 718 (UNS N07718) under cathodic polarization, over a wide range of loading conditions. Fatigue crack growth rate increased with decreasing frequency over a range of Kmax and K conditions. In most cases, there was no evidence of a plateau in fatigue crack growth rate at low frequencies. The fatigue crack growth rate over the range of conditions evaluated were influenced by static crack growth rate at Kmax. The principle of superposition of fatigue crack growth and static crack growth was used to rationalize the observed crack growth rate response. Static crack growth rate of alloy 718 measured under constant K conditions, was lower than that measured under rising displacement conditions. A crack tip strain rate based model was used to rationalize the fatigue crack growth rate behavior and the static crack growth rate behavior under constant K. However, the formulation of the model for the rising K was not able to rationalize the crack growth rate under rising displacement conditions.