scholarly journals Preparation of Spherical Sub-Micron Alumina from Hainan Kaolin

CONVERTER ◽  
2021 ◽  
pp. 317-325
Author(s):  
Kai Xu, Jiafei Li, Yongming Zhang
Keyword(s):  
Particle Size ◽  
Uniform Design ◽  
Average Particle Size ◽  
Acid Leaching ◽  
Optimization Method ◽  
Source Material ◽  
Process Conditions ◽  
Alumina Powder ◽  
Average Particle ◽  
Uniform Dispersion

It is an effective way to prepare alumina by replacing bauxite with aluminous minerals. It was studied that the preparation of spherical sub-micron alumina from Hainan kaolin by alginate assisted dispersion. The results of the experiment showed that the alumina content in Hainan kaolin is more than 38%. The t process parameters as of extracting alumina by acid leaching were optimized by uniform design optimization method. The alumina extraction rate reached more than 97% with optimized process conditions. It was used as aluminum source material that he aluminum salt obtained from Hainan kaolin was treated with impurity removal. With this source material, and the purified alginate AG was used as dispersant，the α- Alumina powder with good sphericity, uniform dispersion and average particle size of about 350 was prepared.

scholarly journals Catalyst materials based on plasma-processed alumina nanopowder

2012 ◽  
Vol 77 (12) ◽  
pp. 1799-1806 ◽  
Author(s):  
Eriks Palcevskis ◽  
Lidija Kulikova ◽  
Vera Serga ◽  
Antons Cvetkovs ◽  
Svetlana Chornaja ◽  
...  
Keyword(s):  
Particle Size ◽  
Platinum Catalyst ◽  
Average Particle Size ◽  
Alumina Powder ◽  
Average Particle ◽  
Glycerol Oxidation ◽  
Plasma Technology ◽  
Oxidation By Molecular Oxygen ◽  
Prepared Material ◽  
Alumina Nanopowder

A platinum catalyst for glycerol oxidation by molecular oxygen has been developed applying the extractive-pyrolytic method and using, as a support, a fine alumina powder with an average particle size of 30-60 nm processed by plasma technology. The extractive-pyrolytic method (EPM) allows affixing small amounts of catalytic metals (1-5%) with the particle size ranging from several nanometers to several tens of nanometers onto the surface of the support. The prepared material - 4.8 wt. % platinum on nano-sized alumina - can be used as a catalyst for glycerol oxidation by oxygen with conversion up to 84%, in order to produce some organic acids (glyceric and lactic acid) with a selectivity of about 60%.

Process Parameters Optimization of Direct Synthesis Nano Magnesium Fluoride Powders

2012 ◽  
Vol 184-185 ◽  
pp. 1146-1149
Author(s):  
Ping Li ◽  
Hai Yang Wang ◽  
Wan E Wu ◽  
Shuai Ling
Keyword(s):  
Particle Size ◽  
Orthogonal Experiment ◽  
Direct Synthesis ◽  
Average Particle Size ◽  
Parameters Optimization ◽  
Magnesium Fluoride ◽  
Process Conditions ◽  
Average Particle ◽  
X Ray ◽  
Mgcl2 Concentration

To reduce average particle size，magnesium fluoride was directly synthesized from MgF2 and NH4F，the product was characterized by X-ray diffractomer，scanning electron microscopy. Orthogonal experiment was used to explore the influences of factors on the average particle size. Found that the effect order of factors on the average particle size is MgCl2 concentration，NH4F concentration，reaction temperature，reaction time，in the optimization of process conditions，average particle size is 23.1 nm.

scholarly journals Synthesis of submicronic α-alumina from local aluminum slags

2021 ◽  
pp. 53-53
Author(s):  
A. Benkhelif ◽  
M. Kolli ◽  
M. Hamidouche
Keyword(s):  
Particle Size ◽  
Extraction Efficiency ◽  
Average Particle Size ◽  
Alumina Powder ◽  
Average Particle ◽  
Ceramic Fibers ◽  
Transition Alumina ◽  
Future Studies ◽  
Refractory Ceramic ◽  
Precipitation Ph

