scholarly journals The Microbiologically Influenced Corrosion of L245NS Carbon Steel by Sulfate-Reducing Bacteria in H2S Solutions

2018 ◽  
pp. 9416-9427
Author(s):  
Haobo Yu ◽  
Keyword(s):  
Carbon Steel ◽  
Sulfate Reducing Bacteria ◽  
Microbiologically Influenced Corrosion ◽  
Sulfate Reducing ◽  
Reducing Bacteria

scholarly journals Effect of Sulfate-Reducing Bacteria (SRB) on the Corrosion of Buried Pipe Steel in Acidic Soil Solution

Coatings ◽  
2021 ◽  
Vol 11 (6) ◽  
pp. 625
Author(s):  
Lijuan Chen ◽  
Bo Wei ◽  
Xianghong Xu
Keyword(s):  
Soil Solution ◽  
Steel Surface ◽  
Pipeline Steel ◽  
Electrochemical Techniques ◽  
Sulfate Reducing Bacteria ◽  
Acidic Soil ◽  
Microbiologically Influenced Corrosion ◽  
Soil Environment ◽  
Sulfate Reducing ◽  
Reducing Bacteria

The influence of sulfate-reducing bacteria (SRB) on the corrosion behaviors of X80 pipeline steel was investigated in a soil environment by electrochemical techniques and surface analysis. It was found that SRB grew well in the acidic soil environment and further attached to the coupon surface, resulting in microbiologically influenced corrosion (MIC) of the steel. The corrosion process of X80 steel was significantly affected by the SRB biofilm on the steel surface. Steel corrosion was inhibited by the highly bioactive SRB biofilm at the early stage of the experiment, while SRB can accelerate the corrosion of steel at the later stage of the experiment. The steel surface suffered severe pitting corrosion in the SRB-containing soil solution.

scholarly journals Microbial Corrosion of API 5L X-70 Carbon Steel by ATCC 7757 and Consortium of Sulfate-Reducing Bacteria

2014 ◽  
Vol 2014 ◽  
pp. 1-7 ◽  
Author(s):  
Arman Abdullah ◽  
Nordin Yahaya ◽  
Norhazilan Md Noor ◽  
Rosilawati Mohd Rasol
Keyword(s):  
Weight Loss ◽  
Carbon Steel ◽  
Corrosion Rate ◽  
Sulfate Reducing Bacteria ◽  
Desulfovibrio Vulgaris ◽  
Corrosion Morphology ◽  
Sulfate Reducing ◽  
Weight Loss Method ◽  
Loss Method ◽  
Reducing Bacteria

Various cases of accidents involving microbiology influenced corrosion (MIC) were reported by the oil and gas industry. Sulfate reducing bacteria (SRB) have always been linked to MIC mechanisms as one of the major causes of localized corrosion problems. In this study, SRB colonies were isolated from the soil in suspected areas near the natural gas transmission pipeline in Malaysia. The effects of ATCC 7757 and consortium of isolated SRB upon corrosion on API 5L X-70 carbon steel coupon were investigated using a weight loss method, an open circuit potential method (OCP), and a potentiodynamic polarization curves method in anaerobic conditions. Scanning electron microscopy (SEM) and energy dispersive X-ray spectroscopy (EDS) were then used to determine the corrosion morphology in verifying the SRB activity and corrosion products formation. Results from the study show that the corrosion rate (CR) of weight loss method for the isolated SRB is recorded as 0.2017 mm/yr compared to 0.2530 mm/yr for ATCC 7757. The Tafel plot recorded the corrosion rate of 0.3290 mm/yr for Sg. Ular SRB and 0.2500 mm/yr forDesulfovibrio vulgaris. The results showed that the consortia of isolated SRB were of comparable effects and features with the single ATCC 7757 strain.

scholarly journals Formation of Biofilms and Biocorrosion on AISI-1020 Carbon Steel Exposed to Aqueous Systems Containing Different Concentrations of a Diesel/Biodiesel Mixture

2011 ◽  
Vol 2011 ◽  
pp. 1-6 ◽  
Author(s):  
Ivanilda Ramos de Melo ◽  
Severino Leopoldino Urtiga Filho ◽  
Fernando Jorge Santos Oliveira ◽  
Francisca Pessoa de França
Keyword(s):  
Carbon Steel ◽  
Sulfate Reducing Bacteria ◽  
Experimental Conditions ◽  
Exposed Area ◽  
Sulfate Reducing ◽  
Corrosion Rates ◽  
Biodiesel Blend ◽  
Corrosion Pits ◽  
Reducing Bacteria ◽  
Significant Concentration

Environmental and economic concerns accelerated biofuels research and industrial production. Many countries have been using diesel and biodiesel blends as fuels justifying research on biofilms formation and metals corrosion. Cylinders made of AISI-1020 carbon steel with an exposed area of 1587 mm2, water, and water associated with B3 fuel (diesel/biodiesel blend at 97 : 3 v/v) were used.The formation of biofilms was detected, and biocorrosion was detected on AISI-1020. The results showed a variation in sessile microflora during the experiments. In the biofilms, a significant concentration of aerobic, anaerobic, IOB,Pseudomonas aeruginosa, and sulfate-reducing bacteria was observed. The corrosion rates varied between0.45±0.01and0.12±0.01 mm/year, depending on the experimental conditions. The main corrosion products identified were various forms of FeOOH, magnetite, and all forms of FexSy. In systems where there were high levels of sulfate reducing bacteria, corrosion pits were observed. In addition, the aliphatic hydrocarbons present in the fluid containing 10% B3 were totally degraded.

Sign in / Sign up

Export Citation Format

Share Document