SOME OBSERVATIONS ON THE STRESS-CORROSION CRACKING OF THREE COMMERCIAL TITANIUM ALLOYS

1967 ◽  
Author(s):  
James C. Williams
Keyword(s):  
Titanium Alloys ◽  
Stress Corrosion ◽  
Stress Corrosion Cracking ◽  
Corrosion Cracking ◽  
Commercial Titanium

The Effects of Microstructural Variations on Stress-Corrosion Cracking Susceptibility of Ti-8Al-1Mo-1V Alloy on Marinized Gas Turbines

1967 ◽  
Author(s):  
W. P. Danesi ◽  
R. A. Sprague ◽  
M. J. Donachie
Keyword(s):  
Titanium Alloys ◽  
Stress Corrosion ◽  
High Temperatures ◽  
Stress Corrosion Cracking ◽  
Gas Turbines ◽  
Effective Means ◽  
Corrosion Cracking ◽  
Corrosion Testing ◽  
Time Operation ◽  
Long Time

Salt can cause titanium alloys to crack, and if long-time operation of titanium hardwares in salt atmospheres is expected, effective means must be found to eliminate or control this tendency. The authors describe in detail their stress-corrosion testing of titanium alloys, and the results are plotted in a number of tables. Figures show stress-versus-temperature charts at different high temperatures, and the microstructure of the alloy after testing is illustrated. The results of the tests are evaluated and a brief summary is given.

The mechanism of aqueous stress-corrosion cracking of α + β titanium alloys

2017 ◽  
Vol 125 ◽  
pp. 29-39 ◽  
Author(s):  
Sheng Cao ◽  
Suming Zhu ◽  
Chao Voon Samuel Lim ◽  
Xigen Zhou ◽  
Xiaobo Chen ◽  
...  
Keyword(s):  
Titanium Alloys ◽  
Stress Corrosion ◽  
Stress Corrosion Cracking ◽  
Corrosion Cracking
Sign in / Sign up

Export Citation Format

Share Document