In this study, a high valued product submicronic ?-alumina is successfully extracted from aluminum slags generated by the local aluminum industry. The extraction technique is based on the leaching of slags by H2SO4 followed by precipitation. The coarser aluminum-rich fractions of the slags are used in this study instead of the finer oxide-rich fractions that were commonly used in previous studies. The precipitation of the leached slags by NH4OH is controlled by zetameter in order to determine the optimal precipitation pH. Then, the obtained gel showing the higher precipitation rate and the finer particle size is calcined at 1200 ?C and characterized by XRF, XRD, FTIR, SEM, EDS and laser granulometry. Even without any pretreatment of slags, the XRF analysis reveals that a high purity and high extraction efficiency of 99.2% and 93.75% respectively can be achieved just at a leaching acid concentration of 15%. XRD spectrum shows that the produced alumina is a pure a-corundum, which is confirmed by FTIR spectrum showing only the Al-O bonds. The laser granulometry shows that the recovered powder exhibit a wide particle size distribution. It is between 50 nm and 20 ?m while the average particle size (d50) is about 400 nm. SEM observations reveal that the grains are in the form of submicronic whiskers. The above characteristics allow the obtained alumina powder in this study to be used in the usual applications of alumina such as refractory, ceramic fibers, abrasive, etc. The obtained powders may assume also applications as a thermally stable substitute for the commonly used transition alumina powders, which need further investigations in future studies.

scholarly journals Research on the Influence of the Manufacturing Process Conditions of Iron Sintered with the Addition of Layered Lubricating Materials on its Selected Properties

Materials ◽  
2020 ◽  
Vol 13 (21) ◽  
pp. 4782
Author(s):  
Wieslaw Urbaniak ◽  
Tomasz Majewski ◽  
Ryszard Wozniak ◽  
Judyta Sienkiewicz ◽  
Jozef Kubik ◽  
...  
Keyword(s):  
Particle Size ◽  
Boron Nitride ◽  
Coefficient Of Friction ◽  
Tribological Properties ◽  
Hexagonal Boron Nitride ◽  
Average Particle Size ◽  
Layered Materials ◽  
Process Conditions ◽  
Average Particle ◽  
Average Grain Size

The purpose of the conducted experiments was to test the selected properties of materials intended for porous sintered bearings containing layered materials in the form of powders with an average particle size of 0.5–1.5 μm, with very good tribological properties. The subject of the research was a sinter based on iron powder with the addition of layered materials; molybdenum disulfide MoS2 (average particle size 1.5 μm), tungsten disulfide WS2 (average particle size 0.6 μm), hexagonal boron nitride, h-BN (average particle size 0.5 and 1.5 μm) with two different porosities. The article presents the results of density and porosity tests, compressive strength, metallographic and tribological tests and the assessment of changes in the surface condition occurring during the long storage period. The use of layered additives allows for an approximately 20% lower coefficient of friction. In the case of sulfides, the technological process of pressing 250 MPa, 350 MPa, and sintering at a temperature of 1120 °C allows us to obtain a material with good strength and tribological properties, better than in the case of h-BN. However, the main problem is the appearance of elements from the decomposition of sulfide compounds in the material matrix, which results in rapid material degradation. In hexagonal boron nitride, such disintegration under these conditions does not occur; the material as observed does not degrade. In this case, the material is characterized by lower hardness, resulting from a different behavior of hexagonal boron nitride in the pressing and sintering process; in this case, pressing at a pressure of 350 MPa seems to be too low. However, taking into account that even with these technological parameters, the obtained material containing 2.5% h-BN with an average grain size of 1.5 μm allowed obtaining a coefficient of friction at the level of 0.41, which, with very good material durability, seems to be very positive news before further tests.

scholarly journals Production of fine zinc borate in industrial scale

2012 ◽  
Vol 18 (4-1) ◽  
pp. 547-553 ◽  
Author(s):  
Gaye Çakal
Keyword(s):  
Particle Size ◽  
Average Particle Size ◽  
Scale Up ◽  
Lag Time ◽  
Pilot Scale ◽  
Zinc Borate ◽  
Industrial Scale ◽  
Process Conditions ◽  
Average Particle ◽  
Scale Production

In this study, zinc borate production in an industrial scale batch reactor was carried out at the optimum process conditions determined in the previous studies performed at the laboratory and pilot scale reactors. The production was done via the heterogeneous reaction of boric acid and zinc oxide. The samples were characterized by chemical analysis, XRD, TGA, SEM and particle size distribution. The final product which was obtained in the industrial scale reactor was 2ZnO.3B2O3.3H2O. The kinetic data for the zinc borate production reaction fit to a modified logistic model where the lag time was taken into account. As observed, the reaction time was influenced by scaling up. There was a lag time of 120 min for the industrial scale production and thus, the reaction completion time was 70 min longer compared to pilot scale. It should be emphasized that the specific reaction rate, k; as well as the average particle size and the hydration temperature of zinc borate are unaffected by scale up.

Determination of grinding parameters of fenugreek seed

1970 ◽  
Vol 26 (1) ◽  
pp. 16 ◽  
Author(s):  
S Balasubramanian ◽  
Rajkumar Rajkumar ◽  
K K Singh
Keyword(s):  
Particle Size ◽  
Energy Consumption ◽  
Moisture Content ◽  
Specific Energy ◽  
Feed Rate ◽  
Average Particle Size ◽  
Specific Energy Consumption ◽  
Average Particle ◽  
Fenugreek Seeds ◽  
Fenugreek Seed

Experiment to identify ambient grinding conditions and energy consumed was conducted for fenugreek. Fenugreek seeds at three moisture content (5.1%, 11.5% and 17.3%, d.b.) were ground using a micro pulverizer hammer mill with different grinding screen openings (0.5, 1.0 and 1.5 mm) and feed rate (8, 16 and 24 kg h-1) at 3000 rpm. Physical properties of fenugreek seeds were also determined. Specific energy consumptions were found to decrease from 204.67 to 23.09 kJ kg-1 for increasing levels of feed rate and grinder screen openings. On the other hand specific energy consumption increased with increasing moisture content. The highest specific energy consumption was recorded for 17.3% moisture content and 8 kg h-1 feed rate with 0.5 mm screen opening. Average particle size decreased from 1.06 to 0.39 mm with increase of moisture content and grinder screen opening. It has been observed that the average particle size was minimum at 0.5 mm screen opening and 8 kg h-1 feed rate at lower moisture content. Bond’s work index and Kick’s constant were found to increase from 8.97 to 950.92 kWh kg-1 and 0.932 to 78.851 kWh kg-1 with the increase of moisture content, feed rate and grinder screen opening, respectively. Size reduction ratio and grinding effectiveness of fenugreek seed were found to decrease from 4.11 to 1.61 and 0.0118 to 0.0018 with the increase of moisture content, feed rate and grinder screen opening, respectively. The loose and compact bulk densities varied from 219.2 to 719.4 kg m-3 and 137.3 to 736.2 kg m-3, respectively.  

Formulating SLN and NLC as Innovative Drug Delivery Systems for Non-Invasive Routes of Drug Administration

2020 ◽  
Vol 27 (22) ◽  
pp. 3623-3656 ◽  
Author(s):  
Bruno Fonseca-Santos ◽  
Patrícia Bento Silva ◽  
Roberta Balansin Rigon ◽  
Mariana Rillo Sato ◽  
Marlus Chorilli
Keyword(s):  
Drug Delivery ◽  
Particle Size ◽  
Drug Release ◽  
Drug Loading ◽  
Average Particle Size ◽  
Delivery Systems ◽  
Average Particle ◽  
Minor Importance ◽  
Routes Of Administration ◽  
Non Invasive

Colloidal carriers diverge depending on their composition, ability to incorporate drugs and applicability, but the common feature is the small average particle size. Among the carriers with the potential nanostructured drug delivery application there are SLN and NLC. These nanostructured systems consist of complex lipids and highly purified mixtures of glycerides having varying particle size. Also, these systems have shown physical stability, protection capacity of unstable drugs, release control ability, excellent tolerability, possibility of vectorization, and no reported production problems related to large-scale. Several production procedures can be applied to achieve high association efficiency between the bioactive and the carrier, depending on the physicochemical properties of both, as well as on the production procedure applied. The whole set of unique advantages such as enhanced drug loading capacity, prevention of drug expulsion, leads to more flexibility for modulation of drug release and makes Lipid-based nanocarriers (LNCs) versatile delivery system for various routes of administration. The route of administration has a significant impact on the therapeutic outcome of a drug. Thus, the non-invasive routes, which were of minor importance as parts of drug delivery in the past, have assumed added importance drugs, proteins, peptides and biopharmaceuticals drug delivery and these include nasal, buccal, vaginal and transdermal routes. The objective of this paper is to present the state of the art concerning the application of the lipid nanocarriers designated for non-invasive routes of administration. In this manner, this review presents an innovative technological platform to develop nanostructured delivery systems with great versatility of application in non-invasive routes of administration and targeting drug release.

Azithromycin nanosuspension preparation using evaporative precipitation into aqueous solution (EPAS) method and its comparative dissolution study

2020 ◽  
Vol 17 ◽  
Author(s):  
Mohammad Hossain Shariare ◽  
Tonmoy Kumar Mondal ◽  
Hani Alothaid ◽  
Md. Didaruzzaman Sohel ◽  
MD Wadud ◽  
...  
Keyword(s):  
Aqueous Solution ◽  
Particle Size ◽  
Dissolution Rate ◽  
Average Particle Size ◽  
Scale Up ◽  
Average Particle ◽  
Total Drug ◽  
Residual Solvent ◽  
Dissolution Study ◽  
Drug Content

Aim: EPAS (evaporative precipitation into aqueous solution) was used in the current studies to prepare azithromycin nanosuspensions and investigate the physicochemical characteristics for the nanosuspension batches with the aim of enhancing the dissolution rate of the nanopreparation to improve bioavailability. Methods: EPAS method used in this study for preparing azithromycin nanosuspension was achieved through developing an in-house instrumentation method. Particle size distribution was measured using Zetasizer Nano S without sample dilution. Dissolved azithromycin nanosuspensions were also compared with raw azithromycin powder and commercially available products. Total drug content of nanosuspension batches were measured using an Ultra-Performance Liquid Chromatography (UPLC) system with Photodiode Array (PDA) detector while residual solvent was measured using gas chromatography (GC). Results: The average particle size of azithromycin nanosuspension was 447.2 nm and total drug content was measured to be 97.81% upon recovery. Dissolution study data showed significant increase in dissolution rate for nanosuspension batch when compared to raw azithromycin and commercial version (microsuspension). The residual solvent found for azithromycin nanosuspension is 0.000098023 mg/ mL or 98.023 ppb. Conclusion: EPAS was successfully used to prepare azithromycin nanoparticles that exhibited significantly enhanced dissolution rate. Further studies are required to scale up the process and determine long term stability of the nanoparticles.

scholarly journals Evaluation of the Effects of Filler Fineness on the Properties of an Epoxy Asphalt Mixture

Materials ◽  
2021 ◽  
Vol 14 (8) ◽  
pp. 2003
Author(s):  
Wei Xu ◽  
Jintao Wei ◽  
Zhengxiong Chen ◽  
Feng Wang ◽  
Jian Zhao
Keyword(s):  
Particle Size ◽  
Average Particle Size ◽  
Asphalt Mixture ◽  
Average Particle ◽  
Fine Dust ◽  
Bonding Structure ◽  
Epoxy Asphalt ◽  
Mineral Powder ◽  
Marshall Stability ◽  
Mixture Sample

The type and fineness of a filler significantly affect the performance of an asphalt mixture. There is a lack of specific research on the effects of filler fineness and dust from aggregates on the properties of epoxy asphalt (EA) mixtures. The effects of aggregate dust and mineral powder on the properties of an EA mixture were evaluated. These filler were tested to determine their fineness, specific surface area and mineral composition. The effects of these fillers on the EA mastic sample and mixture were evaluated. The morphology of the EA mastic samples was analyzed using scanning electron microscopy (SEM). The effects of the fillers on the Marshall stability, tensile strength and fatigue performance of the EA mixture were evaluated. The dust from the aggregates exhibited an even particle size distribution, and its average particle size was approximately 20% of that of the mineral powder. The SEM microanalysis showed that the EA mastic sample containing relatively fine dust formed a tight and dense interfacial bonding structure with the aggregate. The EA mixture sample containing filler composed of dust from aggregate had a significantly higher strength and longer fatigue life than that of the EA sample containing filler composed of mineral powder.

scholarly journals Surface Activity of Humic Acid and Its Sub-Fractions from Forest Soil

2021 ◽  
Vol 13 (15) ◽  
pp. 8122
Author(s):  
Shijie Tian ◽  
Weiqiang Tan ◽  
Xinyuan Wang ◽  
Tingting Li ◽  
Fanhao Song ◽  
...  
Keyword(s):  
Surface Tension ◽  
Particle Size ◽  
Humic Acid ◽  
Forest Soil ◽  
Surface Activity ◽  
Self Assembly ◽  
Average Particle Size ◽  
Gaussian Model ◽  
Exponential Model ◽  
Average Particle

Surface activity of humic acid (HA) and its six sub-fractions isolated from forest soil were characterized by surface tension measurements, dynamic light scattering, and laser doppler electrophoresis. The surface tension of HA and its sub-fractions reduced from 72.4 mN·m−1 to 36.8 mN·m−1 in exponential model with the increasing concentration from 0 to 2000 mg·L−1. The critical micelle concentration (CMC) and Z-average particle size ranged from 216–1024 mg·L−1 and 108.2–186.9 nm for HA and its sub-fractions, respectively. The CMC have related with alkyl C, O-alkyl C, aromatic C, and carbonyl C (p < 0.05), respectively, and could be predicted with the multiple linear regression equation of CMC, CMC = 18896 − 6.9 × C-296 × alkyl C-331 × aromatic C-17019 × H/C + 4054 × HB/HI (p < 0.05). The maximum particle size was 5000 nm after filtered by a membrane with pore size of 450 nm, indicating HA and its sub-fractions could progressed self-assembly at pH 6.86. The aggregate sizes of number-base particle size distributions were mainly in six clusters including 2 ± 1 nm, 5 ± 2 nm, 10 ± 3 nm, 21 ± 8 nm, 40 ± 10 nm, and >50 nm analyzed by Gaussian model that maybe due to the inconsistency of the components and structures of the HA sub-fractions, requiring further study. It is significance to explore the surface activity of HA and its sub-fractions, which is helpful to clarify the environmental behavior of HA.

Sign in / Sign up

Export Citation Format

Share Document